Biocompatible Diselenide-Containing Protein Hydrogels with Effective Visible-Light-Initiated Self-Healing Properties.

ABSTRACT: Smart hydrogels are typical functional soft materials, but their functional and mechanical properties are compromised upon micro- or macro-mechanical damage. In contrast, hydrogels with self-healing properties overcome this limitation. Herein, a dual dynamic bind, cross-linked, self-healing protein hydrogel is prepared, based on Schiff base bonds and diselenide bonds. The Schiff base bond is a typical dynamic covalent bond and the diselenide bond is an emerging dynamic covalent bond with a visible light response, which gives the resulting hydrogel a dual response in visible light and a desirable self-healing ability. The diselenide-containing protein hydrogels were biocompatible due to the fact that their main component was protein. In addition, the hydrogels loaded with glucose oxidase (GOx) could be transformed into sols in glucose solution due to the sensitive response of the diselenide bonds to the generated hydrogen peroxide (H₂O₂) by enzymatic catalysis. This work demonstrated a diselenide-containing protein hydrogel that could efficiently self-heal up to nearly 100% without compromising their mechanical properties under visible light at room temperature.

SUBMITTER: Liu S

PROVIDER: S-EPMC8707953 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:The mechanical properties of synthetic hydrogels traditionally have been controlled with the concentration, molecular weight, or stoichiometry of the macromolecular building blocks used for hydrogel formation. Recently, the rate of formation has been recognized as an important and effective handle for controlling the mechanical properties of these water-swollen polymer networks, owing to differences in network heterogeneity (e.g., defects) that arise based on the rate of gelation. Building upon this, in this work, we investigate a rate-based approach for controlling mechanical properties of hydrogels both initially and temporally with light. Specifically, synthetic hydrogels are formed with visible light-initiated thiol-ene 'click' chemistry (PEG-8-norbornene, dithiol linker, LAP photoinitiator with LED lamp centered at 455 nm), using irradiation conditions to control the rate of formation and the mechanical properties of the resulting hydrogels. Further, defects within these hydrogels were subsequently exploited for temporal modulation of mechanical properties with a secondary cure using low doses of long wavelength UV light (365 nm). The elasticity of the hydrogel, as measured with Young's and shear moduli, was observed to increase with increasing light intensity and concentration of photoinitiator used for hydrogel formation. In situ measurements of end group conversion during hydrogel formation with magic angle spinning (MAS 1H NMR) correlated with these mechanical properties measurements, suggesting that both dangling end groups and looping contribute to the observed mechanical properties. Dangling end groups provide reactive handles for temporal stiffening of hydrogels with a secondary UV-initiated thiol-ene polymerization, where an increase in Young's modulus by a factor of ~ 2.5x was observed. These studies demonstrate how the rate of photopolymerization can be tuned with irradiation wavelength, intensity, and time to control the properties of synthetic hydrogels, which may prove useful in a variety of applications from coatings to biomaterials for controlled cell culture and regenerative medicine.

Dataset Information

Biocompatible Diselenide-Containing Protein Hydrogels with Effective Visible-Light-Initiated Self-Healing Properties.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets