Structural and Electrochemical Properties of Physically and Chemically Activated Carbon Nanoparticles for Supercapacitors.

ABSTRACT: The demand for supercapacitors has been high during the integration of renewable energy devices into the electrical grid. Although activated carbon materials have been widely utilized as supercapacitor electrodes, the need for economic and sustainable processes to extract and activate carbon nanomaterials is still crucial. In this work, the biomass waste of date palm fronds is converted to a hierarchical porous nanostructure of activated carbon using simple ball-milling and sonication methods. Chemical and physical activation agents of NaOH and CO₂, receptively, were applied on two samples separately. Compared with the specific surface area of 603.5 m²/g for the CO₂-activated carbon, the NaOH-activated carbon shows a higher specific surface area of 1011 m²/g with a finer nanostructure. Their structural and electrochemical properties are functionalized to enhance electrode-electrolyte contact, ion diffusion, charge accumulation, and redox reactions. Consequently, when used as electrodes in an H₂SO₄ electrolyte for supercapacitors, the NaOH-activated carbon exhibits an almost two-fold higher specific capacitance (125.9 vs. 56.8 F/g) than that of the CO₂-activated carbon at the same current density of 1 A/g. Moreover, using carbon cloth as a current collector provides mechanical flexibility to our electrodes. Our practical approach produces cost-effective, eco-friendly, and flexible activated carbon electrodes with a hierarchical porous nanostructure for supercapacitor applications.

SUBMITTER: Alhebshi NA

PROVIDER: S-EPMC8746510 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Electrochemical and Capacitive Properties of Carbon Dots/Reduced Graphene Oxide Supercapacitors.

Project description:There is much recent interest in graphene-based composite electrode materials because of their excellent mechanical strengths, high electron mobilities, and large specific surface areas. These materials are good candidates for applications in supercapacitors. In this work, a new graphene-based electrode material for supercapacitors was fabricated by anchoring carbon dots (CDs) on reduced graphene oxide (rGO). The capacitive properties of electrodes in aqueous electrolytes were systematically studied by galvanostatic charge-discharge measurements, cyclic voltammetry, and electrochemical impedance spectroscopy. The capacitance of rGO was improved when an appropriate amount of CDs were added to the material. The CD/rGO electrode exhibited a good reversibility, excellent rate capability, fast charge transfer, and high specific capacitance in 1 M H₂SO₄. Its capacitance was as high as 211.9 F/g at a current density of 0.5 A/g. This capacitance was 74.3% higher than that of a pristine rGO electrode (121.6 F/g), and the capacitance of the CD/rGO electrode retained 92.8% of its original value after 1000 cycles at a CDs-to-rGO ratio of 5:1.

| S-EPMC5245759 | biostudies-literature

Structural Properties of Chemically Functionalized Carbon Nanotube Thin Films.

Project description:Buckypapers are thin sheets of randomly entangled carbon nanotubes, which are highly porous networks. They are strong candidates for a number of applications, such as reinforcing materials for composites. In this work, buckypapers were produced from multiwall carbon nanotubes, pre-treated by two different chemical processes, either an oxidation or an epoxidation reaction. Properties, such as porosity, the mechanical and electrical response are investigated. It was found that the chemical pretreatment of carbon nanotubes strongly affects the structural properties of the buckypapers and, consecutively, their mechanical and electrical performance.

| S-EPMC5458945 | biostudies-other

Effects of Precursors and Carbon Nanotubes on Electrochemical Properties of Electrospun Nickel Oxide Nanofibers-Based Supercapacitors.

Project description:Supercapacitors have been considered as one of the main energy storage devices. Recently, electrospun nanofibers have served as promising supercapacitor electrodes because of their high surface area, high porosity, flexibility, and resistance to aggregation. Here, we investigate the effects of electrospinning parameters and nickel precursors on the nanostructure of electrospun nickel oxide (NiO), as well as on their electrochemical performance as supercapacitor electrodes. In contrast to the case of using nickel nitrate, increasing the nickel acetate molar concentration maintains the flexible fibrous sheet morphology of the as-spun sample during the polycondensation and calcination of NiO. As a result, our flexible electrode of NiO nanofibers derived from nickel acetate (NiO-A) exhibits much better electrochemical performance values than that of nickel nitrate-derived NiO. To further improve the electrochemical storage performance, we combined NiO-A nanofibers with single-walled carbon nanotubes (CNTs) as a hybrid electrode. In both half-cell and full-cell configurations, the hybrid electrode displayed a higher and steadier areal capacitance than the NiO-A nanofibers because of the synergetic effect between the NiO-A nanofibers and CNTs. Altogether, this work demonstrates the potency of the hybrid electrodes combined with the electrospun NiO-A nanofibers and CNTs for supercapacitor applications.

| S-EPMC8465373 | biostudies-literature

Polypyrrole/Carbon Nanotube Freestanding Electrode with Excellent Electrochemical Properties for High-Performance All-Solid-State Supercapacitors.

Project description:In this study, a facile and environmentally friendly method was used to prepare a freestanding supercapacitor electrode displaying excellent areal capacitance and good cycle life performance. First, we prepared polypyrrole nanoparticles (PPyNP) through a simple in situ chemical polymerization using the plant-derived material curcumin as a bioavailable template. A PPyNP/f-CNT freestanding composite electrode of high mass loading (ca. 14 mg cm-2) was prepared after blending the mixtures of the prepared PPyNP and functionalized CNTs (f-CNTs). The performance of the as-prepared material as a supercapacitor electrode was evaluated in a three-electrode setup using aqueous 1 M H2SO4 as the electrolyte. The PPyNP/f-CNT freestanding composite electrode exhibited a high areal capacitance of 4585 mF cm-2 and a corresponding volumetric capacitance of 176.35 F cm-3 at a current density of 2 mA cm-2. A symmetric all-solid-state supercapacitor assembled using two identical pieces of PPyNP/f-CNT composite electrodes exhibited maximum areal energy and power density of 129.24 μW h cm-2 and 12.5 mW cm-2, respectively. Besides, this supercapacitor device exhibited good cycle life performance, with 79.03% capacitance retention after 10,000 charge/discharge cycles. These results suggest practical applications for these PPyNP/f-CNT freestanding composite electrode-based symmetric all-solid-state supercapacitors.

| S-EPMC7114166 | biostudies-literature

Composite Structural Supercapacitors: High-Performance Carbon Nanotube Supercapacitors through Ionic Liquid Localisation.

Project description:Composite structural supercapacitors (SSC) are an attractive technology for aerospace vehicles; however, maintaining strength whilst adding energy storage to composite structures has been difficult. Here, SSCs were manufactured using aerospace-grade composite materials and CNT mat electrodes. A new design methodology was explored where the supercapacitor electrolyte was localised within the composite structure, achieving good electrochemical performance within the active region, whilst maintaining excellent mechanical performance elsewhere. The morphologies of these localised SSC designs were characterised with synchrotron X-ray fluorescence microscopy and synchrotron X-ray micro-computed tomography and could be directly correlated with both electrochemical and mechanical performance. One configuration used an ionogel with an ionic liquid (IL) electrolyte, which assisted localisation and achieved 2640 mW h kg-1 at 8.37 W kg-1 with a corresponding short beam shear (SBS) strength of 71.5 MPa in the active area. A separate configuration with only IL electrolyte achieved 758 mW h kg-1 at 7.87 W kg-1 with SBS strength of 106 MPa in the active area. Both configurations provide a combined energy and strength superior to results previously reported in the literature for composite SSCs.

| S-EPMC9330893 | biostudies-literature

Electrochemical properties of an activated carbon xerogel monolith from resorcinol-formaldehyde for supercapacitor electrode applications.

Project description:Activated carbon xerogel monoliths were prepared from resorcinol and formaldehyde via a catalyst-free and template-free hydrothermal polycondensation reaction, followed by pyrolysis and activation. The ratio of resorcinol (R) to distilled water (W) was varied to afford an interconnected pore structure with controlled pore size, while the pyrolysis temperature was optimized to give high specific surface area. Activation was carried out at 700 °C after soaking the samples in 6 M KOH aqueous solution. The same process, called "heat treatment", was also carried out without soaking in KOH for comparison. The weight loss upon pyrolysis, activation and heat treatment and the weight gain via KOH soaking were measured. Field emission scanning electron microscopy (FE-SEM), X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, X-ray diffraction (XRD), thermogravimetric analysis (TGA) and an N2 sorption instrument were utilized for characterization. Additionally, electrochemical properties were evaluated using cyclic voltammetry (CV), galvanostatic charge-discharge (GCD) and electrochemical impedance spectroscopy (EIS) with a 3-electrode system, while a 2-electrode system was also employed for selected samples. The highest specific capacitance of 323 F g-1 via GCD at 1 A g-1 was obtained at the R/W ratio of 45 and with 500 °C pyrolysis. In addition, this sample also exhibited 89.4% retention at 20 A g-1 in the current density variation and 100% retention in 5000 cycling tests.

| S-EPMC9042302 | biostudies-literature

Self-Discharge Processes in Symmetrical Supercapacitors with Activated Carbon Electrodes.

Project description:The self-discharge of an electric double-layer capacitor with composite activated carbon electrodes and aqueous electrolyte (1 M MgSO4) was studied in detail. Under a long-term potentiostatic charge (stabilization), a decrease in the discharge capacity was observed in the region of voltages exceeding 0.8 V. The self-discharge process consists of two phases. In the initial phase, the cell voltage drop is due to the charge redistribution inside electrodes. During the main phase, the charge transfer between the electrodes determines the voltage drop. The optimal stabilization time of the self-discharge was found to be 50 min at 1.4 V. Hydrophilization of the negative electrode occurred during long-term polarization due to the formation of epoxy functional groups.

| S-EPMC10573834 | biostudies-literature

Deciphering the Structural, Textural, and Electrochemical Properties of Activated BN-Doped Spherical Carbons.

Project description:In this study, the effect of K₂CO₃ activation on the structural, textural, and electrochemical properties of carbon spheres (CSs) and boron and nitrogen co-doped carbon spheres (BN-CSs) was evaluated. Activation of the CSs and BN-CSs by K₂CO₃ resulted in increased specific surface areas and ID/IG ratios. From the X-ray photoelectron spectroscopy (XPS) results, the BN-CSs comprised of 64% pyridinic-N, 24% pyrrolic-N and 7% graphitic-N whereas the activated BN-CSs had 19% pyridinic-N, 40% pyrrolic-N and 22% graphitic-N displaying the effect of activation on the type of N configurations in BN-CSs. A possible BN-co-doping and activation mechanism for the BN-CSs is proposed. Electrochemical analysis of the electrode materials revealed that BN doping, carbon morphology, structure, and porosity played a crucial role in enhancing the capacitive behavior of the CSs. As a proof of concept, a symmetric device comprising the activated BN-CSs displayed a specific power of 800 W kg-1 at a specific current of 1 A g-1 within an operating cell potential of 1.6 V in a 3 M KNO₃ electrolyte. The study illustrated for the first time the role of K₂CO₃ activation in influencing the physical and surface properties of template-free activated BN-CSs as potential electrode materials for energy storage systems.

| S-EPMC6474088 | biostudies-other

Flax-Derived Carbon: A Highly Durable Electrode Material for Electrochemical Double-Layer Supercapacitors.

Project description:Owing to their low cost, good performance, and high lifetime stability, activated carbons (ACs) with a large surface area rank among the most popular materials deployed in commercially available electrochemical double-layer (EDLC) capacitors. Here, we report a simple two-step synthetic procedure for the preparation of activated carbon from natural flax. Such ACs possess a very high specific surface area (1649 m2 g-1) accompanied by a microporous structure with the size of pores below 2 nm. These features are behind the extraordinary electrochemical performance of flax-derived ACs in terms of their high values of specific capacitance (500 F g-1 at a current density of 0.25 A g-1 in the three-electrode setup and 189 F g-1 at a current density of 0.5 A g-1 in two-electrode setup.), high-rate stability, and outstanding lifetime capability (85% retention after 150,000 charging/discharging cycles recorded at the high current density of 5 A g-1). These findings demonstrate that flax-based ACs have more than competitive potential compared to standard and commercially available activated carbons.

| S-EPMC8466636 | biostudies-literature

Structural and Electrochemical Evolution of Water Hyacinth-Derived Activated Carbon with Gamma Pretreatment for Supercapacitor Applications

Project description: Not available

| S-EPMC11242469 | biostudies-literature