Fermi-Level Modulation of Chemical Vapor Deposition-Grown Monolayer Graphene via Nanoparticles to Macromolecular Dopants.

ABSTRACT: It is critical to modulate the Fermi level of graphene for the development of high-performance electronic and optoelectronic devices. Here, we have demonstrated the modulation of the Fermi level of chemical vapor deposition (CVD)-grown monolayer graphene (MLG) via doping with nanoparticles to macromolecules such as titanium dioxide nanoparticles (TiO₂ NPs), nitric acid (HNO₃), octadecyltrimethoxysilane (OTS) self-assembled monolayer (SAM), and poly(3,4-ethylene-dioxythiophene):polystyrene sulfonate (PEDOT:PSS). The electronic properties of pristine and doped graphene samples were investigated by Raman spectroscopy and electrical transport measurements. The right shifting of G and 2D peaks and reduction in 2D to G peak intensity ratio (I _2D/I _G) assured that the dopants induced a p-type doping effect. Upon doping, the shifting of the Dirac point towards positive voltage validates the increment of the hole concentration in graphene and thus downward shift of the Fermi level. More importantly, the combination of HNO₃/TiO₂ NP doping on graphene yields a substantially larger change in the Fermi level of MLG. Our study may be useful for the development of graphene-based high-performance flexible electronic devices.

SUBMITTER: Singh AK

PROVIDER: S-EPMC8756573 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Vacuum level dependent photoluminescence in chemical vapor deposition-grown monolayer MoS 2.

Project description:The stronger photoluminescence (PL) in chemical vapor deposition (CVD) grown monolayer MoS2 has been attributed to its high crystal quality compared with that in mechanically exfoliated (ME) crystal, which is contrary to the cognition that the ME crystal usually have better crystal quality than that of CVD grown one and it is expected with a better optical quality. In this report, the reason of abnormally strong PL spectra in CVD grown monolayer crystal is systematically investigated by studying the in-situ opto-electrical exploration at various environments for both of CVD and ME samples. High resolution transmission electron microscopy is used to investigate their crystal qualities. The stronger PL in CVD grown crystal is due to the high p-doping effect of adsorbates induced rebalance of exciton/trion emission. The first principle calculations are carried out to explore the interaction between adsorbates in ambient and defects sites in MoS2, which is consistent to the experimental phenomenon and further confirm our proposed mechanisms.

| S-EPMC5711928 | biostudies-literature

Top-gated chemical vapor deposition grown graphene transistors with current saturation.

Project description:Graphene transistors are of considerable interest for radio frequency (rf) applications. In general, transistors with large transconductance and drain current saturation are desirable for rf performance, which is however nontrivial to achieve in graphene transistors. Here we report high-performance top-gated graphene transistors based on chemical vapor deposition (CVD) grown graphene with large transconductance and drain current saturation. The graphene transistors were fabricated with evaporated high dielectric constant material (HfO(2)) as the top-gate dielectrics. Length scaling studies of the transistors with channel length from 5.6 ?m to 100 nm show that complete current saturation can be achieved in 5.6 ?m devices and the saturation characteristics degrade as the channel length shrinks down to the 100-300 nm regime. The drain current saturation was primarily attributed to drain bias induced shift of the Dirac points. With the selective deposition of HfO(2) gate dielectrics, we have further demonstrated a simple scheme to realize a 300 nm channel length graphene transistors with self-aligned source-drain electrodes to achieve the highest transconductance of 250 ?S/?m reported in CVD graphene to date.

| S-EPMC3236244 | biostudies-literature

High Performance Hall Sensors Built on Chemical Vapor Deposition-Grown Bilayer Graphene.

Project description:Graphene has been considered as an excellent channel material for constructing magnetic sensors or Hall elements with high sensitivity and linearity. Compared to intensively reported graphene Hall elements (GHEs) fabricated on monolayer graphene, the exploration on bilayer graphene-based Hall elements is very rare. Here, we first investigate the performance and potential of Hall elements built on chemical vapor deposition-grown bilayer graphene. Without applying any gate voltage, the bilayer GHEs exhibit a typical voltage sensitivity of 119 mV/VT and current sensitivity of 397 V/AT, which are higher than those in the monolayer GHEs, indicating the better performance in practical applications. Moreover, the bilayer GHEs present obviously lower noise and then the minimum detection magnetic field compared to the monolayer ones. Hall elements built on bilayer graphene show certain unique advantages and can be used as an important supplement to mainstreaming monolayer GHEs.

| S-EPMC9330160 | biostudies-literature

Monolayer Single-Crystal 1T'-MoTe2 Grown by Chemical Vapor Deposition Exhibits Weak Antilocalization Effect.

Project description:Growth of transition metal dichalcogenide (TMD) monolayers is of interest due to their unique electrical and optical properties. Films in the 2H and 1T phases have been widely studied but monolayers of some 1T'-TMDs are predicted to be large-gap quantum spin Hall insulators, suitable for innovative transistor structures that can be switched via a topological phase transition rather than conventional carrier depletion [ Qian et al. Science 2014 , 346 , 1344 - 1347 ]. Here we detail a reproducible method for chemical vapor deposition of monolayer, single-crystal flakes of 1T'-MoTe2. Atomic force microscopy, Raman spectroscopy, X-ray photoelectron spectroscopy, and transmission electron microscopy confirm the composition and structure of MoTe2 flakes. Variable temperature magnetotransport shows weak antilocalization at low temperatures, an effect seen in topological insulators and evidence of strong spin-orbit coupling. Our approach provides a pathway to systematic investigation of monolayer, single-crystal 1T'-MoTe2 and implementation in next-generation nanoelectronic devices.

| S-EPMC5893939 | biostudies-literature

Low-Humidity Sensing Properties of Multi-Layered Graphene Grown by Chemical Vapor Deposition.

Project description:Humidity sensing is fundamental in some applications, as humidity can be a strong interferent in the detection of analytes under environmental conditions. Ideally, materials sensitive or insensitive towards humidity are strongly needed for the sensors used in the first or second case, respectively. We present here the sensing properties of multi-layered graphene (MLG) upon exposure to different levels of relative humidity. We synthesize MLG by chemical vapor deposition, as shown by Raman spectroscopy, Atomic Force Microscopy (AFM) and Scanning Electron Microscopy (SEM). Through an MLG-based resistor, we show that MLG is scarcely sensitive to humidity in the range 30%-70%, determining current variations in the range of 0.005%/%relative humidity (RH) well below the variation induced by other analytes. These findings, due to the morphological properties of MLG, suggest that defective MLG is the ideal sensing material to implement in gas sensors operating both at room temperature and humid conditions.

| S-EPMC7313702 | biostudies-literature

Precisely aligned graphene grown on hexagonal boron nitride by catalyst free chemical vapor deposition.

Project description:To grow precisely aligned graphene on h-BN without metal catalyst is extremely important, which allows for intriguing physical properties and devices of graphene/h-BN hetero-structure to be studied in a controllable manner. In this report, such hetero-structures were fabricated and investigated by atomic resolution scanning probe microscopy. Moiré patterns are observed and the sensitivity of moiré interferometry proves that the graphene grains can align precisely with the underlying h-BN lattice within an error of less than 0.05°. The occurrence of moiré pattern clearly indicates that the graphene locks into h-BN via van der Waals epitaxy with its interfacial stress greatly released. It is worthy to note that the edges of the graphene grains are primarily oriented along the armchair direction. The field effect mobility in such graphene flakes exceeds 20,000 cm(2)·V(-1)·s(-1) at ambient condition. This work opens the door of atomic engineering of graphene on h-BN, and sheds light on fundamental research as well as electronic applications based on graphene/h-BN hetero-structure.

| S-EPMC3773621 | biostudies-literature

Data for direct chemical deposition of PbS on chemical vapor deposition grown-graphene for high performance photovoltaic infrared photo-detectors.

Project description:Over the past decades, graphene has attracted much attention from the scientific community due to its broad applications in the optoelectronics industries [1]. Owing to graphene's high transmission and high electrical conductivity, diverse functional materials/graphene hybridized heterostructures and interfaces are under extensive investigation to satisfy the increasing interest in the need for bendable, flexible and high performance optoelectronic devices [2]. Due to the good atomic lattice structure of graphene, varying heterostructures have been formed by depositing different functional materials directly on graphene [3], [4], [5]. We fabricated a vertical photovoltaic type G/PbS/Ti device by making use of the Ti/PbS Schottky junction and discussed the photocurrent transient characteristics. Lead sulfide (PbS) was deposited directly on large area CVD (Chemical vapor deposition) graphene by CBD (Chemical bath deposition). Temperature dependent photocurrent spectra of our G/PbS/Ti photovoltaic devices were measured by a Fourier transformed infrared (FTIR) set-up. In this paper, we present the experimental procedures and the raw experimental data for the direct chemical deposition of PbS on CVD-graphene for high performance photovoltaic infrared photo-detectors. The manuscript is already available [6].

| S-EPMC7494446 | biostudies-literature

Real-space imaging of acoustic plasmons in large-area graphene grown by chemical vapor deposition.

Project description:An acoustic plasmon mode in a graphene-dielectric-metal structure has recently been spotlighted as a superior platform for strong light-matter interaction. It originates from the coupling of graphene plasmon with its mirror image and exhibits the largest field confinement in the limit of a sub-nm-thick dielectric. Although recently detected in the far-field regime, optical near-fields of this mode are yet to be observed and characterized. Here, we demonstrate a direct optical probing of the plasmonic fields reflected by the edges of graphene via near-field scattering microscope, revealing a relatively small propagation loss of the mid-infrared acoustic plasmons in our devices that allows for their real-space mapping at ambient conditions even with unprotected, large-area graphene grown by chemical vapor deposition. We show an acoustic plasmon mode that is twice as confined and has 1.4 times higher figure of merit in terms of the normalized propagation length compared to the graphene surface plasmon under similar conditions. We also investigate the behavior of the acoustic graphene plasmons in a periodic array of gold nanoribbons. Our results highlight the promise of acoustic plasmons for graphene-based optoelectronics and sensing applications.

| S-EPMC7895983 | biostudies-literature

Large-area high-throughput synthesis of monolayer graphene sheet by Hot Filament Thermal Chemical Vapor Deposition.

Project description:We report hot filament thermal CVD (HFTCVD) as a new hybrid of hot filament and thermal CVD and demonstrate its feasibility by producing high quality large area strictly monolayer graphene films on Cu substrates. Gradient in gas composition and flow rate that arises due to smart placement of the substrate inside the Ta filament wound alumina tube accompanied by radical formation on Ta due to precracking coupled with substrate mediated physicochemical processes like diffusion, polymerization etc., led to graphene growth. We further confirmed our mechanistic hypothesis by depositing graphene on Ni and SiO(2)/Si substrates. HFTCVD can be further extended to dope graphene with various heteroatoms (H, N, and B, etc.,), combine with functional materials (diamond, carbon nanotubes etc.,) and can be extended to all other materials (Si, SiO(2), SiC etc.,) and processes (initiator polymerization, TFT processing) possible by HFCVD and thermal CVD.

| S-EPMC3448070 | biostudies-literature

Origin of the relatively low transport mobility of graphene grown through chemical vapor deposition.

Project description:The reasons for the relatively low transport mobility of graphene grown through chemical vapor deposition (CVD-G), which include point defect, surface contamination, and line defect, were analyzed in the current study. A series of control experiments demonstrated that the determinant factor for the low transport mobility of CVD-G did not arise from point defects or surface contaminations, but stemmed from line defects induced by grain boundaries. Electron microscopies characterized the presence of grain boundaries and indicated the polycrystalline nature of the CVD-G. Field-effect transistors based on CVD-G without the grain boundary obtained a transport mobility comparative to that of Kish graphene, which directly indicated the detrimental effect of grain boundaries. The effect of grain boundary on transport mobility was qualitatively explained using a potential barrier model. Furthermore, the conduction mechanism of CVD-G was also investigated using the temperature dependence measurements. This study can help understand the intrinsic transport features of CVD-G.

| S-EPMC3313616 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data