Electrochemically Initiated Synthesis of Polyacrylamide Microgels and Core-shell Particles.

ABSTRACT: Herein, we developed a simple procedure for synthesizing micrometer-sized microgel particles as a suspension in an aqueous solution and thin films deposited as shells on different inorganic cores. A sufficiently high constant potential was applied to the working electrode to commence the initiator decomposition that resulted in gelation. Under hydrodynamic conditions, this initiation allowed preparing different morphology microgels at room temperature. Importantly, neither heating nor UV-light illumination was needed to initiate the polymerization. Moreover, thin films of the cross-linked gel were anchored on different core substrates, including silica and magnetic nanoparticles. Scanning electron microscopy and transmission electron microscopy imaging confirmed the microgel particles' and films' irregular shape and porous structure. Energy-dispersive X-ray spectroscopy indicated that the core coating with the microgel film was successful. Dynamic light scattering measured the micrometer size of gel particles with different combinations of acrylic monomers. Thermogravimetric analysis and the first-derivative thermogravimetric analysis revealed that the microgels' thermal stability of different compositions was different. Fourier-transform infrared and ¹³C NMR spectroscopy showed successful copolymerization of the main, functional, and cross-linking monomers.

SUBMITTER: Yasmeen N

PROVIDER: S-EPMC8762648 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:A unique design paradigm to form core-shell particles based on interfacial radical polymerization is described. The interfacial initiation system is comprised of an enzymatic reaction between glucose and glucose oxidase (GOx) to generate hydrogen peroxide, which, in the presence of iron (Fe(2+)), generates hydroxyl radicals that initiate polymerization. Shell formation on prefabricated polymeric cores is achieved by localizing the initiation reaction to the interface of the core and a surrounding aqueous monomer formulation into which it is immersed. The interfacially confined initiation reaction is accomplished by incorporating one or more of the initiating species in the particle core and the remainder of the complementary initiating components in the surrounding media such that interactions and the resulting initiation reaction occur at the interface. This work is focused on engineering the reaction behavior and mass transport processes to promote interfacially confined polymerization, controlling the rate of shell formation, and manipulating the structure of the core-shell particle. Specifically, incorporating GOx in the precursor solution used to fabricate cores ranging from 100 to 200 μm, and the remainder of the complementary initiating components and monomer in the bulk solution prior to interfacial polymerization yielded shells whose average thickness was 20 μm after 4 min of immersion and at a bulk iron concentration of 12.5 mM. When the locations of glucose and GOx are interchanged, the average thickness of the shell was 15 or 100 μm for bulk iron concentrations of 45 and 12.5 mM, respectively. The initial locations of glucose and GOx also determine the degree of interpenetration of the core and the shell. Specifically, for a bulk iron concentration of 45 mM, the thickness of the interpenetrating layer averaged 12 μm when GOx was initially within the core, whereas no interpenetrating layer was observed when glucose was incorporated in the core. The polymeric shell formed by this technique is also demonstrated to be self-supporting following core degradation. This behavior is accomplished by fabricating the particle core hydrogel from monomers possessing degradable groups that can be irreversibly cleaved by light exposure following shell formation. When the coated particle was exposed to light, the shell remained intact while the core degraded as evidenced by a dramatic change in diffusion coefficient of fluorescent beads immobilized within the core.

Dataset Information

Electrochemically Initiated Synthesis of Polyacrylamide Microgels and Core-shell Particles.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets