Novel Dispersion of 1D Nanofiber Fillers for Fast Ion-Conducting Nanocomposite Polymer Blend Quasi-Solid Electrolytes for Dye-Sensitized Solar Cells.

ABSTRACT: Electrospun nanocomposite polymer blend poly(vinylidene difluoride-co-hexafluoropropylene) (PVDF-HFP)/poly(methyl methacrylate) (PMMA) membranes with a novel dispersion of x wt % of one-dimensional (1D) TiO₂ nanofiber fillers (x = 0.0-0.8 in steps of 0.2) were developed using the electrospinning technique. The developed nanocomposite polymer membranes were activated using various redox agents such as LiI, NaI, KI, and tetrabutyl ammonium iodide (TBAI). Introduction of the 1D TiO₂ nanofiber fillers improves the amorphous nature of the blended polymer membrane, as confirmed through X-ray diffraction (XRD) and Fourier transform infrared (FTIR), and yielded an electrolyte uptake of over 480% for a 6 wt % TiO₂ nanofiber filler-dispersed sample. PVDF-HFP/PMMA-1D 6 wt % TiO₂ nanofiber fillers with the LiI-based redox electrolyte provided a high conductivity of 2.80 × 10^-2 S cm^-1 and a power conversion efficiency (PCE) of 8.08% to their fabricated dye-sensitized solar cells (DSSCs). The observed better ionic conductivity and efficiency of the fabricated DSSCs could be due to the faster movement of the smaller-ionic-radius (Li) ions entrapped inside the amorphous polymer. This enhanced mobility of ions in the quasi-solid electrolyte leads to faster regeneration of the depleting electrons in the photoanode, resulting in improved efficiency. Further, the achieved high conductivity was analyzed in terms of the dynamics and relaxation mechanisms involved by the ionic charge carriers with complex impedance spectroscopy using a random barrier model and Havriliak-Negami formulation. It was observed that the high-conducting PVDF-HFP/PMMA-1D 6 wt % TiO₂ nanofiber fillers with LiI-based redox electrolyte show better ac conductivity parameters such as a σ of 5.82 × 10^-2 S cm^-1, ω_e (12685 rad s^-1), τ_e (0.909 × 10^-4 s), and n (0.578). Also, dielectric studies revealed that the high-conducting sample has a higher dielectric constant and subsequently high loss. The J-V characteristics were studied using the equivalent circuit of a single-diode model, and the parameters influencing the photovoltaic performance were determined by Symbiotic Organisms Search (SOS) algorithm. The results suggest that the high-efficient sample possesses a minimum series resistance of 1.33 Ω and a maximum shunt resistance of 997 Ω. Hence, the highest-conducting electrospun-blended polymeric nanocomposite (PVDF-HFP-PMMA-6 wt % TiO₂ nanofiber fillers) with LiI-based redox agent and tert-butyl pyridine (TBP) additive as the polymer quasi-solid electrolyte nanofibrous membrane can be a better electrolyte for high-performance dye-sensitized solar cell applications.

SUBMITTER: Subramanian V

PROVIDER: S-EPMC8772319 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Understanding how cells migrate in fibrous environments is important in wound healing, immune function, and cancer progression. A key question is how fiber orientation and network geometry influence cell movement. Here we describe a quantitative, modeling-based approach toward identifying the mechanisms by which cells migrate in fibrous geometries having well controlled orientation. Specifically, U251 glioblastoma cells were seeded onto non-electrospinning Spinneret based tunable engineering parameters fiber substrates that consist of networks of suspended 400 nm diameter nanofibers. Cells were classified based on the local fiber geometry and cell migration dynamics observed by light microscopy. Cells were found in three distinct geometries: adhering two a single fiber, adhering to two parallel fibers, and adhering to a network of orthogonal fibers. Cells adhering to a single fiber or two parallel fibers can only move in one dimension along the fiber axis, whereas cells on a network of orthogonal fibers can move in two dimensions. We found that cells move faster and more persistently in 1D geometries than in 2D, with cell migration being faster on parallel fibers than on single fibers. To explain these behaviors mechanistically, we simulated cell migration in the three different geometries using a motor-clutch based model for cell traction forces. Using nearly identical parameter sets for each of the three cases, we found that the simulated cells naturally replicated the reduced migration in 2D relative to 1D geometries. In addition, the modestly faster 1D migration on parallel fibers relative to single fibers was captured using a correspondingly modest increase in the number of clutches to reflect increased surface area of adhesion on parallel fibers. Overall, the integrated modeling and experimental analysis shows that cell migration in response to varying fibrous geometries can be explained by a simple mechanical readout of geometry via a motor-clutch mechanism.

Project description:BackgroundHere, electrospun fibers based on a blend of polycaprolactone (PCL), poly(ethylene glycol) (PEG), and gelatin methacryloyl (GelMA) were developed. The careful choice of this polymer combination allowed for the preparation of a biomaterial that preserved the mechanical strength of PCL, while at the same time improving the hydrophilicity of the blended material and human osteoblast maturation.MethodsThe morphology, chemical structure, wettability, and mechanical properties before and after UV photocrosslinking were evaluated. Furthermore, human osteoblasts (hFOB) were cultivated for up to 21 days on the scaffolds, and their potential to upregulate cell proliferation, alkaline phosphatase (ALP) activity, and calcium deposition were investigated.ResultsContact angle measurement results showed that the developed scaffolds presented hydrophilic properties after PEG and GelMA incorporation before (25°) and after UV photocross-linking (69°) compared to pure PCL (149°). PCL:PEG:GelMA-UV displayed a slight increase in mechanical strength (elastic modulus ~37 MPa) over PCL alone (~33 MPa). Normally, an increase in strength of fibers leads to a decrease in elongation at break, due to the material becoming less deformable and stiffer, thus leading to breaks at low strain. This behavior was observed by comparing PCL (elongation at break ~106%) and PCL:PEG:GelMA-UV (~50%). Moreover, increases in ALP activity (10-fold at day 14) and calcium deposition (1.3-fold at day 21) by hFOBs were detected after PEG and GelMA incorporation after UV photocross-linking compared to pure PCL. Ultrathin and hydrophilic fibers were obtained after PEG and GelMA incorporation after UV photocrosslinking, but the strength of PCL was maintained. Interestingly, those ultrathin fiber characteristics improved hFOB functions.ConclusionThese findings appear promising for the use of these electrospun scaffolds, based on the combination of polymers used here for numerous orthopedic applications.

Dataset Information

Novel Dispersion of 1D Nanofiber Fillers for Fast Ion-Conducting Nanocomposite Polymer Blend Quasi-Solid Electrolytes for Dye-Sensitized Solar Cells.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets