Structural, Morphological, Electrical and Electrochemical Properties of PVA: CS-Based Proton-Conducting Polymer Blend Electrolytes.

ABSTRACT: Polymer blend electrolytes based on poly(vinyl alcohol):chitosan (PVA:CS) incorporated with various quantities of ammonium iodide were prepared and characterized using a range of electrochemical, structural and microscopic techniques. In the structural analysis, X-ray diffraction (XRD) was used to confirm the buildup of the amorphous phase. To reveal the effect of dopant addition on structural changes, field-emission scanning electron microscope (FESEM) was used. The protrusions of salt aggregates with large quantity were seen at the surface of the formed films at 50 wt.% of the added salt. The nature of the relationship between conductivity and dielectric properties was shown using electrochemical impedance spectroscopy (EIS). The EIS spectra were fitted with electrical equivalent circuits (EECs). It was observed that both dielectric constant and dielectric loss were high in the low-frequency region. For all samples, loss tangent and electric modulus plots were analyzed to become familiar with the relaxation behavior. Linear sweep voltammetry (LSV) and transference number measurement (TNM) were recorded. A relatively high cut-off potential for the polymer electrolyte was obtained at 1.33 V and both values of the transference number for ion (tion) and electronic (telec) showed the ion dominant as charge carrier species. The TNM and LSV measurements indicate the suitability of the samples for energy storage application if their conductivity can be more enhanced.

SUBMITTER: Shahab Marf A

PROVIDER: S-EPMC7231387 | biostudies-literature | 2020 Apr

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Structural, Morphological, Electrical and Electrochemical Properties of PVA: CS-Based Proton-Conducting Polymer Blend Electrolytes.

Shahab Marf Ayub A Abdullah Ranjdar M RM Aziz Shujahadeen B SB

Membranes 20200415 4

Polymer blend electrolytes based on poly(vinyl alcohol):chitosan (PVA:CS) incorporated with various quantities of ammonium iodide were prepared and characterized using a range of electrochemical, structural and microscopic techniques. In the structural analysis, X-ray diffraction (XRD) was used to confirm the buildup of the amorphous phase. To reveal the effect of dopant addition on structural changes, field-emission scanning electron microscope (FESEM) was used. The protrusions of salt aggregat ...[more]

PMID: 32326628

Similar Datasets

Project description:Electrospun nanocomposite polymer blend poly(vinylidene difluoride-co-hexafluoropropylene) (PVDF-HFP)/poly(methyl methacrylate) (PMMA) membranes with a novel dispersion of x wt % of one-dimensional (1D) TiO2 nanofiber fillers (x = 0.0-0.8 in steps of 0.2) were developed using the electrospinning technique. The developed nanocomposite polymer membranes were activated using various redox agents such as LiI, NaI, KI, and tetrabutyl ammonium iodide (TBAI). Introduction of the 1D TiO2 nanofiber fillers improves the amorphous nature of the blended polymer membrane, as confirmed through X-ray diffraction (XRD) and Fourier transform infrared (FTIR), and yielded an electrolyte uptake of over 480% for a 6 wt % TiO2 nanofiber filler-dispersed sample. PVDF-HFP/PMMA-1D 6 wt % TiO2 nanofiber fillers with the LiI-based redox electrolyte provided a high conductivity of 2.80 × 10-2 S cm-1 and a power conversion efficiency (PCE) of 8.08% to their fabricated dye-sensitized solar cells (DSSCs). The observed better ionic conductivity and efficiency of the fabricated DSSCs could be due to the faster movement of the smaller-ionic-radius (Li) ions entrapped inside the amorphous polymer. This enhanced mobility of ions in the quasi-solid electrolyte leads to faster regeneration of the depleting electrons in the photoanode, resulting in improved efficiency. Further, the achieved high conductivity was analyzed in terms of the dynamics and relaxation mechanisms involved by the ionic charge carriers with complex impedance spectroscopy using a random barrier model and Havriliak-Negami formulation. It was observed that the high-conducting PVDF-HFP/PMMA-1D 6 wt % TiO2 nanofiber fillers with LiI-based redox electrolyte show better ac conductivity parameters such as a σ of 5.82 × 10-2 S cm-1, ωe (12685 rad s-1), τe (0.909 × 10-4 s), and n (0.578). Also, dielectric studies revealed that the high-conducting sample has a higher dielectric constant and subsequently high loss. The J-V characteristics were studied using the equivalent circuit of a single-diode model, and the parameters influencing the photovoltaic performance were determined by Symbiotic Organisms Search (SOS) algorithm. The results suggest that the high-efficient sample possesses a minimum series resistance of 1.33 Ω and a maximum shunt resistance of 997 Ω. Hence, the highest-conducting electrospun-blended polymeric nanocomposite (PVDF-HFP-PMMA-6 wt % TiO2 nanofiber fillers) with LiI-based redox agent and tert-butyl pyridine (TBP) additive as the polymer quasi-solid electrolyte nanofibrous membrane can be a better electrolyte for high-performance dye-sensitized solar cell applications.

Dataset Information

Structural, Morphological, Electrical and Electrochemical Properties of PVA: CS-Based Proton-Conducting Polymer Blend Electrolytes.

Publications

Structural, Morphological, Electrical and Electrochemical Properties of PVA: CS-Based Proton-Conducting Polymer Blend Electrolytes.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets