Leaching and Geochemical Modelling of an Electric Arc Furnace (EAF) and Ladle Slag Heap.

ABSTRACT: Old metallurgical dumps across Europe represent a loss of valuable land and a potential threat to the environment, especially to groundwater (GW). The Javornik electric arc furnace (EAF) and ladle slag heap, situated in Slovenia, was investigated in this study. The environmental impact of the slag heap was evaluated by combining leaching characterization tests of landfill samples and geochemical modelling. It was shown that throughout the landfill the same minerals and sorptive phases control the leaching of elements of potential concern, despite variations in chemical composition. Although carbonation of the disposed steel slags occurred (molar ratio CO₃/(Ca+Mg) = 0.53) relative to fresh slag, it had a limited effect on the leaching behaviour of elements of potential concern. The leaching from the slag heaps had also a limited effect on the quality of the GW. A site-specific case, however, was that leachates from the slag heap were strongly diluted, since a rapid flow of GW fed from the nearby Sava River was observed in the landfill area. The sampling and testing approach applied provides a basis for assessing the long-term impact of release and is a good starting point for evaluating future management options, including beneficial uses for this type of slag.

SUBMITTER: Loncnar M

PROVIDER: S-EPMC8778747 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Self-Healing Analysis of Half-Warm Asphalt Mixes Containing Electric Arc Furnace (EAF) Slag and Reclaimed Asphalt Pavement (RAP) using a Novel Thermomechanical Healing Treatment.

Project description:Nowadays, the self-healing of asphalt pavements promoted by microwave radiation heating energy is gaining attention and strength in the scientific community. However, most of these studies are only conceptual and, thus, remain shrouded in uncertainty regarding technology development, economy, and application effect. Therefore, there are several efforts underway to offer more effective assisted healing treatments that are capable of overcoming such uncertainties. This paper aims to assess and quantify the healing performance rates (HR) of half-warm recycled asphalt (HWRA) mixtures containing electric arc furnace (EAF) slag and total recycled asphalt pavement (RAP) rates. To this end, a novel assisted thermomechanical healing treatment (i.e., a recompaction-based technique and microwave heating energy) was put forward to promote the potential healing effect of this treatment on the mechanical properties of the asphalt mixtures. In order to do this, three microwave heating temperatures (25 °C, 60 °C, and 80 °C) and three mechanical recompaction levels (0, 25, and 50 gyrations) were selected. After that, the healing performance rates (%, HR) of the asphalt mixtures were calculated by repeated indirect tensile strength (ITS) and indirect tensile stiffness modulus (ITSM). The results indicated that the 8% EAF slag mixture was found to provide significant microwave heating energy savings by up to 69% compared with the benchmark 100% RAP mixture, and, at the same time, it experienced a remarkable stiffness recovery response of 140% of the initial mechanical properties. These findings encourage greater confidence in promoting this innovative thermomechanical-based healing treatment for in-situ surface course asphalt mixtures of road pavements.

| S-EPMC7321439 | biostudies-literature

Stabilization of a Clayey Soil with Ladle Metallurgy Furnace Slag Fines.

Project description:The research study described in this paper investigated the potential to use steel furnace slag (SFS) as a stabilizing additive for clayey soils. Even though SFS has limited applications in civil engineering infrastructure due to the formation of deleterious expansion in the presence of water, the free CaO and free MgO contents allow for the SFS to be a potentially suitable candidate for clayey soil stabilization and improvement. In this investigation, a kaolinite clay was stabilized with 10% and 15% ladle metallurgy furnace (LMF) slag fines by weight. This experimental study also included testing of the SFS mixtures with the activator calcium chloride (CaCl2), which was hypothesized to accelerate the hydration of the dicalcium silicate phase in the SFS, but the results show that the addition of CaCl2 was not found to be effective. Relative to the unmodified clay, the unconfined compressive strength increased by 67% and 91% when 10% and 15% LMF slag were utilized, respectively. Likewise, the dynamic modulus increased by 212% and 221% by adding 10% and 15% LMF slag, respectively. Specifically, the LMF slag fines are posited to primarily contribute to a mechanical rather than chemical stabilization mechanism. Overall, these findings suggest the effective utilization of SFS as a soil stabilization admixture to overcome problems associated with dispersive soils, but further research is required.

| S-EPMC7579171 | biostudies-literature

---Mechanical behavior of textile reinforced alkali-activated mortar based on fly ash, metakaolin and ladle furnace slag.

Project description:The need for repair and maintenance has become dominant in the European construction sector. This, combined with the urge to decrease CO 2 emissions, has resulted in the development of lower carbon footprint repair solutions such as textile reinforced mortars (TRM) based on alkali-activated materials (AAM). Life cycle studies indicate that AAM CO 2 savings, when compared to Portland cement, range from 80% to 30%. Furthermore, in this study, recycled aggregates were considered with the aim to promote a circular economy mindset. AAM mortars formulation based on fly ash, ladle furnace slag and metakaolin were tested for compressive and flexural strength. Three out of all formulations were chosen for an analysis on the potential of these mortars to be used for TRM applications. Tensile and shear bond tests, combined with a concrete substrate, were executed as indicators of the TRM effectiveness. Scanning electron microscopy and chemical analysis based on energy dispersive X-ray spectroscopy were used to interpret the results and reveal the reasons behind the different level of performance of these composites. Results indicated that TRM based on high calcium fly ash are unsuitable for structural strengthening applications due to low bond between matrix and/or substrate and fibers. Metakaolin-based TRM showed good performance both in terms of tensile strength and bond capacity, which suggests potential as a repair mortar.

| S-EPMC10445836 | biostudies-literature

Pragmatic analysis of the electric submerged arc furnace continuum.

Project description:A transient mathematical model was developed for the description of fluid flow, heat transfer and electromagnetic phenomena involved in the production of ferronickel in electric arc furnaces. The key operating variables considered were the thermal and electrical conductivity of the slag and the shape, immersion depth and applied electric potential of the electrodes. It was established that the principal stimuli of the velocities in the slag bath were the electric potential and immersion depth of the electrodes and the thermal and electrical conductivities of the slag. Additionally, it was determined that, under the set of operating conditions examined, the maximum slag temperature ranged between 1756 and 1825?K, which is in accordance with industrial measurements. Moreover, it was affirmed that contributions to slag stirring due to Lorentz forces and momentum forces due to the release of carbon monoxide bubbles from the electrode surface were negligible.

| S-EPMC5627078 | biostudies-literature

Recovery of scandium and neodymium from blast furnace slag using acid baking-water leaching.

Project description:The current study puts the emphasis on developing a pyro-hydrometallurgical process, called acid baking-water leaching, to recover scandium and neodymium from blast furnace slag produced by the ironmaking industry. In this process, the feed is mixed with concentrated sulfuric acid, digested at 200-400 °C, and leached in water at ambient conditions. This process offers several advantages including less acidic waste generation and rapid kinetics. With fundamental investigations into the digestion mechanism, acid to slag mass ratio and baking temperature are determined to have the most significant positive and negative impacts, respectively. At low acid to slag ratio, the silicate bearing phases in the feed do not digest, resulting in low extraction. At 200 °C baking temperature, a hydrated aluminum sulfate ((Al(H2O)6)2(SO4)3(H2O)4.4) phase with weak hydrogen bonds is formed that leaches in water rapidly (<10 min); while at 400 °C, Al2(SO4)3 with strong ionic bonds is formed that leaches at slower kinetics (>4 h). Fundamental investigations into the water leaching process indicate that the diffusion of water through the firm solid product (ash layer) is the rate determining step. We expect the results of this study would help enable valorization of industrial byproducts, in particular ironmaking slag.

| S-EPMC9056533 | biostudies-literature

Characteristics of the Supersonic Combustion Coherent Jet for Electric Arc Furnace Steelmaking.

Project description:Herein, a supersonic combustion coherent jet is proposed based on current coherent jet technology to improve the impact capacity of a coherent jet and increase the stirring intensity of the electric arc furnace (EAF) bath. Further, numerical simulations and an experimental analysis are combined to study the supersonic combustion coherent jet characteristics, including the Mach number, dynamic pressure, static temperature, vorticity, and turbulence intensity, in the EAF steelmaking environment. The results show that the supersonic combustion coherent jet exhibits stable combustion in a high-temperature EAF steelmaking environment. The supersonic combustion flame generated by the supersonic shrouding fuel gas can envelop the main oxygen jet more effectively than current coherent jets. Furthermore, the velocity attenuation, vorticity, and turbulence intensity performances of the supersonic combustion coherent jet are better when compared with those of the current coherent jet. The velocity core length of the main oxygen jet for the supersonic combustion coherent jet is 30% longer than that of the current coherent jet, resulting in an improved impact capacity and stirring intensity of the molten bath.

| S-EPMC6862147 | biostudies-literature

Three-dimensional computational fluid dynamics analysis of an electric submerged arc furnace.

Project description:A computational fluid dynamics (CFD) method is proposed to analyze the operation of a submerged electric arc furnace (SAF) used in ferronickel production. A three-dimensional mathematical model was used for the time-dependent solution of the fluid flow, heat transfer and electromagnetic phenomena. The slag's physical properties, which play a crucial role in the SAF operation, were previously determined using classical molecular dynamics simulations and empirical relationships. The analysis revealed that the main slag properties affecting SAF operation are density, viscosity and electrical conductivity-the latter two being mutually dependent. The high electrical conductivity values of the slag favor melting via the high Joule heat produced within the slag region. Calculation of the dimensionless Péclet and Reynolds numbers revealed that the slag velocities play a decisive role in heat transfer and further indicate that the slag flow is laminar. The average slag velocity calculated 0.0001 m/s with maxima in the vicinity of the electrodes.

| S-EPMC8417227 | biostudies-literature

Leaching heap invasion and leaching solution invasion

Project description:Leaching microbial invasion Raw sequence reads

| PRJNA451049 | ENA

Geopolymer Based on Mechanically Activated Air-cooled Blast Furnace Slag.

Project description:An efficient solution to increase the sustainability of building materials is to replace Portland cement with alkali-activated materials (AAM). Precursors for those systems are often based on water-cooled ground granulated blast furnace slags (GGBFS). Quenching of blast furnace slag can be done also by air but in that case, the final product is crystalline and with a very low reactivity. The present study aimed to evaluate the cementitious properties of a mechanically activated (MCA) air-cooled blast furnace slag (ACBFS) used as a precursor in sodium silicate alkali-activated systems. The unreactive ACBFS was processed in a planetary ball mill and its cementing performances were compared with an alkali-activated water-cooled GGBFS. Mixes based on mechanically activated ACBFS reached the 7-days compressive strength of 35 MPa and the 28-days compressive strength 45 MPa. The GGBFS-based samples showed generally higher compressive strength values.

| S-EPMC7085006 | biostudies-literature

Hydration of dicalcium silicate and diffusion through neo-formed calcium-silicate-hydrates at weathered surfaces control the long-term leaching behaviour of basic oxygen furnace (BOF) steelmaking slag.

Project description:Alkalinity generation and toxic trace metal (such as vanadium) leaching from basic oxygen furnace (BOF) steel slag particles must be properly understood and managed by pre-conditioning if beneficial reuse of slag is to be maximised. Water leaching under aerated conditions was investigated using fresh BOF slag at three different particle sizes (0.5-1.0, 2-5 and 10 × 10 × 20 mm blocks) and a 6-month pre-weathered block. There were several distinct leaching stages observed over time associated with different phases controlling the solution chemistry: (1) free-lime (CaO) dissolution (days 0-2); (2) dicalcium silicate (Ca2SiO4) dissolution (days 2-14) and (3) Ca-Si-H and CaCO3 formation and subsequent dissolution (days 14-73). Experiments with the smallest size fraction resulted in the highest Ca, Si and V concentrations, highlighting the role of surface area in controlling initial leaching. After ~2 weeks, the solution Ca/Si ratio (0.7-0.9) evolved to equal those found within a Ca-Si-H phase that replaced dicalcium silicate and free-lime phases in a 30- to 150-μm altered surface region. V release was a two-stage process; initially, V was released by dicalcium silicate dissolution, but V also isomorphically substituted for Si into the neo-formed Ca-Si-H in the alteration zone. Therefore, on longer timescales, the release of V to solution was primarily controlled by considerably slower Ca-Si-H dissolution rates, which decreased the rate of V release by an order of magnitude. Overall, the results indicate that the BOF slag leaching mechanism evolves from a situation initially dominated by rapid hydration and dissolution of primary dicalcium silicate/free-lime phases, to a slow diffusion limited process controlled by the solubility of secondary Ca-Si-H and CaCO3 phases that replace and cover more reactive primary slag phases at particle surfaces.

| S-EPMC5891564 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data