Where ppm Quantities of Silsesquioxanes Make a Difference-Silanes and Cage Siloxanes as TiO2 Dispersants and Stabilizers for Pigmented Epoxy Resins.
Ontology highlight
ABSTRACT:
SUBMITTER: Brzakalski D
PROVIDER: S-EPMC8779391 | biostudies-literature |
REPOSITORIES: biostudies-literature
Similar Datasets
Project description:One of the types of negative tone photoresists is composed of at least a catalyst, a solvent, and epoxy resin. This is the primary raw material for lithography technology. To ensure high-quality pattern transfer in the lithography process, it is crucial to control the properties of the photoresist. In this work, a set of resins based on Bisphenol-A were synthesized. The obtained resins have been characterized regarding the chain size and its derivative products. As a second step, an epoxidation reaction was performed and the epoxy groups were quantified. The profile of the resins, obtained by mass spectroscopy (ESI-µ-TOF-MS), showed that it is possible to tune the chain sizes of the polymers and their derivate by controlling the parameters of the polymerization reaction. Three profiles of resins were achieved in this study. Nuclear magnetic resonance (NMR) indicates an epoxidation in the range of 96%, when comparing the phenolic peak intensity before and after the reaction. Differential Scan Calorimetry (DSC) measurements confirmed the different oligomer profiles of resins, showing different glass transition temperatures.
| S-EPMC6780111 | biostudies-literature
Project description:Epoxy resin is indispensable for modern industry because of its excellent mechanical properties, chemical resistance, and excellent moldability. To date, various methods have been used to investigate the physical properties of the cured product and the kinetics of the curing process, but its microscopic dynamics have been insufficiently studied. In this study, the microscopic dynamics in the curing process of a catalytic epoxy resin were investigated under different temperature conditions utilizing X-ray photon correlation spectroscopy. Our results revealed that the temperature conditions greatly affected the dynamical heterogeneity and cross-linking density of the cured materials. An overview of the microscopic mechanism of the curing process was clearly presented through comparison with the measurement results of other methods, such as 1H-pulse nuclear magnetic resonance spectroscopy. The quantification of such heterogeneous dynamics is particularly useful for optimizing the curing conditions of various materials to improve their physical properties.
| S-EPMC8129072 | biostudies-literature
Project description:The use of renewable resources for plastic production is an imperious need for the reduction of the carbon footprint and the transition towards a circular economy. With that goal in mind, fully biobased epoxy resins have been designed and prepared by combining epoxidized linseed oil, lignin, and a biobased diamine derived from fatty acid dimers. The aromatic structures in lignin provide hardness and strength to an otherwise flexible and breakable epoxy resin. The curing of the system was investigated by infrared spectroscopy and differential scanning calorimetry (DSC). The influence of the different components on the thermo-mechanical properties of the epoxy resins was analyzed by DSC, thermal gravimetric analysis (TGA), and tensile tests. As the content of lignin in the resin increases, so does the glass transition, the Young's modulus, and the onset of thermal degradation. This correlation is non-linear, and the higher the percentage of lignin, the more pronounced the effect. All the components of the epoxy resin being commodity chemicals, the present system provides a realistic opportunity for the preparation of fully biorenewable resins at an industrial scale.
| S-EPMC7179237 | biostudies-literature
Project description:Epoxy resin plays a key role in composite matrices and DGEBA is the major precursor used. With the aim of favouring the use of bio resources, epoxy resins can be prepared from lignin. In particular, diglycidyl ether of isoeugenol derivatives are good candidates for the replacement of DGEBA. This article presents an effective and eco-friendly way to prepare epoxy resin derived from isoeugenol (BioIgenox), making its upscale possible. BioIgenox has been totally characterized by NMR, FTIR, MS and elemental analyses. Curing of BioIgenox and camphoric anhydride with varying epoxide function/anhydride molar ratios has allowed determining an optimum ratio near 1/0.9 based on DMA and DSC analyses and swelling behaviours. This thermoset exhibits a Tg measured by DMA of 165 °C, a tensile storage modulus at 40 °C of 2.2 GPa and mean 3-point bending stiffness, strength and strain at failure of 3.2 GPa, 120 MPa and 6.6%, respectively. Transposed to BioIgenox/hexahydrophtalic anhydride, this optimized formulation gives a thermoset with a Tg determined by DMA of 140 °C and a storage modulus at 40 °C of 2.6 GPa. The thermal and mechanical properties of these two thermosets are consistent with their use as matrices for structural or semi-structural composites.
| S-EPMC7023557 | biostudies-literature
Project description:ObjectivesThis study probes how modifiedapproaches for filler surface treatment in dental composites based on alternative silanes and functional nanogel additives affects physicochemical properties of these materials with a focus on polymerization stress development.MethodsNanogels were synthesized from isobornyl methacrylate, ethoxylated bisphenol-A dimethacrylate and isocyanatoethyl methacrylate followed by partial further reaction with 2-hydroxyethyl methacrylate to provide both isocyanate and methacrylate functionalization. A barium glass filler (˜1 μm particle size) was treated with either γ-methacryloxypropyltrimethoxysilane (MPS), N-methylaminopropyltrimethoxy (MAP) or N-allylaminopropyltrimethoxy (AAP) silanes. The reactive nanogels were then covalently attached to the aminosilane-treated fillers. Surface treatment was characterized by thermogravimetric analysis (TGA) and diffuse reflectance infrared spectroscopy (DR-IR). Composites were formulated with 60 wt% of the various functionalized fillers and the materials were evaluated for polymerization kinetics, polymerization stress (PS), volumetric shrinkage, mechanical properties and photorheology. Data were evaluated by one-way ANOVA and Tukey's test at 5% significance level.ResultsFiller surface treatments were confirmed by TGA and DR-IR analyses. Nanogel-functionalized fillers significantly reduced PS up to 20%, while the degree of conversion and elastic modulus were not compromised. Similar storage modulus development during polymerization was observed among materials by photorheology although the rate of polymerization was significantly increased for nanogel-based treatments. A significant decrease in flexural strength was observed for amino functional silane groups; however, there was no statistical difference in strength for the MPS control group compared with the nanogel-modified composites.SignificanceFiller surface treatment modified with a reactive nanogel enables significant PS reduction, without compromise to degree of conversion or mechanical properties of dental composites.
| S-EPMC6530473 | biostudies-literature
Project description:Poly(phenyl-substituted siloxanes/silsesquioxanes) are obtained by the Piers⁻Rubinsztajn (PR) reaction of hydrogen-containing siloxanes (HCS) with diphenyldialkoxysilanes such as diphenyldimethoxysilane and diphenyldiethoxysilane catalyzed by tris(pentafluorophenyl)borane. 29Si nuclear magnetic resonance (NMR) spectroscopy, gel permeation chromatography, and refractive index analysis revealed that apart from phenyl substituents and complex structures such as molecular bridges composed of D₂Ph2[(C₆H₅)₂Si(OSi)₂], structures also existed in these polymers, having high refractive indexes (above 1.50) and high molecular weights (75.60 KDa·mol-1). As revealed by thermogravimetric analysis, these polymers have high thermal stability as well, with temperature at 5% mass loss (T5%) increasing by 182.5 °C and Rw (residual weight ratio) increasing by 5.17 times from 14.63% to 75.60%, as compared to HCS, exhibiting its potential application as resins for resisting strong heat. Such high-refractive-index and temperature-resistant poly(phenyl-substituted siloxanes/silsesquioxanes) with Si⁻H and alkoxy functional groups can be used as a good addition-type crosslinking agent with adhesion-promoting properties or a special curing agent that can solidify silicone materials through simultaneous addition and condensation reactions, which has potential application in the light-emitting diode (LED) packaging industry.
| S-EPMC6403990 | biostudies-literature
Project description:The current trend for future flame retardants (FRs) goes to novel efficient halogen-free materials, due to the ban of several halogenated FRs. Among the most promising alternatives are phosphorus-based FRs, and of those, polymeric materials with complex shape have been recently reported. Herein, we present novel halogen-free aromatic and aliphatic hyperbranched polyphosphoesters (hbPPEs), which were synthesized by olefin metathesis polymerization and investigated them as a FR in epoxy resins. We compare their efficiency (aliphatic vs. aromatic) and further assess the differences between the monomeric compounds and the hbPPEs. The decomposition and vaporizing behavior of a compound is an important factor in its flame-retardant behavior, but also the interaction with the pyrolyzing matrix has a significant influence on the performance. Therefore, the challenge in designing a FR is to optimize the chemical structure and its decomposition pathway to the matrix, with regards to time and temperature. This behavior becomes obvious in this study, and explains the superior gas phase activity of the aliphatic FRs.
| S-EPMC6864611 | biostudies-literature
Project description:A persistent challenge in predictive molecular modeling of thermoset polymers is to capture the effects of chemical composition and degree of crosslinking (DC) on dynamical and mechanical properties with high computational efficiency. We established a new coarse-graining (CG) approach that combines the energy renormalization method with Gaussian process surrogate models of the molecular dynamics simulations. This allows a machine-learning informed functional calibration of DC-dependent CG force field parameters. Taking versatile epoxy resins consisting of Bisphenol A diglycidyl ether combined with curing agent of either 4,4-Diaminodicyclohexylmethane or polyoxypropylene diamines, we demonstrated excellent agreement between all-atom and CG predictions for density, Debye-Waller factor, Young's modulus and yield stress at any DC. We further introduce a surrogate model enabled simplification of the functional forms of 14 non-bonded calibration parameters by quantifying the uncertainty of a candidate set of high-dimensional/flexible calibration functions. The framework established provides an efficient methodology for chemistry-specific, large-scale investigations of the dynamics and mechanics of epoxy resins.
| S-EPMC8612124 | biostudies-literature
Project description:Two phosphorus-containing cage-like silsesquioxane derivatives were synthesized as reactive or additive flame retardants for epoxy resin. The silsesquioxanes were obtained via an epoxide ring-opening reaction using a 10-hydroxy-9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPA). In one derivative containing in its structure 4 glycidoxypropyl and 4 phosphate groups, denoted as 4P4GS, only half of the epoxy rings was reacted with phosphate to obtain a reactive additive, while in the second derivative containing 8 phosphate groups, denoted as 8PS, all epoxy groups were converted, thus an additive modifier was obtained. The silsesquioxanes containing phosphorus atoms and the reactive phosphorus-free silsesquioxane derivative (octakis[(3-glycidoxypropyl)dimethylsiloxy]octasilsesquioxane (8GS)) were used to prepare hybrid materials based on epoxy resin. To compare the impact of the structure of silsesquioxane derivatives on the properties of hybrid materials, a number of samples containing 1, 5, and 10% of the modifiers making a series of epoxy materials containing additive or reactive modifiers, were obtained. The modified epoxies were studied using scanning electron microscopy and energy-dispersive X-ray spectroscopy (SEM-EDS), thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), nanoindentation, water contact angle, and cone calorimetry tests to assess the effects of the modifier structure on the physicochemical properties of the investigated materials.
| S-EPMC7730412 | biostudies-literature
Project description:Here we investigate the relationship between thermomechanical properties and chemical structure of well-characterized lignin-based epoxy resins. For this purpose, technical lignins from eucalyptus and spruce, obtained from the Kraft process, were used. The choice of lignins was based on the expected differences in molecular structure. The lignins were then refined by solvent fractionation, and three fractions with comparable molecular weights were selected to reduce effects of molar mass on the properties of the final thermoset resins. Consequently, any differences in thermomechanical properties are expected to correlate with molecular structure differences between the lignins. Oxirane moieties were selectively introduced to the refined fractions, and the resulting lignin epoxides were subsequently cross-linked with two commercially available polyether diamines (Mn = 2000 and 400) to obtain lignin-based epoxy resins. Molecular-scale characterization of the refined lignins and their derivatives were performed by 31P NMR, 2D-NMR, and DSC methods to obtain the detailed chemical structure of original and derivatized lignins. The thermosets were studied by DSC, DMA, and tensile tests and demonstrated diverse thermomechanical properties attributed to structural components in lignin and selected amine cross-linker. An epoxy resin with a lignin content of 66% showed a Tg of 79 °C from DMA, Young's modulus of 1.7 GPa, tensile strength of 66 MPa, and strain to failure of 8%. The effect of molecular lignin structure on thermomechanical properties was analyzed, finding significant differences between the rigid guaiacyl units in spruce lignin compared with sinapyl units in eucalyptus lignin. The methodology points toward rational design of molecularly tailored lignin-based thermosets.
| S-EPMC7997103 | biostudies-literature