Insight into Chemical Recycling of Flexible Polyurethane Foams by Acidolysis.

ABSTRACT: Acidolysis is emerging as a promising method for recycling polyurethane foam (PUF) waste. Here, we present highly efficient acidolysis of PUFs with adipic acid (AA) by heating the reaction mixtures with microwaves. The influence of experimental conditions, such as reaction temperature, time, and amount of the degradation reagent, on the polyol functionality, molecular weight characteristics, the presence of side products, and the degree of degradation of the remaining PUF hard segments was studied by matrix-assisted laser desorption/ionization time-of-flight mass spectroscopy (MALDI-TOF MS), nuclear magnetic resonance (NMR), size-exclusion chromatography (SEC) coupled to a multidetection system, and Fourier transform infrared (FT-IR) spectroscopy. The purified recycled polyols were used for the synthesis of flexible PUFs. The morphology and mechanical properties of the PUFs show that the degree of functionalization of the polyol by the carboxylic end groups, which is higher for larger amounts of AA used to degrade the PUFs, significantly affects the quality and performance of the flexible PUFs from the recycled polyols.

SUBMITTER: Grdadolnik M

PROVIDER: S-EPMC8790754 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:The role of various additives (emulsifier, anti-dripping agent) and formulation procedures (pre-dispersion of solid additives in polyol via milling) which influence the flame retardancy of 6,6'-[ethan-1,2-diylbis(azandiyl)]bis(6H-dibenzo[c,e][1,2]oxaphosphin-6-oxid) (EDA-DOPO) containing flexible polyurethane foams has been investigated in this work. For comparison, the flame retardancy of two additional structurally-analogous bridged 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO)-based compounds, i.e., ethanolamine-DOPO (ETA-DOPO) and ethylene glycol-DOPO (EG-DOPO) were also evaluated together with EDA-DOPO in flexible PU foams of various formulations. The flame retardancy of these three bridged-DOPO compounds depends on the type of PU formulation. For certain PU formulations containing EDA-DOPO, lower fire performance was observed. Addition of emulsifier and polytetrafluoroethylene (PTFE) to these PU formulations influenced positively the flame retardancy of EDA-DOPO/PU foams. In addition, dispersion of EDA-DOPO and PTFE via milling in polyol improved the flame retardancy of the PU foams. Mechanistic studies performed using a microscale combustion calorimeter (MCC) and its coupling to FTIR showed no difference in the combustion efficiency of the bridged-DOPO compounds in PU foams. From MCC experiments it can be concluded that these bridged-DOPO compounds and their decomposition products may work primarily in the gas phase as flame inhibitors. The physiochemical behavior of additives in PU formulation responsible for the improvement in the flame retardancy of PU foams was further investigated by studying the dripping behavior of the PU foams in the UL 94 HB test. A high-speed camera was used to study the dripping behavior in the UL 94 HB test and results indicate a considerable reduction of the total number of melt drips and flaming drips for the flame retardant formulations. This reduction in melt drips and flaming drips during the UL 94 HB tests help PU foams achieve higher fire classification.

Dataset Information

Insight into Chemical Recycling of Flexible Polyurethane Foams by Acidolysis.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets