Synthesis of poly(N-isopropylacrylamide) polymer crosslinked with an AIE-active azonaphthol for thermoreversible fluorescence.

ABSTRACT: A fluorescent polymer was synthesized using N-isopropylacrylamide (NIPAM) crosslinked with a divinylazonaphthol monomer via radical emulsion polymerization. Because the crosslinked polymer contained an aggregation-induced emissive (AIE) azonaphthol-based crosslinker, a thermoreversible sol-gel transformation and gelation-induced reversible fluorescence alteration were successfully attained in an aqueous medium. Like typical PNIPAM, the size and transmittance of the polymer dramatically decreased near the lower critical solution temperature (LCST, 36 °C). Such gelation facilitated aggregation of the polymer chains, resulting in the close contact between azonaphthol groups producing fluorescence. The crosslinked polymer exhibited changes in dual properties: one is related to PNIPAM structural alteration, which corresponds to conventional swelling/shrinkage behavior; and the other is involved in the reversible fluorescence change in response to the swelling/shrinkage. Because the major backbone of the polymer was composed of NIPAM with an LCST at 36 °C, the resultant polymer is expected to have potential applications in biologically related fields.

SUBMITTER: Oh M

PROVIDER: S-EPMC9057382 | biostudies-literature | 2020 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Synthesis of poly(N-isopropylacrylamide) polymer crosslinked with an AIE-active azonaphthol for thermoreversible fluorescence.

Oh Mintaek M Yoon Yeoju Y Lee Taek Seung TS

RSC advances 20201027 64

A fluorescent polymer was synthesized using N-isopropylacrylamide (NIPAM) crosslinked with a divinylazonaphthol monomer via radical emulsion polymerization. Because the crosslinked polymer contained an aggregation-induced emissive (AIE) azonaphthol-based crosslinker, a thermoreversible sol-gel transformation and gelation-induced reversible fluorescence alteration were successfully attained in an aqueous medium. Like typical PNIPAM, the size and transmittance of the polymer dramatic ...[more]

PMID: 35518410

Similar Datasets

Project description:The thermoreversible sol-gel transition for an ionic liquid (IL) solution of isotactic-rich poly (N-isopropylacrylamides) (PNIPAMs) is investigated by rheological technique. The meso-diad content of PNIPAMs ranges between 47% and 79%, and molecular weight (Mn) is ~35,000 and ~70,000 g/mol for two series of samples. PNIPAMs are soluble in 1-butyl-3-methylimidazolium bis(trifluoromethanesulfonyl) imide ([BMIM][TFSI]) at high temperatures but undergo a gelation with decreasing temperatures. The transition temperature determined from G'-G" crossover increases with isotacticity, consistent with the previous cloud-point result at the same scanning rate, indicating imide groups along the same side of backbones are prone to be aggregated for formation of a gel. The transition point based on Winter-Chambon criterion is on average higher than that of the G'-G" crossover method and is insensitive to tacticity and molecular weight, since it correlates with percolation of globules rather than the further formation of elastic network (G' > G"). For the first time, the phase diagram composed of both G'-G" crossover points for gelation and cloud points is established in PNIPAM/IL mixtures. For low-Mn PNIPAMs, the crossover-point line intersects the cloud-point line. Hence, from solution to opaque gel, the sample will experience two different transitional phases, either clear gel or opaque sol. A clear gel is formed due to partial phase separation of isotactic segments that could act as junctions of network. However, when the partial phase separation is not faster than the formation of globules, an opaque sol will be formed. For high-Mn PNIPAMs, crossover points are below cloud points at all concentrations, so their gelation only follows the opaque sol route. Such phase diagram is attributed to the poorer solubility of high-Mn polymers for entropic reasons. The phase diagram composed of Winter-Chambon melting points, crossover points for melting, and clear points is similar with the gelation phase diagram, confirming the mechanism above.

Dataset Information

Synthesis of poly(N-isopropylacrylamide) polymer crosslinked with an AIE-active azonaphthol for thermoreversible fluorescence.

Publications

Synthesis of poly(<i>N</i>-isopropylacrylamide) polymer crosslinked with an AIE-active azonaphthol for thermoreversible fluorescence.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets