Bifunctional acid-base mesoporous silica@aqueous miscible organic-layered double hydroxides.

ABSTRACT: A facile method for the synthesis of a series of mesoporous silica nanoporous (MSN) aqueous miscible organic layered double hydroxide core@shell nanocomposites using MCM-41, Al-MCM-41, SBA-15, and MCM-48 as the core is reported. These materials exhibit hierarchical morphologies with high surface areas and good porosity. Chemically, these materials offer controllable bifunctional basicity and acidity.

SUBMITTER: Suo H

PROVIDER: S-EPMC9060557 | biostudies-literature | 2019 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Bifunctional acid-base mesoporous silica@aqueous miscible organic-layered double hydroxides.

Suo Hongri H Duan Haohong H Chen Chunping C Buffet Jean-Charles JC O'Hare Dermot D

RSC advances 20190128 7

A facile method for the synthesis of a series of mesoporous silica nanoporous (MSN) aqueous miscible organic layered double hydroxide core@shell nanocomposites using MCM-41, Al-MCM-41, SBA-15, and MCM-48 as the core is reported. These materials exhibit hierarchical morphologies with high surface areas and good porosity. Chemically, these materials offer controllable bifunctional basicity and acidity. ...[more]

PMID: 35518067

Similar Datasets

Core-shell zeolite@aqueous miscible organic-layered double hydroxides.

Project description:We report a general method for the synthesis of core-shell hybrid materials containing a microporous zeolite core with an aqueous miscible organic-layered double hydroxide (AMO-LDH) shell using a simple in situ coprecipitation method. For example, zeolite-HY@AMO-Mg2Al-CO3-LDH contains a 150 nm hierarchical AMO-Mg2Al-CO3-LDH surface coating on zeolite-HY. It exhibits a similar BET surface area (698 m2 g-1) as the parent zeolite-HY but this surface area has been re-allocated between microspores and mesopores. We believe that surface aluminium sites act as nucleation sites for the formation of the LDH coating and so robustly links it into the zeolite lattice. We expect that this new hybrid structure with micropores dominating in the core and mesopores populating the shell will provide a desirable new hybrid structure type for adsorption or catalysis.

| S-EPMC5975924 | biostudies-literature

Stability Trends in Mono-Metallic 3d Layered Double Hydroxides.

Project description:Layered double hydroxides (LDHs) constitute a unique group of 2D materials that can deliver exceptional catalytic, optical, and electronic performance. However, they usually suffer from low stability compared to their oxide counterparts. Using density functional calculations, we quantitatively demonstrate the crucial impact of the intercalants (i.e., water, lactate, and carbonate) on the stability of a series of common LDHs based on Mn, Fe, and Co. We found that intercalation with the singly charged lactate results in higher stability in all these LDH compounds, compared to neutral water and doubly charged carbonate. Furthermore, we show that the dispersion effect aids the stability of these LDH compounds. This investigation reveals that certain intercalants enhance LDH stability and alter the bandgap favourably.

| S-EPMC9029406 | biostudies-literature

Waste foundry sand/MgFe-layered double hydroxides composite material for efficient removal of Congo red dye from aqueous solution.

Project description:We aimed to obtain magnesium/iron (Mg/Fe)-layered double hydroxides (LDHs) nanoparticles-immobilized on waste foundry sand-a byproduct of the metal casting industry. XRD and FT-IR tests were applied to characterize the prepared sorbent. The results revealed that a new peak reflected LDHs nanoparticles. In addition, SEM-EDS mapping confirmed that the coating process was appropriate. Sorption tests for the interaction of this sorbent with an aqueous solution contaminated with Congo red dye revealed the efficacy of this material where the maximum adsorption capacity reached approximately 9127.08?mg/g. The pseudo-first-order and pseudo-second-order kinetic models helped to describe the sorption measurements, indicating that the physical and chemical forces governed the removal process.

| S-EPMC7005020 | biostudies-literature

Hydrothermal synthesis of multi-cationic high-entropy layered double hydroxides.

Project description:High-entropy materials are compositionally complex materials which often contain five or more elements. The most commonly studied materials in this field are alloys and oxides, where their composition allows for tunable materials properties. High-entropy layered double hydroxides have been recently touted as the next focus for the field of high-entropy materials to expand into. However, most previous work on multi-cationic layered double hydroxides has focused on syntheses with 5 or less cations in the structure. To bridge this gap into high-entropy materials, this work explores the range and extent of different compositional combinations for high-entropy double layered hydroxides. Specifically, pure layered double hydroxides were synthesized with different combinations of 7 cations (Mg, Co, Cu, Zn, Ni, Al, Fe, Cr) as well as one combination of 8 cations by utilizing a hydrothermal synthesis method. Furthermore, magnetic properties of the 8-cation LDH were investigated.

| S-EPMC9475562 | biostudies-literature

Upscaling the urea method synthesis of CoAl layered double hydroxides

Project description: Not available

| S-EPMC10509544 | biostudies-literature

Polymer/Iron-Based Layered Double Hydroxides as Multifunctional Wound Dressings.

Project description:This work presents the development of multifunctional therapeutic membranes based on a high-performance block copolymer scaffold formed by polyether (PE) and polyamide (PA) units (known as PEBA) and layered double hydroxide (LDH) biomaterials, with the aim to study their uses as wound dressings. Two LDH layer compositions were employed containing Mg2+ or Zn2+, Fe3+ and Al3+ cations, intercalated with chloride anions, abbreviated as Mg-Cl or Zn-Cl, or intercalated with naproxenate (NAP) anions, abbreviated as Mg-NAP or Zn-NAP. Membranes were structurally and physically characterized, and the in vitro drug release kinetics and cytotoxicity assessed. PEBA-loading NaNAP salt particles were also prepared for comparison. Intercalated NAP anions improved LDH-polymer interaction, resulting in membranes with greater mechanical performance compared to the polymer only or to the membranes containing the Cl-LDHs. Drug release (in saline solution) was sustained for at least 8 h for all samples and release kinetics could be modulated: a slower, an intermediate and a faster NAP release were observed from membranes containing Zn-NAP, NaNAP and Mg-NAP particles, respectively. In general, cell viability was higher in the presence of Mg-LDH and the membranes presented improved performance in comparison with the powdered samples. PEBA containing Mg-NAP sample stood out among all membranes in all the evaluated aspects, thus being considered a great candidate for application as multifunctional therapeutic dressings.

| S-EPMC7700130 | biostudies-literature

Synthesis of Mg-Al Mixed Oxides with Markedly High Surface Areas from Layered Double Hydroxides with Organic Sulfonates.

Project description:Mg-Al mixed oxides with record-high surface areas and basic site concentrations were synthesized from Mg-Al layered double hydroxides with interlayer isethionate (Ise) or 3-hydroxy-1-propanesulfonate (HPS). Anion exchange of interlayer CO3 2- in synthetic hydrotalcites with the organic sulfonates induces disorders in layer stacking as characterized by powder X-ray diffraction and enables facile delamination in water. Thermal treatment of materials anion-exchanged by Ise (MgAl-Ise) and HPS (MgAl-HPS) in N2 and H2 resulted in the formation of Mg-Al mixed oxides with marked enhancement in Brunauer-Emmett-Teller (BET) surface area relative to those treated in air. Treatment in a flow of H2 is particularly effective, doubling the surface area of mixed oxides derived from MgAl-Ise relative to those obtained in a flow of N2. A higher degree of disorder in layer stacking in MgAl-HPS than MgAl-Ise resulted in the formation of Mg-Al mixed oxides with higher surface areas than those from MgAl-Ise. As a result, thermal activation of MgAl-HPS in a flow of H2 yielded Mg-Al mixed oxides with the highest BET surface area (410 m2 g-1) and CO2 uptake (1.6 mmol g-1 at 25 °C and 100 kPa) in all samples. These values are significantly higher than those obtained from the initial hydrotalcites as well as those reported in the literature with similar Mg-Al ratios. Investigation of the thermal activation steps by thermogravimetric analysis and mass spectrometry indicates that the key factors to achieve high surface area and CO2 uptake are to weaken interactions between layers by inducing stacking disorders and to facilitate the removal of interlayer sulfonates by preventing the formation of sulfates from them via thermal activation under a reducing environment.

| S-EPMC6643649 | biostudies-literature

Dissolution of Mesoporous Silica Supports in Aqueous Solutions: Implications for Mesoporous Silica-based Water Treatment Processes.

Project description:Under pH 7 - 10 conditions, the mesoporous silica supports proposed for use in water treatment are relatively unstable. In batch experiments conducted in pH 7 solutions, the commonly used support SBA-15 dissolved quickly, releasing approximately 30 mg/L of dissolved silica after 2 hours. In column experiments, more than 45% of an initial mass of 0.25 g SBA-15 dissolved within 2 days when a pH 8.5 solution flowed through the column. In a mixed iron oxide/SBA-15 system, the dissolution of SBA-15 changed the iron oxide reactivity toward H(2)O(2) decomposition, because dissolved silica deposited on iron oxide surface and changed its catalytic active sites. As with SBA-15, other mesoporous silica materials including HMS, MCM-41, four types of functionalized SBA-15, and two types of metal oxide-containing SBA-15 also dissolved under circumneutral pH solutions. The dissolution of mesoporous silica materials raises questions about their use under neutral and alkaline pH in aqueous solutions, because silica dissolution might compromise the behavior of the material.

| S-EPMC3465675 | biostudies-literature

Interaction of Pristine Hydrocalumite-Like Layered Double Hydroxides with Carbon Dioxide.

Project description:The layered double hydroxides (LDHs) of Ca2+ and trivalent cations, Al3+ and Fe3+, are single-source precursors to generate supported CaO, which picks up CO2 from the gas phase in the temperature range 350-550 °C. The supports are ternary oxides, mayenite, and Ca2Fe2O5. The uptake capacity of the Fe3+-containing LDH at 1.9 mmol g-1 is two times the capacity of the Al3+-containing LDH. The product of CO2 uptake is calcite CaCO3. It is observed that the intercalated chloride ions reduce the thermal penalty by inducing the early decomposition of CaCO3. In the case of the chloride-intercalated LDHs of Ca2+ and Fe3+, the CaCO3 formed is completely decomposed at 900 °C. This is in contrast with the CaCO3 formed from bare CaO, which shows no sign of decomposition at 900 °C under similar conditions. This work shows that the hydrocalumite-like LDHs are candidate materials for CO2 mineralization.

| S-EPMC6648629 | biostudies-literature

Effect of Drying on the Fabrication of MgAl Layered Double Hydroxides.

Project description:This study aimed to evaluate the synthesis of MgAl/LDH from the drying process perspective, evaluating the influence of temperature (75-90 °C) and time (16-20 h) in the drying process. The synthesis was performed, maintaining a ratio of 2:1 of Mg/Al, and the drying was conducted according to a 22 experimental design: four axial points and three repetitions at the central point. The surface area and pore diameter ranged from 4.09 to 18.55 m2/g and 12.50 to 24.46 nm. Fourier transform infrared (FTIR) analysis indicated the drying-caused variation of the LDH typical bands intensities. Scanning electron microscopy (SEM) images showed the tendency of the increase of agglomeration with the temperature elevation. The drying parameters' influence was evident for X-ray diffraction (XRD) analysis observing the crystallite size increment, from 13.10 to 38.94 nm, and basal spacing variation, from 7.52 to 7.64 Å. The statistical models for growing crystal and reduction of the basal spacing were physically consistent but with low values of R 2. The drying time and temperature had a considerable influence on the chemical, physical, structural, and morphological properties of LDH.

| S-EPMC8388087 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data