Hybrid catalysts based on N-heterocyclic carbene anchored on hierarchical zeolites.

ABSTRACT: Hybrid materials have been synthesized by anchoring a N-heterocyclic carbene (NHC) precursor on different inorganic zeolitic supports with hierarchical porosity, in particular hierarchical HZSM-5 and SAPO-5. Hierarchical porous inorganic supports have been obtained both by top-down and bottom-up approaches and the role of hierarchical porosity has been evaluated. A detailed physico-chemical characterization has been performed on the organic-inorganic hybrids using a multi-technique approach (XRD, volumetric and thermogravimetric analysis, ssNMR and FTIR) in order to establish a structure-property relationship. The hybrids were tested in the benzoin condensation reaction of furfural, a base catalyzed reaction.

SUBMITTER: Gianotti E

PROVIDER: S-EPMC9074450 | biostudies-literature | 2019 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Hybrid catalysts based on N-heterocyclic carbene anchored on hierarchical zeolites.

Gianotti Enrica E Miletto Ivana I Ivaldi Chiara C Paul Geo G Marchese Leonardo L Meazza Marta M Rios Ramon R Raja Robert R

RSC advances 20191031 61

Hybrid materials have been synthesized by anchoring a N-heterocyclic carbene (NHC) precursor on different inorganic zeolitic supports with hierarchical porosity, in particular hierarchical HZSM-5 and SAPO-5. Hierarchical porous inorganic supports have been obtained both by top-down and bottom-up approaches and the role of hierarchical porosity has been evaluated. A detailed physico-chemical characterization has been performed on the organic-inorganic hybrids using a multi-technique approach (XRD ...[more]

PMID: 35528109

Similar Datasets

Project description:In this paper, the ultrasonic-assisted desilication technique was reported as an attractive and efficient way for the preparation of hierarchical zeolites with MFI structure type. The prepared materials were used as active catalysts for the dehydration of ethanol into diethyl ether and ethylene. For all catalysts, the selectivity to diethyl ether was ca 95% or higher up to 210 °C, with catalytic activity in the range of 40-68%. In case of desilicated zeolites, at 270-290 °C, the conversion of ethanol was full with selectivity to ethylene ca 80%. MFI-type commercial zeolite was treated with a sodium and/or tetrabutylammonium hydroxide aqueous solutions (NaOH or NaOH/TBAOH) for 30 min. In the case of the application of ultrasounds, a QSonica Q700 sonicator (60 W and 20 kHz) equipped with a "1" diameter horn was used. In all cases, desilication was performed in an ice bath in order to keep the procedure conditions at low temperature. It was indicated that the use of ultrasounds during desilication procedure caused higher extraction of silicon and aluminum, which was connected with an elevated mesoporosity in relation to the samples modified in the absence of ultrasounds. Ultrasonic-assisted treatment of MFI-type zeolite caused also an apparent formation of numerous holes inside zeolite grains, resembling the look of "swiss cheese". Furthermore, it was indicated that the samples prepared using ultrasonic irradiation exhibited enhanced catalytic properties in the dehydration of ethanol. For instance, MFI-type zeolite treated with NaOH/TBAOH alkaline mixture containing 10 mol% of TBAOH in the presence of ultrasounds (M-10 s) demonstrated higher both conversion of ethanol (59% vs. 47%) and selectivity to diethyl ether (95% vs. 93%) in comparison with zeolite modified conventionally (M-10c). The best catalyst was zeolite ultrasonically desilicated with NaOH/TBAOH solution of 70 mol% of TBAOH (M-70s). Generally, this catalyst indicated the highest conversion of ethanol, very high selectivity to diethyl ether (94-100%) at 150-210 °C and the highest selectivity to ethylene among investigated catalysts (21%, 66% and 84%) at 230 °C, 250 oC and 270 °C.

Dataset Information

Hybrid catalysts based on N-heterocyclic carbene anchored on hierarchical zeolites.

Publications

Hybrid catalysts based on N-heterocyclic carbene anchored on hierarchical zeolites.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets