Repeatable Self-Healing of a Protective Coating Based on Vegetable-Oil-Loaded Microcapsules.

ABSTRACT: Generally, microcapsule-based self-healing materials have the limitation of single local self-healing. A few studies have reported repeatable self-healing in these microcapsular materials, but there is a challenge to develop multi-cycle self-healing materials that have the advantages of easier preparation and a more efficient operation. In this work, a mixture of two vegetable oils, soybean and olive oil, was used as a healing agent. The atmospheric oxygen-induced reaction behavior (in the presence of a catalyst) was investigated for various compositions of the vegetable oil mixtures; infrared spectroscopy, recovery testing, and viscoelasticity measurement were performed to find an optimum composition of the healing agent. Microcapsules loaded with soybean oil and catalyst-containing olive oil were separately prepared and used to prepare a dual-capsule self-healing coating. It was demonstrated through optical and scanning electron microscopy that, upon scribing the self-healing coating, the vegetable oils flowed out from microcapsules to self-heal the damaged area. When the healed area of the self-healing coating was re-scribed, self-healing was repeated, which was confirmed by scanning electron microscopy (SEM) and anticorrosion and electrochemical testing. Our new repeatable self-healing coating provides the merits of easy preparation, no need for external intervention such as light irradiation, and an environmentally-friendly nature.

SUBMITTER: Song YK

PROVIDER: S-EPMC9146027 | biostudies-literature | 2022 May

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Repeatable Self-Healing of a Protective Coating Based on Vegetable-Oil-Loaded Microcapsules.

Song Young-Kyu YK Kim Hyun-Woo HW Chung Chan-Moon CM

Polymers 20220515 10

Generally, microcapsule-based self-healing materials have the limitation of single local self-healing. A few studies have reported repeatable self-healing in these microcapsular materials, but there is a challenge to develop multi-cycle self-healing materials that have the advantages of easier preparation and a more efficient operation. In this work, a mixture of two vegetable oils, soybean and olive oil, was used as a healing agent. The atmospheric oxygen-induced reaction behavior (in the prese ...[more]

PMID: 35631895

Similar Datasets

Project description:Contemporary studies of self-healing polymer composites are based on microcapsules synthesized using synthetic and toxic polymers, biopolymers, etc. via methods such as in situ polymerization, electrospraying, and air atomization. Herein, we synthesized a healing agent, epoxy (EPX) encapsulated calcium carbonate (CC) microcapsules, which was used to prepare self-healing EPX composites as a protective coating for metals. The CC microcapsules were synthesized using two facile methods, namely, the soft-template method (STM) and the in situ emulsion method (EM). Microcapsules prepared using the STM (ST-CC) were synthesized using sodium dodecyl sulphate (SDS) surfactant micelles as the soft-template, while the microcapsules prepared using the EM (EM-CC) were synthesized in an oil-in-water (O/W) in situ emulsion. These prepared CC microcapsules were characterized using light microscopy (LMC), field emission scanning electron microscopy (FE-SEM), fourier transform infrared spectroscopy (FTIR), nuclear magnetic resonance spectroscopy (NMR), and thermogravimetric analysis (TGA). The synthesized ST-CC microcapsules were spherical in shape, with an average diameter of 2.5 μm and an average shell wall thickness of 650 nm, while EM-CC microcapsules had a near-spherical shape with an average diameter of 3.4 μm and an average shell wall thickness of 880 nm. The ST-CC capsules exhibited flake-like rough surfaces while EM-CC capsules showed smooth bulgy surfaces. The loading capacity of ST-CC and EM-CC microcapsules were estimated using TGA and found to be 11% and 36%, respectively. The FTIR and NMR spectra confirmed the EPX encapsulation and the unreactive nature of the loaded EPX with the inner walls of CC microcapsules. The synthesized CC microcapsules were further incorporated into an EPX matrix to prepare composite coatings with 10 (w/w%), 20 (w/w%), and 50 (w/w%) capsule loadings. The prepared EPX composite coatings were scratched and observed using FE-SEM and LMC to evaluate the release of encapsulated EPX inside the CC capsules, which is analogous to the healing behaviour. Moreover, EPX composite coatings with 20 (w/w%) and 50 (w/w%) of ST-CC showed better healing performances. Thus, it was observed that ST-CC microcapsules outperformed EM-CC. Additionally, the EPX/CC coatings showed remarkable self-healing properties by closing the gaps of the scratch surfaces. Thus, these formaldehyde-free, biocompatible, biodegradable, and non-toxic CC based EPX composite coatings hold great potential to be used as a protective coating for metal substrates. Primary results detected significant corrosion retardancy due to the self-healing coatings under an accelerated corrosion process, which was performed with a salt spray test.

Dataset Information

Repeatable Self-Healing of a Protective Coating Based on Vegetable-Oil-Loaded Microcapsules.

Publications

Repeatable Self-Healing of a Protective Coating Based on Vegetable-Oil-Loaded Microcapsules.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets