Enhancing the mechanical properties and providing bioactive potential for graphene oxide/montmorillonite hybrid dental resin composites.

ABSTRACT: This in vitro study synthetized hybrid composite nanoparticles of graphene oxide (GO) and montmorillonite MMt (GO-MMt) by ultrasound treatments. Samples were characterized by X-ray diffraction, FT-Raman, FTIR, TEM and SEM. The effect of their incorporation (0.3% and 0.5%) on the mechanical properties in a resin-based composite (RBC) and their bioactivity potential were evaluated. The specimens were characterized by evaluating their 3-point flexural strength (n = 6), modulus of elasticity (n = 6), degree of conversion (n = 6), microhardness (n = 6), contact angle (n = 3) and SEM analysis (n = 3). In vitro test in SBF were conducted in the RBCs modified by the hybrid. Overall, the synthetized hybrid composite demonstrated that GO was intercalated with MMt, showing a more stable compound. ANOVA and Tukey test showed that RBC + 0.3% GO-MMt demonstrated superior values of flexural strength, followed by RBC + 0.5% GO-MMt (p < 0.05) and both materials showed higher values of microhardness. All groups presented a contact angle below 90°, characterizing hydrophilic materials. RBCs modified by the hybrid showed Ca and P deposition after 14 days in SBF. In conclusion, RBCs composed by the hybrid showed promising results in terms of mechanical properties and bioactive potential, extending the application of GO in dental materials.

SUBMITTER: Velo MMAC

PROVIDER: S-EPMC9205868 | biostudies-literature | 2022 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Enhancing the mechanical properties and providing bioactive potential for graphene oxide/montmorillonite hybrid dental resin composites.

Velo Marilia Mattar de Amôedo Campos MMAC Filho Francisco Gilmário Nunes FGN de Lima Nascimento Tatiana Rita TR Obeid Alyssa Teixeira AT Castellano Lúcio Cançado LC Costa Reginaldo Mendonça RM Brondino Nair Cristina Margarido NCM Fonseca Maria Gardennia MG Silikas Nikolaos N Mondelli Rafael Francisco Lia RFL

Scientific reports 20220617 1

This in vitro study synthetized hybrid composite nanoparticles of graphene oxide (GO) and montmorillonite MMt (GO-MMt) by ultrasound treatments. Samples were characterized by X-ray diffraction, FT-Raman, FTIR, TEM and SEM. The effect of their incorporation (0.3% and 0.5%) on the mechanical properties in a resin-based composite (RBC) and their bioactivity potential were evaluated. The specimens were characterized by evaluating their 3-point flexural strength (n = 6), modulus of elasticity (n = 6) ...[more]

PMID: 35715426

Similar Datasets

Project description:BackgroundThis study aimed to develop ion-releasing and antibacterial resin-based dental sealants comprising 3 to 6 wt% monocalcium phosphate monohydrate (MCPM, M), 3 to 6 wt% bioactive glass (BAG, B), and 3 to 6 wt% polylysine (PLS, P). The physical properties, mechanical performance, cytotoxicity, and inhibition of S. mutans biofilm by these materials were subsequently evaluated.MethodsFive experimental dental sealants were formulated as follows: F1 (M6B6P6), F2 (M6B6P3), F3 (M3B3P6), F4 (M3B3P3), and F5 (M0B0P0, serving as the control). ClinproXT (CP, 3 M, Saint Paul, MN, USA) was used for commercial comparison. The degree of monomer conversion (DC) was determined using attenuated total reflectance-Fourier transform infrared spectroscopy (n = 5). The biaxial flexural strength (n = 6) and Vickers surface microhardness (n = 5) of the materials were evaluated after a 24-hour immersion in water. The element release over 4 weeks was measured using inductively coupled plasma-optical emission spectrometry (ICP-OES) (n = 3). The cell viability of mouse fibrosarcoma cells exposed to the extract was assessed via an MTT assay (n = 3). Additionally, the inhibition of S. mutans biofilm was tested (n = 3). Statistical analysis was conducted using one-way ANOVA and the Tukey HSD test.ResultsThe lowest DC among experimental sealants was obtained from F1 (66 ± 4%), which was significantly higher than CP (54 ± 2%, p < 0.001). The lowest biaxial flexural strength was obtained from F3 (131 ± 47 MPa). This was comparable to that of CP (140 ± 58 MPa, p = 0.992). The lowest surface microhardness among experimental materials was detected with F2 (19 ± 2 Vickers hardness number), which was higher than that of CP (12 ± 1 Vickers hardness number, p = 0.003). Furthermore, high cell viability of > 90% after exposure to extracts from the experimental materials was detected, which was similar to that observed with CP. Additionally, the experimental materials exhibited higher Ca and P release compared to CP and showed a potential trend for reducing S. mutans biofilm formation. Increasing additive concentrations exhibited minimal effects on material properties, except for enhanced elemental release and a slight reduction in BFM with higher PLS content.ConclusionThe experimental sealants provided sufficient physical and mechanical strength and maintained cell viability and bacterial inhibition with higher elemental release than the commercial product.

Dataset Information

Enhancing the mechanical properties and providing bioactive potential for graphene oxide/montmorillonite hybrid dental resin composites.

Publications

Enhancing the mechanical properties and providing bioactive potential for graphene oxide/montmorillonite hybrid dental resin composites.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets