One-Pot Synthesis of Cellulose/MXene/PVA Foam for Efficient Methylene Blue Removal.

ABSTRACT: Ti₃C₂T_x MXene has attracted considerable interest as a new emerging two-dimensional material for environmental remediation due to its high adsorption capacity. However, its use is greatly limited by its poor mechanical properties, low processability and recyclability, and the low dispersity of such powder materials. In this work, a porous adsorbent (C-CMP) containing cellulose nanocrystals (CNC), Ti₃C₂T_x MXene and polyvinyl alcohol (PVA) was prepared by a simple and environmentally-friendly foaming method. Glutaraldehyde was used as crosslinker to improve the mechanical properties and boost the adsorption efficiency of methylene blue (MB) molecules. Fourier transform infrared (FT-IR), elemental analysis (EDX) and thermogravimetric analysis (TGA) further confirmed that the preparation of the C-CMP foam and cross-linking reaction were successful. Scanning electron microscope (SEM) indicated that the macropores were distributed homogeneously. The adsorption experiment showed that maximum adsorption capacity of MB can reach 239.92 mg·g^-1 which was much higher than anionic dye (methyl orange, 45.25 mg·g^-1). The adsorption behavior fitted well with the Langmuir isotherm and pseudo-second-order kinetic models. Thermodynamic analysis indicated that the adsorption process was spontaneous and endothermic. Based on FT-IR, EDX and X-ray photoelectron spectroscopy (XPS) analysis, the adsorption mechanism between C-CMP and MB molecules was attributed to electrostatic interaction.

SUBMITTER: Zhao W

PROVIDER: S-EPMC9268378 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

One-Pot Route towards Active TiO₂ Doped Hierarchically Porous Cellulose: Highly Efficient Photocatalysts for Methylene Blue Degradation.

Project description:In this study, novel photocatalyst monolith materials were successfully fabricated by a non-solvent induced phase separation (NIPS) technique. By adding a certain amount of ethyl acetate (as non-solvent) into a cellulose/LiCl/N,N-dimethylacetamide (DMAc) solution, and successively adding titanium dioxide (TiO₂) nanoparticles (NPs), cellulose/TiO₂ composite monoliths with hierarchically porous structures were easily formed. The obtained composite monoliths possessed mesopores, and two kinds of macropores. Scanning Electron Microscope (SEM), Energy Dispersive Spectroscopy (EDS), Fourier Transform Infrared Spectroscopy (FT-IR), X-ray Diffraction (XRD), Brunauer-Emmett-Teller (BET), and Ultraviolet-visible Spectroscopy (UV-Vis) measurements were adopted to characterize the cellulose/TiO₂ composite monolith. The cellulose/TiO₂ composite monoliths showed high efficiency of photocatalytic activity in the decomposition of methylene blue dye, which was decomposed up to 99% within 60 min under UV light. Moreover, the composite monoliths could retain 90% of the photodegradation efficiency after 10 cycles. The novel NIPS technique has great potential for fabricating recyclable photocatalysts with highly efficiency.

| S-EPMC5506969 | biostudies-other

Efficient Adsorption of Methylene Blue by Porous Biochar Derived from Soybean Dreg Using a One-Pot Synthesis Method.

Project description:Soybean dreg is a by-product of soybean products production, with a large consumption in China. Low utilization value leads to random discarding, which is one of the important sources of urban pollution. In this work, porous biochar was synthesized using a one-pot method and potassium bicarbonate (KHCO3) with low-cost soybean dreg (SD) powder as the carbon precursor to investigating the adsorption of methylene blue (MB). The prepared samples were characterized with scanning electron microscopy (SEM), transmission electron microscopy (TEM), elemental analyzer (EA), Brunauer-Emmett-Teller (BET), X-ray diffractometer (XRD), Raman spectroscopy (Raman), Fourier transform infrared spectrometer (FTIR), and X-ray photoelectron spectroscopy (XPS). The obtained SDB-K-3 showed a high specific surface area of 1620 m2 g-1, a large pore volume of 0.7509 cm3 g-1, and an average pore diameter of 1.859 nm. The results indicated that the maximum adsorption capacity of SDB-K-3 to MB could reach 1273.51 mg g-1 at 318 K. The kinetic data were most consistent with the pseudo-second-order model and the adsorption behavior was more suitable for the Langmuir isotherm equation. This study demonstrated that the porous biochar adsorbent can be prepared from soybean dreg by high value utilization, and it could hold significant potential for dye wastewater treatment in the future.

| S-EPMC7865629 | biostudies-literature

Sawdust-Based Cellulose Nanocrystals Incorporated with ZnO Nanoparticles as Efficient Adsorption Media in the Removal of Methylene Blue Dye.

Project description:The continuous increase in the wastes generated from forestry, timber, and paper industries has engendered the need for their transformation into economically viable materials for the benefit of mankind. This study reports the preparation and application of sawdust-derived cellulose nanocrystals (CNC) incorporated with zinc oxide as a novel adsorbent for the removal of methylene blue (MB) from water. The CNC/ZnO nanocomposite was characterized using Fourier transform infrared, X-ray diffraction (XRD), and scanning electron microscopy. The amount of MB adsorbed was determined by a UV-vis spectrophotometer. The microscopic analysis revealed that the nanocomposite had a narrow particle size range and exhibited both spherical and rod-like morphologies. The XRD analysis of the nanocomposite showed characteristic high-intensity peaks in the range of 30-75° attributed to the presence of ZnO nanoparticles, which were responsible for the enhancement of the crystallinity of the nanocomposite. The results revealed a relationship between the MB removal efficiency and changes in solution pH, nanocomposite dosage, initial concentration, temperature, and reaction time. The adsorption equilibrium isotherm, measured in the temperature range of 25-45 °C and using a concentration of 20-100 mg/L, showed that the MB sorption followed the Langmuir isotherm with a maximum adsorption capacity of 64.93 mg/g. A pseudo-second-order kinetic model gave the best fit to the experimental data. Based on adsorption performance, the CNC/ZnO nanocomposite offers prospects for further research and application in amelioration of dye-containing effluent.

| S-EPMC7408268 | biostudies-literature

Synthesis and characterization of Cu(OH)<sub>2</sub>-NWs-PVA-AC Nano-composite and its use as an efficient adsorbent for removal of methylene blue.

Project description:The present study focused on the synthesis of copper hydroxide nanowires decorated on activated carbon (Cu(OH)2-NWs-PVA-AC). The obtained Cu(OH)2-NWs-PVA-AC Nano-composite was distinguished by XRD, SEM, EDX, BET, FTIR and XPS respectively. Besides, different variables such as solution pH, and initial dye concentration, contact time, and temperature were performed on the adsorption efficiency of MB in a small batch reactor. Further, the experimental results are analyzed by various kinetic models via PFO, PSO, intra-particle diffusion and Elovich models, and the results revealed that among the kinetic models, PSO shows more suitability. In addition, different adsorption isotherms were applied to the obtained experimental data and found that Langmuir-Freundlich and Langmuir isotherm were best fits with the maximum adsorption capacity of 139.9 and 107.6 mg/g, respectively. The Nano-composite has outstanding MB removal efficiency of 94-98.5% with a span of 10 min. and decent adsorption of about 98.5% at a pH of 10. Thermodynamic constants like Gibbs free energy, entropy, and enthalpy were analyzed from the temperature reliance. The results reveal the adsorption processes are spontaneous and exothermic in nature. The high negative value of ΔG° (- 44.11 to - 48.86 kJ/mol) and a low negative value of ΔH° (- 28.96 kJ/mol) show the feasibility and exothermic nature of the adsorption process. The synthesized dye was found to be an efficient adsorbent for the potential removal of cationic dye (methylene blue) from wastewater within a short time.

| S-EPMC7970965 | biostudies-literature

Ultra-Highly Efficient Removal of Methylene Blue Based on Graphene Oxide/TiO2/Bentonite Sponge.

Project description:An ultra-highly efficient Graphene Oxide/TiO2/Bentonite (GO/TiO2/Bent) sponge was synthesized using an in situ hydrothermal method. GO/TiO2/Bent sponge with a GO mass concentration of 10% exhibited the highest treatment efficiency of methylene blue (MB), combining adsorption and photocatalytic degradation, and achieved a maximum removal efficiency of 100% within about 70 min. To further prove the ultra-high removal capacity of the sponge, the concentration of MB in water increased to ten times the original concentration. At so high a MB concentration, the removal rate was still as high as 80% in 90 min. The photocatalytic mechanism of GO/TiO2/Bent sponge was discussed through XPS, PL and radicals quenching experiments. Here Bent can immobilize TiO2 and react with a photo-generated hole to increase the amount of hydroxyl radical; effectively enhancing the degradation of MB.GO sponge enlarges the sensitivity range of TiO2 to visible light by increasing the charge separation of TiO2 and reducing the recombination of photo-generated electron-hole pairs. Additionally, GO sponge with an interconnected porous structure provides an effective platform to immobilize TiO2/bent and makes them be easily recovered. The as-prepared sponge develops a simple and cost-effective strategy to realize the ultra-highly efficient treatment of dyes in wastewater.

| S-EPMC7078707 | biostudies-literature

Porous three-dimensional graphene foam/Prussian blue composite for efficient removal of radioactive (137)Cs.

Project description:In this study, a simple one-step hydrothermal reaction is developed to prepare composite based on Prussian blue (PB)/reduced graphene oxide foam (RGOF) for efficient removal of radioactive cesium ((137)Cs) from contaminated water. Scanning electron microscopy and transmission electron microscopy show that cubic PB nanoparticles are decorated on the RGO surface. Owing to the combined benefits of RGOF and PB, the composite shows excellent removal efficiency (99.5%) of (137)Cs from the contaminated water. The maximum adsorption capacity is calculated to be 18.67?mg/g. An adsorption isotherm fit-well the Langmuir model with a linear regression correlation value of 0.97. This type of composite is believed to hold great promise for the clean-up of (137)Cs from contaminated water around nuclear plants and/or after nuclear accidents.

| S-EPMC4680859 | biostudies-other

Easy Preparation of Liposome@PDA Microspheres for Fast and Highly Efficient Removal of Methylene Blue from Water.

Project description:Mussel-inspired chemistry was usefully exploited here with the aim of developing a high-efficiency, environmentally friendly material for water remediation. A micro-structured material based on polydopamine (PDA) was obtained by using liposomes as templating agents and was used for the first time as an adsorbent material for the removal of methylene blue (MB) dye from aqueous solutions. Phospholipid liposomes were made by extrusion and coated with PDA by self-polymerization of dopamine under simple and mild conditions. The obtained Liposome@PDA microspheres were characterized by DLS and Zeta potential analysis, TEM microscopy, and FTIR spectroscopy. The effects of pH, temperature, MB concentration, amount of Liposome@PDA, and contact time on the adsorption process were investigated. Results showed that the highest adsorption capacity was obtained in weakly alkaline conditions (pH = 8.0) and that it could reach up to 395.4 mg g-1 at 298 K. In addition, adsorption kinetics showed that the adsorption behavior fits a pseudo-second-order kinetic model well. The equilibrium adsorption data, instead, were well described by Langmuir isotherm. Thermodynamic analysis demonstrated that the adsorption process was endothermic and spontaneous (ΔG0 = -12.55 kJ mol-1, ΔH0 = 13.37 kJ mol-1) in the investigated experimental conditions. Finally, the applicability of Liposome@PDA microspheres to model wastewater and the excellent reusability after regeneration by removing MB were demonstrated.

| S-EPMC8584841 | biostudies-literature

Synthesis of TiO2NWS@AuNPS Composite Catalyst for Methylene Blue Removal.

Project description:In this article, HBP-NH₂-modified titania nanowire (TiO2NWS)-decorated Au nanoparticles (TiO2NWS@AuNPS) were synthesized by one-step method. The role of HBP-NH₂ concentration in the formation of TiO2NWS was investigated. The fineness and uniformity of pure TiO2NWS were enhanced by absorbed amino groups from amino-terminated hyperbranched polymer (HBP-NH₂). The morphology and crystal structure of TiO2NWS and TiO2NWS@AuNPS were examined by transmission electron microscopy (TEM), X-ray diffraction (XRD), and Fournier transform infrared (FTIR) spectroscopy. The chemical states of gold, titanium and oxygen were analyzed by X-ray photoelectron spectroscopy (XPS). The results showed that at the concentration of HBP-NH₂ 100 g/L, the mean diameter of TiO2NWS was nearly 72 nm and Au nanoparticles were uniformly distributed on the surface of TiO2NWS. The presence of AuNPS improved the photocatalytic properties of TiO2NWS under UV light irradiation. The Au load was believed to improve the utilization rate of the photoelectron and activated the adsorbed oxygen. The obtained TiO2NWS@AuNPS decomposed 99.6% methylene blue (MB) after 300 min when subjected to UV light irradiation. After five cycles of the catalyzing process, the TiO2NWS@AuNPS still retained over 90% of its catalytic ability for MB. The Au deposition was found responsible for the high catalytic activity of TiO2NWS@AuNPS.

| S-EPMC6025176 | biostudies-literature

Sorghum-Waste-Derived High-Surface Area KOH-Activated Porous Carbon for Highly Efficient Methylene Blue and Pb(II) Removal.

Project description:With the development of the environment and human society, the removal of metal ions and dyes in wastewater treatment remains an urgent problem to solve. In this work, two biomass carbon adsorbents were synthesized by a KOH activation and carbonization route using sorghum stem and root as carbon precursors. In comparison with the samples without KOH activation, the pore structure of the KOH-activated carbon has been dramatically improved. The findings show that the specific surface areas of the adsorbents by sorghum stem (S1) and sorghum root (R1) were 948.6 and 168.1 m2 g-1, respectively. Meanwhile, the abundant OH- and COO- groups on the surface of these adsorbents endow them with negative polarity, thereby exhibiting excellent adsorption performance for removing methylene blue (MB) and Pb(II) from wastewater. The adsorption amount and removal rate of S1 were 98.1 mg g-1 and 98.08%, respectively, for MB, whereas those of R1 were 197.6 mg g-1 and 98.82% for the Pb(II) ion, respectively. Our findings offer an invaluable insight into designing and synthesizing a highly efficient sustainable adsorbent to remove MB and Pb(II) based on biomass agricultural waste.

| S-EPMC7301384 | biostudies-literature

Efficient Removal of Methylene Blue and Ciprofloxacin from Aqueous Solution Using Flower-like, Nanostructured ZnO Coating under UV Irradiation.

Project description:Flower-like ZnO architectures assembled with many nanorods were successfully synthesized through Thermionic Vacuum Arc, operated both in direct current (DC-TVA) and a pulsed mode (PTVA), and coupled with annealing in an oxygen atmosphere. The prepared coatings were analysed by scanning-electron microscopy with energy-dispersive X-ray-spectroscopy (SEM-EDX), X-ray-diffraction (XRD), and photoluminescence (PL) measurements. By simply modifying the TVA operation mode, the morphology and uniformity of ZnO nanorods can be tuned. The photocatalytic performance of synthesized nanostructured ZnO coatings was measured by the degradation of methylene-blue (MB) dye and ciprofloxacin (Cipro) antibiotic. The ZnO (PTVA) showed enhancing results regarding the photodegradation of target contaminants. About 96% of MB molecules were removed within 60 min of UV irradiation, with a rate constant of 0.058 min-1, which is almost nine times higher than the value of ZnO (DC-TVA). As well, ZnO (PTVA) presented superior photocatalytic activity towards the decomposition of Cipro, after 240 min of irradiation, yielding 96% degradation efficiency. Moreover, the agar-well diffusion assay performance against both Gram-positive and Gram-negative bacteria confirms the degradation of antibiotic molecules by the UV/ZnO (PTVA) approach, without the formation of secondary hazardous products during the photocatalysis process. Repeated cyclic usage of coatings revealed excellent reusability and operational stability.

| S-EPMC9267983 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data