One-Pot Route towards Active TiO₂ Doped Hierarchically Porous Cellulose: Highly Efficient Photocatalysts for Methylene Blue Degradation.

ABSTRACT: In this study, novel photocatalyst monolith materials were successfully fabricated by a non-solvent induced phase separation (NIPS) technique. By adding a certain amount of ethyl acetate (as non-solvent) into a cellulose/LiCl/N,N-dimethylacetamide (DMAc) solution, and successively adding titanium dioxide (TiO₂) nanoparticles (NPs), cellulose/TiO₂ composite monoliths with hierarchically porous structures were easily formed. The obtained composite monoliths possessed mesopores, and two kinds of macropores. Scanning Electron Microscope (SEM), Energy Dispersive Spectroscopy (EDS), Fourier Transform Infrared Spectroscopy (FT-IR), X-ray Diffraction (XRD), Brunauer-Emmett-Teller (BET), and Ultraviolet-visible Spectroscopy (UV-Vis) measurements were adopted to characterize the cellulose/TiO₂ composite monolith. The cellulose/TiO₂ composite monoliths showed high efficiency of photocatalytic activity in the decomposition of methylene blue dye, which was decomposed up to 99% within 60 min under UV light. Moreover, the composite monoliths could retain 90% of the photodegradation efficiency after 10 cycles. The novel NIPS technique has great potential for fabricating recyclable photocatalysts with highly efficiency.

SUBMITTER: Sun X

PROVIDER: S-EPMC5506969 | biostudies-other | 2017 Mar

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

One-Pot Synthesis of Cellulose/MXene/PVA Foam for Efficient Methylene Blue Removal.

Project description:Ti3C2Tx MXene has attracted considerable interest as a new emerging two-dimensional material for environmental remediation due to its high adsorption capacity. However, its use is greatly limited by its poor mechanical properties, low processability and recyclability, and the low dispersity of such powder materials. In this work, a porous adsorbent (C-CMP) containing cellulose nanocrystals (CNC), Ti3C2Tx MXene and polyvinyl alcohol (PVA) was prepared by a simple and environmentally-friendly foaming method. Glutaraldehyde was used as crosslinker to improve the mechanical properties and boost the adsorption efficiency of methylene blue (MB) molecules. Fourier transform infrared (FT-IR), elemental analysis (EDX) and thermogravimetric analysis (TGA) further confirmed that the preparation of the C-CMP foam and cross-linking reaction were successful. Scanning electron microscope (SEM) indicated that the macropores were distributed homogeneously. The adsorption experiment showed that maximum adsorption capacity of MB can reach 239.92 mg·g-1 which was much higher than anionic dye (methyl orange, 45.25 mg·g-1). The adsorption behavior fitted well with the Langmuir isotherm and pseudo-second-order kinetic models. Thermodynamic analysis indicated that the adsorption process was spontaneous and endothermic. Based on FT-IR, EDX and X-ray photoelectron spectroscopy (XPS) analysis, the adsorption mechanism between C-CMP and MB molecules was attributed to electrostatic interaction.

| S-EPMC9268378 | biostudies-literature

Boosted Visible-Light Photodegradation of Methylene Blue by V and Co Co-Doped TiO₂.

Project description:In this work, TiO₂ photocatalysts, co-doped with transition metal ions vanadium (V) and cobalt (Co) ((V,Co)⁻TiO₂), were synthesized by the sol⁻gel method. The synthesized photocatalysts were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), nitrogen adsorption and desorption measurement, UV-Vis absorption and photoluminescence spectrum (PL) spectra. The results show that V and Co co-doping has significant effects on sample average crystalline grain size, absorption spectrum, recombination efficiency of photo-induced electron-hole pairs (EHPs), and photocatalytic degradation efficiency of methylene blue (MB). (V,Co)⁻TiO₂ photocatalyst exhibits an obvious red shift of the absorption edge to 475 nm. Photocatalytic degradation rate of (V,Co)⁻TiO₂ sample for MB in 60 min is 92.12% under a Xe lamp with a cut-off filter (λ > 400 nm), which is significantly higher than 56.55% of P25 under the same conditions. The first principles calculation results show that V and Co ions doping introduces several impurity energy levels, which can modulate the location of the valence band and conduction band. An obvious lattice distortion is produced in the meantime, resulting in the decrease in photo-generated EHP recombination. Thus, (V,Co)⁻TiO₂ photocatalyst performance is significantly improved.

| S-EPMC6213182 | biostudies-literature

Template-Free, Solid-State Synthesis of Hierarchically Macroporous S-Doped TiO2 Nano-Photocatalysts for Efficient Water Remediation.

Project description:Nanosized sulfur-doped titanium dioxide emerged as an attractive photocatalyst in various environmental remediation applications, yet most synthesis methods require hazardous sulfurizing agents and intricate synthesis procedures. Herein, we present a facile, sustainable, and environmentally friendly preparation process for the production of visible-light-active meso-macroporous sulfur-doped anatase TiO2 (S-TiO2) nanoparticles for the first time. This strategy encompasses solventless mixing of titanium salt and surfeit yet nontoxic abundant elemental sulfur under continuous ball milling and moderate thermoannealing. The characterizations of as-obtained S-TiO2 nanoparticles showed enhanced physicochemical properties including distinctive surface features composed of hierarchical hollow macroporous channels having nanostructured mesoporous core walls. The annealing temperature was observed to control the structure and extent of sulfur doping in TiO2. Upon insertion of a sulfur atom into the TiO2 lattice, the band gap energy of S-TiO2 was significantly lowered, facilitating the enhanced photochemical activity. Owing to the effective S doping (1.7-2.8 atom %), and the interconnected hollow meso-macroporous nanostructure, the resulting nanosized S-TiO2 exhibited unique adsorption properties and superior photocatalytic efficiency for the rapid degradation of hazardous organic dyes and phenols for water remediation. The presented strategy holds high potential to provide rapid production of a hierarchical and highly porous S-TiO2 photocatalyst on a large scale for various environmental remediation and other myriad photochemical applications.

| S-EPMC7161069 | biostudies-literature

Hydrogen peroxide route to Sn-doped titania photocatalysts.

Project description:UnlabelledBackgroundThe work aims at improving photocatalytic activity of titania under Vis light irradiation using modification by Sn ions and an original, simple synthesis method. Tin-doped titania catalysts were prepared by thermal hydrolysis of aqueous solutions of titanium peroxo-complexes in the presence of SnCl4 or SnCl2 using an original, proprietary "one pot" synthesis not employing organic solvents, metallo-organic precursors, autoclave aging nor post-synthesis calcination. The products were characterized in details by powder diffraction, XPS, UV-vis, IR, and Raman spectroscopies, electron microscopy and surface area and porosity measurementsResultsThe presence of tin in synthesis mixtures favors the formation of rutile and brookite at the expense of anatase, decreases the particle size of all formed titania polymorphs, and extends light absorption of titania to visible light region >400 nm by both red shift of the absorption edge and introduction of new chromophores. The photocatalytic activity of titania under UV irradiation and >400 nm light was tested by decomposition kinetics of Orange II dye in aqueous solutionConclusionsDoping by Sn improves titania photoactivity under UV light and affords considerable photoactivity under >400 nm light due to increased specific surface area and a phase heterogeneity of the Sn-doped titania powders.

| S-EPMC3531300 | biostudies-literature

Effective photocatalytic degradation and physical adsorption of methylene blue using cellulose/GO/TiO2 hydrogels.

Project description:Environmentally friendly cellulose/GO/TiO2 hydrogel photocatalyst has been successfully fabricated via a green, simple, and one-step method and evaluated as the photocatalyst and adsorbent for the removal of methylene blue (MB). The XRD and FTIR analysis suggested the strong interaction among cellulose, GO and TiO2, resulting from the formation of hydrogen bonds. Due to the unique porous structure of cellulose hydrogel and introduction of GO, the cellulose/GO/TiO2 hydrogel showed superior (degradation ratio ∼ 93%) and reproducible (no significant change during the ten consecutive cycles) performance in the removal of MB under UV light. Consequently, the prepared cellulose/GO/TiO2 hydrogel can be applied as an eco-friendly, high-performance, reproducible, and stable photocatalyst and adsorbent for the removal of MB. This green hydrogel is a promising candidate for dye wastewater treatment. Moreover, this work is expected to extend the scope of bio-templated synthesis of other nanomaterials for various applications.

| S-EPMC9055038 | biostudies-literature

Efficient Adsorption of Methylene Blue by Porous Biochar Derived from Soybean Dreg Using a One-Pot Synthesis Method.

Project description:Soybean dreg is a by-product of soybean products production, with a large consumption in China. Low utilization value leads to random discarding, which is one of the important sources of urban pollution. In this work, porous biochar was synthesized using a one-pot method and potassium bicarbonate (KHCO3) with low-cost soybean dreg (SD) powder as the carbon precursor to investigating the adsorption of methylene blue (MB). The prepared samples were characterized with scanning electron microscopy (SEM), transmission electron microscopy (TEM), elemental analyzer (EA), Brunauer-Emmett-Teller (BET), X-ray diffractometer (XRD), Raman spectroscopy (Raman), Fourier transform infrared spectrometer (FTIR), and X-ray photoelectron spectroscopy (XPS). The obtained SDB-K-3 showed a high specific surface area of 1620 m2 g-1, a large pore volume of 0.7509 cm3 g-1, and an average pore diameter of 1.859 nm. The results indicated that the maximum adsorption capacity of SDB-K-3 to MB could reach 1273.51 mg g-1 at 318 K. The kinetic data were most consistent with the pseudo-second-order model and the adsorption behavior was more suitable for the Langmuir isotherm equation. This study demonstrated that the porous biochar adsorbent can be prepared from soybean dreg by high value utilization, and it could hold significant potential for dye wastewater treatment in the future.

| S-EPMC7865629 | biostudies-literature

Hierarchically Porous Zirconia Monolith Fabricated from Bacterial Cellulose and Preceramic Polymer.

Project description:A hierarchically porous zirconia (ZrO2) monolith was successfully fabricated by using bacterial cellulose (BC) as a biotemplate and preceramic polymer as a zirconium resource, via freeze-drying and two-step calcination process. Images of scanning electron microscopy showed that the ZrO2 monolith well-replicated a three-dimensional reticulated structure of pristine BC and possessed good morphology stability till 1100 °C in air. Results of N2 adsorption/desorption and mercury porosimetry analysis revealed the hierarchically porous structure and large specific area (9.7 m2·g-1) of the ZrO2 monolith, respectively. Patterns of X-ray powder diffraction indicated that the monoclinic phase and tetragonal phase coexisted in the ZrO2 monolith with the former as the main phase. In addition, the ZrO2 monolith possessed low bulk density (0.13 g·cm-3) and good mechanical strength. These properties suggest that the as-prepared ZrO2 monolith has a great potential to serve as an ideal catalyst or catalyst support.

| S-EPMC6641484 | biostudies-literature

Hierarchically Porous, Biphasic, and C-Doped TiO2 for Solar Photocatalytic Degradation of Dyes and Selective Oxidation of Benzyl Alcohol.

Project description:Macroporous TiO2 monoliths were synthesized by self-sustained combustion reactions of molded pellets made up of a mixture of TiCl4 as a precursor, urea as a fuel, ammonium nitrate as an oxidizer, and starch as a binder. The porous TiO2 monoliths were found to be a heterostructure of anatase and rutile phases, in addition to being doped with carbon. Variation in the amount of starch yielded porous monoliths of different anatase-rutile ratios (increasing rutile component from 0 to 40%) but comparable Brunauer-Emmett-Teller (BET) surface area (∼30 m2 g-1). The porous monoliths obtained, where the TiCl4/starch mass ratio was 2.17, exhibit exceptional photocatalytic activity in the degradation of dyes (methylene blue and methyl orange) and selective oxidation of benzyl alcohol to benzaldehyde under natural sunlight. The synergistic combination of high surface area, porous network, lowered band gap due to heterostructured anatase-rutile polymorphs, and the presence of doped carbon renders the macroporous TiO2 an efficient photocatalyst.

| S-EPMC8154131 | biostudies-literature

Studies on Kinetics, Isotherms, Thermodynamics and Adsorption Mechanism of Methylene Blue by N and S Co-Doped Porous Carbon Spheres.

Project description:Heteroatom-doped carbon is widely used in the fields of adsorbents, electrode materials and catalysts due to its excellent physicochemical properties. N and S co-doped porous carbon spheres (N,S-PCSs) were synthesized using glucose and L-cysteine as carbon and heteroatom sources using a combined hydrothermal and KOH activation process. The physicochemical structures and single-factor methylene blue (MB) adsorption properties of the N,S-PCSs were then studied. The optimized N,S-PCSs-1 possessed a perfect spherical morphology with a 2-8-μm diameter and a large specific area of 1769.41 m2 g-1, in which the N and S contents were 2.97 at% and 0.88 at%, respectively. In the single-factor adsorption experiment for MB, the MB adsorption rate increased with an increase in carbon dosage and MB initial concentration, and the adsorption reached equilibrium within 2-3 h. The pseudo-second-order kinetic model could excellently fit the experimental data with a high R2 (0.9999). The Langmuir isothermal adsorption equation fitted well with the experimental results with an R2 value of 0.9618, and the MB maximum adsorption quantity was 909.10 mg g-1. The adsorption of MB by N,S-PCSs-1 was a spontaneous, endothermic, and random process based on the thermodynamics analyses. The adsorption mechanism mainly involved Van der Waals force adsorption, π-π stacking, hydrogen bonds and Lewis acid-base interactions.

| S-EPMC8308386 | biostudies-literature

Effective Disposal of Methylene Blue and Bactericidal Benefits of Using GO-Doped MnO2 Nanorods Synthesized through One-Pot Synthesis.

Project description:Graphene oxide (GO)-doped MnO2 nanorods loaded with 2, 4, and 6% GO were synthesized via the chemical precipitation route at room temperature. The aim of this work was to determine the catalytic and bactericidal activities of prepared nanocomposites. Structural, optical, and morphological properties as well as elemental composition of samples were investigated with advanced techniques such as X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, UV-visible (vis) spectroscopy, photoluminescence (PL), energy-dispersive spectrometry (EDS), and high-resolution transmission electron microscopy (HR-TEM). XRD measurements confirmed the monoclinic structure of MnO2. Vibrational mode and rotational mode of functional groups (O-H, C=C, C-O, and Mn-O) were evaluated using FTIR results. Band gap energy and blueshift in the absorption spectra of MnO2 and GO-doped MnO2 were identified with UV-vis spectroscopy. Emission spectra were attained using PL spectroscopy, whereas elemental composition of prepared materials was recorded with scanning electron microscopy (SEM)-EDS. Moreover, HR-TEM micrographs of doped and undoped MnO2 revealed elongated nanorod-like structure. Efficient degradation of methylene blue enhanced the catalytic activity in the presence of a reducing agent (NaBH4); this was attributed to the implantation of GO on MnO2 nanorods. Furthermore, substantial inhibition areas were measured for Escherichia coli (EC) ranging 2.10-2.85 mm and 2.50-3.15 mm at decreased and increased levels for doped MnO2 nanorods and 3.05-4.25 mm and 4.20-5.15 mm for both attentions against SA, respectively. In silico molecular docking studies suggested the inhibition of FabH and DNA gyrase of E. coli and Staphylococcus aureus as a possible mechanism behind the bactericidal activity of MnO2 and MnO2-doped GO nanoparticles (NPs).

| S-EPMC8482489 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data