Physical Adsorption of Graphene Oxide onto Polymer Latexes and Characterization of the Resulting Nanocomposite Particles.

ABSTRACT: Polymer/graphene oxide (GO) nanocomposite particles were prepared via heteroflocculation between 140-220 nm cationic latex nanoparticles and anionic GO nanosheets in either acidic or basic conditions. It is demonstrated that nanocomposite particles can be formed using either poly(2-vinylpyridine)-b-poly(benzyl methacrylate) (P2VP-PBzMA) block copolymer nanoparticles prepared by reversible-addition chain-transfer (RAFT)-mediated polymerization-induced self-assembly (PISA), or poly(ethylene glycol)methacrylate (PEGMA)-stabilized P2VP latexes prepared by traditional emulsion polymerization. These two latexes are different morphologically as the P2VP-PBzMA block copolymer latexes have P2VP steric stabilizer chains in their corona, whereas the PEGMA-stabilized P2VP particles have a P2VP core and a nonionic steric stabilizer. Nevertheless, both the P2VP-PBzMA and PEGMA-stabilized P2VP latexes are cationic at low pH. Thus, the addition of GO to these latexes causes flocculation to occur immediately due to the opposite charges between the anionic GO nanosheets and cationic latexes. Control heteroflocculation experiments were conducted using anionic sterically stabilized poly(potassium 3-sulfopropyl methacrylate)-b-poly(benzyl methacrylate) (PKSPMA-PBzMA) and nonionic poly(benzyl methacrylate) (PBzMA) nanoparticles to demonstrate that polymer/GO nanocomposite particles were not formed. The degree of flocculation and the strength of electrostatic interaction between the cationic polymer latexes and GO were assessed using disc centrifuge photosedimentometry (DCP), transmission electron microscopy (TEM), and UV-visible spectrophotometry. These studies suggest that the optimal conditions for the formation of polymer/GO nanocomposite particles were GO contents between 10% and 20% w/w relative to latex, with the latexes containing P2VP in their corona having a stronger electrostatic attraction to the GO sheets.

SUBMITTER: Wen SP

PROVIDER: S-EPMC9281389 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Incorporating unmodified silica nanoparticles onto polymer latexes to fabricate aqueous polymer dispersions without relying on electrostatic attraction during the Pickering emulsion polymerization process still faces challenges. For negatively charged silica nanoparticles to successfully adsorb onto polymer latexes, particularly in an anionic initiator emulsion polymerization system, they have remained elusive without the use of auxiliary monomers and cationic initiators. This study investigates various experimental parameters, such as emulsion polymerization temperature, monomer solubility, salt concentration, and cation type, to elucidate the factors influencing the adsorption of unmodified silica nanoparticles in Pickering emulsion polymerization. While poly(methyl methacrylate) (PMMA)/SiO2 hybrid latexes can be obtained under pH conditions of 5-6 and at temperatures of 65 °C or below, the loading rate of silica nanoparticles decreases as the reaction temperature increases, resulting in bare PMMA latexes without silica nanoparticle adsorption at temperatures exceeding 70 °C. Introducing styrene (St) into the monomer mixture with methyl methacrylate in a ratio of up to 10 wt % leads to a gradual decrease in silica nanoparticle loading rate, from 27.3 to 8.2 wt %, attributed to the low solubility of St in water. Furthermore, the presence of sodium ions (Na+) is found to be crucial for silica nanoparticle adsorption onto PMMA latexes, as the sodium ions have a stabilizing effect on both the silica nanoparticles and the silica nanoparticle-armored latexes. These findings highlight the complex nature of Pickering emulsion polymerization in the presence of unmodified silica nanoparticles, demonstrating that the loading rate of silica nanoparticles onto polymer latexes is influenced by various factors. These insights pave the way for developing aqueous polymer dispersions with high silica nanoparticle loading rates onto polymer latexes, which is a desirable trait in the coating industry.

Dataset Information

Physical Adsorption of Graphene Oxide onto Polymer Latexes and Characterization of the Resulting Nanocomposite Particles.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets