Fabrication of Durable Superhydrophobic Surface for Versatile Oil/Water Separation Based on HDTMS Modified PPy/ZnO

ABSTRACT: Superhydrophobic materials have been widely applied in rapid removal and collection of oils from oil/water mixtures for increasing damage to environment and human beings caused by oil-contaminated wastewater and oil spills. Herein, superhydrophobic materials were fabricated by a novel polypyrrole (PPy)/ZnO coating followed by hexadecyltrimethoxysilane (HDTMS) modification for versatile oil/water separation with high environmental and excellent reusability. The prepared superhydrophobic surfaces exhibited water contact angle (WCA) greater than 150° and SA less than 5°. The superhydrophobic fabric could be applied for separation of heavy oil or light oil/water mixtures and emulsions with the separation efficiencies above 98%. The coated fabric also realized highly efficient separation with harsh environmental solutions, such as acid, alkali, salt, and hot water. The superhydrophobic fabric still remained, even after 80 cycles of separation and 12 months of storage in air, proving excellent durability. These novel superhydrophobic materials have indicated great development potentials for oil/water separation in practical applications.

SUBMITTER: Fan S

PROVIDER: S-EPMC9322026 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:The fluoride-free fabrication of superhydrophobic materials for the separation of oil/water mixtures has received widespread attention because of frequent offshore oil exploration and chemical leakage. In recent years, oil/water separation materials, based on metal meshes, have drawn much attention, with significant advantages in terms of their high mechanical strength, easy availability, and long durability. However, it is still challenging to prepare superhydrophobic metal meshes with high-separation capacity, low costs, and high recyclability for dealing with oil-water separation. In this work, a superhydrophobic and super oleophilic stainless steel mesh (SSM) was successfully prepared by anchoring Fe2O3 nanoclusters (Fe2O3-NCs) on SSM via the in-situ flame synthesis method and followed by further modification with octadecyltrimethoxysilane (OTS). The as-prepared SSM with Fe2O3-NCs and OTS (OTS@Fe2O3-NCs@SSM) was confirmed by a field emission scanning electron microscope (FESEM), transmission electron microscope (TEM), energy dispersive spectrometer (EDS), X-ray photoelectron spectrometer (XPS), and X-ray diffractometer (XRD). The oil-water separation capacity of the sample was also measured. The results show that the interlaced and dense Fe2O3-NCs, composed of Fe2O3 nanoparticles, were uniformly coated on the surface of the SSM after the immerging-burning process. Additionally, a compact self-assembled OTS layer with low surface energy is coated on the surface of Fe2O3-NCs@SSM, leading to the formation of OTS@Fe2O3-NCs@SSM. The prepared OTS@Fe2O3-NCs@SSM shows excellent superhydrophobicity, with a water static contact angle of 151.3°. The separation efficiencies of OTS@Fe2O3-NCs@SSM for the mixtures of oil/water are all above 98.5%, except for corn oil/water (97.5%) because of its high viscosity. Moreover, the modified SSM exhibits excellent stability and recyclability. This work provides a facile approach for the preparation of superhydrophobic and super oleophilic metal meshes, which will lead to advancements in their large-scale applications on separating oil/water mixtures.

Dataset Information

Fabrication of Durable Superhydrophobic Surface for Versatile Oil/Water Separation Based on HDTMS Modified PPy/ZnO

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets