Alkali Niobate Powder Synthesis Using an Emerging Microwave-Assisted Hydrothermal Method.

ABSTRACT: For more than five decades, alkali niobate-based materials (K_xNa_1-xNbO₃) have been one of the most promising lead-free piezoelectric materials researched to be used in electronics, photocatalysis, energy storage/conversion and medical applications, due to their important health and environmentally friendly nature. In this paper, our strategy was to synthetize the nearest reproductible composition to K_xNa_1-xNbO₃ (KNN) with x = 0.5, placed at the limit of the morphotropic phase boundary (MPB) with the presence of both polymorphic phases, orthorhombic and tetragonal. The wet synthesis route was chosen to make the mix crystal powders, starting with the suspension preparation of Nb₂O₅ powder and KOH and NaOH alkaline solutions. Hydrothermal microwave-assisted maturation (HTMW), following the parameter variation T = 200-250 °C, p = 47-60 bar and dwelling time of 30-90 min, was performed. All powders therefore synthesized were entirely K_xN_1-xNbO₃ solid solutions with x = 0.06-0.69, and the compositional, elemental, structural and morphological characterization highlighted polycrystalline particle assemblage with cubic and prismatic morphology, with sizes between 0.28 nm and 2.95 μm and polymorphic O-T phase coexistence, and a d₃₃ piezoelectric constant under 1 pC/N of the compacted unsintered and unpoled discs were found.

SUBMITTER: Dumitrescu CR

PROVIDER: S-EPMC9369762 | biostudies-literature | 2022 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Alkali Niobate Powder Synthesis Using an Emerging Microwave-Assisted Hydrothermal Method.

Dumitrescu Cristina-Rodica CR Surdu Vasile-Adrian VA Stroescu Hermine H Nicoara Adrian-Ionut AI Neacsu Ionela Andreea IA Trusca Roxana R Andronescu Ecaterina E Ciocan Lucian Toma LT

Materials (Basel, Switzerland) 20220806 15

For more than five decades, alkali niobate-based materials (KxNa1-xNbO3) have been one of the most promising lead-free piezoelectric materials researched to be used in electronics, photocatalysis, energy storage/conversion and medical applications, due to their important health and environmentally friendly nature. In this paper, our strategy was to synthetize the nearest reproductible composition to KxNa1-xNbO<sub ...[more]

PMID: 35955357

Similar Datasets

Project description:The exploitation of unavoidable food supply chain wastes resulting from primary and secondary processing for chemicals, materials, and bioenergy is an important concept in the drive towards circular-based, resource-efficient biorefineries rather than petroleum refineries. The potential production of hydrogels (materials) from unavoidable food supply chain wastes, which are naturally rich in biopolymers such as cellulose, hemicellulose, pectin, and lignin, represents an interesting opportunity. However, these intertwined and interconnected biopolymers require separation and deconstruction prior to any useful application. Thus, this study aims to explore the formation of hydrogels from defibrillated celluloses (MW-DFCs) produced via acid-free stepwise microwave hydrothermal processing of blackcurrant pomace residues. Initially, pectin was removed from blackcurrant pomace residues (MW, 100-160 °C), and the resultant depectinated residues were reprocessed at 160 °C. The pectin yield increased from 2.36 wt.% (MW, 100 °C) to 3.07 wt.% (MW, 140 °C) and then decreased to 2.05 wt.% (MW, 160 °C). The isolated pectins were characterized by attenuated total reflectance infrared spectroscopy (ATR-IR), thermogravimetric analysis (TGA), and 13C NMR (D2O). The cellulosic-rich residues were reprocessed (MW, 160 °C) and further characterized by ATR-IR, TGA, and Klason lignin analysis. All the MW-DFCs contained significant lignin content, which prevented hydrogel formation. However, subsequent bleaching (H2O2/OH-) afforded off-white samples with improved gelling ability at the concentration of 5% w/v. Confocal laser microscopy (CLSM) revealed the removal of lignin and a more pronounced cellulosic-rich material. In conclusion, the microwave-assisted defibrillation of blackcurrant pomace, an exploitable unavoidable food supply chain waste, affords cellulosic-rich materials with the propensity to form hydrogels which may serve useful applications when put back into food products, pharmaceuticals, cosmetics, and home and personal care products.

Dataset Information

Alkali Niobate Powder Synthesis Using an Emerging Microwave-Assisted Hydrothermal Method.

Publications

Alkali Niobate Powder Synthesis Using an Emerging Microwave-Assisted Hydrothermal Method.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets