Microstructural Evolution and Hardness Responses of 7050 Al Alloy during Processing.

ABSTRACT: The thermal-mechanical process (TMP) plays an important role in the industrial production of 7050 Al alloys for aircraft components. In this work, the microstructural evolution and influence on hardness of a 7050 alloy ingot, during the process from preheating, deformation and cooling to final heat treatment, have been investigated considering the effect of temperature and the post-deformation cooling path. The results showed that an increasing temperature and decreasing cooling rate during TMP can lead to enhanced hardness of the alloy after heat treatment. Moreover, the variation of recrystallization before and after heat treatment was strongly dependent on the cooling path after deformation. Finally, this study provided a general understanding on the relationship between microstructural evolution and harness of the 7050 alloy.

SUBMITTER: Zhou Y

PROVIDER: S-EPMC9413579 | biostudies-literature | 2022 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Microstructural Evolution and Hardness Responses of 7050 Al Alloy during Processing.

Zhou Yuting Y Zhou Jie J Xiao Xinrui X Li Shishan S Cui Mingliang M Zhang Peng P Long Shuai S Zhang Jiansheng J

Materials (Basel, Switzerland) 20220816 16

The thermal-mechanical process (TMP) plays an important role in the industrial production of 7050 Al alloys for aircraft components. In this work, the microstructural evolution and influence on hardness of a 7050 alloy ingot, during the process from preheating, deformation and cooling to final heat treatment, have been investigated considering the effect of temperature and the post-deformation cooling path. The results showed that an increasing temperature and decreasing cooling rate during TMP ...[more]

PMID: 36013770

Similar Datasets

Project description:This study investigated the metallurgical, mechanical properties and quality of coatings fabricated by direct laser metal deposition (DLMD) on Ti-6Al-4V, which were affected by the DLMD optimized process parameters. A 3-kW continuous wave ytterbium laser system (YLS) attached to a KUKA robot was used for the process. An analysis was conducted to determine the quality of the coatings in terms of hardness and wear resistance. Variables such as the time of interlayer deposition, thickness of the substrate, the initial temperature of the substrate, and the number of deposited layers were also investigated. The independent/collective effect that each process parameter had on the metallurgical and mechanical properties of the deposited Ti-6Al-4V were made clear when the processing parameters were varied. Minute pores/defects that significantly affect the metallurgical and mechanical properties of clads were also identified. The results obtained from the designed experiments showed that the depth of Heat Affected Zone (HAZ) was inversely proportional to the thickness of the substrate; as the thickness of the substrate was increased, the HAZ depth decreased. Moreover, the intensity of the laser power also affects the HAZ depth. In addition, it was discovered that the initial conditions of the substrate at room temperature also affected the coatings in relation to pre-heated conditions. The analysis conducted in identifying and quantifying the porosity showed indication that the factors such as scanning speed, laser power and powder feed rate had a predominant influence on the porosity. The grain form and structure as well as the mechanical properties of the cladded layer were significantly affected by the optimized process parameters of DLMD process. The parameters investigated had a significant impact on the hardness and wear resistance performance. Furthermore, the results revealed that the highest hardness of one of the coatings was 1.97-times the substrate which had a hardness value of 302 HV. The outstanding wear resistance performance of Al-Si-Sn-Cu/Ti-6Al-4V composite coating is attributed to major hard intermetallic phases.

Dataset Information

Microstructural Evolution and Hardness Responses of 7050 Al Alloy during Processing.

Publications

Microstructural Evolution and Hardness Responses of 7050 Al Alloy during Processing.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets