Dynamics of Solid-Electrolyte Interphase Formation on Silicon Electrodes Revealed by Combinatorial Electrochemical Screening.

ABSTRACT: Revealing how formation protocols influence the properties of the solid-electrolyte interphase (SEI) on Si electrodes is key to developing the next generation of Li-ion batteries. SEI understanding is, however, limited by the low-throughput nature of conventional characterisation techniques. Herein, correlative scanning electrochemical cell microscopy (SECCM) and shell-isolated nanoparticles for enhanced Raman spectroscopy (SHINERS) are used for combinatorial screening of the SEI formation under a broad experimental space (20 sets of different conditions with several repeats). This novel approach reveals the heterogeneous nature and dynamics of the SEI electrochemical properties and chemical composition on Si electrodes, which evolve in a characteristic manner as a function of cycle number. Correlative SECCM/SHINERS has the potential to screen thousands of candidate experiments on a variety of battery materials to accelerate the optimization of SEI formation methods, a key bottleneck in battery manufacturing.

SUBMITTER: Martin-Yerga D

PROVIDER: S-EPMC9543478 | biostudies-literature | 2022 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Dynamics of Solid-Electrolyte Interphase Formation on Silicon Electrodes Revealed by Combinatorial Electrochemical Screening.

Martín-Yerga Daniel D Milan David C DC Xu Xiangdong X Fernández-Vidal Julia J Whalley Laura L Cowan Alexander J AJ Hardwick Laurence J LJ Unwin Patrick R PR

Angewandte Chemie (International ed. in English) 20220713 34

Revealing how formation protocols influence the properties of the solid-electrolyte interphase (SEI) on Si electrodes is key to developing the next generation of Li-ion batteries. SEI understanding is, however, limited by the low-throughput nature of conventional characterisation techniques. Herein, correlative scanning electrochemical cell microscopy (SECCM) and shell-isolated nanoparticles for enhanced Raman spectroscopy (SHINERS) are used for combinatorial screening of the SEI formation under ...[more]

PMID: 35699678

Similar Datasets

Project description:Silicon is a promising next-generation anode to increase energy density over commercial graphite anodes, but calendar life remains problematic. In this work, scanning electrochemical microscopy was used to track the site-specific reactivity of a silicon thin film surface over time to determine if undesirable Faradaic reactions were occurring at the formed solid electrolyte interphase (SEI) during calendar aging in four case scenarios: formation between 1.5 V and 100 mV with subsequent rest starting at (1) 1.5 V and (2) 100 mV and formation between 0.75 V and 100 mV with subsequent rest starting at (3) 0.75 V and (4) 100 mV. In all cases, the electrical passivation of silicon decreased with increasing time and potential relative to Li/Li+ over a 3 day period. Along with the decrease in passivation, the homogeneity of passivation over a 500 μm2 area decreased with time. Despite some local "hot spots" of reactivity, the areal uniformity of passivation suggests global SEI failure (e.g., SEI dissolution) rather than localized (e.g., cracking) failure. The silicon delithiated to 1.5 V vs Li/Li+ was less passivated than the lithiated silicon (at the beginning of rest, the forward rate constants, kf, for ferrocene redox were 7.19 × 10-5 and 3.17 × 10-7 m/s, respectively) and was also found to be more reactive than the pristine silicon surface (kf of 5 × 10-5 m/s). This reactivity was likely the result of SEI oxidation. When the cell was only delithiated up to 0.75 V versus Li/Li+, the surface was still passivating (kf of 6.11 × 10-6 m/s), but still less so than the lithiated surface (kf of 3.03 × 10-9 m/s). This indicates that the potential of the anode should be kept at or below ∼0.75 V vs Li/Li+ to prevent decreasing SEI passivation. This information will help with tuning the voltage windows for prelithiation in Si half cells and the operating voltage of Si full cells to optimize calendar life. The results provided should encourage the research community to investigate chemical, rather than mechanical, modes of failure during calendar aging and to stop using the typical convention of 1.5 V as a cutoff potential for cycling Si in half cells.

Dataset Information

Dynamics of Solid-Electrolyte Interphase Formation on Silicon Electrodes Revealed by Combinatorial Electrochemical Screening.

Publications

Dynamics of Solid-Electrolyte Interphase Formation on Silicon Electrodes Revealed by Combinatorial Electrochemical Screening.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets