Cold Sintering of Li_6.4La₃Zr_1.4Ta_0.6O₁₂/PEO Composite Solid Electrolytes.

ABSTRACT: Ceramic/polymer composite solid electrolytes integrate the high ionic conductivity of in ceramics and the flexibility of organic polymers. In practice, ceramic/polymer composite solid electrolytes are generally made into thin films rather than sintered into bulk due to processing temperature limitations. In this work, Li_6.4La₃Zr_1.4Ta_0.6O₁₂ (LLZTO)/polyethylene-oxide (PEO) electrolyte containing bis(trifluoromethanesulfonyl)imide (LiTFSI) as the lithium salt was successfully fabricated into bulk pellets via the cold sintering process (CSP). Using CSP, above 80% dense composite electrolyte pellets were obtained, and a high Li-ion conductivity of 2.4 × 10^-4 S cm^-1 was achieved at room temperature. This work focuses on the conductivity contributions and microstructural development within the CSP process of composite solid electrolytes. Cold sintering provides an approach for bridging the gap in processing temperatures of ceramics and polymers, thereby enabling high-performance composites for electrochemical systems.

SUBMITTER: He B

PROVIDER: S-EPMC9572155 | biostudies-literature | 2022 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Cold Sintering of Li6.4La3Zr1.4Ta0.6O12/PEO Composite Solid Electrolytes.

He Binlang B Kang Shenglin S Zhao Xuetong X Zhang Jiexin J Wang Xilin X Yang Yang Y Yang Lijun L Liao Ruijin R

Molecules (Basel, Switzerland) 20221010 19

Ceramic/polymer composite solid electrolytes integrate the high ionic conductivity of in ceramics and the flexibility of organic polymers. In practice, ceramic/polymer composite solid electrolytes are generally made into thin films rather than sintered into bulk due to processing temperature limitations. In this work, Li6.4La3Zr1.4Ta0.6O12 (LLZTO)/polyethylene-oxide (PEO) electrolyte containing bis(trifluoromethanesulfonyl)imide (LiTFSI) as ...[more]

PMID: 36235290

Similar Datasets

Project description:Several "Beyond Li-Ion Battery" concepts such as all solid-state batteries and hybrid liquid/solid systems envision the use of a solid electrolyte to protect Li-metal anodes. These configurations are very attractive due to the possibility of exceptionally high energy densities and high (dis)charge rates, but they are far from being realized practically due to a number of issues including high interfacial resistance and difficulties associated with fabrication. One of the most promising solid electrolyte systems for these applications is Al or Ga stabilized Li7La3Zr2O12 (LLZO) based on high ionic conductivities and apparent stability against reduction by Li metal. Nevertheless, the fabrication of dense LLZO membranes with high ionic conductivity and low interfacial resistances remains challenging; it definitely requires a better understanding of the structural and electrochemical properties. In this study, the phase transition from garnet (Ia3̅d, No. 230) to "non-garnet" (I4̅3d, No. 220) space group as a function of composition and the different sintering behavior of Ga and Al stabilized LLZO are identified as important factors in determining the electrochemical properties. The phase transition was located at an Al:Ga substitution ratio of 0.05:0.15 and is accompanied by a significant lowering of the activation energy for Li-ion transport to 0.26 eV. The phase transition combined with microstructural changes concomitant with an increase of the Ga/Al ratio continuously improves the Li-ion conductivity from 2.6 × 10-4 S cm-1 to 1.2 × 10-3 S cm-1, which is close to the calculated maximum for garnet-type materials. The increase in Ga content is also associated with better densification and smaller grains and is accompanied by a change in the area specific resistance (ASR) from 78 to 24 Ω cm2, the lowest reported value for LLZO so far. These results illustrate that understanding the structure-properties relationships in this class of materials allows practical obstacles to its utilization to be readily overcome.

Dataset Information

Cold Sintering of Li_6.4La₃Zr_1.4Ta_0.6O₁₂/PEO Composite Solid Electrolytes.

Publications

Cold Sintering of Li<sub>6.4</sub>La<sub>3</sub>Zr<sub>1.4</sub>Ta<sub>0.6</sub>O<sub>12</sub>/PEO Composite Solid Electrolytes.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets