Thickness profiling of electron transparent aluminium alloy foil using convergent beam electron diffraction.

ABSTRACT: Convergent beam electron diffraction (CBED) was used to profile the thickness of aluminium alloys foils prepared by using the twinjet electropolishing method. The two-beam CBED condition was obtained by exciting the {200}$\{ {200} \}$ and {111}$\{ {111} \}$ aluminium diffracted g-vector. The aluminium alloy foil thicknesses were calculated at different distances from the sample hole edge. In areas where only one Kossel-Möllenstedt (K-M) minima fringe was obtained, the thickness was determined by matching the experimental with simulated convergent beam diffraction patterns. In areas far away from the sample edge, the thickness of foils was high enough to generate at least two (K-M) minima fringes, required for linear regression fitting.

SUBMITTER: Bendo A

PROVIDER: S-EPMC9804362 | biostudies-literature | 2022 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Thickness profiling of electron transparent aluminium alloy foil using convergent beam electron diffraction.

Bendo Artenis A Moshtaghi Masoud M Smith Matthew M Jin Zelong Z Xiong Yida Y Matsuda Kenji K Zhou Xiaorong X

Journal of microscopy 20220822 1

Convergent beam electron diffraction (CBED) was used to profile the thickness of aluminium alloys foils prepared by using the twinjet electropolishing method. The two-beam CBED condition was obtained by exciting the { 200 } $\{ {200} \}$ and { 111 } $\{ {111} \}$ aluminium diffracted g-vector. The aluminium alloy foil thicknesses were calculated at different distances from the sample hole edge. In areas where only one Kossel-Möllenstedt (K-M) minima fringe was obtained, the thickness was det ...[more]

PMID: 35916115

Similar Datasets

Three-beam convergent-beam electron diffraction for measuring crystallographic phases.

Project description:Under almost all circumstances, electron diffraction patterns contain information about the phases of structure factors, a consequence of the short wavelength of an electron and its strong Coulombic interaction with matter. However, extracting this information remains a challenge and no generic method exists. In this work, a set of simple analytical expressions is derived for the intensity distribution in convergent-beam electron diffraction (CBED) patterns recorded under three-beam conditions. It is shown that these expressions can be used to identify features in three-beam CBED patterns from which three-phase invariants can be extracted directly, without any iterative refinement processes. The octant, in which the three-phase invariant lies, can be determined simply by inspection of the indexed CBED patterns (i.e. the uncertainty of the phase measurement is ±22.5°). This approach is demonstrated with the experimental measurement of three-phase invariants in two simple test cases: centrosymmetric Si and non-centrosymmetric GaAs. This method may complement existing structure determination methods by providing direct measurements of three-phase invariants to replace 'guessed' invariants in ab initio phasing methods and hence provide more stringent constraints to the structure solution.

| S-EPMC6211523 | biostudies-literature

Coherent convergent-beam time-resolved X-ray diffraction.

Project description:The use of coherent X-ray lasers for structural biology allows the use of nanometre diameter X-ray beams with large beam divergence. Their application to the structure analysis of protein nanocrystals and single particles raises new challenges and opportunities. We discuss the form of these coherent convergent-beam (CCB) hard X-ray diffraction patterns and their potential use for time-resolved crystallography, normally achieved by Laue (polychromatic) diffraction, for which the monochromatic laser radiation of a free-electron X-ray laser is unsuitable. We discuss the possibility of obtaining single-shot, angle-integrated rocking curves from CCB patterns, and the dependence of the resulting patterns on the focused beam coordinate when the beam diameter is larger or smaller than a nanocrystal, or smaller than one unit cell. We show how structure factor phase information is provided at overlapping interfering orders and how a common phase origin between different shots may be obtained. Their use in refinement of the phase-sensitive intensity between overlapping orders is suggested.

| S-EPMC4052862 | biostudies-other

Electron Beam Transparent Boron Doped Diamond Electrodes for Combined Electrochemistry-Transmission Electron Microscopy.

Project description:The majority of carbon based transmission electron microscopy (TEM) platforms (grids) have a significant sp2 carbon component. Here, we report a top down fabrication technique for producing freestanding, robust, electron beam transparent and conductive sp3 carbon substrates from boron doped diamond (BDD) using an ion milling/polishing process. X-ray photoelectron spectroscopy and electrochemical measurements reveal the sp3 carbon character and advantageous electrochemical properties of a BDD electrode are retained during the milling process. TEM diffraction studies show a dominant (110) crystallographic orientation. Compared with conventional carbon TEM films on metal supports, the BDD-TEM electrodes offer superior thermal, mechanical and electrochemical stability properties. For the latter, no carbon loss is observed over a wide electrochemical potential range (up to 1.80 V vs RHE) under prolonged testing times (5 h) in acid (comparable with accelerated stress testing protocols). This result also highlights the use of BDD as a corrosion free electrocatalyst TEM support for fundamental studies, and in practical energy conversion applications. High magnification TEM imaging demonstrates resolution of isolated, single atoms on the BDD-TEM electrode during electrodeposition, due to the low background electron scattering of the BDD surface. Given the high thermal conductivity and stability of the BDD-TEM electrodes, in situ monitoring of thermally induced morphological changes is also possible, shown here for the thermally induced crystallization of amorphous electrodeposited manganese oxide to the electrochemically active γ-phase.

| S-EPMC9585633 | biostudies-literature

Controlled Electron-Beam Synthesis of Transparent Hydrogels for Drug Delivery Applications.

Project description:In this study, we highlight hydrogels prepared by electron-beam polymerization. In general, the electron-beam-polymerized hydrogels showed improved mechanical and optical transmittances compared to the conventional UV-cured hydrogels. They were more elastic and had a higher crosslinking density. Additionally, they were transparent over a broader wavelength range. The dependence of the mechanical and optical properties of the hydrogels on the number of single differential and total irradiation doses was analyzed in detail. The hydrogels were prepared for usage as a drug delivery material with methylene blue as a drug model. In the first set of experiments, methylene blue was loaded reversibly after the hydrogel synthesis. Electron-beam-polymerized hydrogels incorporated twice as much methylene blue compared to the UV-polymerized gels. Furthermore, the release of the model drug was found to depend on the crosslinking degree of the hydrogels. In addition, electron-beam polymerization enabled the irreversible binding of the drug molecules if they were mixed with monomers before polymerization.

| S-EPMC6473313 | biostudies-literature

Convergent beam electron holography for analysis of van der Waals heterostructures.

Project description:The van der Waals heterostructures, which explore the synergetic properties of 2D materials when assembled into 3D stacks, have already brought to life a number of exciting phenomena and electronic devices. Still, the interaction between the layers in such assembly, possible surface reconstruction, and intrinsic and extrinsic defects are very difficult to characterize by any method, because of the single-atomic nature of the crystals involved. Here we present a convergent beam electron holographic technique which allows imaging of the stacking order in such heterostructures. Based on the interference of electron waves scattered on different crystals in the stack, this approach allows one to reconstruct the relative rotation, stretching, and out-of-plane corrugation of the layers with atomic precision. Being holographic in nature, our approach allows extraction of quantitative information about the 3D structure of the typical defects from a single image covering thousands of square nanometers. Furthermore, qualitative information about the defects in the stack can be extracted from the convergent diffraction patterns even without reconstruction, simply by comparing the patterns in different diffraction spots. We expect that convergent beam electron holography will be widely used to study the properties of van der Waals heterostructures.

| S-EPMC6055151 | biostudies-literature

Three-dimensional surface topography of graphene by divergent beam electron diffraction.

Project description:There are only a handful of scanning techniques that can provide surface topography at nanometre resolution. At the same time, there are no methods that are capable of non-invasive imaging of the three-dimensional surface topography of a thin free-standing crystalline material. Here we propose a new technique-the divergent beam electron diffraction (DBED) and show that it can directly image the inhomogeneity in the atomic positions in a crystal. Such inhomogeneities are directly transformed into the intensity contrast in the first-order diffraction spots of DBED patterns and the intensity contrast linearly depends on the wavelength of the employed probing electrons. Three-dimensional displacement of atoms as small as 1 angstrom can be detected when imaged with low-energy electrons (50-250 eV). The main advantage of DBED is that it allows visualization of the three-dimensional surface topography and strain distribution at the nanometre scale in non-scanning mode, from a single shot diffraction experiment.

| S-EPMC5316882 | biostudies-literature

Dislocation substructures in pure aluminium after creep deformation as studied by electron backscatter diffraction

Project description:In the present work, electron backscatter diffraction is used to investigate the influence of crystal orientation and stress level on the dislocation structures generated during primary and steady-state creep in pure aluminium (99.8%). The goal is to characterize features of the microstructure with a statistically sound approach. In the present work, electron backscatter diffraction was used to determine the microscopic dislocation structures generated during creep (with tests interrupted at the steady state) in pure 99.8% aluminium. This material was investigated at two different stress levels, corresponding to the power-law and power-law breakdown regimes. The results show that the formation of subgrain cellular structures occurs independently of the crystallographic orientation. However, the density of these cellular structures strongly depends on the grain crystallographic orientation with respect to the tensile axis direction, with 〈111〉 grains exhibiting the highest densities at both stress levels. It is proposed that this behaviour is due to the influence of intergranular stresses, which is different in 〈111〉 and 〈001〉 grains.

| S-EPMC9348881 | biostudies-literature

Monte Carlo simulation for scanning technique with scattering foil free electron beam: A proof of concept study.

Project description:This study investigated the potential of a newly proposed scattering foil free (SFF) electron beam scanning technique for the treatment of skin cancer on the irregular patient surfaces using Monte Carlo (MC) simulation. After benchmarking of the MC simulations, we removed the scattering foil to generate SFF electron beams. Cylindrical and spherical phantoms with 1 cm boluses were generated and the target volume was defined from the surface to 5 mm depth. The SFF scanning technique with 6 MeV electrons was simulated using those phantoms. For comparison, volumetric modulated arc therapy (VMAT) plans were also generated with two full arcs and 6 MV photon beams. When the scanning resolution resulted in a larger separation between beams than the field size, the plan qualities were worsened. In the cylindrical phantom with a radius of 10 cm, the conformity indices, homogeneity indices and body mean doses of the SFF plans (scanning resolution = 1°) vs. VMAT plans were 1.04 vs. 1.54, 1.10 vs. 1.12 and 5 Gy vs. 14 Gy, respectively. Those of the spherical phantom were 1.04 vs. 1.83, 1.08 vs. 1.09 and 7 Gy vs. 26 Gy, respectively. The proposed SFF plans showed superior dose distributions compared to the VMAT plans.

| S-EPMC5426680 | biostudies-literature

Electrochemical, Tribological and Biocompatible Performance of Electron Beam Modified and Coated Ti6Al4V Alloy.

Project description:Vacuum cathodic arc TiN coatings with overlaying TiO2 film were deposited on polished and surface roughened by electron beam modification (EBM) Ti6Al4V alloy. The substrate microtopography consisted of long grooves formed by the liner scan of the electron beam with appropriate frequencies (500 (AR500) and 850 (AR850) Hz). EBM transformed the α + β Ti6Al4V mixed structure into a single α'-martensite phase. Тhe gradient TiN/TiO2 films deposited on mechanically polished (AR) and EBM (AR500 and AR850) alloys share the same surface chemistry and composition (almost stoichiometric TiN, anatase and rutile in different ratios) but exhibit different topographies (Sa equal to approximately 0.62, 1.73, and 1.08 μm, respectively) over areas of 50 × 50 μm. Although the nanohardness of the coatings on AR500 and AR850 alloy (approximately 10.45 and 9.02 GPa, respectively) was lower than that measured on the film deposited on AR alloy (about 13.05 GPa), the hybrid surface treatment offered improvement in critical adhesive loads, coefficient of friction, and wear-resistance of the surface. In phosphate buffer saline, all coated samples showed low corrosion potentials and passivation current densities, confirming their good corrosion protection. The coated EBM samples cultured with human osteoblast-like MG63 cells demonstrated increased cell attachment, viability, and bone mineralization activity especially for the AR500-coated alloy, compared to uncoated polished alloy. The results underline the synergetic effect between the sub-micron structure and composition of TiN/TiO2 coating and microarchitecture obtained by EBM.

| S-EPMC8232333 | biostudies-literature

Electron beam irradiated silver nanowires for a highly transparent heater.

Project description:Transparent heaters have attracted increasing attention for their usefulness in vehicle windows, outdoor displays, and periscopes. We present high performance transparent heaters based on Ag nanowires with electron beam irradiation. We obtained an Ag-nanowire thin film with 48 ohm/sq of sheet resistance and 88.8% (substrate included) transmittance at 550 nm after electron beam irradiation for 120 sec. We demonstrate that the electron beam creates nano-soldering at the junctions of the Ag nanowires, which produces lower sheet resistance and improved adhesion of the Ag nanowires. We fabricated a transparent heater with Ag nanowires after electron beam irradiation, and obtained a temperature of 51 °C within 1 min at an applied voltage of 7 V. The presented technique will be useful in a wide range of applications for transparent heaters.

| S-EPMC4671054 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data