High-Performance Photoinitiating Systems for LED-Induced Photopolymerization.

ABSTRACT: Currently, increasing attention has been focused on light-emitting diodes (LEDs)-induced photopolymerization. The common LEDs (e.g., LED at 365 nm and LED at 405 nm) possess narrow emission bands. Due to their light absorption properties, most commercial photoinitiators are sensitive to UV light and cannot be optimally activated under visible LED irradiation. Although many photoinitiators have been designed for LED-induced free radical polymerization and cationic polymerization, there is still the issue of the mating between photoinitiators and LEDs. Therefore, the development of novel photoinitiators, which could be applied under LED irradiation, is significant. Many photoinitiating systems have been reported in the past decade. In this review, some recently developed photoinitiators used in LED-induced photopolymerization, mainly in the past 5 years, are summarized and categorized as Type Ⅰ photoinitiators, Type Ⅱ photoinitiators, and dye-based photoinitiating systems. In addition, their light absorption properties and photoinitiation efficiencies are discussed.

SUBMITTER: Liu S

PROVIDER: S-EPMC9860695 | biostudies-literature | 2023 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

High-Performance Photoinitiating Systems for LED-Induced Photopolymerization.

Liu Shaohui S Borjigin Timur T Schmitt Michael M Morlet-Savary Fabrice F Xiao Pu P Lalevée Jacques J

Polymers 20230109 2

Currently, increasing attention has been focused on light-emitting diodes (LEDs)-induced photopolymerization. The common LEDs (e.g., LED at 365 nm and LED at 405 nm) possess narrow emission bands. Due to their light absorption properties, most commercial photoinitiators are sensitive to UV light and cannot be optimally activated under visible LED irradiation. Although many photoinitiators have been designed for LED-induced free radical polymerization and cationic polymerization, there is still t ...[more]

PMID: 36679223

Similar Datasets

Project description:In this article, different substituents (benzoyl, acetyl, styryl) are introduced onto the carbazole scaffold to obtain 8 novel carbazole derivatives. Interestingly, a benzoyl substituent, connected to a carbazole group, could form a benzophenone moiety, which composes a monocomponent Type II benzophenone-carbazole photoinitiator (PI). The synergetic effect of the benzophenone moiety and the amine in the carbazole moiety is expected to produce high performance photoinitiating systems (PISs) for the free radical photopolymerization (FRP). For different substituents, clear effects on the light absorption properties are demonstrated using UV-Visible absorption spectroscopy. Benzophenone-carbazole PIs can initiate the FRP of acrylates alone (monocomponent Type II photoinitiator behavior). In addition, fast polymerization rates and high function conversions of acrylate are observed when an amine and/or an iodonium salt are added in systems. Benzophenone-carbazole PIs have good efficiencies in cationic photopolymerization (CP) upon LED @ 365 nm irradiation in the presence of iodonium salt. In contrast, other PIs without synergetic effect demonstrate unsatisfied photopolymerization profiles in the same conditions. The best PIS identified for the free radical photopolymerization were used in three-dimensional (3D) printing. Steady state photolysis and fluorescence quenching experiments were carried out to investigate the reactivity and the photochemistry and photophysical properties of PIs. The free radicals, generated from the studied PISs, are detected by the electron spin resonance - spin trapping technique. The proposed chemical mechanisms are provided and the structure/reactivity/efficiency relationships are also discussed. All the results showed that the benzophenone-carbazole PIs have a good application potential, and this work provides a rational design route for PI molecules. Remarkably, BPC2-BPC4, C6, C8 were never synthetized before; therefore, 5 of the 8 compounds are completely new.

Project description:Vat photopolymerization additive manufacturing (Vat AM) technologies have found niche industrial use being able to produce personalized parts in moderate quantity. However, Vat AM lacks in its ability to produce parts of satisfactory thermal and mechanical properties for structural applications. The purpose of this investigation was to develop high-performance resins with glass transition temperatures (Tg) above 200 °C for Vat AM, evaluate the properties of the produced thermosets and establish a structure-property relationship of the thermosets produced. Herein, we have developed SLA-type resins that feature bio-derived monomer hesperetin trimethacrylate (HTM) synthesized from the flavonone hesperetin. Diluents 4-acryloyl morpholine, styrene, 4-methyl styrene and 4-tert butylstyrene (tbutylsty) were photocured with HTM as the monomer and all produced thermosets with Tg values above 200 °C. Investigations of suitable crosslinkers urethane dimethacrylate, the vinyl ester CN 151 and Ebecryl 4859 (Eb4859) showed that each crosslinker displayed different benefits when formulated with HTM as the monomer and tbutylSty as the diluent (HTM:crosslinker:tbutylSty with mass ratio 2:1:2). The crosslinker CN 151 produced the thermoset of greatest onset of thermal decomposition temperature (T0) of 352 °C. Eb4859 produced the thermoset of highest tensile strength, 19 ± 7 MPa, amongst the set of varied crosslinkers. The formulation featuring UDM (HTM:UDM:tbutysty) offered ease of processing and was seemingly the easiest to print. Investigations of reactive diluent showed that styrene produced the thermoset of the highest extent of cure and the overall highest tensile strength, 25 ± 5 MPa, while tbutylSty produced the thermoset with the greatest Tan-δ Tg, 231 °C. HTM was synthesized, formulated with diluents, crosslinkers and initiators. The HTM resins were then 3D printed to produce thermosets of Tg values greater than 200 °C. The polymer properties were evaluated and a structure-reactivity relationship was discussed.

Dataset Information

High-Performance Photoinitiating Systems for LED-Induced Photopolymerization.

Publications

High-Performance Photoinitiating Systems for LED-Induced Photopolymerization.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets