High-speed scanning ablation of dental hard tissues with a λ = 9.3 μm CO2 laser: adhesion, mechanical strength, heat accumulation, and peripheral thermal damage.

ABSTRACT: CO(2) lasers can be operated at high laser pulse repetition rates for the rapid and precise removal of dental decay. Excessive heat accumulation and peripheral thermal damage is a concern when using high pulse repetition rates. Peripheral thermal damage can adversely impact the mechanical strength of the irradiated tissue, particularly for dentin, and reduce the adhesion characteristics of the modified surfaces. The interpulpal temperature rise was recorded using microthermocouples situated at the roof of the pulp chamber on teeth that were occlusally ablated using a rapidly-scanned CO(2) laser operating at 9.3 μm with a pulse duration of 10 to 15 μs and repetition rate of 300 Hz over a 2 min time course. The adhesion strength of laser treated enamel and dentin surfaces was measured for various laser scanning parameters with and without post-ablation acid etching using the single-plane shear test. The mechanical strength of laser-ablated dentin surfaces were determined via the four-point bend test and compared to control samples prepared with 320 grit wet sand paper to simulate conventional preparations. Thermocouple measurements indicated that the temperature remained below ambient temperature if water-cooling was used. There was no discoloration of either dentin or enamel laser treated surfaces, the surfaces were uniformly ablated, and there were no cracks visible. Four-point bend tests yielded mean mechanical strengths of 18.2 N (s.d. = 4.6) for ablated dentin and 18.1 N (s.d. = 2.7) for control (p > 0.05). Shear tests yielded mean bond strengths approaching 30 MPa for both enamel and dentin under certain irradiation conditions. These values were slightly lower than nonirradiated acid-etched control samples. Additional studies are needed to determine if the slightly lower bond strength than the acid-etched control samples is clinically significant. These measurements demonstrate that enamel and dentin surfaces can be rapidly ablated by CO(2) lasers with minimal peripheral thermal and mechanical damage and without excessive heat accumulation.

SUBMITTER: Nguyen D

PROVIDER: S-EPMC3160453 | biostudies-other | 2011 Jul

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:Loss-of-function mutations in ALPL result in hypophosphatasia (HPP), an inborn error of metabolism that causes defective skeletal and dental mineralization. ALPL encodes tissue-nonspecific alkaline phosphatase, an enzyme expressed in bone, teeth, liver, and kidney that hydrolyzes the mineralization inhibitor inorganic pyrophosphate. As Alpl-null mice die before weaning, we aimed to generate mouse models of late-onset HPP with extended life spans by engineering a floxed Alpl allele, allowing for conditional gene ablation (conditional knockout [cKO]) when crossed with Cre recombinase transgenic mice. The authors hypothesized that targeted deletion of Alpl in osteoblasts and selected dental cells ( Col1a1-cKO) or deletion in chondrocytes, osteoblasts, and craniofacial mesenchyme ( Prx1-cKO) would phenocopy skeletal and dental manifestations of late-onset HPP. Col1a1-cKO and Prx1-cKO mice were viable and fertile, and they did not manifest the epileptic seizures characteristic of the Alpl-/- model of severe infantile HPP. Both cKO models featured normal postnatal body weight but significant reduction as compared with wild type mice by 8 to 12 wk. Plasma alkaline phosphatase for both cKO models at 24 wk was reduced by approximately 75% as compared with controls. Radiography revealed profound skeletal defects in cKO mice, including rachitic changes, hypomineralized long bones, deformations, and signs of fractures. Microcomputed tomography confirmed quantitative differences in cortical and trabecular bone, including decreased cortical thickness and mineral density. Col1a1-cKO mice exhibited classic signs of HPP dentoalveolar disease, including short molar roots with thin dentin, lack of acellular cementum, and osteoid accumulation in alveolar bone. Prx1-cKO mice exhibited the same array of periodontal defects but featured less affected molar dentin. Both cKO models exhibited reduced alveolar bone height and 4-fold increased numbers of osteoclast-like cells versus wild type at 24 wk, consistent with HPP-associated periodontal disease. These novel models of late-onset HPP can inform on long-term skeletal and dental manifestations and will provide essential tools to further studies of etiopathologies and therapeutic interventions.

Dataset Information

High-speed scanning ablation of dental hard tissues with a λ = 9.3 μm CO2 laser: adhesion, mechanical strength, heat accumulation, and peripheral thermal damage.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets