Plasma-assisted atomic layer deposition of Al(2)O(3) and parylene C bi-layer encapsulation for chronic implantable electronics.

ABSTRACT: Encapsulation of biomedical implants with complex three dimensional geometries is one of the greatest challenges achieving long-term functionality and stability. This report presents an encapsulation scheme that combines Al(2)O(3) by atomic layer deposition with parylene C for implantable electronic systems. The Al(2)O(3)-parylene C bi-layer was used to encapsulate interdigitated electrodes, which were tested invitro by soak testing in phosphate buffered saline solution at body temperature (37 °C) and elevated temperatures (57 °C and 67 °C) for accelerated lifetime testing up to 5 months. Leakage current and electrochemical impedance spectroscopy were measured for evaluating the integrity and insulation performance of the coating. Leakage current was stably about 15 pA at 5 V dc, and impedance was constantly about 3.5 MΩ at 1 kHz by using electrochemical impedance spectroscopy for samples under 67 °C about 5 months (approximately equivalent to 40 months at 37 °C). Alumina and parylene coating lasted at least 3 times longer than parylene coated samples tested at 80 °C. The excellent insulation performance of the encapsulation shows its potential usefulness for chronic implants.

SUBMITTER: Xie X

PROVIDER: S-EPMC3443113 | biostudies-other | 2012 Aug

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Aluminum Nitride Transition Layer for Power Electronics Applications Grown by Plasma-Enhanced Atomic Layer Deposition.

Project description:Aluminum nitride (AlN) films have been grown using novel technological approaches based on plasma-enhanced atomic layer deposition (PEALD) and in situ atomic layer annealing (ALA). The growth of AlN layers was carried out on Si<100> and Si<111> substrates at low growth temperature. The investigation of crystalline quality of samples demonstrated that PEALD grown layers were polycrystalline, but ALA treatment improved their crystallinity. A thick polycrystalline AlN layer was successfully regrown by metal-organic chemical vapor deposition (MOCVD) on an AlN PEALD template. It opens up the new possibilities for the formation of nucleation layers with improved quality for subsequent growth of semiconductor nitride compounds.

| S-EPMC6384632 | biostudies-literature

Plasma-Assisted Atomic Layer Deposition of IrO2 for Neuroelectronics.

Project description:In vitro and in vivo stimulation and recording of neuron action potential is currently achieved with microelectrode arrays, either in planar or 3D geometries, adopting different materials and strategies. IrO2 is a conductive oxide known for its excellent biocompatibility, good adhesion on different substrates, and charge injection capabilities higher than noble metals. Atomic layer deposition (ALD) allows excellent conformal growth, which can be exploited on 3D nanoelectrode arrays. In this work, we disclose the growth of nanocrystalline rutile IrO2 at T = 150 °C adopting a new plasma-assisted ALD (PA-ALD) process. The morphological, structural, physical, chemical, and electrochemical properties of the IrO2 thin films are reported. To the best of our knowledge, the electrochemical characterization of the electrode/electrolyte interface in terms of charge injection capacity, charge storage capacity, and double-layer capacitance for IrO2 grown by PA-ALD was not reported yet. IrO2 grown on PtSi reveals a double-layer capacitance (Cdl) above 300 µF∙cm-2, and a charge injection capacity of 0.22 ± 0.01 mC∙cm-2 for an electrode of 1.0 cm2, confirming IrO2 grown by PA-ALD as an excellent material for neuroelectronic applications.

| S-EPMC10052997 | biostudies-literature

High-κ Dielectric on ReS₂: In-Situ Thermal Versus Plasma-Enhanced Atomic Layer Deposition of Al₂O₃.

Project description:We report an excellent growth behavior of a high-κ dielectric on ReS₂, a two-dimensional (2D) transition metal dichalcogenide (TMD). The atomic layer deposition (ALD) of an Al₂O₃ thin film on the UV-Ozone pretreated surface of ReS₂ yields a pinhole free and conformal growth. In-situ half-cycle X-ray photoelectron spectroscopy (XPS) was used to monitor the interfacial chemistry and ex-situ atomic force microscopy (AFM) was used to evaluate the surface morphology. A significant enhancement in the uniformity of the Al₂O₃ thin film was deposited via plasma-enhanced atomic layer deposition (PEALD), while pinhole free Al₂O₃ was achieved using a UV-Ozone pretreatment. The ReS₂ substrate stays intact during all different experiments and processes without any formation of the Re oxide. This work demonstrates that a combination of the ALD process and the formation of weak S⁻O bonds presents an effective route for a uniform and conformal high-κ dielectric for advanced devices based on 2D materials.

| S-EPMC6479988 | biostudies-literature

Nanometer-thick conformal pore sealing of self-assembled mesoporous silica by plasma-assisted atomic layer deposition.

Project description:On a porous substrate, regular atomic layer deposition (ALD) not only takes place on top of the substrate but also penetrates into the internal porosity. Here we report a plasma-assisted process in which the ALD precursors are chosen to be nonreactive unless triggered by plasma, so that ALD can be spatially defined by the supply of plasma irradiation. Since plasma cannot penetrate within the internal porosity, ALD has been successfully confined to the immediate surface. This not only gives a possible solution for sealing of porous low dielectric constant films with a conformal layer of nm-scale thickness but also enables us to progressively reduce the pore size of mesoporous materials in a sub-A/cycle fashion for membrane formation.

| S-EPMC2707262 | biostudies-literature

Uniform Atomic Layer Deposition of Al2O3 on Graphene by Reversible Hydrogen Plasma Functionalization.

Project description:A novel method to form ultrathin, uniform Al2O3 layers on graphene using reversible hydrogen plasma functionalization followed by atomic layer deposition (ALD) is presented. ALD on pristine graphene is known to be a challenge due to the absence of dangling bonds, leading to nonuniform film coverage. We show that hydrogen plasma functionalization of graphene leads to uniform ALD of closed Al2O3 films down to 8 nm in thickness. Hall measurements and Raman spectroscopy reveal that the hydrogen plasma functionalization is reversible upon Al2O3 ALD and subsequent annealing at 400 °C and in this way does not deteriorate the graphene's charge carrier mobility. This is in contrast with oxygen plasma functionalization, which can lead to a uniform 5 nm thick closed film, but which is not reversible and leads to a reduction of the charge carrier mobility. Density functional theory (DFT) calculations attribute the uniform growth on both H2 and O2 plasma functionalized graphene to the enhanced adsorption of trimethylaluminum (TMA) on these surfaces. A DFT analysis of the possible reaction pathways for TMA precursor adsorption on hydrogenated graphene predicts a binding mechanism that cleans off the hydrogen functionalities from the surface, which explains the observed reversibility of the hydrogen plasma functionalization upon Al2O3 ALD.

| S-EPMC5384478 | biostudies-literature

Particle atomic layer deposition.

Project description:The functionalization of fine primary particles by atomic layer deposition (particle ALD) provides for nearly perfect nanothick films to be deposited conformally on both external and internal particle surfaces, including nanoparticle surfaces. Film thickness is easily controlled from several angstroms to nanometers by the number of self-limiting surface reactions that are carried out sequentially. Films can be continuous or semi-continuous. This review starts with a short early history of particle ALD. The discussion includes agitated reactor processing, both atomic and molecular layer deposition (MLD), coating of both inorganic and polymer particles, nanoparticles, and nanotubes. A number of applications are presented, and a path forward, including likely near-term commercial products, is given.

| S-EPMC6320374 | biostudies-literature

Impact of Ions on Film Conformality and Crystallinity during Plasma-Assisted Atomic Layer Deposition of TiO2.

Project description:This work demonstrates that ions have a strong impact on the growth per cycle (GPC) and material properties during plasma-assisted atomic layer deposition (ALD) of TiO2 (titanium dioxide), even under mild plasma conditions with low-energy (<20 eV) ions. Using vertical trench nanostructures and microscopic cavity structures that locally block the flux of ions, it is observed that the impact of (low-energy) ions is an important factor for the TiO2 film conformality. Specifically, it is demonstrated that the GPC in terms of film thickness can increase by 20 to >200% under the influence of ions, which is correlated with an increase in film crystallinity and an associated strong reduction in the wet etch rate (in 30:1 buffered HF). The magnitude of the influence of ions is observed to depend on multiple parameters such as the deposition temperature, plasma exposure time, and ion energy, which may all be used to minimize or exploit this effect. For example, a relatively moderate influence of ions is observed at 200 °C when using short plasma steps and a grounded substrate, providing a low ion-energy dose of ∼1 eV nm-2 cycle-1, while a high effect is obtained when using extended plasma exposures or substrate biasing (∼100 eV nm-2 cycle-1). This work on TiO2 shows that detailed insight into the role of ions during plasma ALD is essential for precisely controlling the film conformality, material properties, and process reproducibility.

| S-EPMC8280614 | biostudies-literature

Oxygen Recombination Probability Data for Plasma-Assisted Atomic Layer Deposition of SiO2 and TiO2.

Project description:Atomic layer deposition (ALD) can provide nanometer-thin films with excellent conformality on demanding three-dimensional (3D) substrates. This also holds for plasma-assisted ALD, provided that the loss of reactive radicals through surface recombination is sufficiently low. In this work, we determine the surface recombination probability r of oxygen radicals during plasma ALD of SiO2 and TiO2 for substrate temperatures from 100 to ∼240 °C and plasma pressures from 12 to 130 mTorr (for SiO2). For both processes, the determined values of r are very low, i.e., ∼10-4 or lower, and decrease with temperature and pressure down to ∼10-5 within the studied ranges. Accordingly, deposition on trench structures with aspect ratios (ARs) of <200 is typically not significantly limited by recombination and obtaining excellent film conformality is relatively facile. For higher AR values, e.g., approaching 1000, the plasma time needed to reach saturation increases exponentially and becomes increasingly dependent on the process conditions and the corresponding value of r. Similar dependence on process conditions can be present for plasma ALD of other materials as well, where, in certain cases, film growth is already recombination-limited for AR values of ∼10. Radical recombination data and trends as provided by this work are valuable for optimizing plasma ALD throughput and feasibility for high-AR applications and can also serve as input for modeling of radical recombination mechanisms.

| S-EPMC8162759 | biostudies-literature

Electrical Properties of Ultrathin Platinum Films by Plasma-Enhanced Atomic Layer Deposition.

Project description:The ability to deposit thin and conformal films has become of great importance because of downscaling of devices. However, because of nucleation difficulty, depositing an electrically stable and thin conformal platinum film on an oxide nucleation layer has proven challenging. By using plasma-enhanced atomic layer deposition (PEALD) and TiO2 as a nucleation layer, we achieved electrically continuous PEALD platinum films down to a thickness of 3.7 nm. Results show that for films as thin as 5.7 nm, the Mayadas-Shatzkes (MS) model for electrical conductivity and the Tellier-Tosser model for temperature coefficient of resistance hold. Although the experimental values start to deviate from the MS model below 5.7 nm because of incomplete Pt coverage, the films still show root mean square electrical stability better than 50 ppm over time, indicating that these films are not only electrically continuous but also sufficiently reliable for use in many practical applications.

| S-EPMC6407042 | biostudies-literature

Low-temperature remote plasma enhanced atomic layer deposition of ZrO2/zircone nanolaminate film for efficient encapsulation of flexible organic light-emitting diodes.

Project description:Encapsulation is essential to protect the air-sensitive components of organic light-emitting diodes (OLEDs) such as active layers and cathode electrodes. In this study, hybrid zirconium inorganic/organic nanolaminates were fabricated using remote plasma enhanced atomic layer deposition (PEALD) and molecular layer deposition at a low temperature. The nanolaminate serves as a thin-film encapsulation layer for OLEDs. The reaction mechanism of PEALD process was investigated using an in-situ quartz crystal microbalance (QCM) and in-situ quadrupole mass spectrometer (QMS). The bonds present in the films were determined by Fourier transform infrared spectroscopy. The primary reaction byproducts in PEALD, such as CO, CO2, NO, H2O, as well as the related fragments during the O2 plasma process were characterized using the QMS, indicating a combustion-like reaction process. The self-limiting nature and growth mechanisms of the ZrO2 during the complex surface chemical reaction of the ligand and O2 plasma were monitored using the QCM. The remote PEALD ZrO2/zircone nanolaminate structure prolonged the transmission path of water vapor and smooth surface morphology. Consequently, the water barrier properties were significantly improved (reaching 3.078?×?10-5?g/m2/day). This study also shows that flexible OLEDs can be successfully encapsulated to achieve a significantly longer lifetime.

| S-EPMC5216332 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data