Both high reliability and giant electrocaloric strength in BaTiO₃ ceramics.

ABSTRACT: BaTiO₃ has a giant electrocaloric strength, |ΔT|/|ΔE|, because of a large latent heat and a sharp phase transition. The electrocaloric strength of a new single crystal, as giant as 0.48 K·cm/kV, is twice larger than the previous best result, but it remarkably decreased to 0.18 K·cm/kV after several times of thermal cycles accompanied by alternating electric fields, because the field-induced phase transition and domain switching resulted in numerous defects such as microcracks. The ceramics prepared from nano-sized powders showed a high electrocaloric strength of 0.14 K·cm/kV, comparable to the single crystals experienced electrocaloric cycles, because of its unique microstructure after proper sintering process. Moreover, its properties did not change under the combined effects of thermal cycles and alternating electric fields, i.e. it has both large electrocaloric effect and good reliability, which are desirable for practical applications.

SUBMITTER: Bai Y

PROVIDER: S-EPMC3792410 | biostudies-other | 2013

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Tuning the electrocaloric enhancement near the morphotropic phase boundary in lead-free ceramics.

Project description:The need for more energy-efficient and environmentally-friendly alternatives in the refrigeration industry to meet global emission targets has driven efforts towards materials with a potential for solid state cooling. Adiabatic depolarisation cooling, based on the electrocaloric effect (ECE), is a significant contender for efficient new solid state refrigeration techniques. Some of the highest ECE performances reported are found in compounds close to the morphotropic phase boundary (MPB). This relationship between performance and the MPB makes the ability to tune the position of the MPB an important challenge in electrocaloric research. Here, we report direct ECE measurements performed on MPB tuned NBT-06BT bulk ceramics with a combination of A-site substitutions. We successfully shift the MPB of these lead-free ceramics closer to room temperature, as required for solid state refrigeration, without loss of the criticality of the system and the associated ECE enhancement.

| S-EPMC4911558 | biostudies-literature

Large Electrocaloric Effect in Relaxor Ferroelectric and Antiferroelectric Lanthanum Doped Lead Zirconate Titanate Ceramics.

Project description:Both relaxor ferroelectric and antiferroelectric materials can individually demonstrate large electrocaloric effects (ECE). However, in order to further enhance the ECE it is crucial to find a material system, which can exhibit simultaneously both relaxor ferroelectric and antiferroelectric properties, or easily convert from one into another in terms of the compositional tailoring. Here we report on a system, in which the structure can readily change from antiferroelectric into relaxor ferroelectric and vice versa. To this end relaxor ferroelectric Pb0.89La0.11(Zr0.7Ti0.3)0.9725O3 and antiferroelectric Pb0.93La0.07(Zr0.82Ti0.18)0.9825O3 ceramics were designed near the antiferroelectric-ferroelectric phase boundary line in the La2O3-PbZrO3-PbTiO3 phase diagram. Conventional solid state reaction processing was used to prepare the two compositions. The ECE properties were deduced from Maxwell relations and Landau-Ginzburg-Devonshire (LGD) phenomenological theory, respectively, and also directly controlled by a computer and measured by thermometry. Large electrocaloric efficiencies were obtained and comparable with the results calculated via the phenomenological theory. Results show great potential in achieving large cooling power as refrigerants.

| S-EPMC5366905 | biostudies-literature

Giant electrocaloric materials energy efficiency in highly ordered lead scandium tantalate.

Project description:Electrocaloric materials are promising working bodies for caloric-based technologies, suggested as an efficient alternative to the vapor compression systems. However, their materials efficiency defined as the ratio of the exchangeable electrocaloric heat to the work needed to trigger this heat remains unknown. Here, we show by direct measurements of heat and electrical work that a highly ordered bulk lead scandium tantalate can exchange more than a hundred times more electrocaloric heat than the work needed to trigger it. Besides, our material exhibits a maximum adiabatic temperature change of 3.7 K at an electric field of 40 kV cm-1. These features are strong assets in favor of electrocaloric materials for future cooling devices.

| S-EPMC8172889 | biostudies-literature

Giant Negative Electrocaloric Effect in Anti-Ferroelectric (Pb0.97La0.02)(Zr0.95Ti0.05)O3 Ceramics.

Project description:A giant electrocaloric effect is reported in (Pb0.97La0.02)(Zr0.95Ti0.05)O3 anti-ferroelectric ceramics. These samples were fabricated by a solid-state mixed oxide technique. Dielectric analyses were employed to investigate the anti-ferroelectric (AFE) and ferroelectric (FE) phase transitions of the sample. During the heating process, the phase transition from the orthorhombic anti-ferroelectric phase (AFEO) to the tetragonal anti-ferroelectric phase (AFET) occurs at 155 °C, and the phase transition from AFET to PE occurs at 225 °C. Using the Maxwell relationship, the entropy change ?S and adiabatic temperature change ?T were obtained at different electric fields ranging from 40 to 65 kV/cm. The maximum adiabatic temperature change (?T max = -7.47 K) was obtained at 50 kV/cm, which was attributed to the field-induced phase transformation between the anti-ferroelectric and ferroelectric phases. These results showed that PLZT2/95/5 ceramics possess a large negative electrocaloric effect value, which could be applied in achieving cooling power as refrigerants.

| S-EPMC6740168 | biostudies-literature

Giant electrocaloric response in smectic liquid crystals with direct smectic-isotropic transition.

Project description:Electrocaloric materials have become a viable technology for solid state heat management applications. We demonstrate both theoretically and experimentally that liquid crystals (LCs) can be exploited as efficient electrocaloric materials. Numerical and experimental investigations determine the conditions under which the strongest electrocaloric effect (ECE) responses are expected in LCs. Specifically, we show that a large ECE can be expected at the isotropic-nematic and in particular at the isotropic-smectic A phase transition. In our theoretical study, LC ordering is modelled using a Landau - de Gennes - Ginzburg mesoscopic approach. The simulation results are in qualitative agreement with our high precision electrocaloric measurements conducted on 8CB and 12CB liquid crystals. In the latter, we obtained ΔTEC ~ 6.5 K, corresponding to the largest response measured so far in LCs. The fluid property of LC electrocaloric heat cooling elements could lead to the development of devices with a higher coefficient of performance and thus better cooling power yield per mass of the ECE-based device.

| S-EPMC6370888 | biostudies-literature

Full strength and toughness recovery after repeated cracking and healing in bone-like high temperature ceramics.

Project description:Bones of humans and animals combine two unique features, namely: they are brittle yet have a very high fracture toughness linked to the tortuosity of the crack path and they have the ability to repeatedly heal local fissures such that full recovery of overall mechanical properties is obtained even if the local bone structure is irreversibly changed by the healing process. Here it is demonstrated that Ti2AlC MAX phase metallo-ceramics also having a bone-like hierarchical microstructure and also failing along zig-zag fracture surfaces similarly demonstrate repeated full strength and toughness recovery at room temperature, even though the (high temperature) healing reaction involves the local formation of dense and brittle alumina within the crack. Full recovery of the fracture toughness depends on the healed zone thickness and process zone size formed in the alumina reaction product. A 3-dimensional finite element method (FEM) analysis of the data obtained from a newly designed wedge splitting test allowed full extraction of the local fracture properties of the healed cracks.

| S-EPMC7643164 | biostudies-literature

Giant electrocaloric effect in ferroelectric nanotubes near room temperature.

Project description:Ferroelectric perovskite oxides possess large electrocaloric effect, but only at high temperature, which limits their potential as next generation solid state cooling devices. Here, we demonstrate from phase field simulations that a giant adiabatic temperature change exhibits near room temperature in the strained ferroelectric PbTiO₃ nanotubes, which is several times in magnitude larger than that of PbTiO₃ thin films. Such giant adiabatic temperature change is attributed to the extrinsic contribution of unusual domain transition, which involves a dedicated interplay among the electric field, strain, temperature and polarization. Careful selection of external strain allows one to harness the extrinsic contribution to obtain large adiabatic temperature change in ferroelectric nanotubes near room temperature. Our finding provides a novel insight into the electrocaloric response of ferroelectric nanostructures and leads to a new strategy to tailor and improve the electrocaloric properties of ferroelectric materials through domain engineering.

| S-EPMC4289897 | biostudies-other

Temperature independence of piezoelectric properties for high-performance BiFeO3-BaTiO3 lead-free piezoelectric ceramics up to 300 °C.

Project description:The temperature-dependence behaviors of ferroelectric, piezoelectric, k p and electrical-field-induced strain were carefully evaluated for high-performance BiFeO3-0.3BaTiO3 (BF-0.3BT) ceramics. There results indicate, combined with Rayleigh analysis and temperature-dependence XRD and PFM, that the increase of strain and large signal with increasing the temperature from room temperature to 180 °C is related to the joint effect of intrinsic contribution (lattice expansion) and extrinsic contribution (domain switching). With further increasing the temperature to 300 °C, the large signal d 33 and electrical-field-induced strain mildly decrease because of the increase of conductivity for BF-0.3BT ceramics. However, different from strain and large signal the small signal d 33(E0) and k p exhibit excellent temperature stability behavior as the temperature increases from room temperature to 300 °C.

| S-EPMC9088175 | biostudies-literature

BaTiO3/MWNTs/Polyvinylidene Fluoride Ternary Dielectric Composites with Excellent Dielectric Property, High Breakdown Strength, and High-Energy Storage Density.

Project description:To improve the dielectric performance of polyvinylidene fluoride (PVDF), BaTiO3/MWNTs/PVDF ternary composites were prepared by the solution casting method. The percolation threshold (fraction of MWNTs) has dropped greatly below 0.4 vol %, with the enhancement of dielectric constant and breakdown field. For the BaTiO3/MWNTs/PVDF (11.5/0.35/88.15) composite, the dielectric constant is 59, the loss is below 0.055, and the maximum operating electric field is 324 MV/m, so the discharged energy density can be of up to 10.3 J/cm3 with the efficiency of above 77.2%. The reason of improvement was revealed by the scanning electron microscope images and the X-ray diffraction data. It is found that uniform distribution of filler in the composites and the increase of the β phase of polymers result in the enhancement of polarization and improvement of dielectric constant of PVDF. The third-phase spherical inorganic particles prevent the formation of conductive networks and improve the uniformity of local electric field, so the breakdown strength of composites can be enhanced greatly. Here, this paper provides a method to get the composites with high energy storage density for supercapacitors.

| S-EPMC6648649 | biostudies-literature

Simultaneous improvements of strength and toughness in topologically interlocked ceramics.

Project description:Topologically interlocked materials (TIMs) are an emerging class of architectured materials based on stiff building blocks of well-controlled geometries which can slide, rotate, or interlock collectively providing a wealth of tunable mechanisms, precise structural properties, and functionalities. TIMs are typically 10 times more impact resistant than their monolithic form, but this improvement usually comes at the expense of strength. Here we used 3D printing and replica casting to explore 15 designs of architectured ceramic panels based on platonic shapes and their truncated versions. We tested the panels in quasi-static and impact conditions with stereoimaging, image correlation, and 3D reconstruction to monitor the displacements and rotations of individual blocks. We report a design based on octahedral blocks which is not only tougher (50×) but also stronger (1.2×) than monolithic plates of the same material. This result suggests that there is no upper bound for strength and toughness in TIMs, unveiling their tremendous potential as structural and multifunctional materials. Based on our experiments, we propose a nondimensional "interlocking parameter" which could guide the exploration of future architectured systems.

| S-EPMC6140525 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data