Fano resonance in anodic aluminum oxide based photonic crystals.

ABSTRACT: Anodic aluminum oxide based photonic crystals with periodic porous structure have been prepared using voltage compensation method. The as-prepared sample showed an ultra-narrow photonic bandgap. Asymmetric line-shape profiles of the photonic bandgaps have been observed, which is attributed to Fano resonance between the photonic bandgap state of photonic crystal and continuum scattering state of porous structure. And the exhibited Fano resonance shows more clearly when the sample is saturated ethanol gas than air-filled. Further theoretical analysis by transfer matrix method verified these results. These findings provide a better understanding on the nature of photonic bandgaps of photonic crystals made up of porous materials, in which the porous structures not only exist as layers of effective-refractive-index material providing Bragg scattering, but also provide a continuum light scattering state to interact with Bragg scattering state to show an asymmetric line-shape profile.

SUBMITTER: Shang GL

PROVIDER: S-EPMC3884230 | biostudies-other | 2014

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Publications

Fano resonance in anodic aluminum oxide based photonic crystals.

Shang Guo Liang GL Fei Guang Tao GT Zhang Yao Y Yan Peng P Xu Shao Hui SH Ouyang Hao Miao HM Zhang Li De LD

Scientific reports 20140108

Anodic aluminum oxide based photonic crystals with periodic porous structure have been prepared using voltage compensation method. The as-prepared sample showed an ultra-narrow photonic bandgap. Asymmetric line-shape profiles of the photonic bandgaps have been observed, which is attributed to Fano resonance between the photonic bandgap state of photonic crystal and continuum scattering state of porous structure. And the exhibited Fano resonance shows more clearly when the sample is saturated eth ...[more]

PMID: 24398625

Similar Datasets

Engineering of Hybrid Nanoporous Anodic Alumina Photonic Crystals by Heterogeneous Pulse Anodization.

Project description:In this study, we present an advanced nanofabrication approach, so-called 'heterogeneous pulse anodization' (HPA), in which galvanostatic stepwise and apodized sinusoidal pulse anodizations are combined in a single process. This novel anodization method enables the precise optical engineering of the characteristic photonic stopbands (PSBs) of nanoporous anodic alumina photonic crystals (NAA-PCs). The resulting structures are hybrid PCs (Hy-NAA-PCs) composed of distributed Bragg reflectors (DBRs) and apodized gradient-index filters (APO-GIFs) embedded within the same PC structure. The modification of various anodization parameters such as anodization period, relative and total anodization time, structural arrangement of PCs within Hy-NAA-PCs, and pore widening time allows the fine-tuning of the PSBs' features (i.e. number, position and bandwidth of central wavelength) across the spectral regions. The effects of these fabrication parameters are systematically assessed, revealing that the positions of the characteristic transmission bands of Hy-NAA-PCs are highly controllable. Our study provides a comprehensive rationale towards the development of unique Hy-NAA-PCs with controllable optical properties, which could open new opportunities for a plethora of applications.

| S-EPMC6013466 | biostudies-literature

Functionalized anodic aluminum oxide membrane-electrode system for enzyme immobilization.

Project description:A nanoporous membrane system with directed flow carrying reagents to sequentially attached enzymes to mimic nature’s enzyme complex system was demonstrated. Genetically modified glycosylation enzyme, OleD Loki variant, was immobilized onto nanometer-scale electrodes at the pore entrances/exits of anodic aluminum oxide membranes through His6-tag affinity binding. The enzyme activity was assessed in two reactions—a one-step “reverse” sugar nucleotide formation reaction (UDP-Glc) and a two-step sequential sugar nucleotide formation and sugar nucleotide-based glycosylation reaction. For the one-step reaction, enzyme specific activity of 6–20 min(–1) on membrane supports was seen to be comparable to solution enzyme specific activity of 10 min(–1). UDP-Glc production efficiencies as high as 98% were observed at a flow rate of 0.5 mL/min, at which the substrate residence time over the electrode length down pore entrances was matched to the enzyme activity rate. This flow geometry also prevented an unwanted secondary product hydrolysis reaction, as observed in the test homogeneous solution. Enzyme utilization increased by a factor of 280 compared to test homogeneous conditions due to the continuous flow of fresh substrate over the enzyme. To mimic enzyme complex systems, a two-step sequential reaction using OleD Loki enzyme was performed at membrane pore entrances then exits. After UDP-Glc formation at the entrance electrode, aglycon 4-methylumbelliferone was supplied at the exit face of the reactor, affording overall 80% glycosylation efficiency. The membrane platform showed the ability to be regenerated with purified enzyme as well as directly from expression crude, thus demonstrating a single-step immobilization and purification process.

| S-EPMC4148145 | biostudies-literature

Dual effects of ultrasound on fabrication of anodic aluminum oxide.

Project description:Ultrasound has been proven to enhance the mass transfer process and impact the fabrication of anodic aluminum oxide (AAO). However, the different effects of ultrasound propagating in different media make the specific target and process of ultrasound in AAO remain unclear, and the effects of ultrasound on AAO reported in previous studies are contradictory. These uncertainties have greatly limited the application of ultrasonic-assisted anodization (UAA) in practice. In this study, the bubble desorption and mass transfer enhancement effects were decoupled based on an anodizing system with focused ultrasound, such that the dual effects of ultrasound on different targets were distinguished. The results showed that ultrasound has the dual effects on AAO fabrication. Specifically, ultrasound focused on the anode has a nanopore-expansion effect on AAO, leading to a 12.24 % improvement in fabrication efficiency. This was attributed to the promotion of interfacial ion migration through ultrasonic-induced high-frequency vibrational bubble desorption. However, AAO nanopores were observed to shrink when ultrasound was focused on the electrolyte, accompanied by a 25.85 % reduction in fabrication efficiency. The effects of ultrasound on mass transfer through jet cavitation appeared to be the reason for this phenomenon. This study resolved the paradoxical phenomena of UAA in previous studies and is expected to guide AAO application in electrochemistry and surface treatments.

| S-EPMC10352598 | biostudies-literature

Nano sand filter with functionalized nanoparticles embedded in anodic aluminum oxide templates.

Project description:Since the ancient Egyptians had used sand as filter media for water purification, its principle has been inherited through generations and it is still being used now in industries. The sand filter consists of sand literally, and the voids within the sand bed are the pores for filtration. Here we present a filtration principle using nanoparticles, so that the voids between the nanoparticles can be considered as effective pores in nanoscale dimension. Anodic aluminum oxide (AAO) membrane has been used as the working template, and the nanoparticles have been injected and embedded within the pores of the AAO template. Nanoparticles with multiple sizes have been used in order to obtain smaller voids. Moreover, the nanoparticles have been functionalized, or electrically charged, with arginine/phenylalanine (RF) peptide group. In this way, filtration performance for charged particles or molecules, such as methylene blue, has been enhanced. Consequently, this study is expected to provide a new principle for fabrication of nano voids, or nano pores, and for filtration in nanoscale dimension.

| S-EPMC5120303 | biostudies-literature

Fabrication of Silica Nanoparticle Monolayer Arrays Using an Anodic Aluminum Oxide Template.

Project description:Non-close-packed (NCP) silica nanoparticle monolayer arrays (SNMA) on ordered porous anodic aluminum oxide (AAO) templates were fabricated for the first time by a novel two-step spin-coating technique. The obtained NCP-SNMA-AAO was composed of silica nanoparticles (average primary particle size of 440 nm) and well-organized nanopores on the AAO substrates. NCP-SNMA-AAO with a supporting ratio of 87% silica nanoparticles showed a hydrophilic surface (water contact angle of 51.0°), while the original AAO substrate shows a hydrophobic surface (water contact angle of 107.9°). The maximum coefficient of static friction was decreased by 29% (0.327 → 0.233). The coefficient of dynamic friction was also decreased by 20% (0.281 → 0.226). We found that controlling the silica supporting ratio using the two-step spin-coating technique is an effective approach for surface modification of an AAO substrate.

| S-EPMC6733172 | biostudies-literature

Enabling enhanced emission and low-threshold lasing of organic molecules using special Fano resonances of macroscopic photonic crystals.

Project description:The nature of light interaction with matter can be dramatically altered in optical cavities, often inducing nonclassical behavior. In solid-state systems, excitons need to be spatially incorporated within nanostructured cavities to achieve such behavior. Although fascinating phenomena have been observed with inorganic nanostructures, the incorporation of organic molecules into the typically inorganic cavity is more challenging. Here, we present a unique optofluidic platform comprising organic molecules in solution suspended on a photonic crystal surface, which supports macroscopic Fano resonances and allows strong and tunable interactions with the molecules anywhere along the surface. We develop a theoretical framework of this system and present a rigorous comparison with experimental measurements, showing dramatic spectral and angular enhancement of emission. We then demonstrate that these enhancement mechanisms enable lasing of only a 100-nm thin layer of diluted solution of organic molecules with substantially reduced threshold intensity, which has important implications for organic light-emitting devices and molecular sensing.

| S-EPMC3752230 | biostudies-literature

Super-spreading on superamphiphilic micro-organized nanochannel anodic aluminum oxide surfaces for heat dissipation.

Project description:Nature-inspired superamphiphilic surfaces have drawn tremendous attention owing to its extreme liquid-loving behaviors. Herein, a micro-organized nano-channel (Mo-Na) superamphiphilic anodic aluminum oxide (AAO) surface with long-lasting superamphiphilic property is prepared by a facile one-step anodization method with controllable temperature change. Analysis of dynamic wetting behaviors on superamphiphilic Mo-Na AAO surfaces for various liquids reveals that the spreading factor is in negative correlation with the surface tension and liquid polarity. Detailed observation of the three-phase contact line shows a micro-scale capillary film on superamphiphilic Mo-Na AAO surfaces, which results from the horizontal component of the capillary force. Taking advantage of the superamphiphilic property, water droplets can spread completely on these Mo-Na AAO surfaces within a short time, which can be applied for efficient heat dissipation. Moreover, the unique AAO surface with Mo-Na structures also offers an effective template for future efforts in AAO-based composite devices.

| S-EPMC8027538 | biostudies-literature

Optimization of Colloidal Gold Nanoparticles on Porous Anodic Aluminum Oxide Substrates for Refractometric Sensing.

Project description:A new composite metal-insulator-metal (MIM) system consisting of exceptionally dense non-close-packed (NCP) arrays of gold or silver nanoparticles, porous anodic aluminum oxide (PAAO), and bulk aluminum substrate interacts strongly with visible light and may become a very useful component for optical applications. The proposed MIM structure can be synthesized using accessible lithography-free chemical and physical processes (anodization and capillary force assisted colloidal particle deposition) that are suitable for the low-cost production of specialized devices. Here, we present a systematic study to determine the essential MIM structure parameters (nanoparticle size and PAAO layer thickness) for localized surface plasmon resonance (LSPR) refractometric sensing. A performance comparison was done by recording the spectra of scattered light upon angled illumination in media with different refractive indices. A clear advantage for maximizing the signal to background ratio was observed in the case of 60 and 80 nm Au nanoparticles with a PAAO thickness in a narrow range between 300 and 375 nm. Sensitivity exceeding a 200 nm peak wavelength shift per refractive index unit was found for 60 nm Au nanoparticles on approximately 500-nm-thick PAAO. The experimental observations were supported by finite-difference time-domain (FDTD) simulations.

| S-EPMC9648095 | biostudies-literature

Preparation of Aluminum Nanomesh Thin Films from an Anodic Aluminum Oxide Template as Transparent Conductive Electrodes.

Project description:We have employed anodic aluminum oxide as a template to prepare ultrathin, transparent, and conducting Al films with a unique nanomesh structure for transparent conductive electrodes. The anodic aluminum oxide template is obtained through direct anodization of a sputtered Al layer on a glass substrate, and subsequent wet etching creates the nanomesh metallic film. The optical and conductive properties are greatly influenced by experimental conditions. By tuning the anodizing time, transparent electrodes with appropriate optical transmittance and sheet resistance have been obtained. The results demonstrate that our proposed strategy can serve as a potential method to fabricate low-cost TCEs to replace conventional indium tin oxide materials.

| S-EPMC4735723 | biostudies-other

Preparation and Size Control of Efficient and Safe Nanopesticides by Anodic Aluminum Oxide Templates-Assisted Method.

Project description:Efficient and safe nanopesticides play an important role in pest control due to enhancing target efficiency and reducing undesirable side effects, which has become a hot spot in pesticide formulation research. However, the preparation methods of nanopesticides are facing critical challenges including low productivity, uneven particle size and batch differences. Here, we successfully developed a novel, versatile and tunable strategy for preparing buprofezin nanoparticles with tunable size via anodic aluminum oxide (AAO) template-assisted method, which exhibited better reproducibility and homogeneity comparing with the traditional method. The storage stability of nanoparticles at different temperatures was evaluated, and the release properties were also determined to evaluate the performance of nanoparticles. Moreover, the present method is further demonstrated to be easily applicable for insoluble drugs and be extended for the study of the physicochemical properties of drug particles with different sizes.

| S-EPMC8347391 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data