Photoluminescence characterization of polythiophene films incorporated with highly functional molecules such as metallophthalocyanine.

ABSTRACT: The photoluminescence (PL) of conducting polymer polythiophene (PT) films incorporated with metallophthalocyanines (PcMs) such as CuPc, MgPc, FePc, Li2Pc, and CoPc was studied by PL and time-correlated single photon counting (TCSPC) measurements. Polymer films were prepared by electrochemical polymerization and PcMs migrated into the polymer films by a diffusion method using acetonitrile or toluene as a solvent to dissolve the PcMs. The wavelength of PL emission peaks changed significantly depending on the solvent used in the doping process. Using acetonitrile, the observed PL emission peaks originated from the Q band, whereas they were assigned to the Soret band in the case of toluene. TCSPC measurements showed that PL emission took place through a ligand-ligand transition process when using acetonitrile because the average lifetimes were comparable and independent of the central metal ions for CoPc-, Li2Pc-, and MgPc-doped polymer films. Conversely, using toluene, it was found that ligand-ligand emission occurred for Li2Pc-, MgPc-, and FePc-doped films. To identify the cause of the drastic change in PL emission pattern, x-ray photoelectron spectroscopy measurements were obtained. A lower binding energy component appeared in the C 1s core-level spectra of acetonitrile-processed PcM-doped PT films, whereas this component shifted to higher energy and overlapped with the main peak for toluene-processed PcM-doped PT films. The lower binding energy component corresponded to photoelectrons due to the C atoms in the benzene rings of the ligand. Lower binding energy components also appeared in the N 1s core-level spectra of acetonitrile-processed PcM-doped PT films, and this component shifted to higher energy for toluene-processed PcM-doped PT films. These lower energy components were assigned to the core-level peaks due to the N atoms at the meso position bridging between pyrrole rings. This suggests that the electron charge at the N sites of the meso positions in toluene-processed films was smaller than in acetonitrile-processed ones. The changes in energy at benzene C sites and meso N sites suggest that the electronic states of the phthalocyanine in the toluene-processed films were porphyrin-like, so the Soret band became dominant in the PL emission spectrum.

SUBMITTER: Kobe H

PROVIDER: S-EPMC3978906 | biostudies-other | 2013 Jan

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:Background:Local delivery of anti-cancer drugs through a stent is a very promising and anticipated treatment modality for patients who have obstructions in their gastrointestinal tract with malignant tumors. Anticancer drug release via stents, however, needs to be optimized with respect to drug delivery behavior for the stents to be effective for prolonged containment of tumor proliferation and stent re-obstruction. Local stent-based drug delivery has been tested using an effective anti-cancer drug, gemcitabine, but the release from the stent-coated polyurethane films is often too fast and the drug is depleted from the coated film virtually in a day. Methods:To moderate the drug release from a polyurethane film, a gemcitabine-incorporated polyurethane film was enveloped with a pure polyurethane film, with no drug loading, and with a silicone film by solution casting after activation of the silicone film surface with plasma treatment. Results:The pure polyurethane barrier film was effective; the interface of the two were indistinguishable on scanning electron microscopy, and the initial burst, i.e., the cumulative release in a day, decreased from 90 to 26%. The silicone film barrier, on the other hand, was defective as voids were seen using a scanning electron microscope, and micro-separation of the two layers was observed after the film was immersed in phosphate-buffered saline for 1 day during the in vitro drug release study. Conclusions:Enveloping a gemcitabine-releasing polyurethane film with a homo-polymer barrier film was quite effective for moderating the initial burst of gemcitabine, thus, prolonging the release time of the drug. Enveloping the polyurethane film with a silicone film was also possible after plasma treatment of the silicone film surface, but the two films eventually separated in the aqueous environment. More studies are needed to tune the drug release behavior of gemcitabine from the stent covering film before attempting a clinical application of an anti-cancer drug releasing stent.

Dataset Information

Photoluminescence characterization of polythiophene films incorporated with highly functional molecules such as metallophthalocyanine.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets