Characterization of methacrylated type-I collagen as a dynamic, photoactive hydrogel.

ABSTRACT: Type-I collagen is an attractive scaffold material for tissue engineering due to its ability to self-assemble into a fibrillar hydrogel, its innate support of tissue cells through bioactive adhesion sites, and its biodegradability. However, a lack of control of material properties has hampered its utility as a scaffold. We have modified collagen via the addition of methacrylate groups to create collagen methacrylamide (CMA) using a synthesis reaction that allows retention of fundamental characteristics of native collagen, including spontaneous fibrillar self-assembly and enzymatic biodegradability. This method allows for a rapid, five-fold increase in storage modulus upon irradiation with 365 nm light. Fibrillar diameter of CMA was not significantly different from native collagen. Collagenolytic degradability of uncrosslinked CMA was minimally reduced, while photocrosslinked CMA was significantly more resistant to degradation. Live/Dead staining demonstrated that a large majority (71%) of encapsulated mesenchymal stem cells remained viable 24 h after photocrosslinking, which further increased to 81% after 72 h. This material represents a novel platform for creating mechanically heterogeneous environments.

SUBMITTER: Gaudet ID

PROVIDER: S-EPMC4243547 | biostudies-other | 2012 Dec

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Collagen 1 Hydrogel Dynamic Loading Tests

2008-01-11 | GSE10125 | GEO

Bioprinted Gelatin-Recombinant Type III Collagen Hydrogel Promotes Wound Healing.

Project description:Artificial skins are biomaterials that can replace the lost skin or promote the regeneration of damaged skin. Skin regenerative biomaterials are highly applauded because they can exempt patients with severe burns from the painful procedure of autologous skin transplantation. Notwithstanding decades of research, biocompatible, degradable, and printable biomaterials that can effectively promote skin regeneration as a transplantation replacement in clinical use are still scarce. Here, we report one type of all-protein hydrogel material as the product of the enzymatic crosslinking reaction of gelatin and a recombinant type III collagen (rColIII) protein. Doping the rColIII protein in gelatin reduces the inflammatory response as an implant underneath the skin. The all-protein hydrogel can be bioprinted as scaffolds to support the growth and proliferation of 3T3 fibroblast cells. The hydrogel used as a wound dressing promotes wound healing in a rat model of skin damage, showing a faster and healthier recovery than the controls. The rColIII protein in the hydrogel has been shown to play a critical role in skin regeneration. Altogether, this work manifests the development of all-protein gelatin-rColIII hydrogel and demonstrates its use in wound healing. The gelatin-collagen hydrogel wound dressing thereby may become a promising treatment of severe wounds in the future.

| S-EPMC9159484 | biostudies-literature

Amine-reactive crosslinking enhances type 0 collagen hydrogel properties for regenerative medicine.

Project description:IntroductionCollagen is extensively utilised in regenerative medicine due to its highly desirable properties. However, collagen is typically derived from mammalian sources, which poses several limitations, including high cost, potential risk of immunogenicity and transmission of infectious diseases, and ethical and religious constraints. Jellyfish-sourced type 0 collagen represents a safer and more environmentally sustainable alternative collagen source.MethodsThus, we investigated the potential of jellyfish collagen-based hydrogels, obtained from Rhizostoma pulmo (R. pulmo) jellyfish, to be utilised in regenerative medicine. A variety of R. pulmo collagen hydrogels (RpCol hydrogels) were formed by adding a range of chemical crosslinking agents and their physicochemical and biological properties were characterised to assess their suitability for regenerative medicine applications.Results and discussionThe characteristic chemical composition of RpCol was confirmed by Fourier-transform infrared spectroscopy (FTIR), and the degradation kinetics, morphological, and rheological properties of RpCol hydrogels were shown to be adaptable through the addition of specific chemical crosslinking agents. The endotoxin levels of RpCol were below the Food and Drug Administration (FDA) limit for medical devices, thus allowing the potential use of RpCol in vivo. 8-arm polyethylene glycol succinimidyl carboxyl methyl ester (PEG-SCM)-crosslinked RpCol hydrogels preserved the viability and induced a significant increase in the metabolic activity of immortalised human mesenchymal stem/stromal cells (TERT-hMSCs), therefore demonstrating their potential to be utilised in a wide range of regenerative medicine applications.

| S-EPMC11310005 | biostudies-literature

Alginate-Collagen Fibril Composite Hydrogel.

Project description:We report on the synthesis and the mechanical characterization of an alginate-collagen fibril composite hydrogel. Native type I collagen fibrils were used to synthesize the fibrous composite hydrogel. We characterized the mechanical properties of the fabricated fibrous hydrogel using tensile testing; rheometry and atomic force microscope (AFM)-based nanoindentation experiments. The results show that addition of type I collagen fibrils improves the rheological and indentation properties of the hydrogel.

| S-EPMC5455273 | biostudies-literature

Mechanical Characterization of a Dynamic and Tunable Methacrylated Hyaluronic Acid Hydrogel.

Project description:Hyaluronic acid (HA) is a commonly used natural polymer for cell scaffolding. Modification by methacrylate allows it to be polymerized by free radicals via addition of an initiator, e.g., light-sensitive Irgacure, to form a methacrylated hyaluronic acid (MeHA) hydrogel. Light-activated crosslinking can be used to control the degree of polymerization, and sequential polymerization steps allow cells plated onto or in the hydrogel to initially feel a soft and then a stiff matrix. Here, the elastic modulus of MeHA hydrogels was systematically analyzed by atomic force microscopy (AFM) for a number of variables including duration of UV exposure, monomer concentration, and methacrylate functionalization. To determine how cells would respond to a specific two-step polymerization, NIH 3T3 fibroblasts were cultured on the stiffening MeHA hydrogels and found to reorganize their cytoskeleton and spread area upon hydrogel stiffening, consistent with cells originally cultured on substrates of the final elastic modulus.

| S-EPMC4844086 | biostudies-other

Transcription profiling of human dermal fibroblasts after 3 hours of cyclic mechanical loading compared with ni loading - collagen 1 hydrogel dynamic loading tests

Project description:Cell viability and global gene expression was anayzed from collagen 1 hydrogel scaffolds following 3 hours of cyclic mechanical loading and compared with non-loaded scaffolds. Experiment Overall Design: 6 samples are analyzed (2 sets in triplicate). The first set is the Loaded condition in which Collagen 1 hydrogels seeded with Human dermal fibroblasts underwent cyclic loading of 0.1Hz for 180 minutes at 37 degrees Celsius. The second set is the control Unloaded condition in which the Collagen 1 hydrogels seeded with Human dermal fibroblasts are incubated at 37 degrees Celsius with no loading.

2008-06-11 | E-GEOD-10125 | biostudies-arrayexpress

Regulation of cardiomyocyte hypertrophy through dynamic regulation of type I collagen

Project description:Communications between cardiomyocytes and fibroblasts in the heart are thought to occur through both secreted growth factors and via alterations in the structural properties of the extracellular matrix that each of the cell types helps generate. While perturbations in fibroblast activity are known to impact development of cardiomyocyte hypertrophy, the specific role played by collagen in this intercellular communication remains unknown. In this study we addressed this knowledge gap through differential regulation of collagen 1a2 using mouse hearts. The microarray assays reported here were carried out to assess the effects of collagen 1a2 ablation on cardiac transcriptional profiles.

2023-09-15 | GSE204724 | GEO

Photopatternable and photoactive hydrogel for on-demand generation of hydrogen peroxide in cell culture.

Project description:Oxidative stress, largely mediated by reactive oxygen species (ROS), is a nearly ubiquitous component in complex biological processes such as aging and disease. Optimal in vitro methods used in elucidating disease mechanisms would deliver of low levels of hydrogen peroxide, emulating the in vivo pathological state, but current methods are limited by kinetic stability or accurate measurement of the dose administered. Here we present an in vitro platform that exploits anthraquinone catalysts for the photocatalytic production of hydrogen peroxide. This system can be dynamically tuned to provide constant generation of hydrogen peroxide at a desired physiologic rate over at least 14 days and is described using a kinetic model. Material characterization and stability is discussed along with a proof-of-concept in vitro study that assessed the viability of cells as they were oxidatively challenged over 24 h at different ROS generation rates.

| S-EPMC3992930 | biostudies-literature

TiO2 as Photosensitizer and Photoinitiator for Synthesis of Photoactive TiO2-PEGDA Hydrogel Without Organic Photoinitiator.

Project description:The replacement of potentially toxic photoinitiators is of increasing interest regarding the synthesis of biomaterials by photopolymerization. Therefore, we present a new method for the preparation of UV polymerized hydrogels with TiO2 as a photoinitiator. Titania is known to be an excellent photoactive compound which is non-toxic, inert, and cheap. The so-formed hydrogels possess excellent mechanical properties, a high swelling ratio, and high thermal stability. Furthermore, no TiO2 is released from the hydrogels. Thus, the material is highly suitable for medical applications. Additionally, the present TiO2 in the hydrogels remains photoactive as demonstrated by degradation of methylene blue. This enables the application of TiO2-hydrogels in photodynamic therapy.

| S-EPMC6090817 | biostudies-literature

Hydrogel-hydroxyapatite-monomeric collagen type-I scaffold with low-frequency electromagnetic field treatment enhances osteochondral repair in rabbits.

Project description:BackgroundCartilage damage is a common medical issue in clinical practice. Complete cartilage repair remains a significant challenge owing to the inferior quality of regenerative tissue. Safe and non-invasive magnetic therapy combined with tissue engineering to repair cartilage may be a promising breakthrough.MethodsIn this study, a composite scaffold made of Hydroxyapatite-Collagen type-I (HAC) and PLGA-PEG-PLGA thermogel was produced to match the cartilage and subchondral layers in osteochondral defects, respectively. Bone marrow mesenchymal stem cells (BMSC) encapsulated in the thermogel were stimulated by an electromagnetic field (EMF). Effect of EMF on the proliferation and chondrogenic differentiation potential was evaluated in vitro. 4 mm femoral condyle defect was constructed in rabbits. The scaffolds loaded with BMSCs were implanted into the defects with or without EMF treatment. Effects of the combination treatment of the EMF and composite scaffold on rabbit osteochondral defect was detected in vivo.ResultsIn vitro experiments showed that EMF could promote proliferation and chondrogenic differentiation of BMSCs partly by activating the PI3K/AKT/mTOR and Wnt1/LRP6/β-catenin signaling pathway. In vivo results further confirmed that the scaffold with EMF enhances the repair of osteochondral defects in rabbits, and, in particular, cartilage repair.ConclusionHydrogel-Hydroxyapatite-Monomeric Collagen type-I scaffold with low-frequency EMF treatment has the potential to enhance osteochondral repair.

| S-EPMC8590294 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data