Structural, optical, and magnetic properties of NiMoO4 nanorods prepared by microwave sintering.

ABSTRACT: We report on the structural, optical, and magnetic properties of α,β-NiMoO4 nanorods synthesized by annealing the NiMoO4:nH2O precursor at 600°C for 10 minutes in a domestic microwave. The crystalline structure properties of α,β-NiMoO4 were investigated using X-ray diffraction (XRD), Fourier transform infrared (FTIR), and Raman (FT-Raman) spectroscopies. The particle morphologies and size distributions were identified by field emission microscopy (FE-SEM). Experimental data were obtained by magnetization measurements for different applied magnetic fields. Optical properties were analyzed by ultraviolet-visible (UV-vis) and photoluminescence (PL) measurements. Our results revealed that the oxygen atoms occupy different positions and are very disturbed in the lattice and exhibit a particular characteristic related to differences in the length of the chemical bonds (Ni-O and Mo-O) of the cluster structure or defect densities in the crystalline α,β-NiMoO4 nanorods, which are the key to a deeper understanding of the exploitable physical and chemical properties in this study.

SUBMITTER: de Moura AP

PROVIDER: S-EPMC4352760 | biostudies-other | 2015

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:The bimodal-grain-size 7075 aluminium alloys containing varied ratios of large and small 7075 aluminium powders were prepared by spark plasma sintering (SPS). The large powder was 100 ± 15 ?m in diameter and the small one was 10 ± 5 ?m in diameter. The 7075 aluminium alloys was completely densified under the 500 °C sintering temperature and 60 MPa pressure. The large powders constituted coarse grain zone, and the small powders constituted fine grain zone in sintered 7075 aluminium alloys. The microstructural and microchemical difference between the large and small powders was remained in coarse and fine grain zones in bulk alloys after SPS sintering, which allowed for us to investigate the effects of microstructure and microchemistry on passive properties of oxide film formed on sintered alloys. The average diameter of intermetallic phases was 201.3 nm in coarse grain zone, while its vale was 79.8 nm in fine grain zone. The alloying element content in intermetallic phases in coarse grain zone was 33% to 48% higher than that on fine grain zone. The alloying element depletion zone surrounding intermetallic phases in coarse grain zone showed a bigger width and a more severe element depletion. The coarse grain zone in alloys showed a bigger electrochemical heterogeneity as compared to fine grain zone. The passive film formed on coarse grain zone had a thicker thickness and a point defect density of 2.4 × 1024 m-3, and the film on fine grain zone had a thinner thickness and a point defect density of 4.0 × 1023 m-3. The film resistance was 3.25 × 105 ?cm2 on coarse grain zone, while it was 6.46 × 105 ?cm2 on fine grain zone. The passive potential range of sintered alloys increased from 457 mV to 678 mV, while the corrosion current density decreased from 8.59 × 10-7 A/cm2 to 6.78 × 10-7 A/cm2 as fine grain zone increasing from 0% to 100%, which implied that the corrosion resistance of alloys increased with the increasing content of fine grains. The passive film on coarse grain zone exhibited bigger corrosion cavities after pitting initiation compared to that on fine grain zone. The passive film formed on fine grain zone showed a better corrosion resistance. The protectiveness of passive film was mainly determined by defect density rather than the thickness in this work.

Dataset Information

Structural, optical, and magnetic properties of NiMoO4 nanorods prepared by microwave sintering.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets