Temperature dependence of electric transport in few-layer graphene under large charge doping induced by electrochemical gating.

ABSTRACT: The temperature dependence of electric transport properties of single-layer and few-layer graphene at large charge doping is of great interest both for the study of the scattering processes dominating the conductivity at different temperatures and in view of the theoretically predicted possibility to reach the superconducting state in such extreme conditions. Here we present the results obtained in 3-, 4- and 5-layer graphene devices down to 3.5 K, where a large surface charge density up to about 6.8·10(14) cm(-2) has been reached by employing a novel polymer electrolyte solution for the electrochemical gating. In contrast with recent results obtained in single-layer graphene, the temperature dependence of the sheet resistance between 20 K and 280 K shows a low-temperature dominance of a T(2) component - that can be associated with electron-electron scattering - and, at about 100 K, a crossover to the classic electron-phonon regime. Unexpectedly, this crossover does not show any dependence on the induced charge density, i.e. on the large tuning of the Fermi energy.

SUBMITTER: Gonnelli RS

PROVIDER: S-EPMC4407556 | biostudies-other | 2015

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Layer-by-Layer Insight into Electrostatic Charge Distribution of Few-Layer Graphene.

Project description:In few-layer graphene (FLG) systems on a dielectric substrate such as SiO2, the addition of each extra layer of graphene can drastically alter their electronic and structural properties. Here, we map the charge distribution among the individual layers of finite-size FLG systems using a novel spatial discrete model that describes both electrostatic interlayer screening and fringe field effects. Our results reveal that the charge density in the region very close to the edges is screened out an order of magnitude more weakly than that across the central region of the layers. Our discrete model suggests that the interlayer charge screening length in 1-8 layer thick graphene systems depends mostly on the overall gate/molecular doping level rather than on temperature, in particular at an induced charge density >5 × 1012 cm-2, and can reliably be determined to be larger than half the interlayer spacing but shorter than the bilayer thickness. Our model can be used for designing FLG-based devices, and offers a simple rule regarding the charge distribution in FLG: approximately 70%, 20%, 6% and 3% (99% overall) of the total induced charge density reside within the four innermost layers, implying that the gate-induced electric field is not definitely felt by >4th layer.

| S-EPMC5318858 | biostudies-literature

Temperature Dependence of G and D' Phonons in Monolayer to Few-Layer Graphene with Vacancies.

Project description:The defects into the hexagonal network of a sp2-hybridized carbon atom have been demonstrated to have a significant influence on intrinsic properties of graphene systems. In this paper, we presented a study of temperature-dependent Raman spectra of G peak and D' band at low temperatures from 78 to 318?K in defective monolayer to few-layer graphene induced by ion C+ bombardment under the determination of vacancy uniformity. Defects lead to the increase of the negative temperature coefficient of G peak, with a value almost identical to that of D' band. However, the variation of frequency and linewidth of G peak with layer number is contrary to D' band. It derives from the related electron-phonon interaction in G and D' phonon in the disorder-induced Raman scattering process. Our results are helpful to understand the mechanism of temperature-dependent phonons in graphene-based materials and provide valuable information on thermal properties of defects for the application of graphene-based devices.

| S-EPMC7527399 | biostudies-literature

Large room temperature spin-to-charge conversion signals in a few-layer graphene/Pt lateral heterostructure.

Project description:Electrical generation and detection of pure spin currents without the need of magnetic materials are key elements for the realization of full electrically controlled spintronic devices. In this framework, achieving a large spin-to-charge conversion signal is crucial, as considerable outputs are needed for plausible applications. Unfortunately, the values obtained so far have been rather low. Here we exploit the spin Hall effect by using Pt, a non-magnetic metal with strong spin-orbit coupling, to generate and detect pure spin currents in a few-layer graphene channel. Furthermore, the outstanding properties of graphene, with long-distance spin transport and higher electrical resistivity than metals, allow us to achieve in our graphene/Pt lateral heterostructures the largest spin-to-charge output voltage at room temperature reported so far in the literature. Our approach opens up exciting opportunities towards the implementation of spin-orbit-based logic circuits and all electrical control of spin information without magnetic field.Spintronic devices with full electrical control rely on electrical generation and detection of spin currents in the absence of magnetic materials. Here, the authors use Pt, a non-magnetic metal, to generate and detect pure spin currents in a few-layer graphene channel, achieving a remarkable spin-to-charge voltage signal at room temperature.

| S-EPMC5610249 | biostudies-literature

Designed nitrogen doping of few-layer graphene functionalized by selective oxygenic groups.

Project description:Few-layer nitrogen doped graphene was synthesized originating from graphene oxide functionalized by selective oxygenic functional groups (hydroxyl, carbonyl, carboxyl etc.) under hydrothermal conditions, respectively. Transmission electron microscopy (TEM) and atomic force microscopy (AFM) observation evidenced few-layer feature of the graphene oxide. X-ray diffraction (XRD) pattern confirmed phase structure of the graphene oxide and reduced graphene oxide. Nitrogen doping content and bonding configuration of the graphene was determined by X-ray photoelectron spectroscopy (XPS), which indicated that different oxygenic functional groups were evidently different in affecting the nitrogen doping process. Compared with other oxygenic groups, carboxyl group played a crucial role in the initial stage of nitrogen doping while hydroxyls exhibited more evident contribution to the doping process in the late stage of the reaction. Formation of graphitic-like nitrogen species was controlled by a synergistic effect of the involved oxygenic groups (e.g., -COOH, -OH, C-O-C, etc.). The doping mechanism of nitrogen in the graphene was scrutinized. The research in this work may not only contribute to the fundamental understandings of nitrogen doping within graphene but promote the development of producing novel graphene-based devices with designed surface functionalization.

| S-EPMC4266512 | biostudies-literature

Electric double-layer capacitance between an ionic liquid and few-layer graphene.

Project description:Ionic-liquid gates have a high carrier density due to their atomically thin electric double layer (EDL) and extremely large geometrical capacitance Cg. However, a high carrier density in graphene has not been achieved even with ionic-liquid gates because the EDL capacitance CEDL between the ionic liquid and graphene involves the series connection of Cg and the quantum capacitance Cq, which is proportional to the density of states. We investigated the variables that determine CEDL at the molecular level by varying the number of graphene layers n and thereby optimising Cq. The CEDL value is governed by Cq at n < 4, and by Cg at n > 4. This transition with n indicates a composite nature for CEDL. Our finding clarifies a universal principle that determines capacitance on a microscopic scale, and provides nanotechnological perspectives on charge accumulation and energy storage using an ultimately thin capacitor.

| S-EPMC3615339 | biostudies-other

Few-Layer Graphene Sheet-Passivated Porous Silicon Toward Excellent Electrochemical Double-Layer Supercapacitor Electrode.

Project description:Few-layer graphene sheet-passivated porous silicon (PSi) as an outstanding electrochemical double-layer supercapacitor electrode was demonstrated. The PSi matrix was formed by electrochemical etching of a doped silicon wafer and was further surface-passivated with few-layer graphene sheets by a Ni-assisted chemical vapor deposition process where a wide range of porous PSi structures, including mesoporous, macroporous, and hybrid porous structures were created during the graphene growth as temperature increases. The microstructural and graphene-passivation effects on the capacitive performance of the PSi were investigated in detail. The hybrid porous PSi electrode, optimized in terms of capacitive performances, achieves a high areal capacitance of 6.21 mF/cm2 at an ultra-high scan rate of 1000 mV/s and an unusual progressing cyclic stability of 131% at 10,000 cycles. Besides mesopores and macropores, micropores were introduced onto the surfaces of the passivating few-layer graphene sheets with a KOH activation process to further increase the functioning surface area of the hierarchical porous PSi electrode, leading to a boost in the areal capacitance by 31.4% up to 8.16 mF/cm2. The present designed hierarchical porous PSi-based supercapacitor proves to be a robust energy storage device for microelectronic applications that require stable high rate capability.

| S-EPMC6097977 | biostudies-literature

Spectroscopic characterization of charge carrier anisotropic motion in twisted few-layer graphene.

Project description:Graphene, a layer of carbon atoms in a honeycomb lattice, captures enormous interest as probably the most promising component of future electronics thanks to its mechanical robustness, flexibility, and unique charge carrier quasiparticles propagating like massless high energy Dirac fermions. If several graphene layers form a stack, the interaction between them is, on the one hand, weak, allowing realization of various registries between the layers and, on the other hand, strong enough for a wide range tuning of the electronic properties. Here we grow few layer graphene with various number of layers and twist configurations and address the electronic properties of individual atomic layers in single microscopic domains using angle-resolved photoelectron spectromicroscopy. The dependence of the interlayer coupling on the twist angle is analyzed and, in the domains with tri-layers and more, if different rotations are present, the electrons in weaker coupled adjacent layers are shown to have different properties manifested by coexisting van Hove singularities, moiré superlattices with corresponding superlattice Dirac points, and charge carrier group velocity renormalizations. Moreover, pronounced anisotropy in the charge carrier motion, opening a possibility to transform strongly coupled graphene bilayers into quasi one-dimensional conductors, is observed.

| S-EPMC4637862 | biostudies-other

Unforeseen high temperature and humidity stability of FeCl3 intercalated few layer graphene.

Project description:We present the first systematic study of the stability of the structure and electrical properties of FeCl3 intercalated few-layer graphene to high levels of humidity and high temperature. Complementary experimental techniques such as electrical transport, high resolution transmission electron microscopy and Raman spectroscopy conclusively demonstrate the unforseen stability of this transparent conductor to a relative humidity up to 100% at room temperature for 25 days, to a temperature up to 150°C in atmosphere and to a temperature as high as 620°C in vacuum, that is more than twice higher than the temperature at which the intercalation is conducted. The stability of FeCl3 intercalated few-layer graphene together with its unique values of low square resistance and high optical transparency, makes this material an attractive transparent conductor in future flexible electronic applications.

| S-EPMC4286778 | biostudies-literature

Temperature dependence of Coulomb oscillations in a few-layer two-dimensional WS2 quantum dot.

Project description:Standard semiconductor fabrication techniques are used to fabricate a quantum dot (QD) made of WS2, where Coulomb oscillations were found. The full-width-at-half-maximum of the Coulomb peaks increases linearly with temperature while the height of the peaks remains almost independent of temperature, which is consistent with standard semiconductor QD theory. Unlike graphene etched QDs, where Coulomb peaks belonging to the same QD can have different temperature dependences, these results indicate the absence of the disordered confining potential. This difference in the potential-forming mechanism between graphene etched QDs and WS2 QDs may be the reason for the larger potential fluctuation found in graphene QDs.

| S-EPMC4633606 | biostudies-literature

Decoupling Effects of Electrostatic Gating on Electronic Transport and Interfacial Charge-Transfer Kinetics at Few-Layer Molybdenum Disulfide.

Project description:The electronic properties of electrode materials play a crucial role in defining their electrochemical behavior in energy conversion and storage devices. The assembly of van der Waals heterostructures and fabrication into mesoscopic devices enable the dependence of an electrochemical response on electronic properties to be systematically interrogated. Here, we evaluate the effect of charge carrier concentration on heterogeneous electron transfer at few-layer MoS2 electrodes by combining spatially resolved electrochemical measurements with field-effect electrostatic manipulation of band alignment. Steady-state cyclic voltammograms and finite-element simulations reveal a strong modulation of the measured electrochemical response for outer-sphere charge transfer at the electrostatic gate voltage. In addition, spatially resolved voltammetric responses, obtained at a series of locations at the surface of few-layer MoS2, reveal the governing role of in-plane charge transport on the electrochemical behavior of 2D electrodes, especially under conditions of low carrier densities.

| S-EPMC10288603 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data