New horizon for high performance Mg-based biomaterial with uniform degradation behavior: Formation of stacking faults.

ABSTRACT: Designing the new microstructure is an effective way to accelerate the biomedical application of magnesium (Mg) alloys. In this study, a novel Mg-8Er-1Zn alloy with profuse nano-spaced basal plane stacking faults (SFs) was prepared by combined processes of direct-chill semi-continuous casting, heat-treatment and hot-extrusion. The formation of SFs made the alloy possess outstanding comprehensive performance as the biodegradable implant material. The ultimate tensile strength (UTS: 318 MPa), tensile yield strength (TYS: 207 MPa) and elongation (21%) of the alloy with SFs were superior to those of most reported degradable Mg-based alloys. This new alloy showed acceptable biotoxicity and degradation rate (0.34 mm/year), and the latter could be further slowed down through optimizing the microstructure. Most amazing of all, the uniquely uniform in vitro/vivo corrosion behavior was obtained due to the formation of SFs. Accordingly we proposed an original corrosion mechanism for the novel Mg alloy with SFs. The present study opens a new horizon for developing new Mg-based biomaterials with highly desirable performances.

SUBMITTER: Zhang J

PROVIDER: S-EPMC4563571 | biostudies-other | 2015

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Degradation behavior of Mg-based biomaterials containing different long-period stacking ordered phases.

Project description:Long-period stacking ordered (LPSO) phases play an essential role in the development of magnesium alloys because they have a direct effect on mechanical and corrosion properties of the alloys. The LPSO structures are mostly divided to 18R and 14H. However, to date there are no consistent opinions about their degradation properties although both of them can improve mechanical properties. Herein we have successfully obtained two LPSO phases separately in the same Mg-Dy-Zn system and comparatively investigated the effect of different LPSO phases on degradation behavior in 0.9 wt.% NaCl solution. Our results demonstrate that a fine metastable 14H-LPSO phase in grain interior is more effective to improve corrosion resistance due to the presence of a homogeneous oxidation film and rapid film remediation ability. The outstanding corrosion resistant Mg-Dy-Zn based alloys with a metastable 14H-LPSO phase, coupled with low toxicity of alloying elements, are highly desirable in the design of novel Mg-based biomaterials, opening up a new avenue in the area of bio-Mg.

| S-EPMC3885886 | biostudies-other

Stacking faults and superstructures in a layered brownmillerite.

Project description:Single crystals of Ca(4)Fe(2)Mn(0.5)Ti(0.5)O(9) have been synthesized using a flux method. The structural characterization using single-crystal X-ray diffraction revealed the space group Amma and unit-cell dimensions of a = 5.3510 (6), b = 26.669 (3), c = 5.4914 (6) Å. The structure is isotypic with Sr(3)NdFe(3)O(9) [Barrier et al. (2005). Chem. Mater. 17, 6619-6623] and exhibits separated brownmillerite-type layers. One-dimensional diffuse scattering shows that the unit cell is doubled along c by alternating the intra-layer order of tetrahedral chains, causing stacking faults along the b direction. A computer simulation was performed, proving that the observed intensity variations along the diffuse scattering rods originates from two different local structures depending on the configuration of the tetrahedral chains. Selected-area electron diffraction experiments exhibit well ordered regions characterized by satellite reflections corresponding to two different superstructures. Both superstructures can be described using the superspace group A2(1)/m(0βγ)0s, with γ = 0.5 and β ≃ 0.27 or β = 0.

| S-EPMC3222140 | biostudies-literature

Decoupling between Shockley partials and stacking faults strengthens multiprincipal element alloys.

Project description:Mechanical properties are fundamental to structural materials, where dislocations play a decisive role in describing their mechanical behavior. Although the high-yield stresses of multiprincipal element alloys (MPEAs) have received extensive attention in the last decade, the relation between their mechanistic origins remains elusive. Our multiscale study of density functional theory, atomistic simulations, and high-resolution microscopy shows that the excellent mechanical properties of MPEAs have diverse origins. The strengthening effects through Shockley partials and stacking faults can be decoupled in MPEAs, breaking the conventional wisdom that low stacking fault energies are coupled with wide partial dislocations. This study clarifies the mechanistic origins for the strengthening effects, laying the foundation for physics-informed predictive models for materials design.

| S-EPMC8713770 | biostudies-literature

Significant contribution of stacking faults to the strain hardening behavior of Cu-15%Al alloy with different grain sizes.

Project description:It is commonly accepted that twinning can induce an increase of strain-hardening rate during the tensile process of face-centered cubic (FCC) metals and alloys with low stacking fault energy (SFE). In this study, we explored the grain size effect on the strain-hardening behavior of a Cu-15 at.%Al alloy with low SFE. Instead of twinning, we detected a significant contribution of stacking faults (SFs) irrespective of the grain size even in the initial stage of tensile process. In contrast, twinning was more sensitive to the grain size, and the onset of deformation twins might be postponed to a higher strain with increasing the grain size. In the Cu-15 at.%Al alloy with a mean grain size of 47 μm, there was a stage where the strain-hardening rate increases with strain, and this was mainly induced by the SFs instead of twinning. Thus in parallel with the TWIP effect, we proposed that SFs also contribute significantly to the plasticity of FCC alloys with low SFE.

| S-EPMC4652229 | biostudies-other

Impact of Nitrogen on the Selective Closure of Stacking Faults in 3C-SiC.

Project description:Despite the promising properties, the problem of cubic silicon carbide (3C-SiC) heteroepitaxy on silicon has not yet been resolved and its use in microelectronics is limited by the presence of extensive defects. In this paper, we used microphotoluminescence (μ-PL), molten KOH etching, and high-resolution scanning transmission electron microscopy (HRSTEM) to investigate the effect of nitrogen doping on the distribution of stacking faults (SFs) and assess how increasing dosages of nitrogen during chemical vapor deposition (CVD) growth inhibits the development of SFs. An innovative angle-resolved SEM observation approach of molten KOH-etched samples resulted in detailed statistics on the density of the different types of defects as a function of the growth thickness of 3C-SiC free-standing samples with varied levels of nitrogen doping. Moreover, we proceeded to shed light on defects revealed by a diamond-shaped pit. In the past, they were conventionally associated with dislocations (Ds) due to what happens in 4H-SiC, where the formation of pits is always linked with the presence of Ds. In this work, the supposed Ds were observed at high magnification (by HRSTEM), demonstrating that principally they are partial dislocations (PDs) that delimit an SF, whose development and propagation are suppressed by the presence of nitrogen. These results were compared with VESTA simulations, which allowed to simulate the 3C-SiC lattice to design two 3C-lattice domains delimited by different types of SFs. In addition, through previous experimental evidence, a preferential impact of nitrogen on the closure of 6H-like SFs was observed as compared to 4H-like SFs.

| S-EPMC9354508 | biostudies-literature

Local Conduction in Mo xW1- xSe2: The Role of Stacking Faults, Defects, and Alloying.

Project description:Here, we report on the surface conductivity of WSe2 and Mo xW1- xSe2 (0 ? x ? 1) crystals investigated with conductive atomic force microscopy. We found that stacking faults, defects, and chemical heterogeneities form distinct two-dimensional and one-dimensional conduction paths on the transition metal dichalcogenide surface. In the case of WSe2, in addition to step edges, we find a significant amount of stacking faults (formed during the cleaving process) that strongly influence the surface conductivity. These regions are attributed to the alternation of the 2H and 3R polytypism. The stacking faults form regular 2D patterns by alternation of the underlying stacking order, with a periodicity that varies significantly between different regions and samples. In the case of Mo xW1- xSe2, its conductivity has a localized nature, which depends on the underlying chemical composition and the Mo/W ratio. Segregation to W-rich and Mo-rich regions during the growth process leads to nonuniform conduction paths on the surface of the alloy. We found a gradual change of the conductivity moving from one region to the other, reminiscent of lateral band bending. Our results demonstrate the use of C-AFM as a nanoscopic tool to probe the electrical properties of largely inhomogeneous samples and show the complicated nature of the surface conductivity of TMDC alloys.

| S-EPMC5909175 | biostudies-literature

Direct observation of multiple rotational stacking faults coexisting in freestanding bilayer MoS<sub>2</sub>.

Project description:Electronic properties of two-dimensional (2D) MoS2 semiconductors can be modulated by introducing specific defects. One important type of defect in 2D layered materials is known as rotational stacking fault (RSF), but the coexistence of multiple RSFs with different rotational angles was not directly observed in freestanding 2D MoS2 before. In this report, we demonstrate the coexistence of three RSFs with three different rotational angles in a freestanding bilayer MoS2 sheet as directly observed using an aberration-corrected transmission electron microscope (TEM). Our analyses show that these RSFs originate from cracks and dislocations within the bilayer MoS2. First-principles calculations indicate that RSFs with different rotational angles change the electronic structures of bilayer MoS2 and produce two new symmetries in their bandgaps and offset crystal momentums. Therefore, employing RSFs and their coexistence is a promising route in defect engineering of MoS2 to fabricate suitable devices for electronics, optoelectronics, and energy conversion.

| S-EPMC5559605 | biostudies-literature

High content imaging in the screening of biomaterial-induced MSC behavior

Project description:Upon contact with a biomaterial, cells and surrounding tissues respond in a manner dictated by the physicochemical and mechanical properties of the material. Traditionally, cellular responses are monitored using invasive analytical methods that report the expression of genes or proteins. These analytical methods involve assessing commonly used markers for a predefined readout, masking the actual situation induced in the cells. Hence, a broader expression profile of the cellular response should be envisioned, which technically limits up scaling to higher throughput systems. However, it is increasingly recognized that morphometric readouts, obtained non-invasively, are related to gene expression patterns. Here, we introduced distinct surface roughness to three PLA surfaces, by exposure to oxygen plasma of different duration times. The response of mesenchymal stromal cells was compared to smooth untreated PLA surfaces without the addition of differentiation agents. Morphological and genome wide expression profiles revealed underlying cellular changes which was hidden for the commonly used gene markers for osteo-, chondro- and adipogenesis. Using 3 morphometric parameters, obtained by high content imaging, we were able to build a classifier and discriminate between oxygen plasma-induced modified sheets and non-modified PLA sheets where evaluating classical candidates missed this effect. This approach shows the feasibility to use noninvasive morphometric data in high-throughput systems to screen biomaterial surfaces indicating the underlying genetic biomaterial-induced changes.

2018-11-10 | E-MTAB-7352 | biostudies-arrayexpress

Revealing the strengthening contribution of stacking faults, dislocations and grain boundaries in severely deformed LPBF AlSi10Mg alloy.

Project description:In this study, microstructural features direct metal laser melted (DMLM) aluminium-silicon-magnesium (AlSi10Mg) are investigated using advanced transmission electron microscopy (TEM) and high-resolution TEM (HRTEM). The focus is on post-processing by ECAP (Equal Channel Angular Pressing) and its effects on grain refinement, stacking fault formation and dislocation accumulation. In addition, the strength enhancing role of stacking faults is for the first time quantified. The results show that ECAP can increase the yield strength from 294 to 396 MPa, while the elongation increases from 2.4% to 6%. These results show that ECAP processing offers a new approach for producing AlSi10Mg products with improved strength and ductility.

| S-EPMC10533813 | biostudies-literature

Macrophage-Driven Biomaterial Degradation Depends on Scaffold Microarchitecture.

Project description:In situ tissue engineering is a technology in which non-cellular biomaterial scaffolds are implanted in order to induce local regeneration of replaced or damaged tissues. Degradable synthetic electrospun scaffolds are a versatile and promising class of biomaterials for various in situ tissue engineering applications, such as cardiovascular replacements. Functional in situ tissue regeneration depends on the balance between endogenous neo-tissue formation and scaffold degradation. Both these processes are driven by macrophages. Upon invasion into a scaffold, macrophages secrete reactive oxygen species (ROS) and hydrolytic enzymes, contributing to oxidative and enzymatic biomaterial degradation, respectively. This study aims to elucidate the effect of scaffold microarchitecture, i.e., μm-range fiber diameter and fiber alignment, on early macrophage-driven scaffold degradation. Electrospun poly-ε-caprolactone-bisurea (PCL-BU) scaffolds with either 2 or 6 μm (Ø) isotropic or anisotropic fibers were seeded with THP-1 derived human macrophages and cultured in vitro for 4 or 8 days. Our results revealed that macroph age-induced oxidative degradation in particular was dependent on scaffold microarchitecture, with the highest level of ROS-induced lipid peroxidation, NADPH oxidase gene expression and degradation in the 6 μm Ø anisotropic group. Whereas, biochemically polarized macrophages demonstrated a phenotype-specific degradative potential, the observed differences in macrophage degradative potential instigated by the scaffold microarchitecture could not be attributed to either distinct M1 or M2 polarization. This suggests that the scaffold microarchitecture uniquely affects macrophage-driven degradation. These findings emphasize the importance of considering the scaffold microarchitecture in the design of scaffolds for in situ tissue engineering applications and the tailoring of degradation kinetics thereof.

| S-EPMC6497794 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data