Dynamic response of polar nanoregions under an electric field in a paraelectric KTa0.61Nb0.39O3 single crystal near the para-ferroelectric phase boundary.

ABSTRACT: The dynamic response of polar nanoregions under an AC electric field was investigated by measuring the frequency dependence of the quadratic electro-optic (QEO) effect in a paraelectric KTa0.61Nb0.39O3 single crystal near the para-ferroelectric phase boundary (0 °C < T-Tc < 13 °C). The QEO coefficient R11 - R12 reached values as large as 5.96 × 10(-15) m(2)/V(2) at low frequency (500 Hz) and gradually decreased to a nearly stable value as the frequency increased to 300 kHz. Furthermore, a distortion of the QEO effect was observed at low frequency and gradually disappeared as R11 - R12 tended towards stability. The giant QEO effect in the KTa0.61Nb0.39O3 crystal was attributed to the dynamic rearrangement of polar nanoregions and its anomalous distortion can be explained by considering the asymmetric distribution of polar nanoregions.

SUBMITTER: Tian H

PROVIDER: S-EPMC4642581 | biostudies-other | 2015

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Electric field-induced crystallization of ferroelectric hafnium zirconium oxide.

Project description:Ferroelectricity in crystalline hafnium oxide thin films is strongly investigated for the application in non-volatile memories, sensors and other applications. Especially for back-end-of-line (BEoL) integration the decrease of crystallization temperature is of major importance. However, an alternative method for inducing ferroelectricity in amorphous or semi-crystalline hafnium zirconium oxide films is presented here, using the newly discovered effect of electric field-induced crystallization in hafnium oxide films. When applying this method, an outstanding remanent polarization value of 2P[Formula: see text] = 47 [Formula: see text]C/cm[Formula: see text] is achieved for a 5 nm thin film. Besides the influence of Zr content on the film crystallinity, the reliability of films crystallized with this effect is explored, highlighting the controlled crystallization, excellent endurance and long-term retention.

| S-EPMC8594776 | biostudies-literature

THz Electric Field-Induced Second Harmonic Generation in Inorganic Ferroelectric.

Project description:Second Harmonic Generation induced by the electric field of a strong nearly single-cycle terahertz pulse with the peak amplitude of 300 kV/cm is studied in a classical inorganic ferroelectric thin film of (Ba0.8Sr0.2)TiO3. The dependences of the SHG intensity on the polarization of the incoming light is revealed and interpreted in terms of electric polarization induced in the plane of the film. As the THz pulse pumps the medium in the range of phononic excitations, the induced polarization is explained as a dynamical change of the ferrolectric order parameter. It is estimated that under action of the THz pulse the ferroelectric order parameter acquires an in-plane component up to 6% of the net polarization.

| S-EPMC5429639 | biostudies-literature

Observation of Electric-Field-Induced Structural Dislocations in a Ferroelectric Oxide.

Project description:Dislocations are 1D topological defects with emergent electronic properties. Their low dimensionality and unique properties make them excellent candidates for innovative device concepts, ranging from dislocation-based neuromorphic memory to light emission from diodes. To date, dislocations are created in materials during synthesis via strain fields or flash sintering or retrospectively via deformation, for example, (nano)-indentation, limiting the technological possibilities. In this work, we demonstrate the creation of dislocations in the ferroelectric semiconductor Er(Mn,Ti)O3 with nanoscale spatial precision using electric fields. By combining high-resolution imaging techniques and density functional theory calculations, direct images of the dislocations are collected, and their impact on the local electric transport behavior is studied. Our approach enables local property control via dislocations without the need for external macroscopic strain fields, expanding the application opportunities into the realm of electric-field-driven phenomena.

| S-EPMC8155316 | biostudies-literature

Shock growth of ice crystal near equilibrium melting pressure under dynamic compression.

Project description:Crystal growth is governed by an interplay between macroscopic driving force and microscopic interface kinetics at the crystal-liquid interface. Unlike the local equilibrium growth condition, the interplay becomes blurred under local nonequilibrium, which raises many questions about the nature of diverse crystal growth and morphological transitions. Here, we systematically control the growth condition from local equilibrium to local nonequilibrium by using an advanced dynamic diamond anvil cell (dDAC) and generate anomalously fast growth of ice VI phase with a morphological transition from three- to two-dimension (3D to 2D), which is called a shock crystal growth. Unlike expected, the shock growth occurs from the edges of 3D crystal along the (112) crystal plane rather than its corners, which implies that the fast compression yields effectively large overpressure at the crystal-liquid interface, manifesting the local nonequilibrium condition. Molecular dynamics (MD) simulation reproduces the faster growth of the (112) plane than other planes upon applying large overpressure. Moreover, the MD study reveals that the 2D shock crystal growth originates from the similarity of the interface structure between water and the (112) crystal plane under the large overpressure. This study provides insight into crystal growth under dynamic compressions, which makes a bridge for the unknown behaviors of crystal growth between under static and dynamic pressure conditions.

| S-EPMC6500116 | biostudies-literature

Soliton walls paired by polar surface interactions in a ferroelectric nematic liquid crystal.

Project description:Surface interactions are responsible for many properties of condensed matter, ranging from crystal faceting to the kinetics of phase transitions. Usually, these interactions are polar along the normal to the interface and apolar within the interface. Here we demonstrate that polar in-plane surface interactions of a ferroelectric nematic NF produce polar monodomains in micron-thin planar cells and stripes of an alternating electric polarization, separated by [Formula: see text] domain walls, in thicker slabs. The surface polarity binds together pairs of these walls, yielding a total polarization rotation by [Formula: see text]. The polar contribution to the total surface anchoring strength is on the order of 10%. The domain walls involve splay, bend, and twist of the polarization. The structure suggests that the splay elastic constant is larger than the bend modulus. The [Formula: see text] pairs resemble domain walls in cosmology models with biased vacuums and ferromagnets in an external magnetic field.

| S-EPMC9262936 | biostudies-literature

Polar in-plane surface orientation of a ferroelectric nematic liquid crystal: Polar monodomains and twisted state electro-optics.

Project description:We show that surface interactions can vectorially structure the three-dimensional polarization field of a ferroelectric fluid. The contact between a ferroelectric nematic liquid crystal and a surface with in-plane polarity generates a preferred in-plane orientation of the polarization field at that interface. This is a route to the formation of fluid or glassy monodomains of high polarization without the need for electric field poling. For example, unidirectional buffing of polyimide films on planar surfaces to give quadrupolar in-plane anisotropy also induces macroscopic in-plane polar order at the surfaces, enabling the formation of a variety of azimuthal polar director structures in the cell interior, including uniform and twisted states. In a π-twist cell, obtained with antiparallel, unidirectional buffing on opposing surfaces, we demonstrate three distinct modes of ferroelectric nematic electro-optic response: intrinsic, viscosity-limited, field-induced molecular reorientation; field-induced motion of domain walls separating twisted states of opposite chirality; and propagation of polarization reorientation solitons from the cell plates to the cell center upon field reversal. Chirally doped ferroelectric nematics in antiparallel-rubbed cells produce Grandjean textures of helical twist that can be unwound via field-induced polar surface reorientation transitions. Fields required are in the 3-V/mm range, indicating an in-plane polar anchoring energy of wP ∼3 × 10-3 J/m2.

| S-EPMC8179187 | biostudies-literature

Three-dimensional imaging of vortex structure in a ferroelectric nanoparticle driven by an electric field.

Project description:Topological defects of spontaneous polarization are extensively studied as templates for unique physical phenomena and in the design of reconfigurable electronic devices. Experimental investigations of the complex topologies of polarization have been limited to surface phenomena, which has restricted the probing of the dynamic volumetric domain morphology in operando. Here, we utilize Bragg coherent diffractive imaging of a single BaTiO3 nanoparticle in a composite polymer/ferroelectric capacitor to study the behavior of a three-dimensional vortex formed due to competing interactions involving ferroelectric domains. Our investigation of the structural phase transitions under the influence of an external electric field shows a mobile vortex core exhibiting a reversible hysteretic transformation path. We also study the toroidal moment of the vortex under the action of the field. Our results open avenues for the study of the structure and evolution of polar vortices and other topological structures in operando in functional materials under cross field configurations.Imaging of topological states of matter such as vortex configurations has generally been limited to 2D surface effects. Here Karpov et al. study the volumetric structure and dynamics of a vortex core mediated by electric-field induced structural phase transition in a ferroelectric BaTiO3 nanoparticle.

| S-EPMC5561144 | biostudies-literature

Relaxor-Ferroelectric Films for Dielectric Tunable Applications: Effect of Film Thickness and Applied Electric Field.

Project description:The dielectric properties, tunability and figure-of-merit (FOM) of relaxor Pb0.9La0.1(Zr0.52Ti0.48)O3 (PLZT) films have been investigated. Dielectric measurements indicated that the dielectric constant (at zero-bias field), tunability and FOM are enhanced as the film thickness increases, which are mainly attributed to the presence of an interfacial layer near the film-electrode interface. Experimental results illustrated that a slight reduction is observed in both dielectric constant and tunability (-2%) in a wide-frequency range (10 kHz-1 MHz); meanwhile, the FOM value decreases significantly (-17%) with increasing frequency, arising from the higher dielectric loss value. The 1000-nm PLZT film shows the largest tunability of 94.6% at a maximum electric-field of 1450 kV/cm, while the highest FOM factor is 37.6 at 1000 kV/cm, due to the combination of medium tunability (88.7%) and low dielectric loss (0.0236). All these excellent results indicated that the relaxor PLZT films are promising candidates for specific applications in microwave devices.

| S-EPMC8585368 | biostudies-literature

Polarity-dependent nonlinear optics of nanowires under electric field.

Project description:Polar materials display a series of interesting and widely exploited properties owing to the inherent coupling between their fixed electric dipole and any action that involves a change in their charge distribution. Among these properties are piezoelectricity, ferroelectricity, pyroelectricity, and the bulk photovoltaic effect. Here we report the observation of a related property in this series, where an external electric field applied parallel or anti-parallel to the polar axis of a crystal leads to an increase or decrease in its second-order nonlinear optical response, respectively. This property of electric-field-modulated second-harmonic generation (EFM-SHG) is observed here in nanowires of the polar crystal ZnO, and is exploited as an analytical tool to directly determine by optical means the absolute direction of their polarity, which in turn provides important information about their epitaxy and growth mechanism. EFM-SHG may be observed in any type of polar nanostructures and used to map the absolute polarity of materials at the nanoscale.

| S-EPMC8172856 | biostudies-literature

Ferroelectric Metal in Tetragonal BiCoO3/BiFeO3 Bilayers and Its Electric Field Effect.

Project description:By first-principles calculations we investigate the electronic structure of tetragonal BiCoO3/BiFeO3 bilayers with different terminations. The multiferroic insulator BiCoO3 and BiFeO3 transform into metal in all of three models. Particularly, energetically favored model CoO2-BiO exhibits ferroelectric metallic properties, and external electric field enhances the ferroelectric displacements significantly. The metallic character is mainly associated to eg electrons, while t2g electrons are responsible for ferroelectric properties. Moreover, the strong hybridization between eg and O p electrons around Fermi level provides conditions to the coexistence of ferroelectric and metallic properties. These special behaviors of electrons are influenced by the interfacial electronic reconstruction with formed Bi-O electrovalent bond, which breaks OA-Fe/Co-OB coupling partially. Besides, the external electric field reverses spin polarization of Fe/Co ions efficiently, even reaching 100%.

| S-EPMC4738338 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data