Low-temperature direct copper-to-copper bonding enabled by creep on (111) surfaces of nanotwinned Cu.

ABSTRACT: Direct Cu-to-Cu bonding was achieved at temperatures of 150-250 °C using a compressive stress of 100 psi (0.69 MPa) held for 10-60 min at 10(-3) torr. The key controlling parameter for direct bonding is rapid surface diffusion on (111) surface of Cu. Instead of using (111) oriented single crystal of Cu, oriented (111) texture of extremely high degree, exceeding 90%, was fabricated using the oriented nano-twin Cu. The bonded interface between two (111) surfaces forms a twist-type grain boundary. If the grain boundary has a low angle, it has a hexagonal network of screw dislocations. Such network image was obtained by plan-view transmission electron microscopy. A simple kinetic model of surface creep is presented; and the calculated and measured time of bonding is in reasonable agreement.

SUBMITTER: Liu CM

PROVIDER: S-EPMC4649891 | biostudies-other | 2015

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Comparison of oxidation in uni-directionally and randomly oriented Cu films for low temperature Cu-to-Cu direct bonding.

Project description:Cu-to-Cu direct bonding has attracted attention because it has been implemented in CMOS image sensors. Prior to the bonding, the oxides on the Cu surface needs to be removed, yet the surface may oxidize right after cleaning. Thus, oxidation is an inherent issue in the application of Cu direct bonding. Our previous study reported that Cu direct bonding can be achieved below 250?°C by using (111)-oriented nanotwinned Cu because it has the fastest surface diffusivity. However, the oxidation behavior of the nanotwinned Cu is unclear. Here, we examined the oxidation behavior of highly (111) and (200) oriented, and randomly-oriented Cu films at temperatures ranging from 120 to 250?°C. Transmission electron microscopy was used to measure the oxide thickness. The results show that the oxidation rate of (111)-oriented nanotwinned Cu has the lowest oxidation rate among them. Together, it is unique to possess the combination of the fastest surface diffusivity and the lowest oxidation rate.

| S-EPMC6045573 | biostudies-literature

An Electron-Rich Cyclic (Alkyl)(Amino)Carbene on Au(111), Ag(111), and Cu(111) Surfaces.

Project description:The structural properties and binding motif of a strongly ?-electron-donating N-heterocyclic carbene have been investigated on different transition-metal surfaces. The examined cyclic (alkyl)(amino)carbene (CAAC) was found to be mobile on surfaces, and molecular islands with short-range order could be found at high coverage. A combination of scanning tunneling microscopy (STM), X-ray photoelectron spectroscopy (XPS), and density functional theory (DFT) calculations highlights how CAACs bind to the surface, which is of tremendous importance to gain an understanding of heterogeneous catalysts bearing CAACs as ligands.

| S-EPMC7496406 | biostudies-literature

Effect of grain orientations of Cu seed layers on the growth of <111>-oriented nanotwinned Cu.

Project description:We investigate the growth of Cu films on two different Cu seed layers: one with regular <111>-oriented grains and the other with very strong <111>-preferred orientation. It is found that densely-packed nanotwinned Cu (nt-Cu) can be grown by pulsed electroplating on the strong <111>-oriented Cu seed layer without a randomly-oriented transition layer between the nt-Cu and the Cu seed layer. The electroplated nt-Cu grow almost epitaxially on the seed layer and formed <111>-oriented columnar structures. However, with the regular <111>-oriented Cu seed, there is a randomly-oriented transition layer between the nt-Cu and the regular <111>-oriented Cu seed. The results indicate that the seed layer plays a crucial role on the regularity of <111>-oriented nanotwinned Cu.

| S-EPMC4137260 | biostudies-other

Multi-scale Simulation of Equilibrium Step Fluctuations on Cu(111) Surfaces.

Project description:Understanding the nature of active sites is a non-trivial task, especially when the catalyst is sensitively affected by chemical reactions and environmental conditions. The challenge lies on capturing explicitly the dynamics of catalyst evolution during reactions. Despite the complexity of catalyst reconstruction, we can untangle them into several elementary processes, of which surface diffusion is of prime importance. By applying density functional theory-kinetic Monte Carlo (DFT-KMC) simulation employed with cluster expansion (CE), we investigated the microscopic mechanism of surface diffusion of Cu with defects such as steps and kinks. Based on the result, the energetics obtained from CE have shown good agreement with DFT calculations. Various diffusion events during the step fluctuations are discussed as well. Aside from the adatom attachment, the diffusion along the step edge is found to be the dominant mass transport mechanism, indicated by the lowest activation energy. We also calculated time correlation functions at 300, 400, and 500 K. However, the time exponent in the correlation function does not strictly follow the power law behavior due to the limited step length, which inhibits variation in the kink density.

| S-EPMC7931195 | biostudies-literature

Comparing graphene growth on Cu(111) versus oxidized Cu(111).

Project description:The epitaxial growth of graphene on catalytically active metallic surfaces via chemical vapor deposition (CVD) is known to be one of the most reliable routes toward high-quality large-area graphene. This CVD-grown graphene is generally coupled to its metallic support resulting in a modification of its intrinsic properties. Growth on oxides is a promising alternative that might lead to a decoupled graphene layer. Here, we compare graphene on a pure metallic to graphene on an oxidized copper surface in both cases grown by a single step CVD process under similar conditions. Remarkably, the growth on copper oxide, a high-k dielectric material, preserves the intrinsic properties of graphene; it is not doped and a linear dispersion is observed close to the Fermi energy. Density functional theory calculations give additional insight into the reaction processes and help explaining the catalytic activity of the copper oxide surface.

| S-EPMC4411207 | biostudies-literature

Role of Hydrogen Bonding in the Formation of Adenine Chains on Cu(110) Surfaces.

Project description:Understanding the adsorption properties of DNA bases on metal surfaces is fundamental for the rational control of surface functionalization leading to the realisation of biocompatible devices for biosensing applications, such as monitoring of particular parameters within bio-organic environments and drug delivery. In this study, the effects of deposition rate and substrate temperature on the adsorption behavior of adenine on Cu(110) surfaces have been investigated using scanning tunneling microscopy (STM) and density functional theory (DFT) modeling, with a focus on the characterization of the morphology of the adsorbed layers. STM results revealed the formation of one-dimensional linear chains and ladder-like chains parallel to the [110] direction, when dosing at a low deposition rate at room temperature, followed by annealing to 490 K. Two mirror related, well-ordered chiral domains oriented at ±55° with respect to the [110] direction are formed upon deposition on a substrate kept at 490 K. The molecular structures observed via STM are rationalized and qualitatively described on the basis of the DFT modeling. The observation of a variety of ad-layer structures influenced by deposition rate and substrate temperature indicates that dynamic processes and hydrogen bonding play an important role in the self-assembly of adenine on the Cu(110) surface.

| S-EPMC5457020 | biostudies-literature

1,3,5-Benzenetribenzoic Acid on Cu(111) and Graphene/Cu(111): A Comparative STM Study.

Project description:The self-assembly of 1,3,5-benzenetribenzoic acid (BTB) molecules on both Cu(111) and epitaxial graphene grown on Cu(111) were studied by scanning tunneling microscopy (STM) and low-energy electron diffraction (LEED) under ultrahigh vacuum conditions. On Cu(111), the BTB molecules were found to mainly arrange in close-packed structures through H-bonding between the (partially) deprotonated carboxylic acid groups. In addition, porous structures formed by intact BTB molecules-and also based on H-bonding-were observed. On graphene grown on Cu(111) the BTB molecules mainly form porous structures accompanied by small patches of disordered close-packed structures. Upon annealing, BTB adsorbed on Cu(111) is fully deprotonated and arranges in the close-packed structure while in contrast on graphene/Cu(111) the porous network is exclusively formed. This shows that the molecular self-assembly behavior is highly dependent on the first substrate layer: one graphene layer is sufficient to considerably alter the interplay of molecule substrate and intermolecular interactions in favor of the latter interactions.

| S-EPMC5002934 | biostudies-literature

Plasma-assisted oxidation of Cu(100) and Cu(111).

Project description:Oxidized copper surfaces have attracted significant attention in recent years due to their unique catalytic properties, including their enhanced hydrocarbon selectivity during the electrochemical reduction of CO2. Although oxygen plasma has been used to create highly active copper oxide electrodes for CO2RR, how such treatment alters the copper surface is still poorly understood. Here, we study the oxidation of Cu(100) and Cu(111) surfaces by sequential exposure to a low-pressure oxygen plasma at room temperature. We used scanning tunnelling microscopy (STM), low energy electron microscopy (LEEM), X-ray photoelectron spectroscopy (XPS), near edge X-ray absorption fine structure spectroscopy (NEXAFS) and low energy electron diffraction (LEED) for the comprehensive characterization of the resulting oxide films. O2-plasma exposure initially induces the growth of 3-dimensional oxide islands surrounded by an O-covered Cu surface. With ongoing plasma exposure, the islands coalesce and form a closed oxide film. Utilizing spectroscopy, we traced the evolution of metallic Cu, Cu2O and CuO species upon oxygen plasma exposure and found a dependence of the surface structure and chemical state on the substrate's orientation. On Cu(100) the oxide islands grow with a lower rate than on the (111) surface. Furthermore, while on Cu(100) only Cu2O is formed during the initial growth phase, both Cu2O and CuO species are simultaneously generated on Cu(111). Finally, prolonged oxygen plasma exposure results in a sandwiched film structure with CuO at the surface and Cu2O at the interface to the metallic support. A stable CuO(111) surface orientation is identified in both cases, aligned to the Cu(111) support, but with two coexisting rotational domains on Cu(100). These findings illustrate the possibility of tailoring the oxidation state, structure and morphology of metallic surfaces for a wide range of applications through oxygen plasma treatments.

| S-EPMC8565394 | biostudies-literature

Revisit of XPS Studies of Supersonic O<sub>2</sub> Molecular Adsorption on Cu(111): Copper Oxides.

Project description:We report the X-ray photoemission spectroscopy (XPS) characterization of the bulk Cu2O(111) surface and "8" and "29" oxide structures on Cu(111) prepared using a 0.5 eV O2 supersonic molecular beam. We propose a new structural model for the "8" oxide structure and also confirm the previously proposed model for the "29" oxide structure on Cu(111), based on the O 1s XPS spectra. The detection angle dependence of the O 1s spectra supports that the nanopyramidal model is more preferable for the (√3 × √3)R30° Cu2O(111). We also report electronic excitations that O 1s electrons suffer.

| S-EPMC8515815 | biostudies-literature

Ambiphilic Al-Cu Bonding.

Project description:Copper-alumanyl complexes, [LCu-Al(SiNDipp )], where L=carbene=NHCiPr (N,N'-diisopropyl-4,5-dimethyl-2-ylidene) and Me2 CAAC (1-(2,6-diisopropylphenyl)-3,3,5,5-tetramethyl-pyrrolidin-2-ylidene) and featuring unsupported Al-Cu bonds, have been prepared. Divergent reactivity observed with carbodiimides and CO2 implies an ambiphilicity in the Cu-Al interaction that is dependent on the identity of the carbene co-ligand.

| S-EPMC8252794 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data