Critical dependence of magnetostructural coupling and magnetocaloric effect on particle size in Mn-Fe-Ni-Ge compounds.

ABSTRACT: Magnetostructural coupling, which is the coincidence of crystallographic and magnetic transition, has obtained intense attention for its abundant magnetoresponse effects and promising technological applications, such as solid-state refrigeration, magnetic actuators and sensors. The hexagonal Ni2In-type compounds have attracted much attraction due to the strong magnetostructural coupling and the resulted giant negative thermal expansion and magnetocaloric effect. However, the as-prepared samples are quite brittle and naturally collapse into powders. Here, we report the effect of particle size on the magnetostructural coupling and magnetocaloric effect in the Ni2In-type Mn-Fe-Ni-Ge compound, which undergoes a large lattice change across the transformation from paramagnetic austenite to ferromagnetic martensite. The disappearance of martensitic transformation in a large amount of austenitic phase with reducing particle size, to our best knowledge, has not been reported up to now. The ratio can be as high as 40.6% when the MnNi0.8Fe0.2Ge bulk was broken into particles in the size range of 5~15 μm. Meanwhile, the remained magnetostructural transition gets wider and the magnetic hysteresis becomes smaller. As a result, the entropy change drops, but the effective cooling power RCeffe increases and attains to the maximum at particles in the range of 20~40 μm. These observations provide constructive information and highly benefit practical applications for this class of novel magnetoresponse materials.

SUBMITTER: Wu R

PROVIDER: S-EPMC4756685 | biostudies-other | 2016 Feb

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Tunable Magnetocaloric Effect in Ni-Mn-Ga Microwires.

Project description:Magnetic refrigeration is of great interest due to its high energy efficiency, environmental friendliness and low cost. However, undesired hysteresis losses, concentrated working temperature interval (WTI) and poor mechanical stability are vital drawbacks that hinder its practical application. Off-stoichiometric Ni-Mn-Ga Heusler alloys are capable of giant magnetocaloric effect (MCE) and tunable transformation temperatures. Here, by creating Ni-Mn-Ga microwires with diameter of 35-80 ?m using a melt-extraction technique, negligible hysteresis and relatively good mechanical stability are found due to the high specific surface area (SSA) that reduces incompatibility between neighboring grains. The high SSA also favors the element evaporation at high temperatures so that the transformation temperatures can be feasibly adjusted. Tunable magnetocaloric effect owing to different magneto-structural coupling states is realized by (i) composition design and subsequent tuning, which adjusts the temperature difference between the martensite transformation (MT) and the magnetic transition, and (ii) creation of gradient composition distribution state, which manipulates the MT range. Magnetic entropy change ?Sm ~-18.5?J?kg-1 K-1 with relatively concentrated WTI and WTI up to ~60?K with net refrigeration capacity ~240?J?kg-1 at 50?kOe are demonstrated in the present Ni-Mn-Ga microwires. This criterion is also applicable for other small-sized materials.

| S-EPMC6224590 | biostudies-literature

Magnetostructural transformation and magnetocaloric effect of Sn-bonded Mn0.66Fe0.34Ni0.66Fe0.34Si0.66Ge0.34 composite.

Project description:Magnetostructural coupling in MnMX (M = Co or Ni, X = Si or Ge) system attracts considerable attention for the accompanied multi-magnetoresponsive effects. However, due to the large stress generated from the structural transformation, the alloys become shattered or powder-like, hindering the further investigation and their applications. The possible solution is to embed the MnMX powders into metal matrix. In this paper, we choose Mn0.66Fe0.34Ni0.66Fe0.34Si0.66Ge0.34 as a representative of MnMX alloy and produce Mn0.66Fe0.34Ni0.66Fe0.34Si0.66Ge0.34/Sn composite bulk by hot pressing. The magnetostructural-coupled composites exhibit an improved rate of the transformation temperature shift by magnetic field and broadened operating temperature range. Additionally, we also propose a simple formula based on the entropy-temperature diagram to calculate the isothermal entropy change, which is consistent with the results obtained by the Maxwell relation.

| S-EPMC5758529 | biostudies-literature

New Heusler compounds in Ni-Mn-In and Ni-Mn-Sn alloys.

Project description:Rapidly quenched ternary Ni-Mn-T (T?=?In, Sn) alloys exhibit features associated with magnetic skyrmions, so that XRD, TEM, EDS, SAED and HREM investigations were carried out for structural characterization on the two alloy systems. In this paper, we report a new type of Mn-rich Heusler compound with a cubic unit cell, a?=?0.9150?nm in Ni-Mn-In and a?=?0.9051?nm in Ni-Mn-Sn, which coexist with a Ni-rich full-Heusler compound with defects, a?=?0.6094?nm in Ni-Mn-In and a?=?0.6034?nm in Ni-Mn-Sn. A further analysis of the experimental results reveals a close structural relationship between these two compounds.

| S-EPMC6533245 | biostudies-literature

Tuneable Giant Magnetocaloric Effect in (Mn,Fe)₂(P,Si) Materials by Co-B and Ni-B Co-Doping.

Project description:The influence of Co (Ni) and B co-doping on the structural, magnetic and magnetocaloric properties of (Mn,Fe) 2 (P,Si) compounds is investigated by X-ray diffraction (XRD), differential scanning calorimetry, magnetic and direct temperature change measurements. It is found that Co (Ni) and B co-doping is an effective approach to tune both the Curie temperature and the thermal hysteresis of (Mn,Fe) 2 (P,Si) materials without losing either the giant magnetocaloric effect or the positive effect of the B substitution on the mechanical stability. An increase in B concentration leads to a rapid decrease in thermal hysteresis, while an increase in the Co or Ni concentration hardly changes the thermal hysteresis of the (Mn,Fe) 2 (P,Si) compounds. However, the Curie temperature decreases slowly as a function of the Co or Ni content, while it increases dramatically for increasing B concentration. Hence, the co-substitution of Fe and P by Co (Ni) and B, respectively, offers a new control parameter to adjust the Curie temperature and reduce the thermal hysteresis of the (Mn,Fe) 2 (P,Si) materials.

| S-EPMC5344570 | biostudies-other

Enhanced magnetocaloric effect in Ni-Mn-Sn-Co alloys with two successive magnetostructural transformations.

Project description:High magnetocaloric refrigeration performance requires large magnetic entropy change ΔS M and broad working temperature span ΔT FWHM . A fourth element doping of Co in ternary Ni-Mn-Sn alloy may significantly enhance the saturation magnetization of the alloy and thus enhance the ΔS M . Here, the effects of Co-doping on the martensite transformation, magnetic properties and magnetocaloric effects (MCE) of quaternary Ni47-xMn43Sn10Cox (x = 0, 6, 11) alloys were investigated. The martensite transformation temperatures decrease while austenite Curie point increases with Co content increasing to x = 6 and 11, thus broadening the temperature window for a high magnetization austenite (13.5, 91.7 and 109.1 A·m2/kg for x = 0, 6 and 11, respectively). Two successive magnetostructural transformations (A → 10 M and A → 10 M + 6 M) occur in the alloy x = 6, which are responsible for the giant magnetic entropy change ΔS M = 29.5 J/kg·K, wide working temperature span ΔT FWHM = 14 K and large effective refrigeration capacity RC eff = 232 J/kg under a magnetic field of 5.0 T. These results suggest that Ni40.6Mn43.3Sn10.0Co6.1 alloy may act as a potential solid-state magnetic refrigerant working at room temperature.

| S-EPMC5974186 | biostudies-literature

Reversible tuning of magnetocaloric Ni-Mn-Ga-Co films on ferroelectric PMN-PT substrates.

Project description:Tuning functional properties of thin caloric films by mechanical stress is currently of high interest. In particular, a controllable magnetisation or transition temperature is desired for improved usability in magnetocaloric devices. Here, we present results of epitaxial magnetocaloric Ni-Mn-Ga-Co thin films on ferroelectric Pb(Mg1/3Nb2/3)0.72Ti0.28O3 (PMN-PT) substrates. Utilizing X-ray diffraction measurements, we demonstrate that the strain induced in the substrate by application of an electric field can be transferred to the thin film, resulting in a change of the lattice parameters. We examined the consequences of this strain on the magnetic properties of the thin film by temperature- and electric field-dependent measurements. We did not observe a change of martensitic transformation temperature but a reversible change of magnetisation within the austenitic state, which we attribute to the intrinsic magnetic instability of this metamagnetic Heusler alloy. We demonstrate an electric field-controlled entropy change of about 31 % of the magnetocaloric effect - without any hysteresis.

| S-EPMC5663903 | biostudies-literature

Role of disorder when upscaling magnetocaloric Ni-Co-Mn-Al Heusler alloys from thin films to ribbons.

Project description:Research in functional magnetic materials often employs thin films as model systems for finding new chemical compositions with promising properties. However, the scale-up of thin films towards bulk-like structures is challenging, since the material synthesis conditions are entirely different for thin films and e.g. rapid quenching methods. As one of the consequences, the type and degree of order in thin films and melt-spun ribbons are usually different, leading to different magnetic properties. In this work, using the example of magnetocaloric Ni-Co-Mn-Al melt-spun ribbons and thin films, we show that the excellent functional properties of the films can be reproduced also in ribbons, if an appropriate heat treatment is applied, that installs the right degree of order in the ribbons. We show that some chemical disorder is needed to get a pronounced and sharp martensitic transition. Increasing the order with annealing improves the magnetic properties only up to a point where selected types of disorder survive, which in turn compromise the magnetic properties. These findings allow us to understand the impact of the type and degree of disorder on the functional properties, paving the way for a faster transfer of combinatorial thin film research towards bulk-like materials for magnetic Heusler alloys.

| S-EPMC6002362 | biostudies-literature

Nonmonotonic particle-size-dependence of magnetoelectric coupling in strained nanosized particles of BiFeO3.

Project description:Using high resolution powder x-ray and neutron diffraction experiments, we determined the off-centered displacement of the ions within a unit cell and magnetoelectric coupling in nanoscale BiFeO3 (?20-200?nm). We found that both the off-centered displacement of the ions and magnetoelectric coupling exhibit nonmonotonic variation with particle size. They increase as the particle size reduces from bulk and reach maximum around 30?nm. With further decrease in particle size, they decrease precipitously. The magnetoelectric coupling is determined by the anomaly in off-centering of ions around the magnetic transition temperature (T N ). The ions, in fact, exhibit large anomalous displacement around the T N which is analyzed using group theoretical approach. It underlies the nonmonotonic particle-size-dependence of off-centre displacement of ions and magnetoelectric coupling. The nonmonotonic variation of magnetoelectric coupling with particle size is further verified by direct electrical measurement of remanent ferroelectric hysteresis loops at room temperature under zero and ?20?kOe magnetic field. Competition between enhanced lattice strain and compressive pressure appears to be causing the nonmonotonic particle-size-dependence of off-centre displacement while coupling between piezo and magnetostriction leads to nonmonotonicity in the variation of magnetoelectric coupling.

| S-EPMC5829220 | biostudies-literature

Ni nanoparticles on RGO as reusable heterogeneous catalyst: effect of Ni particle size and intermediate composite structures in C-S cross-coupling reaction.

Project description:The present work demonstrates the C-S cross-coupling reaction between aryl halides and thiols using nickel nanoparticles (Ni NPs) supported on reduced graphene oxide (Ni/RGO) as a heterogeneous catalyst. It is observed that the uniformly dispersed Ni NPs supported on RGO could exhibit excellent catalytic activity in C-S cross-coupling reactions and the catalytic application is generalized with diverse coupling partners. Although the electron-rich planar RGO surface helps in stabilizing the agglomeration-free Ni NPs, the catalytic process is found to occur involving Ni(II) species and the recovered catalyst containing both Ni(0)/Ni(II) species is equally efficient in recycle runs. A correlation of loading of Ni species, size of NPs and the intermediate Ni-related heterostructures formed during the catalytic process has been established for the first time, and found to be best in the C-S cross-coupling reaction for Ni(0) and Ni(II) NPs of the average sizes 11-12 nm and 4 nm, respectively.

| S-EPMC5588615 | biostudies-literature

Ge-Fe Carbonyl Cluster Compounds: Ionic Liquids-Based Synthesis, Structures, and Properties.

Project description:Nine Ge-Fe carbonyl cluster compounds are prepared via ionic liquids-based synthesis. This includes the novel compounds [EMIm][Fe(CO)3 I(GeI3 )], [EHIm][Fe(CO)3 I(GeI3 )], [BMIm][GeI2 {Fe(CO)4 }2 (μ-I)][AlCl4 ]2 , [GeI2 {Fe(CO)4 }2 (μ-I)][Fe(AlBr4 )3 ], [BMIm]2 [(FeI2 )0.75 {Fe(CO)2 I(GeI3 )2 }2 ], and [EHIm][Fe(CO)4 (GeI2 )2 Fe(CO)3 GeI3 ] as well as the previously reported compounds (Fe(CO)4 (GeI3 )2 , FeI4 {GeI3 Fe(CO)3 }2 , and Ge12 {Fe(CO)3 }8 (μ-I)4 (EMIm: 1-ethyl-3-methylimidazolium, EHIm: 1-ethylimidazolium, BMIm: 1-butyl-3-methylimidazolium). With this series of compounds, a comparison of synthesis conditions and structural features is possible and, for instance, allows correlating the composition and structure of the respective Ge-Fe carbonyl cluster compounds with the type and acidity of the ionic liquid. With [EMIm][{GeI3 }2 Fe(CO)3 I], moreover, we can exemplarily show the thermal decomposition as a single-source precursor in the ionic liquid, resulting in bimetallic Ge-Fe nanoparticles with small size and narrow size distribution (7.0±1.4 nm).

| S-EPMC7874258 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data