Enhanced Performance of PbS-quantum-dot-sensitized Solar Cells via Optimizing Precursor Solution and Electrolytes.

ABSTRACT: This work reports a PbS-quantum-dot-sensitized solar cell (QDSC) with power conversion efficiency (PCE) of 4%. PbS quantum dots (QDs) were grown on mesoporous TiO2 film using a successive ion layer absorption and reaction (SILAR) method. The growth of QDs was found to be profoundly affected by the concentration of the precursor solution. At low concentrations, the rate-limiting factor of the crystal growth was the adsorption of the precursor ions, and the surface growth of the crystal became the limiting factor in the high concentration solution. The optimal concentration of precursor solution with respect to the quantity and size of synthesized QDs was 0.06 M. To further increase the performance of QDSCs, the 30% deionized water of polysulfide electrolyte was replaced with methanol to improve the wettability and permeability of electrolytes in the TiO2 film, which accelerated the redox couple diffusion in the electrolyte solution and improved charge transfer at the interfaces between photoanodes and electrolytes. The stability of PbS QDs in the electrolyte was also improved by methanol to reduce the charge recombination and prolong the electron lifetime. As a result, the PCE of QDSC was increased to 4.01%.

SUBMITTER: Tian J

PROVIDER: S-EPMC4792143 | biostudies-other | 2016

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Infra-red photoresponse of mesoscopic NiO-based solar cells sensitized with PbS quantum dot.

Project description:Sensitized NiO based photocathode is a new field of investigation with increasing scientific interest in relation with the development of tandem dye-sensitized solar cells (photovoltaic) and dye-sensitized photoelectrosynthetic cells (solar fuel). We demonstrate herein that PbS quantum dots (QDs) represent promising inorganic sensitizers for NiO-based quantum dot-sensitized solar cells (QDSSCs). The solar cell sensitized with PbS quantum dot exhibits significantly higher photoconversion efficiency than solar cells sensitized with a classical and efficient molecular sensitizer (P1 dye?=?4-(Bis-{4-[5-(2,2-dicyano-vinyl)-thiophene-2-yl]-phenyl}-amino)-benzoic acid). Furthermore, the system features an IPCE (Incident Photon-to-Current Efficiency) spectrum that spreads into the infra-red region, reaching operating wavelengths of 950?nm. The QDSSC photoelectrochemical device works with the complexes tris(4,4'-ditert-butyl-2,2'-bipyridine)cobalt(III/II) redox mediators, underscoring the formation of a long-lived charge-separated state. The electrochemical impedance spectrocopy measurements are consistent with a high packing of the QDs upon the NiO surface, the high density of which limits the access of the electrolyte and results in favorable light absorption cross-sections and a significant hole lifetime. These notable results highlight the potential of NiO-based photocathodes sensitized with quantum dots for accessing and exploiting the low-energy part of the solar spectrum in photovoltaic and photocatalysis applications.

| S-EPMC4850376 | biostudies-literature

Enhanced open-circuit voltage of PbS nanocrystal quantum dot solar cells.

Project description:Nanocrystal quantum dots (QD) show great promise toward improving solar cell efficiencies through the use of quantum confinement to tune absorbance across the solar spectrum and enable multi-exciton generation. Despite this remarkable potential for high photocurrent generation, the achievable open-circuit voltage (Voc) is fundamentally limited due to non-radiative recombination processes in QD solar cells. Here we report the highest open-circuit voltages to date for colloidal QD based solar cells under one sun illumination. This Voc of 692 ± 7?mV for 1.4?eV PbS QDs is a result of improved passivation of the defective QD surface, demonstrating Voc(mV)=553Eg/q-59 as a function of the QD bandgap (Eg). Comparing experimental Voc variation with the theoretical upper-limit obtained from one diode modeling of the cells with different Eg, these results clearly demonstrate that there is a tremendous opportunity for improvement of Voc to values greater than 1?V by using smaller QDs in QD solar cells.

| S-EPMC3715763 | biostudies-literature

Improving the Performance of PbS Quantum Dot Solar Cells by Optimizing ZnO Window Layer.

Project description:Comparing with hot researches in absorber layer, window layer has attracted less attention in PbS quantum dot solar cells (QD SCs). Actually, the window layer plays a key role in exciton separation, charge drifting, and so on. Herein, ZnO window layer was systematically investigated for its roles in QD SCs performance. The physical mechanism of improved performance was also explored. It was found that the optimized ZnO films with appropriate thickness and doping concentration can balance the optical and electrical properties, and its energy band align well with the absorber layer for efficient charge extraction. Further characterizations demonstrated that the window layer optimization can help to reduce the surface defects, improve the heterojunction quality, as well as extend the depletion width. Compared with the control devices, the optimized devices have obtained an efficiency of 6.7% with an enhanced V oc of 18%, J sc of 21%, FF of 10%, and power conversion efficiency of 58%. The present work suggests a useful strategy to improve the device performance by optimizing the window layer besides the absorber layer.

| S-EPMC6223798 | biostudies-literature

Optically Resonant Bulk Heterojunction PbS Quantum Dot Solar Cell.

Project description:We design an optically resonant bulk heterojunction solar cell to study optoelectronic properties of nanostructured p-n junctions. The nanostructures yield strong light-matter interaction as well as distinct charge-carrier extraction behavior, which together improve the overall power conversion efficiency. We demonstrate high-resolution substrate conformal soft-imprint lithography technology in combination with state-of-the art ZnO nanoparticles to create a nanohole template in an electron transport layer. The nanoholes are infiltrated with PbS quantum dots (QDs) to form a nanopatterned depleted heterojunction. Optical simulations show that the absorption per unit volume in the cylindrical QD absorber layer is enhanced by 19.5% compared to a planar reference. This is achieved for a square array of QD nanopillars of 330 nm height and 320 nm diameter, with a pitch of 500 nm on top of a residual QD layer of 70 nm, surrounded by ZnO. Electronic simulations show that the patterning results in a current gain of 3.2 mA/cm2 and a slight gain in voltage, yielding an efficiency gain of 0.4%. Our simulations further show that the fill factor is highly sensitive to the patterned structure. This is explained by the electric field strength varying strongly across the patterned absorber. We outline a path toward further optimized optically resonant nanopattern geometries with enhanced carrier collection properties. We demonstrate a 0.74 mA/cm2 current gain for a patterned cell compared to a planar cell in experiments, owing to a much improved infrared response, as predicted by our simulations.

| S-EPMC9527793 | biostudies-literature

Reduced Carrier Recombination in PbS - CuInS2 Quantum Dot Solar Cells.

Project description:Energy loss due to carrier recombination is among the major factors limiting the performance of TiO2/PbS colloidal quantum dot (QD) heterojunction solar cells. In this work, enhanced photocurrent is achieved by incorporating another type of hole-transporting QDs, Zn-doped CuInS2 (Zn-CIS) QDs into the PbS QD matrix. Binary QD solar cells exhibit a reduced charge recombination associated with the spatial charge separation between these two types of QDs. A ~30% increase in short-circuit current density and a ~20% increase in power conversion efficiency are observed in binary QD solar cells compared to cells built from PbS QDs only. In agreement with the charge transfer process identified through ultrafast pump/probe spectroscopy between these two QD components, transient photovoltage characteristics of single-component and binary QDs solar cells reveal longer carrier recombination time constants associated with the incorporation of Zn-CIS QDs. This work presents a straightforward, solution-processed method based on the incorporation of another QDs in the PbS QD matrix to control the carrier dynamics in colloidal QD materials and enhance solar cell performance.

| S-EPMC4448528 | biostudies-literature

Origin of the effects of PEG additives in electrolytes on the performance of quantum dot sensitized solar cells.

Project description:It has been well established that polymer additives in electrolyte can impede the charge recombination processes at the photoanode/electrolyte interface, and improve performance, especially V oc, of the resulting sensitized solar cells. However, there are few reports about the effect of electrolyte additives on counter electrode (CE) performance. Herein, we systematically investigated the effect of polyethylene glycol (PEG) additives with various molecular weights (M w from 300 to 20 000) in polysulfide electrolyte on the performance of two representative CdSe and Zn-Cu-In-Se (ZCISe) quantum dot sensitized solar cells (QDSCs), and explored the mechanism of the observed effects. Electrochemical impedance spectroscopy measurements indicate that all PEG additives can improve the charge recombination resistance at the photoanode/electrolyte interface, therefore suppressing the unwanted charge recombination process, and enhancing the V oc of the resulting cell devices accordingly. On the CE side, with the increase of M w of PEG additives, the initial effect of reducing the charge transfer resistance at the CE/electrolyte interface evolves into an increasing resistance; accordingly the initial positive effect on FF turns into negative one. Accordingly, low M w PEG can improve efficiency for both CdSe (increasing from 6.81% to 7.60%) and ZCISe QDSCs (increasing from 9.26% to 10.20%). High M w PEG is still effective for CdSe QDSCs with an efficiency of 7.38%, but falls flat on ZCISe QDSCs (with an efficiency of 9.11%).

| S-EPMC9085256 | biostudies-literature

Efficient eco-friendly inverted quantum dot sensitized solar cells.

Project description:Recent progress in quantum dot (QD) sensitized solar cells has demonstrated the possibility of low-cost and efficient photovoltaics. However, the standard device structure based on n-type materials often suffers from slow hole injection rate, which may lead to unbalanced charge transport. We have fabricated efficient p-type (inverted) QD sensitized cells, which combine the advantages of conventional QD cells with p-type dye sensitized configurations. Moreover, p-type QD sensitized cells can be used in highly promising tandem configurations with n-type ones. QDs without toxic Cd and Pb elements and with improved absorption and stability were successfully deposited onto mesoporous NiO electrode showing good coverage and penetration according to morphological analysis. Detailed photophysical charge transfer studies showed that high hole injection rates (108 s-1) observed in such systems are comparable with electron injection in conventional n-type QD assemblies. Inverted solar cells fabricated with various QDs demonstrate excellent power conversion efficiencies of up to 1.25%, which is 4 times higher than the best values for previous inverted QD sensitized cells. Attempts to passivate the surface of the QDs show that traditional methods of reduction of recombination in the QD sensitized cells are not applicable to the inverted architectures.

| S-EPMC4936380 | biostudies-literature

Quantum-dot-sensitized solar cell with unprecedentedly high photocurrent.

Project description:The reported photocurrent density (J(SC)) of PbS quantum dot (QD)-sensitized solar cell was less than 19 mA/cm(2) despite the capability to generate 38 mA/cm(2), which results from inefficient electron injection and fast charge recombination. Here, we report on a PbS:Hg QD-sensitized solar cell with an unprecedentedly high J(SC) of 30 mA/cm(2). By Hg(2+) doping into PbS, J(SC) is almost doubled with improved stability. Femtosecond transient study confirms that the improved J(SC) is due to enhanced electron injection and suppressed charge recombination. EXAFS reveals that Pb-S bond is reinforced and structural disorder is reduced by interstitially incorporated Hg(2+), which is responsible for the enhanced electron injection, suppressed recombination and stability. Thanks to the extremely high J(SC), power conversion efficiency of 5.6% is demonstrated at one sun illumination.

| S-EPMC3541510 | biostudies-literature

Detecting trap states in planar PbS colloidal quantum dot solar cells.

Project description:The recently developed planar architecture (ITO/ZnO/PbS-TBAI/PbS-EDT/Au) has greatly improved the power conversion efficiency of colloidal quantum dot photovoltaics (QDPVs). However, the performance is still far below the theoretical expectations and trap states in the PbS-TBAI film are believed to be the major origin, characterization and understanding of the traps are highly demanded to develop strategies for continued performance improvement. Here employing impedance spectroscopy we detect trap states in the planar PbS QDPVs. We determined a trap state of about 0.34 eV below the conduction band with a density of around 3.2 × 1016 cm-3 eV-1. Temperature dependent open-circuit voltage analysis, temperature dependent diode property analysis and temperature dependent build-in potential analysis consistently denotes an below-bandgap activation energy of about 1.17-1.20 eV.

| S-EPMC5109221 | biostudies-literature

Charge Transport in Trap-Sensitized Infrared PbS Quantum-Dot-Based Photoconductors: Pros and Cons.

Project description:Control of quantum-dot (QD) surface chemistry offers a direct approach for the tuning of charge-carrier dynamics in photoconductors based on strongly coupled QD solids. We investigate the effects of altering the surface chemistry of PbS QDs in such QD solids via ligand exchange using 3-mercaptopropionic acid (MPA) and tetrabutylammonium iodide (TBAI). The roll-to-roll compatible doctor-blade technique was used for the fabrication of the QD solid films as the photoactive component in photoconductors and field-effect phototransistors. The ligand exchange of the QD solid film with MPA yields superior device performance with higher photosensitivity and detectivity, which is due to less dark current and lower noise level as compared to ligand exchange with TBAI. In both cases, the mechanism responsible for photoconductivity is related to trap sensitization of the QD solid, in which traps are responsible of high photoconductive gain values, but slow response times under very low incident optical power (<1 pW). At medium⁻high incident optical powers (>100 pW), where traps are filled, both MPA- and TBAI-treated photodevices exhibit similar behavior, characterized by lower responsivity and faster response time, as limited by the mobility in the QD solid.

| S-EPMC6165075 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data