Ultrathin SmCo5 nanoflakes with high-coercivity prepared by solid particle (NaCl) and surfactant co-assisted ball milling.

ABSTRACT: The ultrathin SmCo5 nanoflakes with average thickness smaller than 50 nm are prepared by a novel method of solid particle (NaCl) and surfactant co-assisted ball milling. The as-prepared nanoflakes exhibit a narrower thickness distribution of 10-50 nm and high coercivity of 23 kOe. The possible formation mechanism of nanoflakes are proposed. Temperature dependence of demagnetization curves indicate that the magnetization reversal may be controlled by both nucleation and pinning. The results of X-ray powder diffraction and magnetic measurement for aligned SmCo5 nanoflakes resin composite indicate that the nanoflakes have a high texture degree. The ultrathin thickness and high coercivity are beneficial for preparing the high performance soft/hard coupling magnets and nanocomposite magnets.

SUBMITTER: Zuo WL

PROVIDER: S-EPMC4865853 | biostudies-other | 2016

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Strong textured SmCo5 nanoflakes with ultrahigh coercivity prepared by multistep (three steps) surfactant-assisted ball milling.

Project description:The high coercivity of 26.2 kOe for SmCo5 nanoflakes are obtained by multistep (three steps) surfactant-assisted ball milling. The magnetic properties, phase structure and morphology are studied by VSM, XRD and SEM, respectively. The results demonstrate that the three step ball-milling can keep more complete crystallinity (relatively less defects) during the process of milling compared with one step high energy ball-milling, which enhances the texture degree and coercivity. In addition, the mechanism of coercivity are also studied by the temperature dependence of demagnetization curves for aligned SmCo5 nanoflakes/resin composite, the result indicates that the magnetization reversal could be controlled by co-existed mechanisms of pinning and nucleation.

| S-EPMC4536656 | biostudies-other

Structure and catalytic behaviour of CuO-CeO2 prepared by high-energy ball milling.

Project description:The aim of this study is to prepare CuO-CeO2 composite by means of mechanical milling and to investigate its characteristics as a catalyst. The structural and morphological features of milled samples are observed by X-ray diffractometry and scanning electron microscopy. The redox property and total OSC (oxygen storage capacity) of the milled sample were measured by using GC-TCD and TG-DTA, which are important parameters to indicate the effectiveness of catalysts. Interestingly, reduction of CuO is repeatedly observed when milling of CuO-CeO2 powder mixture is processed in air. The redox property of milled CuO-CeO2 sample is investigated by H2-TPR, where three reduction peaks are observed for 0 h milling and only one broad peak for various other milling times. The total OSC of mechanically driven CuO-CeO2 catalyst is much higher than that of the CeO2-ZrO2 traditional catalyst system at low temperatures.

| S-EPMC6408418 | biostudies-literature

Microstructural Characterization of Calcite-Based Powder Materials Prepared by Planetary Ball Milling.

Project description:In this work, a planetary ball milling was used to modify the surface properties of calcite-based material from waste oyster shell under the rotational speed of 200-600 rpm, grinding time of 5-180 min and sample mass of 1-10 g. The milling significantly changed the microstructural properties of the calcite-based minerals (i.e., surface area, pore volume, true density, and porosity). The surface characterization of the resulting powder should be macroporous and/or nonporous based on the nitrogen adsorption/desorption isotherms. Under the optimal conditions at the rotational speed of 400 rpm, grinding time of 30 min and sample mass of 5 g, the resulting calcite-based powder had larger specific surface area (i.e., 10.64 m²·g-¹) than the starting material (i.e., 4.05 m²·g-1). This finding was also consistent with the measurement of laser-diffraction (i.e., 9.7 vs. 15.0 μm of mean diameter). In addition, the results from the scanning electron microscope (SEM) observation indicated that surface roughness can be enhanced as particle size decreases as a result of particle-particle attrition. Thus, grinding the aquacultural bioresource by a high-energy ball milling can create the fine materials, which may be applied in the fields of inorganic minerals like aggregate and construction material.

| S-EPMC5521309 | biostudies-other

Efficient Preparation of Small-Sized Transition Metal Dichalcogenide Nanosheets by Polymer-Assisted Ball Milling.

Project description:Two-dimensional (2D) transition metal dichalcogenide nanosheets (TMDC NSs) have attracted growing interest due to their unique structure and properties. Although various methods have been developed to prepare TMDC NSs, there is still a great need for a novel strategy combining simplicity, generality, and high efficiency. In this study, we developed a novel polymer-assisted ball milling method for the efficient preparation of TMDC NSs with small sizes. The use of polymers can enhance the interaction of milling balls and TMDC materials, facilitate the exfoliation process, and prevent the exfoliated nanosheets from aggregating. The WSe2 NSs prepared by carboxymethyl cellulose sodium (CMC)-assisted ball milling have small lateral sizes (8~40 nm) with a high yield (~60%). The influence of the experimental conditions (polymer, milling time, and rotation speed) on the size and yield of the nanosheets was studied. Moreover, the present approach is also effective in producing other TMDC NSs, such as MoS2, WS2, and MoSe2. This study demonstrates that polymer-assisted ball milling is a simple, general, and effective method for the preparation of small-sized TMDC NSs.

| S-EPMC9694012 | biostudies-literature

Preparation of Boron Nitride Nanoplatelets via Amino Acid Assisted Ball Milling: Towards Thermal Conductivity Application.

Project description:Hexagonal boron nitride nanoplatelets (BNNPs) have attracted widespread attention due to their unique physical properties and their peeling from the base material. Mechanical exfoliation is a simple, scalable approach to produce single-layer or few-layer BNNPs. In this work, two amino acid grafted boron nitride nanoplatelets, Lys@BNNP and Glu@BNNP, were successfully prepared via ball milling of h-BN with L-Lysine and L-Glutamic acid, respectively. It was found that the dispersion state of Lys@BNNP and Glu@BNNP in water had been effectively stabilized due to the introduction of amino acid moieties which contained a hydrophilic carboxyl group. PVA hydrogel composites with Lys@BNNP and Glu@BNNP as functional fillers were constructed and extensively studied. With 11.3 wt% Lys@BNNP incorporated, the thermal conductivity of Lys@BNNP/PVA hydrogel composite was up to 0.91 W m-1K-1, increased by 78%, comparing to the neat PVA hydrogel. Meanwhile, the mechanical and self-healing properties of the composites were simultaneously largely enhanced.

| S-EPMC7557982 | biostudies-literature

Peptide synthesis: ball-milling, in solution, or on solid support, what is the best strategy?

Project description:While presenting particularly interesting advantages, peptide synthesis by ball-milling was never compared to the two traditional strategies, namely peptide syntheses in solution and on solid support (solid-phase peptide synthesis, SPPS). In this study, the challenging VVIA tetrapeptide was synthesized by ball-milling, in solution, and on solid support. The three strategies were then compared in terms of yield, purity, reaction time and environmental impact. The results obtained enabled to draw some strengths and weaknesses of each strategy, and to foresee what will have to be implemented to build more efficient and sustainable peptide syntheses in the near future.

| S-EPMC7874854 | biostudies-literature

A Ball-Milling-Enabled Reformatsky Reaction.

Project description:An operationally simple one-jar one-step mechanochemical Reformatsky reaction using in situ generated organozinc intermediates under neat grinding conditions has been developed. Notable features of this reaction protocol are that it requires no solvent, no inert gases, and no pre-activation of the bulk zinc source. The developed process is demonstrated to have good substrate scope (39-82 % yield) and is effective irrespective of the initial morphology of the zinc source.

| S-EPMC6619031 | biostudies-literature

Solid Dispersions Obtained by Ball Milling as Delivery Platform of Etodolac, a Model Poorly Soluble Drug.

Project description:Poor water solubility of drugs is a limiting factor for their bioavailability and pharmacological activity. Many approaches are known to improve drug solubility, and among them, the physical method, solid dispersions (SDs), is applied. SDs are physical mixtures of a drug and a carrier, sometimes with the addition of a surfactant, which can be obtained by milling, cryomilling, spray-drying, or lyophilization processes. In this study, solid dispersions with etodolac (ETD-SDs) were prepared by the milling method using different carriers, such as hypromellose, polyvinylpyrrolidone, copovidone, urea, and mannitol. Solubility studies, dissolution tests, morphological assessment, thermal analysis, and FTIR imaging were applied to evaluate the SD properties. It was shown that the ball-milling process can be applied to obtain SDs with ETD. All designed ETD-SDs were characterized by higher water solubility and a faster dissolution rate compared to unprocessed ETD. SDs with amorphous carriers (HPMC, PVP, and PVP/VA) provided greater ETD solubility than dispersions with crystalline features (urea and mannitol). FTIR spectra confirmed the compatibility of ETD with tested carriers.

| S-EPMC11355714 | biostudies-literature

Edge-carboxylated graphene nanosheets via ball milling.

Project description:Low-cost, high-yield production of graphene nanosheets (GNs) is essential for practical applications. We have achieved high yield of edge-selectively carboxylated graphite (ECG) by a simple ball milling of pristine graphite in the presence of dry ice. The resultant ECG is highly dispersable in various solvents to self-exfoliate into single- and few-layer (? 5 layers) GNs. These stable ECG (or GN) dispersions have been used for solution processing, coupled with thermal decarboxylation, to produce large-area GN films for many potential applications ranging from electronic materials to chemical catalysts. The electrical conductivity of a thermally decarboxylated ECG film was found to be as high as 1214 S/cm, which is superior to its GO counterparts. Ball milling can thus provide simple, but efficient and versatile, and eco-friendly (CO(2)-capturing) approaches to low-cost mass production of high-quality GNs for applications where GOs have been exploited and beyond.

| S-EPMC3326447 | biostudies-literature

Ball-Milling-Enabled Reactivity of Manganese Metal*.

Project description:Efforts to generate organomanganese reagents under ball-milling conditions have led to the serendipitous discovery that manganese metal can mediate the reductive dimerization of arylidene malonates. The newly uncovered process has been optimized and its mechanism explored using CV measurements, radical trapping experiments, EPR spectroscopy, and solution control reactions. This unique reactivity can also be translated to solution whereupon pre-milling of the manganese is required.

| S-EPMC8596600 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data