Thickness-dependent transport channels in topological insulator Bi2Se3 thin films grown by magnetron sputtering.

ABSTRACT: We study the low-temperature transport properties of Bi2Se3 thin films grown by magnetron sputtering. A positive magnetoresistance resulting from the weak antilocalization (WAL) effect is observed at low temperatures. The observed WAL effect is two dimensional in nature. Applying the Hikami-Larkin-Nagaoka theory, we have obtained the dephasing length. It is found that the temperature dependence of the dephasing length cannot be described only by the Nyquist electron-electron dephasing, in conflict with prevailing experimental results. From the WAL effect, we extract the number of the transport channels, which is found to increase with increasing the thickness of the films, reflecting the thickness-dependent coupling between the top and bottom surface states in topological insulator. On the other hand, the electron-electron interaction (EEI) effect is observed in temperature-dependent conductivity. From the EEI effect, we also extract the number of the transport channel, which shows similar thickness dependence with that obtained from the analysis of the WAL effect. The EEI effect, therefore, can be used to analyze the coupling effect between the top and bottom surface states in topological insulator like the WAL effect.

SUBMITTER: Wang WJ

PROVIDER: S-EPMC4877920 | biostudies-other | 2016 May

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Effects of Film Thickness on the Residual Stress of Vanadium Dioxide Thin Films Grown by Magnetron Sputtering.

Project description:Vanadium dioxide (VO2) thin films of different thicknesses were prepared by regulating the deposition time (2, 2.5, 3, and 3.5 h). The impact of deposition time on the microstructure, surface morphology, and cross-section morphology was investigated. The results showed that the grain size increased with the film thickness. Meanwhile, the influence of film thickness on the residual stress was evaluated by X-ray diffraction. The phenomenon of "compressive-to-tensile stress transition" was illustrated as the thickness increased. The change of dominant mechanism for residual stress was used for explaining this situation. First, the composition of residual stress indicates that growth stress play a key role. Then, the effect of "atomic shot peening" can be used to explain the compressive stress. Lastly, the increased grain size, lower grain boundary density, and "tight effect" in the progress of film growth cause tensile stress.

| S-EPMC10386697 | biostudies-literature

Fabrication of black aluminium thin films by magnetron sputtering.

Project description:Black aluminium thin films were prepared by direct current (DC) pulsed magnetron sputtering. The N2 concentration in the Ar-N2 mixture that was used as the deposition atmosphere was varied from 0 to 10%, and its impact on the film growth and optical properties was studied. A strong change in the film growth process was observed as a function of the N2 concentration. At a specific N2 concentration of ∼6%, the Al film growth process favoured the formation of a moth-eye-like antireflective surface. This surface morphology, which was similar to the structure of a cauliflower, is known to trap incident light, resulting in films with a very low reflectivity. A diffuse reflectivity lower than 4% was reached in the ultraviolet-visible-near infrared (UV-VIS-NIR) spectral range that corresponds to a value observed for an ultrahigh absorber. We found that for the preparation of black aluminium, the nitrogen content plays an important role in film formation and the resulting film morphology.

| S-EPMC9054304 | biostudies-literature

Optically Active TiO2:Er Thin Films Deposited by Magnetron Sputtering.

Project description:Titanium dioxide photoanodes for hydrogen generation suffer from a profound mismatch between the optical absorption of TiO2 and the solar spectrum. To solve the problem of low solar-to-chemical efficiency, optically active materials are proposed. In this work, TiO2 thin films containing erbium were deposited by radio frequency RF magnetron sputtering under ultrahigh vacuum conditions UHV. Morphology, structural, optical and electronic properties were studied. TiO2:Er thin films are homogenous, with uniform distribution of Er ions and high transparency over the visible VIS range of the light spectrum. However, a profound 0.4 eV blue shift of the fundamental absorption edge with respect to undoped TiO2 was observed, which can be attributed either to the size effect due to amorphization of TiO2 host or to the onset of precipitation of Er2Ti2O7 nanocrystals. Near-infrared NIR to VIS up-conversion is demonstrated upon excitation at 980 nm, while strong green photoluminescence at 525 and 550 nm occurs upon photon absorption at 488 nm.

| S-EPMC8348420 | biostudies-literature

Formation of Thin NiGe Films by Magnetron Sputtering and Flash Lamp Annealing.

Project description:The nickel monogermanide (NiGe) phase is known for its electrical properties such as low ohmic and low contact resistance in group-IV-based electronics. In this work, thin films of nickel germanides (Ni-Ge) were formed by magnetron sputtering followed by flash lamp annealing (FLA). The formation of NiGe was investigated on three types of substrates: on amorphous (a-Ge) as well as polycrystalline Ge (poly-Ge) and on monocrystalline (100)-Ge (c-Ge) wafers. Substrate and NiGe structure characterization was performed by Raman, TEM, and XRD analyses. Hall Effect and four-point-probe measurements were used to characterize the films electrically. NiGe layers were successfully formed on different Ge substrates using 3-ms FLA. Electrical as well as XRD and TEM measurements are revealing the formation of Ni-rich hexagonal and cubic phases at lower temperatures accompanied by the formation of the low-resistivity orthorhombic NiGe phase. At higher annealing temperatures, Ni-rich phases are transforming into NiGe, as long as the supply of Ge is ensured. NiGe layer formation on a-Ge is accompanied by metal-induced crystallization and its elevated electrical resistivity compared with that of poly-Ge and c-Ge substrates. Specific resistivities for 30 nm Ni on Ge were determined to be 13.5 ??·cm for poly-Ge, 14.6 ??·cm for c-Ge, and 20.1 ??·cm for a-Ge.

| S-EPMC7221967 | biostudies-literature

Multitarget Reactive Magnetron Sputtering towards the Production of Strontium Molybdate Thin Films.

Project description:X-ray photoelectron spectroscopy was used to study the direct synthesis of strontium and molybdenum oxide thin films deposited by multitarget reactive magnetron sputtering (MT-RMS). Sr and Mo targets with a purity of 99.9% and 99.5%, respectively, were co-sputtered in an argon-oxygen gas mixture. The chamber was provided with an oxygen background flow plus an additional controlled oxygen supply to each of the targets. We demonstrate that variation in the power applied to the Mo target during MT-RMS enables the production of strontium and molybdenum oxide films with variable concentrations of Mo atoms. Both molybdenum and strontium were found in the oxidized state, and no metallic peaks were detected. The deconvoluted high-resolution XPS spectra of molybdenum revealed the presence of several Mo 3d peaks, which indicates molybdenum bonds in a lower valence state. Contrary to the Mo spectra, the high-resolution strontium Sr 3d spectra for the same samples were very similar, and no additional peaks were detected.

| S-EPMC10056819 | biostudies-literature

Resistive Switching Characteristics of Li-Doped ZnO Thin Films Based on Magnetron Sputtering.

Project description:A kind of devices Pt/Ag/ZnO:Li/Pt/Ti with high resistive switching behaviors were prepared on a SiO2/Si substrate by using magnetron sputtering method and mask technology, composed of a bottom electrode (BE) of Pt/Ti, a resistive switching layer of ZnO:Li thin film and a top electrode (TE) of Pt/Ag. To determine the crystal lattice structure and the Li-doped concentration in the resulted ZnO thin films, X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) tests were carried out. Resistive switching behaviors of the devices with different thicknesses of Li-doped ZnO thin films were studied at different set and reset voltages based on analog and digital resistive switching characteristics. At room temperature, the fabricated devices represent stable bipolar resistive switching behaviors with a low set voltage, a high switching current ratio and a long retention up to 104 s. In addition, the device can sustain an excellent endurance more than 103 cycles at an applied pulse voltage. The mechanism on how the thicknesses of the Li-doped ZnO thin films affect the resistive switching behaviors was investigated by installing conduction mechanism models. This study provides a new strategy for fabricating the resistive random access memory (ReRAM) device used in practice.

| S-EPMC6515171 | biostudies-literature

Study of wide bandgap SnO<sub>x</sub> thin films grown by a reactive magnetron sputtering via a two-step method.

Project description:In the present work, we report on the microstructural and optoelectronic properties of SnOx thin films deposited by a reactive radio frequency magnetron sputtering. After SnOx growth by sputtering under O2/Ar flow, we have used three different treatment methods, namely (1) as deposited films under O2/Ar, (2) vacuum annealed films ex-situ, and (3) air annealed films ex-situ. Effects of the O2/Ar ratios and the growth temperature were investigated for each treatment method. We have thoroughly investigated the structural, optical, electrical and morphology of the different films by several advanced techniques. The best compromise between electrical conductivity and optical transmission for the use of these SnOx films as an n-type TCO was the conditions O2/Ar = 1.5% during the growth process, at 250 °C, followed by a vacuum post thermal annealing performed at 5 × 10-4 Torr. Our results pointed out clear correlations between the growth conditions, the microstructural and optoelectronic properties, where highly electrically conductive films were found to be associated to larger grains size microstructure. Effects of O2/Ar flow and the thermal annealing process were also analysed and discussed thoroughly.

| S-EPMC9468343 | biostudies-literature

Evaluation of mobility in thin Bi2Se3 topological insulator for prospects of local electrical interconnects.

Project description:Three-dimensional (3D) topological insulator (TI) has been conjectured as an emerging material to replace copper (Cu) as an interconnect material because of the suppression of elastic scattering from doping and charge impurities for carrier transport on TI surface. We, therefore via full real-space simulation, examine the feasibility of using thin 3D-TI (Bi2Se3) wire for the local electrical interconnects in the presence of edge roughness, vacancies, acoustic phonons and charge impurities across temperature and Fermi-level by simulating quantum transport through Non-Equilibrium Green Function algorithm. We found that because of the scattering induced by the acoustic phonons, the mobility reduces considerably at the room temperature which complemented with the low density of states near Dirac-point does not position Bi2Se3 3D-TI as a promising material to replace Cu for local interconnects. Properties required in suitable TI material for this application have also been discussed.

| S-EPMC4213797 | biostudies-literature

Combined magnetron sputtering and pulsed laser deposition of TiO 2 and BFCO thin films.

Project description:We report the successful demonstration of a hybrid system that combines pulsed laser deposition (PLD) and magnetron sputtering (MS) to deposit high quality thin films. The PLD and MS simultaneously use the same target, leading to an enhanced deposition rate. The performance of this technique is demonstrated through the deposition of titanium dioxide and bismuth-based perovskite oxide Bi2FeCrO6 (BFCO) thin films on Si(100) and LaAlO3 (LAO) (100). These specific oxides were chosen due to their functionalities, such as multiferroic and photovoltaic properties (BFCO) and photocatalysis (TiO2). We compare films deposited by conventional PLD, MS and PLD combined with MS, and show that under all conditions the latter technique offers an increased deposition rate (+50%) and produces films denser (+20%) than those produced by MS or PLD alone, and without the large clusters found in the PLD-deposited films. Under optimized conditions, the hybrid technique produces films that are two times smoother than either technique alone.

| S-EPMC5451404 | biostudies-literature

Pathways to Tailor Photocatalytic Performance of TiO2 Thin Films Deposited by Reactive Magnetron Sputtering.

Project description:TiO2 thin films are used extensively for a broad range of applications including environmental remediation, self-cleaning technologies (windows, building exteriors, and textiles), water splitting, antibacterial, and biomedical surfaces. While a broad range of methods such as wet-chemical synthesis techniques, chemical vapor deposition (CVD), and physical vapor deposition (PVD) have been developed for preparation of TiO2 thin films, PVD techniques allow a good control of the homogeneity and thickness as well as provide a good film adhesion. On the other hand, the choice of the PVD technique enormously influences the photocatalytic performance of the TiO2 layer to be deposited. Three important parameters play an important role on the photocatalytic performance of TiO2 thin films: first, the different pathways in crystallization (nucleation and growth); second, anatase/rutile formation; and third, surface area at the interface to the reactants. This study aims to provide a review regarding some strategies developed by our research group in recent years to improve the photocatalytic performance of TiO2 thin films. An innovative approach, which uses thermally induced nanocrack networks as an effective tool to enhance the photocatalytic performance of sputter deposited TiO2 thin films, is presented. Plasmonic and non-plasmonic enhancement of photocatalytic performance by decorating TiO2 thin films with metallic nanostructures are also briefly discussed by case studies. In addition to remediation applications, a new approach, which utilizes highly active photocatalytic TiO2 thin film for micro- and nanostructuring, is also presented.

| S-EPMC6748074 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data