Properties of a Laser Shock Wave in Al-Cu Alloy under Elevated Temperatures: A Molecular Dynamics Simulation Study.

ABSTRACT: The laser shock wave (LSW) generated by the interaction between a laser and a material has been widely used in laser manufacturing, such as laser shock peening and laser shock forming. However, due to the high strain rate, the propagation of LSW in materials, especially LSW at elevated temperatures, is difficult to study through experimental methods. A molecular dynamics simulation was used in this study to investigate the propagation of LSW in an Al-Cu alloy. The Hugoniot relations of LSW were obtained at different temperatures and the effects of elevated temperatures on shock velocity and shock pressure were analyzed. Then the elastic and plastic wave of the LSW was researched. Finally, the evolution of dislocations induced by LSW and its mechanism under elevated temperatures was explored. The results indicate that the shock velocity and shock pressure induced by LSW both decrease with the increasing temperatures. Moreover, the velocity of elastic wave and plastic wave both decrease with the increasing treatment temperature, while their difference decreases as the temperature increases. Moreover, the dislocation atoms increases with the increasing temperatures before 2 ps, while it decreases with the increasing temperatures after 2 ps. The reason for the results is related to the formation and evolution of extended dislocations.

SUBMITTER: Meng X

PROVIDER: S-EPMC5344562 | biostudies-other | 2017 Jan

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Structural and compositional study of precipitates in under-aged Cu-added Al-Mg-Si alloy.

Project description:Atomic scale characterization of fine precipitates in an under-aged Cu added Al-Mg-Si alloy was carried out by combination of atomically-resolved annular dark-field scanning transmission electron microscopy and energy dispersive X-ray spectroscopy. Two types of precipitates were observed in the alloy. In the case of ordered ?" precipitates, ?" was proposed as Mg5-xAl2+xSi4 (x ? 1) with solute Cu atoms replacing Al site of ?" precipitate. In the case of disordered precipitates, the precipitates were found to consist of ?" sub-unit cells, three-fold symmetric structure without Cu atoms, Cu containing structures termed as "Cu sub-unit cluster", and Q' sub-unit cells. Among these structures, the morphologies of three-fold symmetric structure without Cu atoms, Cu sub-unit cluster, and Q' sub-unit cell were almost the same, so that these structures should be the clusters of Q' phase. Since the areal density, length and diameter of precipitates were almost equal between Cu free Al-Mg-Si alloy and Cu added Al-Mg-Si alloy, the increase of hardness by Cu addition should be due to the precipitation of Cu related precipitates, such as Cu sub-unit clusters and Q' sub-unit cells.

| S-EPMC6226491 | biostudies-literature

Direct observation of grain rotations during coarsening of a semisolid Al-Cu alloy.

Project description:Sintering is a key technology for processing ceramic and metallic powders into solid objects of complex geometry, particularly in the burgeoning field of energy storage materials. The modeling of sintering processes, however, has not kept pace with applications. Conventional models, which assume ideal arrangements of constituent powders while ignoring their underlying crystallinity, achieve at best a qualitative description of the rearrangement, densification, and coarsening of powder compacts during thermal processing. Treating a semisolid Al-Cu alloy as a model system for late-stage sintering-during which densification plays a subordinate role to coarsening-we have used 3D X-ray diffraction microscopy to track the changes in sample microstructure induced by annealing. The results establish the occurrence of significant particle rotations, driven in part by the dependence of boundary energy on crystallographic misorientation. Evidently, a comprehensive model for sintering must incorporate crystallographic parameters into the thermodynamic driving forces governing microstructural evolution.

| S-EPMC5068287 | biostudies-literature

Mechanical Behavior of AZ31B Mg Alloy Sheets under Monotonic and Cyclic Loadings at Room and Moderately Elevated Temperatures.

Project description:Large-strain monotonic and cyclic loading tests of AZ31B magnesium alloy sheets were performed with a newly developed testing system, at different temperatures, ranging from room temperature to 250 °C. Behaviors showing significant twinning during initial in-plane compression and untwinning in subsequent tension at and slightly above room temperature were recorded. Strong yielding asymmetry and nonlinear hardening behavior were also revealed. Considerable Bauschinger effects, transient behavior, and variable permanent softening responses were observed near room temperature, but these were reduced and almost disappeared as the temperature increased. Different stress-strain responses were inherent to the activation of twinning at lower temperatures and non-basal slip systems at elevated temperatures. A critical temperature was identified to account for the transition between the twinning-dominant and slip-dominant deformation mechanisms. Accordingly, below the transition point, stress-strain curves of cyclic loading tests exhibited concave-up shapes for compression or compression following tension, and an unusual S-shape for tension following compression. This unusual shape disappeared when the temperature was above the transition point. Shrinkage of the elastic range and variation in Young's modulus due to plastic strain deformation during stress reversals were also observed. The texture-induced anisotropy of both the elastic and plastic behaviors was characterized experimentally.

| S-EPMC5453073 | biostudies-other

Influence of Homogenization on Microstructural Response and Mechanical Property of Al-Cu-Mn Alloy.

Project description:The evolution of the microstructures and properties of large direct chill (DC)-cast Al-Cu-Mn alloy ingots during homogenization was investigated. The results revealed that the Al-Cu-Mn alloy ingots had severe microsegregation and the main secondary phase was Al₂Cu, with minimal Al₇Cu₂Fe phase. Numerous primary eutectic phases existed in the grain boundary and the main elements were segregated at the interfaces along the interdendritic region. The grain boundaries became discontinuous, residual phases were effectively dissolved into the matrix, and the segregation degree of all elements was reduced dramatically during homogenization. In addition, the homogenized alloys exhibited improved microstructures with finer grain size, higher number density of dislocation networks, higher density of uniformly distributed θ' or θ phase (Al₂Cu), and higher volume fraction of high-angle grain boundaries compared to the nonhomogenized samples. After the optimal homogenization scheme treated at 535 °C for 10 h, the tensile strength and elongation% were about 24 MPa, 20.5 MPa, and 1.3% higher than those of the specimen without homogenization treatment.

| S-EPMC6025167 | biostudies-literature

Simultaneous increase in strength and ductility by decreasing interface energy between Zn and Al phases in cast Al-Zn-Cu alloy.

Project description:Cast-Al alloys that include a high amount of the second element in their matrix have comparatively high strength but low ductility because of the high volume fraction of strengthening phases or undesirable inclusions. Al-Zn alloys that have more than 30?wt% Zn have a tensile strength below 300?MPa, with elongation under 5% in the as-cast state. However, we found that after substitution of 2% Zn by Cu, the tensile strength of as-cast Al-Zn-Cu alloys was 25% higher and ductility was four times higher than for the corresponding Al-35% Zn alloy. Additionally, for the Al-43% Zn alloy with 2% Cu after 1?h solution treatment at 400?°C and water quenching, the tensile strength unexpectedly reached values close to 600?MPa. For the Al-33% Zn alloy with 2% Cu, the tensile strength was 500?MPa with 8% ductility. The unusual trends of the mechanical properties of Al-Zn alloys with Cu addition observed during processing from casting to the subsequent solution treatment were attributed to the precipitation of Zn in the Al matrix. The interface energy between the Zn particles and the Al matrix decreased when using a solution of Cu in Zn.

| S-EPMC5610273 | biostudies-literature

Developing of nano sized fibrous eutectic silicon in hypereutectic Al-Si alloy by laser remelting.

Project description:Laser surface melting followed by rapid solidification is an effective means to produce very fine microstructures with desirable surface properties because of the high rates of cooling associated with it. In the present study, the effect of rapid cooling on the silicon particle size, distribution, and morphology of hypereutectic Al-17wt.%Si and Al-20wt.%Si alloys have been investigated. A continuous-wave CO2 laser of wavelength 10.6 ?m and a Trumpf Yb-YAG disk laser of wavelength 1.030 ?m were used with a beam diameter of 1 mm and scanning speeds ranging from 5 to 100 mm/s. Rapid solidification increased the solubility of silicon in aluminum to approximately 5wt% and induced non-equilibrium hypoeutectic microstructures comprising large volume fractions of primary ?-Al dendrites and ultrafine Al-Si eutectic of lamellar morphology. Both ?-Al dendrites and the silicon particle sizes were significantly reduced from micron to nanoscale level. The morphology of silicon particles is modified from massive polygonal and plate-like to a mixture of fine flakes with round corners, feathery and fibrous, or a coral-like and thread-like structure. The eutectic silicon size and the interlamellar spacing were reduced to 30 and 10 nm, respectively. Furthermore, most of the silicon crystals in the eutectic region and the aluminum dendrites contained a significant number of twins which were considered as an essential contributor to the mechanism of growth and branching. Microhardness values increased two to threefold due to the refinement of the microstructural constituent.

| S-EPMC7374159 | biostudies-literature

Characterisation of a High-Performance Al-Zn-Mg-Cu Alloy Designed for Wire Arc Additive Manufacturing.

Project description:Ever-increasing demands of industrial manufacturing regarding mechanical properties require the development of novel alloys designed towards the respective manufacturing process. Here, we consider wire arc additive manufacturing. To this end, Al alloys with additions of Zn, Mg and Cu have been designed considering the requirements of good mechanical properties and limited hot cracking susceptibility. The samples were produced using the cold metal transfer pulse advanced (CMT-PADV) technique, known for its ability to produce lower porosity parts with smaller grain size. After material simulations to determine the optimal heat treatment, the samples were solution heat treated, quenched and aged to enhance their mechanical performance. Chemical analysis, mechanical properties and microstructure evolution were evaluated using optical light microscopy, scanning electron microscopy, energy dispersive X-ray spectroscopy, X-ray fluorescence analysis and X-ray radiography, as well as tensile, fatigue and hardness tests. The objective of this research was to evaluate in detail the mechanical properties and microstructure of the newly designed high-performance Al-Zn-based alloy before and after ageing heat treatment. The only defects found in the parts built under optimised conditions were small dispersed porosities, without any visible cracks or lack of fusion. Furthermore, the mechanical properties are superior to those of commercial 7xxx alloys and remarkably independent of the testing direction (parallel or perpendicular to the deposit beads). The presented analyses are very promising regarding additive manufacturing of high-strength aluminium alloys.

| S-EPMC7178362 | biostudies-literature

Precipitation of a new platelet phase during the quenching of an Al-Zn-Mg-Cu alloy.

Project description:A previously undescribed high aspect ratio strengthening platelet phase, herein named the Y-phase, has been identified in a commercial Al-Zn-Mg-Cu alloy. Differential scanning calorimetry indicates that this phase only precipitates at temperature and cooling rate of about 150-250 °C and 0.05-300 K/s, respectively. This precipitate is shown to be responsible for a noticeable improvement in mechanical properties. Aberration corrected scanning transmission electron microscopy demonstrates the minimal thickness (~1.4 nm) precipitate plates are isostructural to those of the T1 (Al2CuLi) phase observed in Al-Cu-Li alloys. Low voltage chemical analysis by energy dispersive X-ray spectroscopy and electron energy loss spectroscopy gives evidence of the spatial partitioning of the Al, Cu and Zn within the Y-phase, as well as demonstrating the incorporation of a small amount of Mg.

| S-EPMC4793252 | biostudies-literature

First-Principles Study on Structure and Stability of GP Zones in Al-Mg-Si(-Cu) Alloy.

Project description:Nanostructured Guinier-Preston (GP) zones are critical for the strength of Al-Mg-Si(-Cu) aluminum alloys. However, there are controversial reports about the structure and growth mechanism of GP zones. In this study, we construct several atomic configurations of GP zones according to the previous research. Then first-principles calculations based on density functional theory were used to investigate the relatively stable atomic structure and GP-zones growth mechanism. The results show that on the (100) plane, GP zones consist of {MgSi} atomic layers without Al atoms, and the size tends to grow up to 2 nm. Along the (100) growth direction, even numbers of {MgSi} atomic layers are more energetically favorable and there exist Al atomic layers to relieve the lattice strain. {MgSi}2Al4 is the most energetically favorable GP-zones configuration, and the substitution sequence of Cu atoms in {MgSi}2Al4 during the aging process is Al → Si → Mg. The growth of GP zones is accompanied by the increase in Mg and Si solute atoms and the decrease in Al atoms. Point defects, such as Cu atoms and vacancies, exhibit different occupation tendencies in GP zones: Cu atoms tend to segregate in the Al layer near the GP zones, while vacancies tend to be captured by the GP zones.

| S-EPMC10254046 | biostudies-literature

Exceptional high fatigue strength in Cu-15at.%Al alloy with moderate grain size.

Project description:It is commonly proposed that the fatigue strength can be enhanced by increasing the tensile strength, but this conclusion needs to be reconsidered according to our study. Here a recrystallized α-Cu-15at.%Al alloy with moderate grain size of 0.62 μm was fabricated by cold rolling and annealing, and this alloy achieved exceptional high fatigue strength of 280 MPa at 10(7) cycles. This value is much higher than the fatigue strength of 200 MPa for the nano-crystalline counterpart (0.04 μm in grain size) despite its higher tensile strength. The remarkable improvement of fatigue strength should be mainly attributed to the microstructure optimization, which helps achieve the reduction of initial damage and the dispersion of accumulated damage. A new strategy of "damage reduction" was then proposed for fatigue strength improvement, to supplement the former strengthening principle. The methods and strategies summarized in this work offer a general pathway for further improvement of fatigue strength, in order to ensure the long-term safety of structural materials.

| S-EPMC4893737 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data