Quantification of the Service Life Extension and Environmental Benefit of Chloride Exposed Self-Healing Concrete.

ABSTRACT: Formation of cracks impairs the durability of concrete elements. Corrosion inducing substances, such as chlorides, can enter the matrix through these cracks and cause steel reinforcement corrosion and concrete degradation. Self-repair of concrete cracks is an innovative technique which has been studied extensively during the past decade and which may help to increase the sustainability of concrete. However, the experiments conducted until now did not allow for an assessment of the service life extension possible with self-healing concrete in comparison with traditional (cracked) concrete. In this research, a service life prediction of self-healing concrete was done based on input from chloride diffusion tests. Self-healing of cracks with encapsulated polyurethane precursor formed a partial barrier against immediate ingress of chlorides through the cracks. Application of self-healing concrete was able to reduce the chloride concentration in a cracked zone by 75% or more. As a result, service life of steel reinforced self-healing concrete slabs in marine environments could amount to 60-94 years as opposed to only seven years for ordinary (cracked) concrete. Subsequent life cycle assessment calculations indicated important environmental benefits (56%-75%) for the ten CML-IA (Center of Environmental Science of Leiden University-Impact Assessment) baseline impact indicators which are mainly induced by the achievable service life extension.

SUBMITTER: Van Belleghem B

PROVIDER: S-EPMC5344592 | biostudies-other | 2016 Dec

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:Brand extension is a marketing strategy leveraging well-established brand to promote new offerings provided as goods or service. The previous neurophysiological studies on goods-to-goods brand extension have proposed that categorization and semantic memory processes are involved in brand extension evaluation. However, it is unknown whether these same processes also underlie service-to-service brand extension. The present study, therefore, aims to investigate neural processes in consumers underlying their judgment of service-to-service brand extension. Specifically, we investigated human electroencephalographic responses to extended services that were commonly considered to fit well or badly with parent brand among consumers. For this purpose, we proposed a new stimulus grouping method to find commonly acceptable or unacceptable service extensions. In the experiment, participants reported the acceptability of 56 brand extension pairs, consisting of parent brand name (S1) and extended service name (S2). From individual acceptability responses, we assigned each pair to one of the three fit levels: high- (i.e., highly acceptable), low-, and mid-fit. Next, we selected stimuli that received high/low-fit evaluations from a majority of participants (i.e., >85%) and assigned them to a high/low population-fit group. A comparison of event-related potentials (ERPs) between population-fit groups through a paired t-test showed significant differences in the fronto-central N2 and fronto-parietal P300 amplitudes. We further evaluated inter-subject variability of these ERP components by a decoding analysis that classified N2 and/or P300 amplitudes into a high, or low population-fit class using a support vector machine. Leave-one-subject-out validation revealed classification accuracy of 60.35% with N2 amplitudes, 78.95% with P300, and 73.68% with both, indicating a relatively high inter-subject variability of N2 but low for P300. This validation showed that fronto-parietal P300 reflected neural processes more consistent across subjects in service-to-service brand extension. We further observed that the left frontal P300 amplitude was increased as fit-level increased across stimuli, indicating a semantic retrieval process to evaluate a semantic link between S1 and S2. Parietal P300 showed a higher amplitude in the high population-fit group, reflecting a similarity-based categorization process. In sum, our results suggest that service-to-service brand extension evaluation may share similar neural processes with goods-to-goods brand extension.

Dataset Information

Quantification of the Service Life Extension and Environmental Benefit of Chloride Exposed Self-Healing Concrete.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets