Spinning Carbon Nanotube Nanothread under a Scanning Electron Microscope.

ABSTRACT: Nanothread with a diameter as small as one hundred nanometers was manufactured under a scanning electron microscope. Made directly from carbon nanotubes, and inheriting their superior electrical and mechanical properties, nanothread may be the world's smallest man-made fiber. The smallest thread that can be spun using a bench-top spinning machine is about 5 microns in diameter. Nanothread is a new material building block that can be used at the nanoscale or plied to form yarn for applications at the micro and macro scales. Preliminary electrical and mechanical properties of nanothread were measured. The resistivity of nanothread is less than 10-5 Ω∙m. The strength of nanothread is greater than 0.5 GPa. This strength was obtained from measurements using special glue that cures in an electron microscope. The glue weakened the thread, thus further work is needed to obtain more accurate measurements. Nanothread will have broad applications in enabling electrical components, circuits, sensors, and tiny machines. Yarn can be used for various macroscale applications including lightweight antennas, composites, and cables.

SUBMITTER: Li W

PROVIDER: S-EPMC5448855 | biostudies-other | 2011 Aug

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Scanning electron microscope studies of human metaphase chromosomes.

Project description:Scanning electron microscopy (SEM) is used to evaluate potential chromosome preparations and staining methods for application in high-resolution three-dimensional X-ray imaging. Our starting point is optical fluorescence microscopy, the standard method for chromosomes, which only gives structural detail at the 200?nm scale. In principle, with suitable sample preparation protocols, including contrast enhancing staining, the surface structure of the chromosomes can be viewed at the 1?nm level by SEM. Here, we evaluate a heavy metal nucleic-acid-specific stain, which gives strong contrast in the backscattered electron signal. This study uses SEM to examine chromosomes prepared in different ways to establish a sample preparation protocol for X-rays. Secondary electron and backscattered electron signals are compared to evaluate the effectiveness of platinum-based stains used to enhance the contrast.

| S-EPMC3900039 | biostudies-literature

Depth sectioning with the aberration-corrected scanning transmission electron microscope.

Project description:The ability to correct the aberrations of the probe-forming lens in the scanning transmission electron microscope provides not only a significant improvement in transverse resolution but in addition brings depth resolution at the nanometer scale. Aberration correction therefore opens up the possibility of 3D imaging by optical sectioning. Here we develop a definition for the depth resolution for scanning transmission electron microscope depth sectioning and present initial results from this method. Objects such as catalytic metal clusters and single atoms on various support materials are imaged in three dimensions with a resolution of several nanometers. Effective focal depth is determined by statistical analysis and the contributing factors are discussed. Finally, current challenges and future capabilities available through new instruments are discussed.

| S-EPMC1413870 | biostudies-literature

Comparing Scanning Electron Microscope and Transmission Electron Microscope Grain Mapping Techniques Applied to Well-Defined and Highly Irregular Nanoparticles.

Project description:Investigating how grain structure affects the functional properties of nanoparticles requires a robust method for nanoscale grain mapping. In this study, we directly compare the grain mapping ability of transmission Kikuchi diffraction (TKD) in a scanning electron microscope to automated crystal orientation mapping (ACOM) in a transmission electron microscope across multiple nanoparticle materials. Analysis of well-defined Au, ZnO, and ZnSe nanoparticles showed that the grain orientations and GB geometries obtained by TKD are accurate and match those obtained by ACOM. For more complex polycrystalline Cu nanostructures, TKD provided an interpretable grain map whereas ACOM, with or without precession electron diffraction, yielded speckled, uninterpretable maps with orientation errors. Acquisition times for TKD were generally shorter than those for ACOM. Our results validate the use of TKD for characterizing grain orientation and grain boundary distributions in nanoparticles, providing a framework for the broader exploration of how microstructure influences nanoparticle properties.

| S-EPMC7033971 | biostudies-literature

Real-Time Measurement of Nanotube Resonator Fluctuations in an Electron Microscope.

Project description:Mechanical resonators based on low-dimensional materials provide a unique platform for exploring a broad range of physical phenomena. The mechanical vibrational states are indeed extremely sensitive to charges, spins, photons, and adsorbed masses. However, the roadblock is often the readout of the resonator, because the detection of the vibrational states becomes increasingly difficult for smaller resonators. Here, we report an unprecedentedly sensitive method to detect nanotube resonators with effective masses in the 10-20 kg range. We use the beam of an electron microscope to resolve the mechanical fluctuations of a nanotube in real-time for the first time. We obtain full access to the thermally driven Brownian motion of the resonator, both in space and time domains. Our results establish the viability of carbon nanotube resonator technology at room temperature and pave the way toward the observation of novel thermodynamics regimes and quantum effects in nanomechanics.

| S-EPMC5354313 | biostudies-literature

Direct spinning and densification method for high-performance carbon nanotube fibers.

Project description:Developing methods to assemble nanomaterials into macroscopic scaffolds is of critical significance at the current stage of nanotechnology. However, the complications of the fabrication methods impede the widespread usages of newly developed materials even with the superior properties in many cases. Here, we demonstrate the feasibility of a highly-efficient and potentially-continuous fiber-spinning method to produce high-performance carbon nanotube (CNT) fiber (CNTF). The processing time is?<1?min from synthesis of CNTs to fabrication of highly densified and aligned CNTFs. CNTFs that are fabricated by the developed spinning method are ultra-lightweight, strong (specific tensile strength?=?4.08?±?0.25?Ntex-1), stiff (specific tensile modulus?=?187.5?±?7.4?Ntex-1), electrically conductive (2,270?S?m2kg-1), and highly flexible (knot efficiency?=?48?±?15%), so they are suitable for various high-value fabric-based applications.

| S-EPMC6609687 | biostudies-literature

Longitudinal and transverse electron paramagnetic resonance in a scanning tunneling microscope

Project description:Longitudinal and transverse magnetic field gradients drive single-atom EPR in an STM owing to piezoelectric excitations. Electron paramagnetic resonance (EPR) spectroscopy is widely used to characterize paramagnetic complexes. Recently, EPR combined with scanning tunneling microscopy (STM) achieved single-spin sensitivity with sub-angstrom spatial resolution. The excitation mechanism of EPR in STM, however, is broadly debated, raising concerns about widespread application of this technique. We present an extensive experimental study and modeling of EPR-STM of Fe and hydrogenated Ti atoms on a MgO surface. Our results support a piezoelectric coupling mechanism, in which the EPR species oscillate adiabatically in the inhomogeneous magnetic field of the STM tip. An analysis based on Bloch equations combined with atomic-multiplet calculations identifies different EPR driving forces. Specifically, transverse magnetic field gradients drive the spin-1/2 hydrogenated Ti, whereas longitudinal magnetic field gradients drive the spin-2 Fe. Also, our results highlight the potential of piezoelectric coupling to induce electric dipole moments, thereby broadening the scope of EPR-STM to nonpolar species and nonlinear excitation schemes.

| S-EPMC7527223 | biostudies-literature

The scanning electron microscope in microbiology and diagnosis of infectious disease.

Project description:Despite being an excellent tool for investigating ultrastructure, scanning electron microscopy (SEM) is less frequently used than transmission electron microscopy for microbes such as viruses or bacteria. Here we describe rapid methods that allow SEM imaging of fully hydrated, unfixed microbes without using conventional sample preparation methods. We demonstrate improved ultrastructural preservation, with greatly reduced dehydration and shrinkage, for specimens including bacteria and viruses such as Ebola virus using infiltration with ionic liquid on conducting filter substrates for SEM.

| S-EPMC4876401 | biostudies-literature

Manipulation of nanoparticles of different shapes inside a scanning electron microscope.

Project description:In this work polyhedron-like gold and sphere-like silver nanoparticles (NPs) were manipulated on an oxidized Si substrate to study the dependence of the static friction and the contact area on the particle geometry. Measurements were performed inside a scanning electron microscope (SEM) that was equipped with a high-precision XYZ-nanomanipulator. To register the occurring forces a quartz tuning fork (QTF) with a glued sharp probe was used. Contact areas and static friction forces were calculated by using different models and compared with the experimentally measured force. The effect of NP morphology on the nanoscale friction is discussed.

| S-EPMC3943919 | biostudies-literature

Direct-Write Printing of Josephson Junctions in a Scanning Electron Microscope.

Project description:Josephson junctions are the building blocks of superconducting electronics, with well-established applications in precision metrology and quantum computing. Fabricating a Josephson junction has been a resource-intensive and multistep procedure, involving lithography and wet-processing, which are not compatible with many applications. Here, we introduce a fully additive direct-write approach, where a scanning electron microscope can print substrate-conformal Josephson devices in a matter of minutes, requiring no additional processing. The junctions are made entirely by electron-beam-induced deposition (EBID) of tungsten carbide. We utilize EBID-tunable material properties to write, in one go, full proximity junctions with superconducting electrodes and metallic weak links and tailor their Josephson coupling. The Josephson behavior of these junctions is established and characterized by their microwave-induced Shapiro response and field-dependent transport. Our efforts provide a versatile and nondestructive alternative to conventional nanofabrication and can be expanded to print three-dimensional superconducting sensor arrays and quantum networks.

| S-EPMC7844821 | biostudies-literature

Scanning gate spectroscopy and its application to carbon nanotube defects.

Project description:A variation of scanning gate microscopy (SGM) is demonstrated in which this imaging mode is extended into an electrostatic spectroscopy. Continuous variation of the SGM probe's electrostatic potential is used to directly resolve the energy spectrum of localized electronic scattering in functioning, molecular scale devices. The technique is applied to the energy-dependent carrier scattering that occurs at defect sites in carbon nanotube transistors, and fitting energy-resolved experimental data to a simple transmission model determines the electronic character of each defect site. For example, a phenolic type of covalent defect is revealed to produce a tunnel barrier 0.1 eV high and 0.5 nm wide.

| S-EPMC3053432 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data