Thermal Annealing Effect on Optical Properties of Binary TiO₂-SiO₂ Sol-Gel Coatings.
Ontology highlight
ABSTRACT:
SUBMITTER: Wang X
PROVIDER: S-EPMC5452115 | biostudies-other | 2012 Dec
REPOSITORIES: biostudies-other
Similar Datasets
Project description:Titanium oxide coatings have been deposited by the sol-gel dip-coating method. Crystallization of titanium oxide coatings was then achieved through thermal annealing at temperatures above 400 °C. The structural properties and surface morphology of the crystallized coatings were studied by micro-Raman spectroscopy and atomic force microscopy, respectively. Characterization technique, based on least-square fitting to the measured reflectance and transmittance spectra, is used to determine the refractive indices of the crystallized TiO₂ coatings. The stability of the synthesized sol was also investigated by dynamic light scattering particle size analyzer. The influence of the thermal annealing on the optical properties was then discussed. The increase in refractive index with high temperature thermal annealing process was observed, obtaining refractive index values from 1.98 to 2.57 at He-Ne laser wavelength of 633 nm. The Raman spectroscopy and atomic force microscopy studies indicate that the index variation is due to the changes in crystalline phase, density, and morphology during thermal annealing.
| S-EPMC5521283 | biostudies-other
Project description:Pure and Fe-doped TiO2 nanoparticles were synthesized by the sol-gel method. The samples were characterized by X-ray diffraction, Raman spectroscopy, BET, UV-vis diffuse reflectance spectroscopy, and scanning electron microscopy. The results show a dependence between the crystallite size and the amount of dopant, which decreases from 13.02 to 12.81 nm. The same behavior was observed in the optical properties, where the band gap decreased from 3.2 to 2.86 eV. The arsenic (V) adsorption was tested in aqueous solution containing 5 mg/L of arsenic and 0.5 g/L of adsorbent at pH 7 and in dark conditions. The results indicate that the TiO2-B sample shows a higher arsenic removal, reaching 88% arsenic removal from the water at pH 7. Thus, it is also shown that the best performance occurs at pH 5, where it reaches an arsenic removal of 94%. Ion competition studies show that arsenic removal capacity is slightly affected by chloride, carbonate, nitrate, and sulfate ions. According to the results, the synthesized samples are a promising material for treating arsenic-contaminated water.
| S-EPMC9565318 | biostudies-literature
Project description:Self-healing polymers are a new class of material that has recently received a lot of attention because of the lifespan improvement it could bring to multiple applications. One of the major challenges is to obtain multifunctional materials which can self-heal and exhibit other interesting properties such as protection against corrosion. In this paper, the effect of the incorporation of an aminosilane on the properties of a self-healing organic polymer containing disulfide bond is studied on films and coatings for aluminium AA2024-T3 using simple one step in situ synthesis. Hybrid coatings with enhanced anticorrosion properties measured by EIS were obtained thanks to the formation of a protective oxide interface layer, while exhibiting wound closure after exposition at 75 °C. The thermal, mechanical and rheological properties of the films with different aminosilane amounts were characterized in order to understand the influence of the slight presence of the inorganic network. Stiffer and reprocessable hybrid films were obtained, capable to recover their mechanical properties after healing. The nanocomposite structure, confirmed by TEM, had a positive effect on the self-healing and stress relaxation properties. These results highlight the potential of sol-gel chemistry to obtain efficient anticorrosion and self-healing coatings.
| S-EPMC8465503 | biostudies-literature
Project description:Sol-gel monoliths based on SiO2, TiO2 and ZrO2 with holographic colourful diffraction on their surfaces were obtained via a sol-gel synthesis and soft lithography combined method. The production was carried out without any additional equipment at near room temperature and atmospheric pressure. The accurately replicated wavy structure with nanoscale size of material particles yields holographic effect and its visibility strongly depends on refractive index (RI) of materials. Addition of multi-walled carbon nanotubes (MWCNTs) in systems increases their RI and lends absorbing properties due to extremely high light absorption constant. Further prospective and intriguing applications based on the most successful samples, MWCNTs-doped titania, were investigated as reversible optical humidity sensor. Owing to such property as reversible resuspension of TiO2 nanoparticles while interacting with water, it was proved that holographic xerogels can repeatedly act as humidity sensors. Materials which can be applied as humidity sensors in dependence on holographic response were discovered for the first time.
| S-EPMC5990830 | biostudies-literature
Project description:Infection is one of the most common causes that leads to joint prosthesis failure. In the present work, biodegradable sol-gel coatings were investigated as a promising controlled release of antibiotics for the local prevention of infection in joint prostheses. Accordingly, a sol-gel formulation was designed to be tested as a carrier for 8 different individually loaded antimicrobials. Sols were prepared from a mixture of MAPTMS and TMOS silanes, tris(tri-methylsilyl)phosphite, and the corresponding antimicrobial. In order to study the cross-linking and surface of the coatings, a battery of examinations (Fourier-transform infrared spectroscopy, solid-state 29Si-NMR spectroscopy, thermogravimetric analysis, SEM, EDS, AFM, and water contact angle, thickness, and roughness measurements) were conducted on the formulations loaded with Cefoxitin and Linezolid. A formulation loaded with both antibiotics was also explored. Results showed that the coatings had a microscale roughness attributed to the accumulation of antibiotics and organophosphites in the surface protrusions and that the existence of chemical bonds between antibiotics and the siloxane network was not evidenced.
| S-EPMC9317242 | biostudies-literature
Project description:For environmental applications, nanosized TiO2-based materials are known as the most important photocatalyst and are intensively studied for their advantages such as their higher activity, lower price, and chemical and photoresist properties. Zn or Cu doped TiO2 nanoparticles with anatase crystalline structure were synthesized by sol-gel process. Titanium (IV) butoxide was used as a TiO2 precursor, with parental alcohol as a solvent, and a hydrolysing agent (ammonia-containing water) was added to obtain a solution with pH 10. The gels were characterized by TG/DTA analysis, SEM, and XPS. Based on TG/DTA results, the temperature of 500 °C was chosen for processing the powders in air. The structure of the samples thermally treated at 500 °C was analysed by XRD and the patterns show crystallization in a single phase of TiO2 (anatase). The surface of the samples and the oxidation states was investigated by XPS, confirming the presence of Ti, O, Zn and Cu. The antibacterial activity of the nanoparticle powder samples was verified using the gram-positive bacterium Staphylococcus aureus. The photocatalytic efficiency of the doped TiO2 nanopowders for degradation of methyl orange (MO) is here examined in order to evaluate the potential applications of these materials for environmental remediation.
| S-EPMC9601293 | biostudies-literature
Project description:Sol-gel processing is an attractive method for large-scale surface coating due to its facile and inexpensive preparation, even with the inclusion of precision nanotopographies. These are desirable traits for metal orthopaedic prostheses where ceramic coatings are known to be osteoinductive and the effects may be amplified through nanotexturing. However there are a few concerns associated with the application of sol-gel technology to orthopaedics. Primarily, the annealing stage required to transform the sol-gel into a ceramic may compromise the physical integrity of the underlying metal. Secondly, loose particles on medical implants can be carcinogenic and cause inflammation so the coating needs to be strongly bonded to the implant. These concerns are addressed in this paper. Titanium, the dominant material for orthopaedics at present, is examined before and after sol-gel processing for changes in hardness and flexural modulus. Wear resistance, bending and pull tests are also performed to evaluate the ceramic coating. The findings suggest that sol-gel coatings will be compatible with titanium implants for an optimum temperature of 500 °C.
| S-EPMC4686541 | biostudies-literature
Project description:Solar drying is a sustainable process that may impact the quality of dried food. This is because, pigments contained in food are sensitive to sunlight, and exposure to ultraviolet radiation can affect them. We applied biopolymer-based coatings on strawberry, from hydro-colloidal solutions of Opuntia ficus indica-mucilage, fenugreek, xanthan gum, gum Arabic, and guar gum to evaluate their potential use as UV filters for solar drying of food. Thermal properties and the optical transmittance, absorbance and reflectance of the coatings were measured to assess their influence on food-sunlight interaction. During the drying experiments, the moisture content, total anthocyanins (TA), and total phenolic compounds (TPC) were measured. Optical and thermal properties are influenced by the biopolymer-based coatings. Also, the optical properties are influenced by the coating thickness. The differences in optical and thermal properties influence the drying process. Differences exist in the drying rate for strawberry slices with coating, compared with those without the coatings. In general, the TA and TPC content in the product are better preserved under solar drying than in control experiments done in a drying oven. A partial transmittance of solar UV radiation is recommended to obtain increased TA and TPC contents in the dried product.
| S-EPMC8115689 | biostudies-literature
Project description:PurposeTo evaluate the efficacy of a nanosilver-based sol-gel coating in preventing biofilm formation on contact lens cases.MethodsAn organic-inorganic hybrid silica-zirconia sol formulation with immobilized silver nanoparticles was deposited on contact lens case coupons. The coated and uncoated coupons were subjected to biofilm formation to Gram-negative and Gram-positive keratitis isolates and ATCC strains using a standard protocol. The biofilms were evaluated using crystal violet, MTT assay, and scanning electron microscope (SEM) examination. The duration of efficacy of the coating was evaluated by exposing the coated and uncoated coupons to a multipurpose lens cleaning solution for various durations up to 30 days and comparing their biofilm characteristics. The cytotoxicity of the coated surface was assessed using cell culture studies.ResultsCross-hatch tests and SEM confirmed the presence of a uniform, well-adhered coating on the surface. The coating resulted in a nearly 95% reduction in biofilm formation of the tested bacteria and was effective despite exposures of up to 30 days to a multipurpose lens cleaning solution. The coating did not exhibit cytotoxicity to human corneal epithelial cells.ConclusionsThe silver nanoparticle-based coating exhibits a good antibiofilm property for both Gram-negative bacilli and Gram-positive cocci and is promising for commercial use in preventing contact lens-related infections.Translational relevanceBiofilm formation on lens cases continues to be an important concern. The proposed coating will help reduce such formations, thus reducing the risk of lens-associated microbial keratitis.
| S-EPMC7794269 | biostudies-literature
Project description:The SiO2/TiO2/Nb2O5 material was set by the sol-gel method and was characterized by several techniques through thermogravimetric, spectroscopic, and textural analyzes. For the two synthesized materials, the specific surface area was 350.0 and 494.0 m2 g-1 (SiTiNb-A and SiTiNb-B, respectively). An enhance of the crystalline order with the temperature increase of the thermal treatment was observed. Through X-ray Photoelectron Spectroscopy analysis, the binding energy values for the Ti 2p and Nb 3d levels showed the insertion of Ti and Nb atoms in the silica matrix. The Electron Dispersive Spectroscopy analyses also confirmed the high dispersion of the metals presented on the materials surface. The Thermogravimetric Analysis showed weight loss for the of 37.6% (SiTiNb-A) and 29.7% (SiTiNb-B). The presence of the crystalline phases TiO2-anatase and monoclinic-Nb2O5 in the materials was confirmed through the data obtained by association of powder X-ray Diffraction and FT-Raman. Values obtained from optical band-gap aimed the dependence of the oxides concentration and the calcination temperature. Finally, the pyridine adsorption studies have indicated the presence of Lewis and Brønsted acid sites.
| S-EPMC7806853 | biostudies-literature