Low Stress Mechanical Properties of Plasma-Treated Cotton Fabric Subjected to Zinc Oxide-Anti-Microbial Treatment.

ABSTRACT: Cotton fabrics are highly popular because of their excellent properties such as regeneration, bio-degradation, softness, affinity to skin and hygroscopic properties. When in contact with the human body, cotton fabrics offer an ideal environment for microbial growth due to their ability to retain oxygen, moisture and warmth, as well as nutrients from spillages and body sweat. Therefore, an anti-microbial coating formulation (Microfresh and Microban together with zinc oxide as catalyst) was developed for cotton fabrics to improve treatment effectiveness. In addition, plasma technology was employed in the study which roughened the surface of the materials, improving the loading of zinc oxides on the surface. In this study, the low stress mechanical properties of plasma pre-treated and/or anti-microbial-treated cotton fabric were studied. The overall results show that the specimens had improved bending properties when zinc oxides were added in the anti-microbial coating recipe. Also, without plasma pre-treatment, anti-microbial-treatment of cotton fabric had a positive effect only on tensile resilience, shear stress at 0.5° and compressional energy, while plasma-treated specimens had better overall tensile properties even after anti-microbial treatment.

SUBMITTER: Kan CW

PROVIDER: S-EPMC5452122 | biostudies-other | 2013 Jan

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:Surface-initiated photopolymerization has been run to synthesize a hydrogel with ZnO particles distributed uniformly along its structure, which has been loaded onto a polyamide fabric. Three samples have been obtained at different concentrations of zinc nitrate (10% (sample PA10); 20% (sample PA20) and 30% (sample PA30) of the weight of the fabric, respectively)) and subjected to gravimetric analysis, scanning electron microscopy and transmission electron microscopy. The effect of the adsorption parameters of the composite material on the removal Drimaren Rot K-7B dye from water has been studied. The Freundlich isotherm describes this process better than the Langmuir isotherm. As the results of the adsorption kinetics show, the process fits well with a pseudo-second-order equation and depends both on the boundary layer and on the structure of the adsorbent itself. The thermodynamic parameters have demonstrated that the process is endothermic and physical. When exposed to ultraviolet light, the discoloration of the dye solution accelerates due to the photocatalytic properties of the composite materials. The addition of H2O2 also speeds up further the process, while the reuse of the materials slows it down, gradually changing the kinetic parameters. The reaction has been attributed to first-order kinetic model, when the active centers of the materials and the number of oxidative radicals formed are numerous and to the second-order kinetic model at a lower reaction activity. Moreover, 52% decolorization of the dye solution (50 mg L-1) in the dark was achieved from composite material PA 30 (13.3 g L-1) in 120 min and 89% under UV light irradiation. The H2O2 addition (0.14 mmol L-1) enhanced it up to 98%. In the second and third use of the photocatalyst, the dye removal decreased to 80% and 60%. Composite material PA30 exhibits antibacterial activity against Gram-negative bacteria E. coli, being most effective at eliminating Gram-positive bacteria S. aureus.

Dataset Information

Low Stress Mechanical Properties of Plasma-Treated Cotton Fabric Subjected to Zinc Oxide-Anti-Microbial Treatment.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets