Developing a Sealing Material: Effect of Epoxy Modification on Specific Physical and Mechanical Properties.

ABSTRACT: To develop a matched sealing material for socket rehabilitation of grey cast iron pipes, an epoxy resin is modified by the addition of different components to improve the flexibility. Three different modifications are made by adding ethylene-propylene diene monomer (EPDM) rubber powder, reactive liquid polymer (ATBN) and epoxidized modifier. In this paper the effect of the modification method as well as the influence of absorption of water on the mechanical and physical properties are analyzed in terms of: tensile strength, modulus of elasticity, adhesion performance, pressure resistance, glass transition temperature and water content. A comparison with neat epoxy shows for all materials that the modulus of elasticity and strength decrease. Unlike other tested modification methods, the modification with rubber powder did not enhance the flexibility. All materials absorb water and a plasticization effect arises with further changes of mechanical and physical properties. The application of the sealant on the grey cast iron leads to a reduction of the strain at break (in comparison to the common tensile test of the pure materials) and has to be evaluated. The main requirement of pressure resistance up to 1 MPa was tested on two chosen materials. Both materials fulfill this requirement.

SUBMITTER: Schoberleitner C

PROVIDER: S-EPMC5452763 | biostudies-other | 2013 Nov

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Evaluation of Mechanical, Physical, and Morphological Properties of Epoxy Composites Reinforced with Different Date Palm Fillers.

Project description:The present study deals with the fabrication of epoxy composites reinforced with 50 wt% of date palm leaf sheath (G), palm tree trunk (L), fruit bunch stalk (AA), and leaf stalk (A) as filler by the hand lay-up technique. The developed composites were characterized and compared in terms of mechanical, physical and morphological properties. Mechanical tests revealed that the addition of AA improves tensile (20.60-40.12 MPa), impact strength (45.71-99.45 J/m), flexural strength (32.11-110.16 MPa) and density (1.13-1.90 g/cm3). The water absorption and thickness swelling values observed in this study were higher for AA/epoxy composite, revealing its higher cellulosic content, compared to the other composite materials. The examination of fiber pull-out, matrix cracks, and fiber dislocations in the microstructure and fractured surface morphology of the developed materials confirmed the trends for mechanical properties. Overall, from results analysis it can be concluded that reinforcing epoxy matrix with AA filler effectively improves the properties of the developed composite materials. Thus, date palm fruit bunch stalk filler might be considered as a sustainable and green promising reinforcing material similarly to other natural fibers and can be used for diverse commercial, structural, and nonstructural applications requiring high mechanical resistance.

| S-EPMC6651275 | biostudies-literature

The Effect of Manufacture Process on Mechanical Properties and Burning Behavior of Epoxy-Based Hybrid Composites.

Project description:The production of hybrid layered composites allows comprehensive modification of their properties and adaptation to the final expectations. Different methods, such as hand lay-up, vacuum bagging, and resin infusion were applied to manufacture the hybrid composites. In turn, fabrics used for manufacturing composites were made of glass (G), aramid (A), carbon (C), basalt (B), and flax (F) fibers. Flexural, puncture impact behavior, and cone calorimetry tests were applied to establish the effect of the manufacturing method and the fabrics layout on the mechanical and fire behavior of epoxy-based laminates. The lowest flammability and smoke emission were noted for composites made by vacuum bagging (approximately 40% lower values of total smoke release compared with composites made by the hand lay-up method). It was demonstrated that multi-layer hybrid composites made by vacuum bagging might enhance the fire safety levels and simultaneously maintain high mechanical properties designed for, e.g., the railway and automotive industries.

| S-EPMC8746176 | biostudies-literature

Short- and Long-Term Epoxy Modification of Bitumen: Modification Kinetics, Rheological Properties, and Microstructure.

Project description:Aiming to gain knowledge in the epoxy-bitumen modification mechanisms, this work explores the effects that epoxy concentration and ambient curing exert on the physico-chemistry and thermo-rheological properties of epoxy-modified binders. Process rheokinetics of epoxy-bitumen blends indicates that binder short-term modification (i.e., during processing) is accelerated by epoxy concentration. Furthermore, a synergistic effect of epoxy concentration and ambient curing is found during long-term modification (i.e., during curing at ambient conditions). As a result, viscous and viscoelastic rheological properties of binders are enhanced at medium/high in-service temperatures, at least, after one month of curing. FTIR (Fourier Transform Infrared spectroscopy) tests and SARAs (Saturates, Aromatics, Resins and Asphaltenes) analysis confirm the existence of esterification/etherification reactions between epoxy oxirane groups and the carbonyl groups available in aromatic and resin molecules. Thus, the new high molecular weight compounds increase the asphaltenic fraction of modified bitumen. Likewise, nonreversing heat flow curves obtained by modulated calorimetry corroborate the formation of such highly structured domains responsible for the final binder performance.

| S-EPMC7182878 | biostudies-literature

Physical limits to sensing material properties.

Project description:All materials respond heterogeneously at small scales, which limits what a sensor can learn. Although previous studies have characterized measurement noise arising from thermal fluctuations, the limits imposed by structural heterogeneity have remained unclear. In this paper, we find that the least fractional uncertainty with which a sensor can determine a material constant λ0 of an elastic medium is approximately [Formula: see text] for a ≫ d ≫ ξ, [Formula: see text], and D > 1, where a is the size of the sensor, d is its spatial resolution, ξ is the correlation length of fluctuations in λ0, Δλ is the local variability of λ0, and D is the dimension of the medium. Our results reveal how one can construct devices capable of sensing near these limits, e.g. for medical diagnostics. We use our theoretical framework to estimate the limits of mechanosensing in a biopolymer network, a sensory process involved in cellular behavior, medical diagnostics, and material fabrication.

| S-EPMC7560877 | biostudies-literature

Lignin-Based Epoxy Resins: Unravelling the Relationship between Structure and Material Properties.

Project description:Here we investigate the relationship between thermomechanical properties and chemical structure of well-characterized lignin-based epoxy resins. For this purpose, technical lignins from eucalyptus and spruce, obtained from the Kraft process, were used. The choice of lignins was based on the expected differences in molecular structure. The lignins were then refined by solvent fractionation, and three fractions with comparable molecular weights were selected to reduce effects of molar mass on the properties of the final thermoset resins. Consequently, any differences in thermomechanical properties are expected to correlate with molecular structure differences between the lignins. Oxirane moieties were selectively introduced to the refined fractions, and the resulting lignin epoxides were subsequently cross-linked with two commercially available polyether diamines (Mn = 2000 and 400) to obtain lignin-based epoxy resins. Molecular-scale characterization of the refined lignins and their derivatives were performed by 31P NMR, 2D-NMR, and DSC methods to obtain the detailed chemical structure of original and derivatized lignins. The thermosets were studied by DSC, DMA, and tensile tests and demonstrated diverse thermomechanical properties attributed to structural components in lignin and selected amine cross-linker. An epoxy resin with a lignin content of 66% showed a Tg of 79 °C from DMA, Young's modulus of 1.7 GPa, tensile strength of 66 MPa, and strain to failure of 8%. The effect of molecular lignin structure on thermomechanical properties was analyzed, finding significant differences between the rigid guaiacyl units in spruce lignin compared with sinapyl units in eucalyptus lignin. The methodology points toward rational design of molecularly tailored lignin-based thermosets.

| S-EPMC7997103 | biostudies-literature

Preparation, Thermal Analysis, and Mechanical Properties of Basalt Fiber/Epoxy Composites.

Project description:In this study, basalt fiber-reinforced polymer (BFRP) composites with epoxy matrix, 20 layers, and volume fraction of fibers Vf = 53.66%, were prepared by a hand lay-up compression molding combined method. The fabric of the basalt fibers is in twill 2/2 weave. Through dynamic mechanical analysis (DMA), their viscoelastic behavior at elevated temperatures and in various frequencies was explored, whereas thermomechanical analysis (TMA) took part in terms of creep recovery and stress-relaxation tests. Moreover, the glass transition temperature (Tg) of the BFRP composites was determined through the peak of the tan? curves while the decomposition of the BFRP composites and basalt fibers, in air or nitrogen atmosphere, was explored through thermogravimetric analysis (TGA). The mechanical behavior of the BFRP composites was investigated by tensile and three-point bending experiments. The results showed that as the frequency is raised, the BFRP composites can achieve slightly higher Tg while, under the same circumstances, the storage modulus curve obtains a less steep decrease in the middle transition region. Moreover, the hand lay-up compression molding hybrid technique can be characterized as efficient for the preparation of polymer matrix composites with a relatively high Vf of over 50%. Remarkably, through the TGA experiments, the excellent thermal resistance of the basalt fibers, in the temperature range 30-900 °C, was revealed.

| S-EPMC7465910 | biostudies-literature

Mechanical properties of epoxy nanocomposites filled with melamine functionalized molybdenum disulfide.

Project description:In this work, a melamine functionalized molybdenum disulfide (M-MoS2) was prepared and used as fillers to form epoxy (EP)/MoS2 nanocomposites. The effects of molybdenum disulfide (MoS2) and melamine functionalized molybdenum disulfide (M-MoS2) loading on the mechanical properties of epoxy composites were investigated and compared. With only addition of 0.8 wt% M-MoS2, the tensile strength and modulus of EP/M-MoS2 nanocomposites showed 4.5 and 4.0 times increase over the neat epoxy. Interestingly, the elongation at break value of EP was also increased with the introduction of M-MoS2 fillers. These properties could result from the good dispersion and strong interfacial adhesion of M-MoS2 fillers and the EP matrix. Therefore, this work provides a facile way to produce of high-performance EP nanocomposites.

| S-EPMC9080842 | biostudies-literature

Effect of Nanoparticles Surface Bonding and Aspect Ratio on Mechanical Properties of Highly Cross-Linked Epoxy Nanocomposites: Mesoscopic Simulations.

Project description:The paper aims to study the mechanical properties of epoxy resin filled with clay nanoparticles (NPs), depending on their shapes and content on the surface of a modifying agent capable of forming covalent bonds with a polymer. The cylindrical clay nanoparticles with equal volume and different aspects ratios (disks, barrel, and stick) are addressed. The NPs' bonding ratio with the polymer (RGC) is determined by the fraction of reactive groups and conversion time and varies from RGC = 0 (non-bonded nanoparticles) to RGC = 0.65 (more than half of the surface groups are linked with the polymer matrix). The performed simulations show the so-called load-bearing chains (LBCs) of chemically cross-linked monomers and modified nanoparticles to determine the mechanical properties of the simulated composites. The introduction of nanoparticles leads to the breaking of such chains, and the chemical cross-linking of NPs with the polymer matrix restores the LBCs and strengthens the composite. At small values of RGC, the largest value of the elastic modulus is found for systems filled with nanoparticles having the smallest surface area, and at high values of RGC, on the contrary, the systems containing disk-shaped particles with the largest surface area have a larger elastic modulus than the others. All calculations are performed within the framework of a mesoscopic model based on accurate mapping of the atomistic structures of the polymer matrix and nanoparticles into coarse-grained representations, which, if necessary, allow reverse data mapping and quantitative assessment of the state of the filled epoxy resin. On the other hand, the obtained data can be used to design the functional materials with specified mechanical properties based on other practically significant polymer matrices and nanofillers.

| S-EPMC8587117 | biostudies-literature

Variation of mechanical and thermal properties in sustainable graphene oxide/epoxy composites.

Project description:In this work, the functional graphene oxide (bGO) was facilely synthesized through a grafted reaction between graphene oxide (GO) and bio-based bis-furan di-epoxide (BFDE). The structure of bGO was confirmed by FTIR spectra and Raman spectra. The properties of polymer composite materials depend on the distribution of the nanofiller in the matrix and due to the presence of polymer chains our bGO sheets exhibit a better dispersibility in solvents and polymer matrix, which provides a potential opportunity for the preparation of BFDE composites with excellent performance. Bio-based BFDE composites containing 0.05-0.5 wt.% of bGO exhibit superior mechanical and thermal properties. The addition of just 0.5?wt% such bGO to an BFDE causes 80%, 49%, 21%, 69% and 97% enhancement in tensile strength, flexural strength, flexural modulus, critical stress intensity factor and critical strain energy release rate, respectively. The thermal decomposition temperature Td of bGO/BFDE composites was increased about ~17?°C compared to blank BFDE sample. In addition, we found that introducing unmodified GO to epoxy matrix lead to an insignificant increase of the thermal property of the resulting GO/BFDE composites. The enhanced mechanical properties and thermal properties of bGO/BFDE composites could be attributed to strong interfacial interactions and high affinity between bGO and epoxy matrix.

| S-EPMC6224379 | biostudies-literature

Physical and Mechanical Characterization of Titica Vine (Heteropsis flexuosa) Incorporated Epoxy Matrix Composites.

Project description:Titica vine (Heteropsis flexuosa) is a typical plant of the Amazon region commonly used for making baskets, bags, brooms and furniture, owing to its stiff fibers. In spite of its interesting properties, there is so far no reported information regarding the use of titica vine fibers (TVFs) in engineering composite materials. In this work, the TVF and its epoxy composites were for the first time physically, thermally and mechanically characterized. Additionally, the effect of two kinds of chemical treatments, one with sodium carbonate and one with calcium lignosulfonate, as well as different volume fractions, 10, 20, 30 and 40 vol%, of TVF-reinforced composites were assessed for corresponding basic properties. The thermogravimetric results of the composites reveal enhanced thermal stability for higher TVF content. In addition, the composite incorporated with 40 vol% of TVFs treated with sodium carbonate absorbed 19% more water than the composites with untreated fibers. By contrast, the calcium lignosulfonate treatment decreased water absorption by 8%. The Charpy and Izod impact tests showed that the composites, incorporated with the highest investigated volume fraction (40 vol%) of TVF, significantly increased the absorbed energy by 18% and 28%, respectively, compared to neat epoxy. ANOVA and Tukey statistical analyses displayed no direct influence of the chemical treatments on the energy absorption of the composites for either impact tests. SEM images revealed the main fracture mechanisms responsible for the performance of TVF composites.

| S-EPMC8659021 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data