Effect of Stretching on Ultraviolet Protection of Cotton and Cotton/Coolmax Blended Weft Knitted Fabric in a Wet State.

ABSTRACT: In this paper, the ultraviolet protection factor (UPF) of plain knitted fabrics made from 20Ne cotton yarns, Coolmax yarn and their combinations in wet, relaxed and stretched states were studied. According to the fiber composition, fabric samples are divided into three groups including Group I (single cotton yarn), Group II (cotton/cotton combination) and Group III (Coolmax/cotton combination) for discussion. In order to study the effect of wet condition on the UPF of different plain knitted fabrics, five wetting solutions, namely: (i) chlorinated pool water; (ii) sea water, (iii) acidic perspiration; (iv) alkaline perspiration and (v) deionized water (DI water) were prepared and the fabrics were wetted with different percentages of 50%, 75% and 100%. The UPF of the plain knitted fabrics in wet, relaxed and stretched states was measured and the results were discussed. In addition, yarn and fabric properties such as yarn tenacity, yarn strength, fiber combination and water vapor transmission, which affect the corresponding UPF values, were used for generating a prediction model in order to determine UPF. Verification of the prediction model was also conducted.

SUBMITTER: Kan CW

PROVIDER: S-EPMC5453141 | biostudies-other | 2013 Dec

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:The urgent demand for scalable, potent, color variable, and comfortable antimicrobial textiles as personal protection equipment (PPE) to help reduce infection transmission in hospitals and healthcare facilities has significantly increased since the start of the COVID-19 pandemic. Here, we explored photodynamic antimicrobial polyethylene terephthalate/cotton (TC) blended fabrics comprised of photosensitizer-conjugated cotton fibers and polyethylene terephthalate (PET) fibers dyed with disperse dyes. A small library of TC blended fabrics was constructed wherein the PET fibers were embedded with traditional disperse dyes dominating the fabric color, thereby enabling variable color expression, while the cotton fibers were covalently coupled with the photosensitizer thionine acetate as the microbicidal agent. Physical (SEM, CLSM, TGA, XPS and mechanical strength) and colorimetric (K/S and CIELab values) characterization methods were employed to investigate the resultant fabrics, and photooxidation studies with DPBF demonstrated the ability of these materials to generate reactive oxygen species (i.e., singlet oxygen) upon visible light illumination. The best results demonstrated a photodynamic inactivation of 99.985% (~ 3.82 log unit reduction, P = 0.0021) against Gram-positive S. aureus, and detection limit inactivation (99.99%, 4 log unit reduction, P ≤ 0.0001) against Gram-negative E. coli upon illumination with visible light (60 min; ~ 300 mW/cm2; λ ≥ 420 nm). Enveloped human coronavirus 229E showed a photodynamic susceptibility of ~ 99.99% inactivation after 60 min illumination (400-700 nm, 65 ± 5 mW/cm2). The presence of the disperse dyes on the fabrics showed no significant effects on the aPDI results, and furthermore, appeared to provide the photosensitizer with some measure of protection from photobleaching, thus improving the photostability of the dual-dyed fabrics. Taken together, these results suggest the feasibility of low cost, scalable and color variable thionine-conjugated TC blended fabrics as potent self-disinfecting textiles.

Dataset Information

Effect of Stretching on Ultraviolet Protection of Cotton and Cotton/Coolmax Blended Weft Knitted Fabric in a Wet State.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets