Performance Comparison of Al-Ti Master Alloys with Different Microstructures in Grain Refinement of Commercial Purity Aluminum.

ABSTRACT: Three types of Al-5Ti master alloys were synthesized by a method of thermal explosion reaction in pure molten aluminum. Performance comparison of Al-5Ti master alloy in grain refinement of commercial purity Al with different additions (0.6%, 1.0%, 1.6%, 2.0%, and 3.0%) and holding time (10, 30, 60 and 120 min) were investigated. The results show that Al-5Ti master alloy with blocky TiAl₃ particles clearly has better refining efficiency than the master alloy with mixed TiAl₃ particles and the master alloy with needle-like TiAl₃ particles. The structures of master alloys, differing by sizes, morphologies and quantities of TiAl₃ crystals, were found to affect the pattern of the grain refining properties with the holding time. The grain refinement effect was revealed to reduce markedly for master alloys with needle-like TiAl₃ crystals and to show the further significant improvement at a longer holding time for the master alloy containing both larger needle-like and blocky TiAl₃ particles. For the master alloy with finer blocky particles, the grain refining effect did not obviously decrease during the whole studied range of the holding time.

SUBMITTER: Ding W

PROVIDER: S-EPMC5453226 | biostudies-other | 2014 May

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:Coating system(s) will be required for Nb-silicide based alloys. Alumina forming alloys that are chemically compatible with the Nb-silicide based alloy substrate could be components of such systems. The intermetallic alloys Nb1.45Si2.7Ti2.25Al3.25Hf0.35 (MG5) and Nb1.35Si2.3Ti2.3Al3.7Hf0.35 (MG6) were studied in the cast, heat treated and isothermally oxidised conditions at 800 and 1200 °C to find out if they are αAl₂O₃ scale formers. A (Al/Si)alloy versus Nb/(Ti + Hf)alloy map, which can be considered to be a map for Multi-Principle Element or Complex Concentrated Nb-Ti-Si-Al-Hf alloys, and a [Nb/(Ti + Hf)]Nb5Si3 versus [Nb/(Ti + Hf)]alloy map were constructed making use of the alloy design methodology NICE and data from a previously studied alloy, and were used to select the alloys MG5 and MG6 that were expected (i) not to pest, (ii) to form αAl₂O₃ scale at 1200 °C, (iii) to have no solid solution, (iv) to form only hexagonal Nb₅Si₃ and (v) to have microstructures consisting of hexagonal Nb₅Si₃, Ti₅Si₃, Ti₅Si₄, TiSi silicides, and tri-aluminides and Al rich TiAl. Both alloys met the requirements (i) to (v). The alumina scale was able to self-heal at 1200 °C. Liquation in the alloy MG6 at 1200 °C was linked with the formation of a eutectic like structure and the TiAl aluminide in the cast alloy. Key to the oxidation of the alloys was the formation (i) of "composite" silicide grains in which the Nb₅Si₃ core was surrounded by the Ti₅Si₄ and TiSi silicides, and (ii) of tri-aluminides with high Al/Si ratio, particularly at 1200 °C and very low Nb/Ti ratio forming in-between the "composite" silicide grains. Both alloys met the "standard definition" of high entropy alloys (HEAs). Compared with HEAs with bcc solid solution and intermetallics, the VEC values of both the alloys were outside the range of reported values. The parameters VEC,  and  of Nb-Ti-Si-Al-Hf coating alloys and non-pesting Nb-silicide based alloys were compared and trends were established. Selection of coating alloys with possible "layered" structures was discussed and alloy compositions were proposed.

Dataset Information

Performance Comparison of Al-Ti Master Alloys with Different Microstructures in Grain Refinement of Commercial Purity Aluminum.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure