Grain Refinement Efficiency in Commercial-Purity Aluminum Influenced by the Addition of Al-4Ti Master Alloys with Varying TiAl₃ Particles.

ABSTRACT: A series of Al-4Ti master alloys with various TiAl₃ particles were prepared via pouring the pure aluminum added with K₂TiF₆ or sponge titanium into three different molds made of graphite, copper, and sand. The microstructure and morphology of TiAl₃ particles were characterized and analyzed by scanning electron microscope (SEM) with energy dispersive spectroscopy (EDS). The microstructure of TiAl₃ particles in Al-4Ti master alloys and their grain refinement efficiency in commercial-purity aluminum were investigated in this study. Results show that there were three different morphologies of TiAl₃ particles in Al-4Ti master alloys: petal-like structures, blocky structures, and flaky structures. The Al-4Ti master alloy with blocky TiAl₃ particles had better and more stable grain refinement efficiency than the master alloys with petal-like and flaky TiAl₃ particles. The average grain size of the refined commercial-purity aluminum always hereditarily followed the size of the original TiAl₃ particles. In addition, the grain refinement efficiency of Al-4Ti master alloys with the same morphology, size, and distribution of TiAl₃ particles prepared through different processes was almost identical.

SUBMITTER: Zhao J

PROVIDER: S-EPMC5457244 | biostudies-other | 2016 Oct

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Performance Comparison of Al-Ti Master Alloys with Different Microstructures in Grain Refinement of Commercial Purity Aluminum.

Project description:Three types of Al-5Ti master alloys were synthesized by a method of thermal explosion reaction in pure molten aluminum. Performance comparison of Al-5Ti master alloy in grain refinement of commercial purity Al with different additions (0.6%, 1.0%, 1.6%, 2.0%, and 3.0%) and holding time (10, 30, 60 and 120 min) were investigated. The results show that Al-5Ti master alloy with blocky TiAl₃ particles clearly has better refining efficiency than the master alloy with mixed TiAl₃ particles and the master alloy with needle-like TiAl₃ particles. The structures of master alloys, differing by sizes, morphologies and quantities of TiAl₃ crystals, were found to affect the pattern of the grain refining properties with the holding time. The grain refinement effect was revealed to reduce markedly for master alloys with needle-like TiAl₃ crystals and to show the further significant improvement at a longer holding time for the master alloy containing both larger needle-like and blocky TiAl₃ particles. For the master alloy with finer blocky particles, the grain refining effect did not obviously decrease during the whole studied range of the holding time.

| S-EPMC5453226 | biostudies-other

Cyclic Deformation of Ultra-Fine Grained Commercial Purity Aluminum Processed by Accumulative Roll-Bonding.

Project description:Accumulative Roll-Bonding (ARB) is one of the more recently developed techniques capable of producing bulk ultra-fine grained (ufg) metals. There are still many aspects of the behavior of ufg metals that lacks an in-depth understanding, such as a generalized view of the factors that govern the cyclic deformation mechanism(s). This study aims to advance the understanding of the cyclic deformation behavior of ufg metals through the systematic investigation of ARB processed aluminum upon cyclic loading. It was found that the cyclic softening response often reported for ufg metals is largely influenced by the microstructure stability as the cyclic softening response is facilitated by grain coarsening which becomes inhibited with highly stable microstructure. On one hand, shear bands resembling braids of dislocations trespassing multiple grains have been observed to operate for the accommodation of the imposed cyclic strain in cases where grain coarsening is largely restricted. On the other hand, it was found that the microstructure stability can be overcome at higher applied cyclic plastic strain levels, leading to grain coarsening and thus a cyclic softening response. The findings in this study have further confirmed that the cyclic softening behavior found in many ufg metals, which may be detrimental in practical applications, can be inhibited by improvements in the microstructure stability.

| S-EPMC5521316 | biostudies-other

Materials informatics approach to understand aluminum alloys.

Project description:The relations between the mechanical properties, heat treatment, and compositions of elements in aluminum alloys are extracted by a materials informatics technique. In our strategy, a machine learning model is first trained by a prepared database to predict the properties of materials. The dependence of the predicted properties on explanatory variables, that is, the type of heat treatment and element composition, is searched using a Markov chain Monte Carlo method. From the dependencies, a factor to obtain the desired properties is investigated. Using targets of 5000, 6000, and 7000 series aluminum alloys, we extracted relations that are difficult to find via simple correlation analysis. Our method is also used to design an experimental plan to optimize the materials properties while promoting the understanding of target materials.

| S-EPMC7476514 | biostudies-literature

Training high-strength aluminum alloys to withstand fatigue.

Project description:The fatigue performance of high strength aluminum alloys used in planes, trains, trucks and automobiles is notoriously poor. Engineers must design around this important limitation to use Al alloys for light-weighting of transportation structures. An alternative concept for microstructure design for improved fatigue strength is demonstrated in this work. Microstructures are designed to exploit the mechanical energy imparted during the initial cycles of fatigue to dynamically heal the inherent weak points in the microstructure. The fatigue life of the highest strength Aluminum alloys is improved by 25x, and the fatigue strength is raised to ~1/2 the tensile strength. The approach embraces the difference between static and dynamic loading and represents a conceptual change in microstructural design for fatigue.

| S-EPMC7566492 | biostudies-literature

Fatigue-Assisted Grain Growth in Al Alloys.

Project description:Stress-assisted grain growth at room temperature is known for materials with nanocrystalline grains. For larger grain sizes, the grain growth usually takes place at higher homologous temperatures even under stress. Here we report, for the first time, significant grain growth at room temperature under fatigue loading in microcrystalline grains (≥10 μm) in Al 7075. We demonstrate that this grain growth at room temperature is similar to non-uniform grain growth due to grain rotation and coalescence rather than the thermally and the stress-assisted driven grain growth. We show that the grain growth is associated with the formation of a strong near-Cu {112}<111> texture component as a result of fatigue-assisted deformation. These changes in microstructural features (viz., grain size, grain orientations and texture) are fundamentally important in understanding the cyclic crack induced deformation behavior and for predicting the fatigue lifetime in structural materials.

| S-EPMC5579296 | biostudies-literature

Intragranular Dispersion of Carbon Nanotubes Comprehensively Improves Aluminum Alloys.

Project description:The room-temperature tensile strength, toughness, and high-temperature creep strength of 2000, 6000, and 7000 series aluminum alloys can be improved significantly by dispersing up to 1 wt% carbon nanotubes (CNTs) into the alloys without sacrificing tensile ductility, electrical conductivity, or thermal conductivity. CNTs act like forest dislocations, except mobile dislocations cannot annihilate with them. Dislocations cannot climb over 1D CNTs unlike 0D dispersoids/precipitates. Also, unlike 2D grain boundaries, even if some debonding happens along 1D CNT/alloy interface, it will be less damaging because fracture intrinsically favors 2D percolating flaws. Good intragranular dispersion of these 1D strengtheners is critical for comprehensive enhancement of composite properties, which entails change of wetting properties and encapsulation of CNTs inside Al grains via surface diffusion-driven cold welding. In situ transmission electron microscopy demonstrates liquid-like envelopment of CNTs into Al nanoparticles by cold welding.

| S-EPMC6051391 | biostudies-literature

Impeding Nucleation for More Significant Grain Refinement.

Project description:Grain refinement has been a topic of extensive research due to its scientific and technological importance as a common industrial practice for over seven decades. The traditional approach to grain refinement has been to reduce nucleation undercooling by the addition of potent nucleant particles. Here we show both theoretically and experimentally that more significant grain refinement can be achieved through increasing nucleation undercooling by using impotent nucleant particles. Based on the concept of explosive grain initiation, this new approach is illustrated by grain initiation maps and grain refinement maps and validated by experiments. It is anticipated that this new approach may lead to a profound change in both nucleation research and industrial practice well beyond metal casting.

| S-EPMC7287079 | biostudies-literature

Ultrasonic Processing of Aluminum?Magnesium Alloys.

Project description:This study evaluated the effect of UltraSonic Treatment (UST) on a range of Al?Mg alloys. Previous research was carried out on single magnesium compositions. However, the amount and type of the alloy addition are known to affect the grain size even under UST, and the aim of this study was to determine whether or not alloy composition plays a similar role in the case of Al?Mg alloys. By testing binary Al?Mg alloys cast under regular casting conditions and under the presence of an ultrasonic field, it was found that while the addition of Mg solute is important, the amount of solute has little effect when UST is applied. It was observed that the grain size was barely affected by extra solute additions in this condition. This is due to the application of UST during solidification, which resulted in a dramatic reduction in the size of the nucleation free zone thus promoting many more successful nucleation events. Acoustic streaming is proposed as the main cause of this reduction in grain size.

| S-EPMC6213928 | biostudies-other

On the Fatigue Performance of Friction-Stir Welded Aluminum Alloys.

Project description:This work was undertaken in an attempt to ascertain the generic characteristics of fatigue behavior of friction-stir welded aluminum alloys. To this end, different alloy grades belonging to both the heat-treatable and non-heat-treatable types in both the cast and wrought conditions were studied. The analysis was based on the premise that the fatigue endurance of sound welds (in which internal flaws and surface quality are not the major issues) is governed by residual stress and microstructure. Considering the relatively low magnitude of the residual stresses but drastic grain refinement attributable to friction-stir welding, the fatigue performance at relatively low cyclic stress was deduced to be dictated by the microstructural factor. Accordingly, the fatigue crack typically nucleated in relatively coarse-grained base material zone; thus, the fatigue strength of the welded joints was comparable to that of the parent metal. At relatively high fatigue stress, the summary (i.e., the cyclic-plus residual-) stress may exceed the material yield strength; thus, the fatigue cracking should result from the preceding macro-scale plastic deformation. Accordingly, the fatigue failure should occur in the softest microstructural region; thus; the fatigue strength of the welded joint may be inferior to that of the original material.

| S-EPMC7579519 | biostudies-literature

A Review of Dissimilar Welding Techniques for Magnesium Alloys to Aluminum Alloys.

Project description:Welding of dissimilar magnesium alloys and aluminum alloys is an important issue because of their increasing applications in industries. In this document, the research and progress of a variety of welding techniques for joining dissimilar Mg alloys and Al alloys are reviewed from different perspectives. Welding of dissimilar Mg and Al is challenging due to the formation of brittle intermetallic compound (IMC) such as Mg17Al12 and Mg₂Al₃. In order to increase the joint strength, three main research approaches were used to eliminate or reduce the Mg-Al intermetallic reaction layer. First, solid state welding techniques which have a low welding temperature were used to reduce the IMCs. Second, IMC variety and distribution were controlled to avoid the degradation of the joining strength in fusion welding. Third, techniques which have relatively controllable reaction time and energy were used to eliminate the IMCs. Some important processing parameters and their effects on weld quality are discussed, and the microstructure and metallurgical reaction are described. Mechanical properties of welds such as hardness, tensile, shear and fatigue strength are discussed. The aim of the report is to review the recent progress in the welding of dissimilar Mg and Al to provide a basis for follow-up research.

| S-EPMC5453224 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data