Properties of Graphene/Shape Memory Thermoplastic Polyurethane Composites Actuating by Various Methods.

ABSTRACT: Shape memory behavior of crystalline shape memory polyurethane (SPU) reinforced with graphene, which utilizes melting temperature as a shape recovery temperature, was examined with various external actuating stimuli such as direct heating, resistive heating, and infrared (IR) heating. Compatibility of graphene with crystalline SPU was adjusted by altering the structure of the hard segment of the SPU, by changing the structure of the graphene, and by changing the preparation method of the graphene/SPU composite. The SPU made of aromatic 4,4'-diphenylmethane diisocyanate (MSPU) exhibited better compatibility with graphene, having an aromatic structure, compared to that made of the aliphatic hexamethylene diisocyanate. The finely dispersed graphene effectively reinforced MSPU, improved shape recovery of MSPU, and served effectively as a filler, triggering shape recovery by resistive or IR heating. Compatibility was enhanced when the graphene was modified with methanol. This improved shape recovery by direct heating, but worsened the conductivity of the composite, and consequently the efficiency of resistive heating for shape recovery also declined. Graphene modified with methanol was more effective than pristine graphene in terms of shape recovery by IR heating.

SUBMITTER: Park JH

PROVIDER: S-EPMC5453273 | biostudies-other | 2014 Feb

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Mechanical Properties of Nonwoven Reinforced Thermoplastic Polyurethane Composites.

Project description:Reinforcement of flexible fibre reinforced plastic (FRP) composites with standard textile fibres is a potential low cost solution to less critical loading applications. The mechanical behaviour of FRPs based on mechanically bonded nonwoven preforms composed of either low or high modulus fibres in a thermoplastic polyurethane (TPU) matrix were compared following compression moulding. Nonwoven preform fibre compositions were selected from lyocell, polyethylene terephthalate (PET), polyamide (PA) as well as para-aramid fibres (polyphenylene terephthalamide; PPTA). Reinforcement with standard fibres manifold improved the tensile modulus and strength of the reinforced composites and the relationship between fibre, fabric and composite's mechanical properties was studied. The linear density of fibres and the punch density, a key process variable used to consolidate the nonwoven preform, were varied to study the influence on resulting FRP mechanical properties. In summary, increasing the strength and degree of consolidation of nonwoven preforms did not translate to an increase in the strength of resulting fibre reinforced TPU-composites. The TPU composite strength was mainly dependent upon constituent fibre stress-strain behaviour and fibre segment orientation distribution.

| S-EPMC5553526 | biostudies-literature

Influence of Characteristics of Thermoplastic Polyurethane on Graphene-Thermoplastic Polyurethane Composite Film.

Project description:Graphene-thermoplastic polyurethane (G-TPU) composite films were fabricated by traditional blending method and tape casting process with commercial graphene sheets as functional fillers and TPU masterbatches of four different melting points as matrix, respectively. The effects of matrix on the distribution of graphene, the electrical conductivity, and infrared (IR) light thermal properties of the G-TPU composite films were investigated. The experimental results reveal that the characteristics of TPU has little influence on the electrical conductivity of the G-TPU composite films, although the four TPU solutions have different viscosities. However, under the same graphene mass content, the thermal conductivity of four G-TPU composite films with different melting points is significantly different. The four kinds of G-TPU composite films have obvious infrared (IR) thermal effect. There is little difference in the temperatures between the composite films prepared by TPU with melting a point of 100 °C, 120 °C, and 140 °C, respectively; however, when the content of graphene is less than 5 wt%, the temperature of the composite film prepared by TPU with a melting point of 163 °C is obviously lower than that of the other three composite films. The possible reason for this phenomenon is related to the structure of TPU.

| S-EPMC7911175 | biostudies-literature

Construction of Fire Safe Thermoplastic Polyurethane/Reduced Graphene Oxide Hierarchical Composites with Electromagnetic Interference Shielding

Project description: Not available

| S-EPMC11243064 | biostudies-literature

Sustainable Engineered Design and Scalable Manufacturing of Upcycled Graphene Reinforced Polylactic Acid/Polyurethane Blend Composites Having Shape Memory Behavior.

Project description:Material design in shape memory polymers (SMPs) carries significant importance in attaining high performance and adjusting the interface between additive and host polymer matrix to increase the degree of recovery. Herein, the main challenge is to enhance the interfacial interactions to provide reversibility during deformation. The present work describes a newly designed composite structure by manufacturing a high-degree biobased and thermally induced shape memory polylactic acid (PLA)/thermoplastic polyurethane (TPU) blend incorporated with graphene nanoplatelets obtained from waste tires. In this design, blending with TPU enhances flexibility, and adding GNP provides functionality in terms of mechanical and thermal properties by enhancing circularity and sustainability approaches. The present work provides a scalable compounding approach for industrial applications of GNP at high shear rates during the melt mixing of single/blend polymer matrices. By evaluating the mechanical performance of the PLA and TPU blend composite composition at a 9:1 weight percentage, the optimum GNP amount was defined as 0.5 wt%. The flexural strength of the developed composite structure was enhanced by 24% and the thermal conductivity by 15%. In addition, a 99.8% shape fixity ratio and a 99.58% recovery ratio were attained within 4 min, resulting in the spectacular enhancement of GNP attainment. This study provides an opportunity to understand the acting mechanism of upcycled GNP in improving composite formulations and to develop a new perspective on the sustainability of PLA/TPU blend composites with an increased biobased degree and shape memory behavior.

| S-EPMC10007146 | biostudies-literature

High Mechanical and Thermal Properties of Epoxy Composites with Liquid Crystalline Polyurethane Modified Graphene.

Project description:Graphene nanosheets (GNs) often result in incompatibility with the hydrophobic polymer matrix, and the tendency to form aggregates during processing. Herein, liquid crystalline polyurethane modified GNs (GPLP) were obtained by π⁻π stacking interactions between GNs and perylene bisimide derivatives, and then in-situ polymerization of liquid-crystalline polyurethane. Spectroscopic studies, elemental analysis, and thermal properties confirmed the successful π⁻π stacking and the integrated structure of GPLP. The good dispersion state of GPLP in the epoxy matrix (EP), and the strong interactions between GPLP and EP, lead to the significant improvement of the thermal and mechanical performance of the GPLP/EP composites. The impact strength, Young's modulus, tensile strength, and toughness of the GPLP/EP composites with 1.47 wt % GNs reached the highest values of 54.31 kJ/m², 530.8 MPa, 112.33 MPa and 863 J/m³, which significantly increased by 210%, 57%, 143%, and 122% compared to that of neat epoxy, respectively. As well, the glass transition temperature increased by a notable 33 °C. It is hoped that this work can be used to exploit more efficient methods to overcome the poor adhesion between GNs and polymers.

| S-EPMC6415506 | biostudies-literature

The Effect of 4-Octyldecyloxybenzoic Acid on Liquid-Crystalline Polyurethane Composites with Triple-Shape Memory and Self-Healing Properties.

Project description:To better understand shape memory materials and self-healing materials, a new series of liquid-crystalline shape memory polyurethane (LC-SMPU) composites, named SMPU-OOBAm, were successfully prepared by incorporating 4-octyldecyloxybenzoic acid (OOBA) into the PEG-based SMPU. The effect of OOBA on the structure, morphology, and properties of the material has been carefully investigated. The results demonstrate that SMPU-OOBAm has liquid crystalline properties, triple-shape memory properties, and self-healing properties. The incorporated OOBA promotes the crystallizability of both soft and hard segments of SMPU, and the crystallization rate of the hard segment of SMPU decreases when the OOBA-content increases. Additionally, the SMPU-OOBAm forms a two-phase separated structure (SMPU phase and OOBA phase), and it shows two-step modulus changes upon heating. Therefore, the SMPU-OOBAm exhibits triple-shape memory behavior, and the shape recovery ratio decreases with an increase in the OOBA content. Finally, SMPU-OOBAm exhibits self-healing properties. The new mechanism can be ascribed to the heating-induced "bleeding" of OOBA in the liquid crystalline state and the subsequent re-crystallization upon cooling. This successful combination of liquid crystalline properties, triple-shape memory properties, and self-healing properties make the SMPU-OOBAm composites ideal for many promising applications in smart optical devices, smart electronic devices, and smart sensors.

| S-EPMC5457044 | biostudies-other

Fast-Responding Bio-Based Shape Memory Thermoplastic Polyurethanes.

Project description:Novel fast response shape-memory polyurethanes were prepared from bio-based polyols, diphenyl methane diisocyanate and butane diol for the first time. The bio-based polyester polyols were synthesized from 9-hydroxynonanoic acid, a product obtained by ozonolysis of fatty acids extracted from soy oil and castor oil. The morphology of polyurethanes was investigated by synchrotron ultra-small angle X-ray scattering, which revealed the inter-domain spacing between the hard and soft phases, the degree of phase separation, and the level of intermixing between the hard and soft phases. We also conducted thorough investigations of the thermal, mechanical, and dielectric properties of the polyurethanes, and found that high crystallization rate of the soft segment gives these polyurethanes unique properties suitable for shape-memory applications, such as adjustable transition temperatures, high degree of elastic elongations, and good mechanical strength. These materials are also potentially biodegradable and biocompatible, therefore suitable for biomedical and environmental applications.

| S-EPMC5621613 | biostudies-literature

Isocyanate Modified GO Shape-Memory Polyurethane Composite.

Project description:Shape-memory composites have benefits for minimally invasive surgery, but their wider applications for bone repair are hindered by conflicts between the mechanical and memory performances, especially at load-bearing locations. In this study, we fabricated a graphene oxide shape-memory polyurethane composite through the chemical combination of graphene oxide and isocyanate, in order to realize satisfactory mechanical and shape-memory effects. As desired, a modulus of ~339 MPa and a shape recovery ratio of 98% were achieved, respectively, in the composite. In addition, finite element analysis demonstrated that, after being implanted in a defective bone through a minimally invasive treatment, where the highest stress was distributed at the implant-bone interface, this composite could offer a generated force during the recovery process. Furthermore, we also discuss the origins of the improved mechanical and memory properties of the composites, which arise from increased net-points and the stable molecular structure inside. Therefore, with its superior structure and properties, we envision that this shape-memory composite can provide new insights toward the practical application of shape-memory polymers and composites in the field of bone repair.

| S-EPMC7022938 | biostudies-literature

Mechanical and Shape Memory Properties of Additively Manufactured Polyurethane (PU)/Halloysite Nanotube (HNT) Nanocomposites.

Project description:This paper investigates the impact of halloysite nanotube (HNT) content on mechanical and shape memory properties of additively manufactured polyurethane (PU)/HNT nanocomposites. The inclusion of 8 wt% HNTs increases their tensile strength by 30.4% when compared with that of virgin PU at 44.75 MPa. Furthermore, consistently significant increases in tensile modulus, compressive strength and modulus, as well as specific energy absorption are also manifested by 47.2%, 34.0%, 125% and 72.7% relative to neat PU at 2.29 GPa, 3.88 MPa, 0.28 GPa and 0.44 kJ/kg respectively. However, increasing HNT content reduces lateral strain due to the restricted mobility of polymeric chains, leading to a decrease in negative Poisson's ratio (NPR). As such, shape recovery ratio and time of PU/HNT nanocomposites are reduced by 9 and 45% with the inclusion of 10 wt% HNTs despite an increasing shape fixity ratio up to 12% relative to those of neat PU.

| S-EPMC11357460 | biostudies-literature

Bactericidal ZnO glass-filled thermoplastic polyurethane and polydimethyl siloxane composites to inhibit biofilm-associated infections.

Project description:This study investigates a novel approach to controlling biofilms of the most frequent pathogens implicated in the etiology of biomaterials-associated infections. New bactericidal filler based on a non-toxic glass, belonging to B2O3-SiO2-Al2O3-Na2O-ZnO system, was used to formulate composites of the most widely used polymers in biomedical applications [i.e. thermoplastic polyurethane (TPU) and polydimethyl siloxane (PDMS)], with varying percentage by weight of the bactericidal glass (5, 15, 25, 35, 50%). Glass-filled polymer composites show dramatically restricted bacterial colonisation and biofilm formation. They exhibit time- and dose-dependent killing, with maximal action at 5 days. The highest activity was found against S.epidermidis biofilm (99% of reduction), one of the most common cause of nosocomial infections. The tensile properties of the obtained glass-filled composites are comparable with the literature data concerning polymeric biomaterials for medical implants and devices. In addition, all the materials presented in this research, revealed an excellent biocompatibility. This was disclosed by cell viability values above 70%, none alteration on erythrocyte membrane or cell functionality in contact with materials (haemolytic index 0-2%), and absence of interferences in blood coagulation (intrinsic, extrinsic and final pathways).

| S-EPMC6391378 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data