A New Epoxy-Based Layered Silicate Nanocomposite Using a Hyperbranched Polymer: Study of the Curing Reaction and Nanostructure Development.

ABSTRACT: Polymer layered silicate (PLS) nanocomposites have been prepared with diglycidyl ether of bisphenol-A (DGEBA) epoxy resin as the matrix and organically modified montmorillonite (MMT) as the clay nanofiller. Resin-clay mixtures with different clay contents (zero, two, five and 10 wt%) were cured, both isothermally and non-isothermally, using a poly(ethyleneimine) hyperbranched polymer (HBP), the cure kinetics being monitored by differential scanning calorimetry (DSC). The nanostructure of the cured nanocomposites was characterized by small angle X-ray scattering (SAXS) and transmission electron microscopy (TEM), and their mechanical properties were determined by dynamic mechanical analysis (DMA) and impact testing. The results are compared with an earlier study of the structure and properties of the same DGEBA-MMT system cured with a polyoxypropylene diamine, Jeffamine. There are very few examples of the use of HBP as a curing agent in epoxy PLS nanocomposites; here, it is found to enhance significantly the degree of exfoliation of these nanocomposites compared with those cured with Jeffamine, with a corresponding enhancement in the impact energy for nanocomposites with the low clay content of 2 wt%. These changes are attributed to the different cure kinetics with the HBP, in which the intra-gallery homopolymerization reaction is accelerated, such that it occurs before the bulk cross-linking reaction.

SUBMITTER: Cortes P

PROVIDER: S-EPMC5453289 | biostudies-other | 2014 Mar

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Cold-Curing Structural Epoxy Resins: Analysis of the Curing Reaction as a Function of Curing Time and Thickness.

Project description:The curing reaction of a commercial cold-curing structural epoxy resin, specifically formulated for civil engineering applications, was analyzed by thermal analysis as a function of the curing time and the sample thickness. Original and remarkable results regarding the effects of curing time on the glass transition temperature and on the residual heat of reaction of the cold-cured epoxy were obtained. The influence of the sample thickness on the curing reaction of the cold-cured resin was also deeply investigated. A highly exothermal reaction, based on a self-activated frontal polymerization reaction, was supposed and verified trough a suitable temperature signal acquisition system, specifically realized for this measurement. This is one of the first studies carried out on the curing behavior of these peculiar cold-cured epoxy resins as a function of curing time and thickness.

| S-EPMC5456125 | biostudies-other

Curing Behavior, Rheological, and Thermal Properties of DGEBA Modified with Synthesized BPA/PEG Hyperbranched Epoxy after Their Photo-Initiated Cationic Polymerization.

Project description:This paper investigates the photo-initiated cationic polymerization of diglycidyl ether of bisphenol A (DGEBA) modified with bisphenol A (BPA)/polyethylene glycol (PEG) hyperbranched epoxy resin. The relationship between curing behavior, rheological, and thermal properties of the modified DGEBA is investigated using photo-differential scanning calorimetry (DSC) and photo-rheometer techniques. It is seen that the addition of the hyperbranched epoxy resin can increase UV conversion (αUV) and reduce gelation time (tgel). After photo-initiation polymerization (dark reaction) occurred, a second exothermic peak in the DSC thermogram takes place: namely, the occurrence of curing reaction owing to the activated monomer (AM) mechanism. Consequently, the glass transition temperature decreased, and at the same time, UV intensity increased which was due to the molecular weight between crosslinking points (Mc). Furthermore, the radius of gyration (Rg) of the network segment is determined via small-angle X-ray scattering (SAXS). It is noted that the higher the Mc, the larger the radius of gyration proves to be, resulting in low glass transition temperature.

| S-EPMC7599708 | biostudies-literature

Reaction mechanism, cure behavior and properties of a multifunctional epoxy resin, TGDDM, with latent curing agent dicyandiamide.

Project description:A novel resin system was prepared using the glycidyl amide type multifunctional epoxy resin N,N,N',N'-tetraglycidyl-4,4'-diaminodiphenylmethane (TGDDM) and latent curing agent dicyandiamide (DICY). The curing reaction mechanism of the TGDDM/DICY system was studied by Fourier transform infrared (FTIR) spectrometry and the non-isothermal cure behaviors of the mixture were investigated with differential scanning calorimetry (DSC) measurements. The FTIR results demonstrated that there were two main reactions occurring in the curing process of the TGDDM/DICY system. The DSC thermogram of the blend exhibited two different cure regimes in the temperature range of 140-358 °C, and the system experienced two autocatalytic curing processes with α = 0.45 as the boundary; the corresponding average activation energies calculated by the Kissinger method were 69.7 and 88.7 kJ mol-1, respectively. In addition, the correlation between activation energy E a and fractional conversion α was determined by applying model-free isoconversional analysis with Flynn-Wall-Ozawa (FWO) and Starink methods. Results showed that both methods revealed similar trends and possessed approximately the same values at each fractional conversion. Activation energy varied greatly with fractional conversion and the possible causes behind the variations were analyzed in detail. The cured TGDDM/DICY exhibited outstanding mechanical and adhesive properties with tensile and shear strengths of 27.1 MPa at 25 °C and12.6 MPa at 200 °C, good dielectric properties with a low dielectric constant of 3.26 at 1000 kHz and a low water absorption of 0.41%.

| S-EPMC9078540 | biostudies-literature

Heterogeneous dynamics in the curing process of epoxy resins.

Project description:Epoxy resin is indispensable for modern industry because of its excellent mechanical properties, chemical resistance, and excellent moldability. To date, various methods have been used to investigate the physical properties of the cured product and the kinetics of the curing process, but its microscopic dynamics have been insufficiently studied. In this study, the microscopic dynamics in the curing process of a catalytic epoxy resin were investigated under different temperature conditions utilizing X-ray photon correlation spectroscopy. Our results revealed that the temperature conditions greatly affected the dynamical heterogeneity and cross-linking density of the cured materials. An overview of the microscopic mechanism of the curing process was clearly presented through comparison with the measurement results of other methods, such as 1H-pulse nuclear magnetic resonance spectroscopy. The quantification of such heterogeneous dynamics is particularly useful for optimizing the curing conditions of various materials to improve their physical properties.

| S-EPMC8129072 | biostudies-literature

Accelerating the Curing of Hybrid Poly(Hydroxy Urethane)-Epoxy Adhesives by the Thiol-Epoxy Chemistry.

Project description:The polyaddition between dicyclic carbonates and diamines leading to poly(hydroxy urethane)s (PHUs) has emerged as the preferred method for the synthesis of green, non-isocyanate polyurethanes. However, when proposed for use as structural adhesives, the long times for completion of aminolysis of the 5-membered cyclic carbonates under ambient conditions force the use of complementary chemistries to accelerate the curing process. In this work, a system that combines an amino-terminated PHU (NH2-PHU-NH2), an epoxy resin, and a thiol compound was employed to develop high-shear strength PHU-epoxy hybrid adhesives able to cure at room temperature in short times. A NH2-PHU-NH2 prepolymer synthesized by using a sub-stoichiometric quantity of dicyclic carbonates was mixed with a bisphenol A-based epoxy resin for the preparation of the structural adhesive. While this adhesive showed good lap-shear strength and shear resistance under static load and temperature, the curing process was slow. In order to speed up the curing process, a thiol (trimethylolpropane tris(3-mercapto propionate)) was added and its impact on the curing process as well as on the adhesive properties was evaluated. The trifunctional thiol additive allowed for faster curing in the presence of the 1,1,3,3-tetramethylguanidine basic catalyst. Moreover, a combination of NH2-PHU-NH2 and the thiol as curing agents for the epoxy resin resulted in adhesives with superior toughness, without any deterioration of the ultimate lap-shear strength or shear resistance under load and temperature, making these adhesives suitable for high-demand applications in the automotive industry.

| S-EPMC9745729 | biostudies-literature

Synthesis of a Degradable High-Performance Epoxy-Ended Hyperbranched Polyester.

Project description:Degradation and recycling of cured thermosetting epoxy resins are major challenges to the industry. Here, a low-viscosity, degradable epoxy-ended hyperbranched polyester (DEHP) is synthesized by a reaction between epichlorohydrin and a carboxyl-ended hyperbranched polyester (DCHP) obtained from an esterification between citric acid and maleic anhydride. The chemical structures of DCHP and DEHP were characterized by Fourier transform infrared and 1H NMR. DEHP has a positive effect on reinforcing and toughening of the diglycidyl ether of bisphenol-A (DGEBA). With an increase in the content and molecular weight of DEHP, the mechanical performances of the cured DEHP/DGEBA composites, including the tensile, flexural, and impact strengths, increase first and then decrease. The improvements on the tensile, flexural, and impact strengths were 34.2-43.4%, 35.6-48.1%, and 117.9-137.8%, respectively. Moreover, the DEHP also promotes degradation of the cured DEHP/DGEBA composites. The degree of degradation of the cured DEHP/DGEBA composites increases with an increase of the DEHP content and molecular weight. The composites containing 12 wt % DEHP can be degraded completely in only about 2 h at about 90 °C, compared with the degradation degree (35%) of cured DGEBA, indicating good degradation and recycling properties of the DEHP.

| S-EPMC6640995 | biostudies-literature

Curing and Molecular Dynamics Simulation of MXene/Phenolic Epoxy Composites with Different Amine Curing Agent Systems.

Project description:Herein, the curing kinetics and the glass transition temperature (Tg) of MXene/phenolic epoxy composites with two curing agents, i.e., 4,4-diaminodiphenyl sulfone (DDS) and dicyandiamine (DICY), are systematically investigated using experimental characterization, mathematical modeling and molecular dynamics simulations. The effect of MXene content on an epoxy resin/amine curing agent system is also studied. These results reveal that the MXene/epoxy composites with both curing agent systems conform to the SB(m,n) two-parameter autocatalytic model. The addition of MXene accelerated the curing of the epoxy composite and increased the Tg by about 20 K. In addition, molecular dynamics were used to simulate the Tg of the cross-linked MXene/epoxy composites and to analyze microstructural features such as the free volume fraction (FFV). The simulation results show that the introduction of MXene improves the Tg and FFV of the simulated system. This is because the introduction of MXene restricts the movement of the epoxy/curing agent system. The conclusions are in good agreement with the experimental results.

| S-EPMC9268527 | biostudies-literature

Tetrafunctional Epoxy Resin-Based Buoyancy Materials: Curing Kinetics and Properties.

Project description:In order to synthesize a new kind of buoyancy material with high-strength, low-density and low-water-absorption and to study the curing reaction of tetraglycidylamine epoxy resin with an aromatic amine curing agent, the non-isothermal differential scanning calorimeter (DSC) method is used to calculate the curing kinetics parameters of N,N,N',N'-tetraepoxypropyl-4,4'-diaminodiphenylmethane epoxy resin (AG-80) and the m-xylylenediamine (m-XDA) curing process. Further, buoyancy materials with different volume fractions of hollow glass microsphere (HGM) compounded with a AG-80 epoxy resin matrix were prepared and characterized. The curing kinetics calculation results show that, for the curing reaction of the AG-80/m-XDA system, the apparent activation energy increases with the conversion rates increasing and the reaction model is the Jander equation (three-dimensional diffusion, 3D, n = 1/2). The experimental results show that the density, compressive strength, saturated water absorption and water absorption rate of the composite with 55 v % HGM are 0.668 g·cm-3, 107.07 MPa, 0.17% and 0.025 h-1/2, respectively. This kind of composite can probably be used as a deep-sea buoyancy material.

| S-EPMC7463793 | biostudies-literature

Development of Cycloaliphatic Epoxy-POSS Nanocomposite Matrices with Lambas Enhanced Resistance to Atomic Oxygen.

Project description:The preparation of ultra-thin CFRP laminates, which incorporate a cycloaliphatic epoxy resin reinforced with polyhedral oligomeric silsesquioxane (POSS) reagent nanofiller, using out-of-autoclave procedure is reported. The influence of the amount of POSS within the laminate on the mechanical properties and surface roughness of the laminates is analysed before and after exposure to atomic oxygen (AO) to simulate the effects of low Earth orbit (LEO). The addition of 5 wt% POSS to the base epoxy leads to an increase in both flexural strength and modulus, but these values begin to fall as the POSS content rises, possibly due to issues with agglomeration. The addition of POSS offers improved resistance against AO degradation with the laminates containing 20 wt% POSS demonstrating the lowest erosion yield (1.67 × 10-24 cm2/atom) after the equivalent of a period of 12 months in a simulated LEO environment. Exposure to AO promotes the formation of a silicon-rich coating layer on the surface of the laminate, which in turn reduces roughness and increases stiffness, as evidenced by measurements of flexural properties and spectral data after exposure.

| S-EPMC7180924 | biostudies-literature

Novel Approaches to In-Situ ATR-FTIR Spectroscopy and Spectroscopic Imaging for Real-Time Simultaneous Monitoring Curing Reaction and Diffusion of the Curing Agent at Rubber Nanocomposite Surface.

Project description:Here, we propose a novel attenuated total reflection Fourier transform infrared (ATR-FTIR) spectroscopy method for simultaneously monitoring the curing reaction and the diffusion behavior of curing agents at the surface of rubber in real-time. The proposed scheme was demonstrated by fluorine rubber (FKM) and FKM/carbon nanotube (CNT) nanocomposites with a target curing agent of triallyl-isocyanurate (TAIC). The broadening and the evolution of the C=O stretching of TAIC were quantitatively analyzed to characterize the reaction and the diffusion. Changes in the width of the C=O stretching indicated the reaction rate at the surface was even faster than that of the bulk as measured by a curemeter. The diffusion coefficient of the curing agent in the course of heating was newly calculated by the initial increase in the absorbance and our model based on Fickian diffusion. The diffusion coefficients of TAIC during curing were evaluated, and its temperature and filler dependency were identified. Cross-sectional ATR-FTIR imaging and in situ ATR-FTIR imaging measurements supported the hypothesis of the unidirectional diffusion of the curing agent towards the heated surface. It was shown that our method of in situ ATR-FTIR can monitor the degrees of cure and the diffusion coefficients of curing agents simultaneously, which cannot be achieved by conventional methods, e.g., rheological measurements.

| S-EPMC8433895 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data